JP2018518433A - ハロゲン化カーボン及びその製造方法 - Google Patents
ハロゲン化カーボン及びその製造方法 Download PDFInfo
- Publication number
- JP2018518433A JP2018518433A JP2017549544A JP2017549544A JP2018518433A JP 2018518433 A JP2018518433 A JP 2018518433A JP 2017549544 A JP2017549544 A JP 2017549544A JP 2017549544 A JP2017549544 A JP 2017549544A JP 2018518433 A JP2018518433 A JP 2018518433A
- Authority
- JP
- Japan
- Prior art keywords
- carbon
- halogenated
- halogenated carbon
- alcohol
- alkaline earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の第1の実施形態では、フッ化カーボンをグラムスケールで製造する好適な方法が提供される。この好適な方法は、フッ素含有アルコール(フッ化アルコールとも称する)とナトリウム金属のソルボサーマル反応を含む。これにより生成されたフッ化カーボンは、超撥水性(超疎水性)及び親油性を示す。
本発明の第2の実施形態では、フッ化アルコールとナトリウムを反応させてフッ化ナトリウムアルコキシドを生成する。この第2の実施形態では、フッ化アルコールとナトリウムとの反応は、フッ化ナトリウムアルコキシドの熱分解を引き起こさない温度(例えば室温)で行う。フッ化ナトリウムアルコキシドを、粉体(例えば、カーボンブラック粉体、無機粒子、金属粉体、金属酸化物粉体など)と混合させるか、または材料(例えば、シリコン、ガラス、金属酸化物、金属など)の表面に堆積させ、次いで、熱的にアニール(即ち分解)してフッ化カーボンを形成する。これを例えば50/50%の水/エタノール混合液中で洗浄すると、材料の表面または粉体が撥水性のフッ化カーボン薄層でコーティングされた複合材料が得られる。
本発明の第3の実施形態では、フッ化アルコールを、粉体(例えば、カーボンブラック粉体、無機粒子、金属粉体、金属酸化物粉体など)と混合させるか、または材料(例えば、シリコン、ガラス、金属酸化物、金属など)の表面に堆積させ、次いで、ナトリウムと反応させた後に、当該反応により生じたアルコキシドを熱分解してフッ化カーボンを生成する。これを例えば50/50%の水/エタノール混合液中で洗浄すると、材料の表面または粉体が撥水性のフッ化カーボン薄層でコーティングされた複合材料が得られる。
以下の実施例は、本発明の説明を目的とするものであり、本発明の限定と解釈されるべきではない。以下の実施例では、全ての化学物質は、供給業者から入手したものを、さらに精製することなく使用した。
C6F13CH2CH2OH+Na---[180°C、分解]--->CFx+H2+HF+NaF+NaO(H)
Claims (19)
- 中空シェル構造を有するナノスケール粒子を含み、前記ナノスケール粒子のシェルがカーボン及びハロゲンを含むハロゲン化カーボン。
- 前記ハロゲンがフッ素を含むことを特徴とする請求項1に記載のハロゲン化カーボン。
- 当該ハロゲン化カーボンが液体分散媒中に分散されていることを特徴とする請求項1に記載のハロゲン化カーボン。
- 前記液体分散媒がエタノールを含むことを特徴とする請求項3に記載のハロゲン化カーボン。
- 当該ハロゲン化カーボンが別の材料の表面または粉体をコーティングしていることを特徴とする請求項1に記載のハロゲン化カーボン。
- アルカリ金属、アルカリ土類金属またはそれらの水素化物とハロゲン化アルコールを反応させ、その後に、前記反応の生成物を熱分解することを含むハロゲン化カーボンの製造方法。
- 前記ハロゲン化アルコールがフッ化アルコールを含むことを特徴とする請求項6に記載の方法。
- 前記アルカリまたはアルカリ土類金属がナトリウムを含むことを特徴とする請求項6に記載の方法。
- 前記アルカリ金属、アルカリ土類金属またはそれらの水素化物と前記ハロゲン化アルコールの前記反応を、前記熱分解を引き起こすのに十分な高い温度で行うことを特徴とする請求項6に記載の方法。
- 前記熱分解によって得られた前記ハロゲン化カーボンを液体分散媒中に分散させる工程を更に含むことを特徴とする請求項6に記載の方法。
- 前記液体分散媒がエタノールを含むことを特徴とする請求項10に記載の方法。
- 前記アルカリ金属、アルカリ土類金属またはそれらの水素化物と前記ハロゲン化アルコールとの前記反応の前記生成物を、前記熱分解の前に、別の材料の表面にコーティングするまたは粉体と混合させることを特徴とする請求項6に記載の方法。
- 前記ハロゲン化アルコールを前記アルカリ金属、アルカリ土類金属またはそれらの水素化物と反応させる前に、前記ハロゲン化アルコールを別の材料の表面にコーティングするまたは粉体と混合させることを特徴とする請求項6に記載の方法。
- アルカリ金属、アルカリ土類金属またはそれらの水素化物とハロゲン化アルコールを反応させ、その後、前記反応の生成物を熱分解することによって生成されたハロゲン化カーボン。
- 前記ハロゲン化アルコールがフッ化アルコールを含むことを特徴とする請求項14に記載のハロゲン化カーボン。
- 前記アルカリまたはアルカリ土類金属がナトリウムを含むことを特徴とする請求項14に記載のハロゲン化カーボン。
- 当該ハロゲン化カーボンが液体分散媒中に分散されていることを特徴とする請求項14に記載のハロゲン化カーボン。
- 前記液体分散媒がエタノールを含むことを特徴とする請求項17に記載のハロゲン化カーボン。
- 当該ハロゲン化カーボンが別の材料の表面または粉体をコーティングしていることを特徴とする請求項14に記載のハロゲン化カーボン。