JP2017143043A - 高分子化合物、中間組成物、負極電極、蓄電装置、負極電極用スラリー、高分子化合物の製造方法、及び負極電極の製造方法 - Google Patents
高分子化合物、中間組成物、負極電極、蓄電装置、負極電極用スラリー、高分子化合物の製造方法、及び負極電極の製造方法 Download PDFInfo
- Publication number
- JP2017143043A JP2017143043A JP2016025070A JP2016025070A JP2017143043A JP 2017143043 A JP2017143043 A JP 2017143043A JP 2016025070 A JP2016025070 A JP 2016025070A JP 2016025070 A JP2016025070 A JP 2016025070A JP 2017143043 A JP2017143043 A JP 2017143043A
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- group
- polymer compound
- polyacrylic acid
- lithium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
請求項2に記載の発明は、蓄電装置の負極用バインダーとして用いられる高分子化合物であって、ポリアクリル酸により構成される鎖状構造と、前記鎖状構造内又は鎖状構造間におけるカルボキシル基同士を接続する架橋構造とを有し、前記架橋構造は、下記一般式(2)〜(4)から選ばれる少なくとも一種の架橋構造であり、前記鎖状構造は、フリーのカルボキシル基と、リチウム塩化されたカルボキシル基とを有することを特徴とする。
請求項3に記載の発明は、請求項1又は請求項2に記載の高分子化合物において、前記フリーのカルボキシル基と前記リチウム塩化されたカルボキシル基との比率が95:5〜25:75の範囲であることを特徴とする。
請求項5に記載の発明は、請求項4に記載の中間組成物において、前記ポリアクリル酸に由来するカルボキシル基の総数を「C」、前記ポリアクリル酸に由来するカルボキシル基のうち、リチウム塩化されたカルボキシル基の総数を「LC」、多官能アミンに由来するアミノ基の総数を「A」としたとき、「「LC」/(「C」−「A」)×100」により求められるリチウム化度が5〜50%の範囲であり、前記混合溶媒における非水溶媒と水との混合割合が2:1〜1:2の範囲であることを特徴とする。
請求項8に記載の発明は、蓄電装置の負極電極であって、請求項1〜3のいずれか一項に記載の高分子化合物を含有する負極用バインダーと、負極活物質とを備え、前記負極活物質は、リチウムを吸蔵及び放出し得る炭素系材料、リチウムと合金化可能な元素、及びリチウムと合金化可能な元素を有する化合物から選ばれる少なくとも一種であることを特徴とする。
請求項10に記載の発明は、蓄電装置の負極電極の製造に用いられる負極電極用スラリーであって、請求項4〜6のいずれか一項に記載の中間組成物と、負極活物質とを含有し、前記負極活物質として、リチウムを吸蔵及び放出し得る炭素系材料、リチウムと合金化可能な元素、及びリチウムと合金化可能な元素を有する化合物から選ばれる少なくとも一種を含有することを特徴とする。
Yが直鎖アルキル基である多官能アミンとしては、例えば、3,3’−ジアミノジフェニルメタン、4,4’−ジアミノジフェニルメタン、3,4’−ジアミノジフェニルメタン、4,4’−エチレンジアニリン、4,4’−ジアミノ−3,3’−ジメチルジフェニルメタン、1,1−ビス(4−アミノフェニル)シクロヘキサン、9、9−ビス(4−アミノフェニル)フルオレン、2,2’−ビス(4−アミノフェニル)ヘキサフルオロプロパン、4,4’−ジアミノベンゾフェノン、4,4’−メチレンビス(2−エチル−6−メチルアニリン)、パラローズアニリンが挙げられる。
「C」 :リチウム化ポリアクリル酸に由来するカルボキシル基の総数(リチウム塩化されたカルボキシル基を含む。)
「LC」:リチウム化ポリアクリル酸に由来するカルボキシル基のうち、リチウム塩化されたカルボキシル基の総数
「A」 :多官能アミンに由来するアミノ基の総数
例えば、(A)リチウム化ポリアクリル酸のリチウム化度が5〜50%の範囲である場合には、非水溶媒と水との混合割合を2:1〜1:2の範囲とすることが好ましい。また、(A)リチウム化ポリアクリル酸のリチウム化度が50〜75%の範囲である場合には、非水溶媒と水との混合割合を1:1〜1:2の範囲とすることが好ましい。
例えば、第2の架橋構造を更に有する高分子化合物として、(A)リチウム化ポリアクリル酸と(B)一般式(1)で示される多官能アミンと、その他の多官能アミンとが縮合してなる高分子化合物であってもよい。この場合、一般式(1)で示される多官能アミン由来の架橋構造に加えて、その他の多官能アミン由来の第2の架橋構造を更に有する高分子化合物となる。この第2の架橋構造を付加することにより、高分子化合物の強度や柔軟性等の物性を調整することができる。
まず、負極活物質、負極用バインダー、溶剤を混合してスラリーを調製する。その際、必要に応じて導電助剤等の他の成分を更に混合してもよい。
また、負極用バインダーとして、他の負極用バインダーを併用してもよい。他の負極用バインダーとしては、例えば、ポリフッ化ビニリデン、ポリ四フッ化エチレン、スチレン−ブタジエンゴム、ポリイミド、ポリアミドイミド、カルボキシメチルセルロース、ポリ塩化ビニル、メタクリル樹脂、ポリアクリロニトリル、変性ポリフェニレンオキシド、ポリエチレンオキシド、ポリエチレン、ポリプロピレン、ポリアクリル酸、フェノール樹脂が挙げられる。
(1)本実施形態の高分子化合物は、(A)リチウム化ポリアクリル酸と、(B)多官能アミンとが縮合してなる化合物であって、リチウム化ポリアクリル酸により構成される鎖状構造は、フリーのカルボキシル基と、リチウム塩化されたカルボキシル基とを有する。また、本実施形態の高分子化合物は、ポリアクリル酸により構成される鎖状構造と、鎖状構造内又は鎖状構造間におけるカルボキシル基同士を接続する架橋構造とを有し、架橋構造は、上記一般式(2)〜(4)から選ばれる少なくとも一種の架橋構造である。鎖状構造は、フリーのカルボキシル基と、リチウム塩化されたカルボキシル基とを有する。
上記構成によれば、架橋構造内に運動が可能な部分構造を有するため、高分子化合物の伸縮性が向上する。これにより、本実施形態の高分子化合物を用いた負極用バインダーは、リチウム等の吸蔵及び放出に伴う膨張及び収縮による体積変化に対して追従しやすくなる。その結果、蓄電装置の特性が高められる。
<試験1>
リチウム化ポリアクリル酸と、特定の分子構造を有する多官能アミンとを縮合してなる高分子化合物を負極用バインダーとして用いた場合における蓄電装置の電池特性を評価した。
(実施例1A:PAA+4,4’−ジアミノジフェニルメタン、リチウム化度10%)
重量平均分子量50,000のPAAを水に溶解させて、30質量%のPAA水溶液を調製し、このPAA水溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。フラスコ内に水酸化リチウム1水和物0.131mg(3.12mmol)を加えて、室温にて30分間撹拌することにより、PAA水溶液に含まれるPAAのカルボキシル基の一部をリチウム塩化した。別途、4,4’−ジアミノジフェニルメタン1.03g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、実施例1Aの中間組成物を、NMPと水との混合溶媒(NMP:水=2:1)に対する溶液の状態で得た。実施例1の中間組成物のリチウム化度は、下記式により算出することができ、その値は10%である。
(実施例1B:PAA+4,4’−ジアミノジフェニルメタン、リチウム化度20%)
水酸化リチウム1水和物の添加量を0.262mg(6.24mmol)に変更した点を除いて、実施例1Aと同様の方法により、実施例1Bの中間組成物を溶液の状態で得た。実施例1Bの中間組成物のリチウム化度は20%である。
水酸化リチウム1水和物の添加量を0.655mg(15.6mmol)に変更した点を除いて、実施例1Aと同様の方法により、実施例1Cの中間組成物を溶液の状態で得た。実施例1Cの中間組成物のリチウム化度は50%である。
重量平均分子量50,000のPAAをNMPに溶解させて、30質量%のPAA/NMP溶液を調製し、このPAA/NMP溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。別途、4,4’−ジアミノジフェニルメタン1.03g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、参考例1の中間組成物を溶液の状態で得た。参考例1の中間組成物のリチウム化度は0%である。
重量平均分子量50,000のPAAを水に溶解させて、30質量%のPAA水溶液を調製し、このPAA水溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。フラスコ内に水酸化リチウム1水和物0.131mg(3.12mmol)を加えて、室温にて30分間撹拌することにより、PAA水溶液に含まれるPAAのカルボキシル基の一部をリチウム塩化した。別途、1,6−ジアミノヘキサン0.603g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、参考例2の中間組成物を溶液の状態で得た。参考例2の中間組成物のリチウム化度は10%である。
得られた実施例の中間組成物を用いて、各中間組成物から得られる高分子化合物を負極用バインダーとする電極シートを作製した。そして、得られた電極シートを用いてリチウムイオン二次電池を作製し、そのリチウムイオン二次電池の電池特性を評価した。
(リチウムイオン二次電池の作製)
電極シートを直径11mmの円形に裁断してなる負極電極(評価極)と、厚さ500μmの金属リチウム箔を直径13mmの円形に裁断してなる正極電極との間にセパレータを挟装して電極体電池とした。電池ケース内に、電極体電池を収容するとともに非水電解質を注入して、電池ケースを密閉することにより、リチウムイオン二次電池を得た。なお、セパレータとしては、ヘキストセラニーズ社製ガラスフィルター及びセルガード社製celgard2400を用いた。非水電解質としては、エチレンカーボネートとジエチルカーボネートとを体積比1:1で混合した混合溶媒に、ヘキサフルオロリン酸リチウムを1Mの濃度となるように溶解させた非水電解質を用いた。
得られたリチウムイオン二次電池について、直流電流0.2mAで負極電極における正極電極に対する電圧が0.01Vになるまで放電を行い、放電が終了してから10分後に、直流電流0.2mAで負極電極における正極電極に対する電圧が1.0Vになるまで充電を行った。このときの放電容量を初期放電容量とするとともに、充電容量を初期充電容量とした。そして、下記式に基づいて初期効率を算出した。その結果を表1に示す。
また、上記の放電及び充電を1サイクルとして、0℃又は25℃において、規定サイクルの充放電を行い、下記式に基づいてサイクル特性を算出した。その結果を表1に示す。
次に、リチウム化PAAと、特定の分子構造を有する多官能アミンとを縮合してなる高分子化合物を負極用バインダーとして用いた場合において、多官能アミンの種類を異ならせた場合における蓄電装置の電池特性の変化について評価した。
重量平均分子量50,000のPAAを水に溶解させて、30質量%のPAA水溶液を調製し、このPAA水溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。フラスコ内に水酸化リチウム1水和物0.131mg(3.12mmol)を加えて、室温にて30分間撹拌することにより、PAA水溶液に含まれるPAAのカルボキシル基の一部をリチウム塩化した。別途、4,4’−ジアミノジフェニルエーテル1.039g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、実施例2の中間組成物を溶液の状態で得た。実施例2の中間組成物のリチウム化度は10%である。
重量平均分子量50,000のPAAを水に溶解させて、30質量%のPAA水溶液を調製し、このPAA水溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。フラスコ内に水酸化リチウム1水和物0.131mg(3.12mmol)を加えて、室温にて30分間撹拌することにより、PAA水溶液に含まれるPAAのカルボキシル基の一部をリチウム塩化した。別途、1,3,5−トリス(4−アミノフェニル)ベンゼン1.824g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、実施例3の中間組成物を溶液の状態で得た。実施例3の中間組成物のリチウム化度は10%である。
重量平均分子量50,000のPAAを水に溶解させて、30質量%のPAA水溶液を調製し、このPAA水溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。フラスコ内に水酸化リチウム1水和物0.131mg(3.12mmol)を加えて、室温にて30分間撹拌することにより、PAA水溶液に含まれるPAAのカルボキシル基の一部をリチウム塩化した。別途、3,3’−ジアミノジフェニルメタン1.029g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、実施例4の中間組成物を溶液の状態で得た。実施例4の中間組成物のリチウム化度は10%である。
重量平均分子量50,000のPAAを水に溶解させて、30質量%のPAA水溶液を調製し、このPAA水溶液10g(PAAのモノマー換算で41.6mmol)を窒素雰囲気下のフラスコ内に分取した。フラスコ内に水酸化リチウム1水和物0.131mg(3.12mmol)を加えて、室温にて30分間撹拌することにより、PAA水溶液に含まれるPAAのカルボキシル基の一部をリチウム塩化した。別途、4,4’−エチレンジアニリン1.101g(5.19mmol)をNMP14gに溶解させて、多官能アミン/NMP溶液を調製した。フラスコ内に多官能アミン/NMP溶液を滴下して、室温にて30分間撹拌した。その後、ディーン・スターク装置を用いて、110℃にて2時間、加熱処理(予備加熱処理)することにより、実施例5の中間組成物を溶液の状態で得た。実施例5の中間組成物のリチウム化度は10%である。
得られた実施例2〜5の中間組成物を用いて、各中間組成物から得られる高分子化合物を負極用バインダーとする電極シートを作製した。また、得られた電極シートを用いてリチウムイオン二次電池を作製し、そのリチウムイオン二次電池の電池特性を評価した。その結果を表2に示す。なお、電極シート及びリチウムイオン二次電池の作成方法、並びにリチウムイオン二次電池の電池特性の評価方法は、試験1の方法と同じである。
次に、リチウム化PAAと、特定の分子構造を有する多官能アミンと、非水溶媒と水の混合溶媒とを含有する中間組成物に関して、リチウム化度及び混合溶媒混合溶媒の混合比率を異ならせた場合における溶解性の変化について評価した。
次に、実施例1Bの中間組成物(PAA+4,4’−ジアミノジフェニルメタン、リチウム化度20%)、及び参考例1の中間組成物(PAA+4,4’−ジアミノジフェニルメタン、リチウム化度0%)について、加熱処理による分子構造の変化を熱走査赤外分光測定により分析した。
測定温度:昇温速度5℃/分にて室温から180℃まで上昇させ、180℃の状態を2時間保持した。その後、昇温速度5℃/分にて180℃から200℃まで上昇させ、200℃の状態を2時間保持した。
積算回数:512回
波数範囲:4000〜400cm−1(MCT検出器)
窓材:KBr(赤外透過下限400cm−1)
参考例1の中間組成物について得られたIRスペクトルとの比較から、実施例1Bの中間組成物について得られたIRスペクトルのみに確認することのできる1583cm−1付近のピークがリチウム塩化したカルボキシル基(COO−)を示すピークであると考えられる。そして、この1583cm−1付近のピークの強度は、室温から200℃までの各測定温度において略一定であった。これらの結果から、中間組成物を縮合反応させる加熱処理(カルボキシル基とアミノ基の縮合反応)の過程、及び加熱処理の後においても、リチウム塩化したカルボキシル基は、そのままの状態で存在していることが分かる。
Claims (11)
- 蓄電装置の負極用バインダーとして用いられる高分子化合物であって、
カルボキシル基の一部がリチウム塩化されたポリアクリル酸と、下記一般式(1)に示す多官能アミンとが縮合してなり、
前記ポリアクリル酸により構成される鎖状構造は、フリーのカルボキシル基と、リチウム塩化されたカルボキシル基とを有することを特徴とする高分子化合物。
- 蓄電装置の負極用バインダーとして用いられる高分子化合物であって、
ポリアクリル酸により構成される鎖状構造と、前記鎖状構造内又は鎖状構造間におけるカルボキシル基同士を接続する架橋構造とを有し、
前記架橋構造は、下記一般式(2)〜(4)から選ばれる少なくとも一種の架橋構造であり、
前記鎖状構造は、フリーのカルボキシル基と、リチウム塩化されたカルボキシル基とを有することを特徴とする高分子化合物。
- 前記フリーのカルボキシル基と前記リチウム塩化されたカルボキシル基との比率が95:5〜25:75の範囲であることを特徴とする請求項1又は請求項2に記載の高分子化合物。
- 蓄電装置の負極用バインダーとして用いられる高分子化合物の中間組成物であって、
カルボキシル基の一部がリチウム塩化されたポリアクリル酸と、下記一般式(1)に示す多官能アミンと、非水溶媒と水の混合溶媒とを含有し、
前記ポリアクリル酸及び前記多官能アミンが前記混合溶媒中に溶解していることを特徴とする中間組成物。
- 前記ポリアクリル酸に由来するカルボキシル基の総数を「C」、
前記ポリアクリル酸に由来するカルボキシル基のうち、リチウム塩化されたカルボキシル基の総数を「LC」、
多官能アミンに由来するアミノ基の総数を「A」としたとき、
「「LC」/(「C」−「A」)×100」
により求められるリチウム化度が5〜50%の範囲であり、
前記混合溶媒における非水溶媒と水との混合割合が2:1〜1:2の範囲であることを特徴とする請求項4に記載の中間組成物。 - 前記ポリアクリル酸に由来するカルボキシル基の総数を「C」、
前記ポリアクリル酸に由来するカルボキシル基のうち、リチウム塩化されたカルボキシル基の総数を「LC」、
多官能アミンに由来するアミノ基の総数を「A」としたとき、
「「LC」/(「C」−「A」)×100」
により求められるリチウム化度が50〜75%の範囲であり、
前記混合溶媒における非水溶媒と水との混合割合が1:1〜1:2の範囲であることを特徴とする請求項4に記載の中間組成物。 - 請求項2又は請求項3に記載の高分子化合物の製造方法であって、
カルボキシル基の一部がリチウム塩化されたポリアクリル酸と、下記一般式(1)に示す多官能アミンとを、非水溶媒と水の混合溶媒中にて150〜230℃で加熱することを特徴とする高分子化合物の製造方法。
- 蓄電装置の負極電極であって、
請求項1〜3のいずれか一項に記載の高分子化合物を含有する負極用バインダーと、負極活物質とを備え、
前記負極活物質は、リチウムを吸蔵及び放出し得る炭素系材料、リチウムと合金化可能な元素、及びリチウムと合金化可能な元素を有する化合物から選ばれる少なくとも一種であることを特徴とする負極電極。 - 請求項8に記載の負極電極と、非水電解質とを備えることを特徴とする蓄電装置。
- 蓄電装置の負極電極の製造に用いられる負極電極用スラリーであって、
請求項4〜6のいずれか一項に記載の中間組成物と、負極活物質とを含有し、
前記負極活物質として、リチウムを吸蔵及び放出し得る炭素系材料、リチウムと合金化可能な元素、及びリチウムと合金化可能な元素を有する化合物から選ばれる少なくとも一種を含有することを特徴とする負極電極用スラリー。 - 蓄電装置の負極電極の製造方法であって、
請求項10に記載の負極電極用スラリーを用いて、集電体に対して負極活物質層を形成することを特徴とする負極電極の製造方法。