JP2017119768A - 多価ヒドロキシ樹脂及びエポキシ樹脂の製造方法 - Google Patents
多価ヒドロキシ樹脂及びエポキシ樹脂の製造方法 Download PDFInfo
- Publication number
- JP2017119768A JP2017119768A JP2015256925A JP2015256925A JP2017119768A JP 2017119768 A JP2017119768 A JP 2017119768A JP 2015256925 A JP2015256925 A JP 2015256925A JP 2015256925 A JP2015256925 A JP 2015256925A JP 2017119768 A JP2017119768 A JP 2017119768A
- Authority
- JP
- Japan
- Prior art keywords
- epoxy resin
- reaction
- resin
- hydroxy resin
- polyvalent hydroxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
なお、一般式(3)で表される多価ヒドロキシ樹脂において、nは、0〜20の数であるが、好ましくは平均値として0.2〜4.0を示す。
このような酸触媒としては、例えば、塩酸、硫酸、燐酸等の鉱酸や、ギ酸、シュウ酸、トリフルオロ酢酸、p−トルエンスルホン酸等の有機酸や、塩化亜鉛、塩化アルミニウム、塩化鉄、三フッ化ホウ素等のルイス酸や、活性白土、シリカ−アルミナ、ゼオライト等の固体酸などが挙げられる。
1)エポキシ当量の測定
電位差滴定装置を用い、溶剤としてクロロホルムを使用し、臭素化テトラエチルアンモニウム酢酸溶液を加え、電位差滴定装置にて0.1mol/L過塩素酸−酢酸溶液を用いて測定した。
自動軟化点装置(明峰社製、ASP−M4SP)を用い、JIS−K−2207に従い環球法にて測定した。
BROOKFIELD製、CAP2000H型回転粘度計を用いて、150℃にて測定した。
試料1.0gをブチルカルビトール25mlに溶解後、1N−KOHプロピレングリコール溶液25mlを加え10分間加熱還流した後、室温まで冷却し、さらに80%アセトン水100mlを加え、0.002N−AgNO3水溶液で電位差滴定を行うことにより測定した。
耐圧容器に粒径を揃えたエポキシ樹脂硬化物10gとイオン交換純水50gを秤量後、加熱抽出を行い、イオンクロマトグラフを用いて、抽出水中の塩素イオン濃度を求め、エポキシ樹脂硬化物の抽出塩素イオン濃度を算出した。
熱機械測定装置(エスアイアイ・ナノテクノロジー株式会社製 EXSTAR6000TMA/6100)により、昇温速度10℃/分の条件でTgを求めた。
回転枠つき恒温器を用いて、250℃における1000時間後の試験片重量と加熱前の試験片重量との差から重量保持率(wt%)を求めた。
1000mlの4口フラスコに、4,4’−ジヒドロキシビフェニル77.5g、ジエチレングリコールジメチルエーテル97.9g、4,4’−ビスクロロメチルビフェニル52.3gを仕込み、窒素気流下、攪拌しながら160℃まで昇温して10時間反応させた。続いて、48%水酸化カリウム溶液3gを加え、130℃で3時間反応させた。反応後、大量の純水に滴下して再沈殿により回収し、淡黄色の樹脂110gを得た。得られた樹脂の全塩素は300ppmであった。
実施例1で得た樹脂110gにエピクロルヒドリン518gを仕込み溶解させた。続いて、減圧下70℃にて49%水酸化ナトリウム水溶液67.4gを4時間かけて滴下し、この滴下中に還流留出した水とエピクロルヒドリンを分離槽で分離しエピクロルヒドリンは反応容器に戻し、水は系外に除いて反応した。反応終了後、濾過により生成した塩を除き、更に水洗したのちエピクロルヒドリンを留去し、エポキシ樹脂108gを得た(エポキシ樹脂A)。得られた樹脂のエポキシ当量は199g/eq.、軟化点は124℃、150℃における溶融粘度は0.59Pa・s、全塩素は1200ppmであった。
1000mlの4口フラスコに、4,4’−ジヒドロキシビフェニル77.5g、ジエチレングリコールジメチルエーテル97.9g、4,4’−ビスクロロメチルビフェニル52.3gを仕込み、窒素気流下、攪拌しながら160℃まで昇温して10時間反応させた。反応後、大量の純粋に滴下して再沈殿により回収し、淡黄色の樹脂112gを得た。得られた樹脂の全塩素は4000ppmであった。
比較例1で得た樹脂112gにエピクロルヒドリン528gを仕込み溶解させた。続いて、減圧下70℃にて49%水酸化ナトリウム水溶液68.6gを4時間かけて滴下し、この滴下中に還流留出した水とエピクロルヒドリンを分離槽で分離しエピクロルヒドリンは反応容器に戻し、水は系外に除いて反応した。反応終了後、濾過により生成した塩を除き、更に水洗したのちエピクロルヒドリンを留去し、エポキシ樹脂110gを得た(エポキシ樹脂B)。得られた樹脂のエポキシ当量は196g/eq.、軟化点は126℃、150℃における溶融粘度は0.68Pa・s、全塩素は2300ppmであった。
上記の実施例2で得られたエポキシ樹脂A、硬化剤、無機充填材と硬化促進剤としてのトリフェニルホスフィンと、その他の添加剤を表1に示す配合割合で混練してエポキシ樹脂組成物を調製した。表中の数値は配合における重量部を示す。
上記の比較例2で得られたエポキシ樹脂B、硬化剤、無機充填材と硬化促進剤としてのトリフェニルホスフィンと、その他の添加剤を表1に示す配合割合で混練してエポキシ樹脂組成物を調製した。表中の数値は配合における重量部を示す。
・硬化剤;トリフェノールメタン型多価ヒドロキシ樹脂(TPM−100(群栄化学工業株式会社製)、OH当量 97.5、軟化点 105℃)
・無機充填剤:球状シリカ(製品名;FB−8S、電気化学工業株式会社製)
・硬化触媒:2−フェニル−4,5−ジヒドロキシメチルイミダゾール(製品名;2PHZ−PW、四国化成株式会社製)
・離型剤:カルナバワックス(製品名;TOWAX171、東亜化成株式会社製)
・着色剤:カーボンブラック(製品名;MA−100、三菱化学株式会社製)
Claims (3)
- 多価ヒドロキシ樹脂の全塩素量が1000ppm以下であることを特徴とする請求項1に記載の多価ヒドロキシ樹脂の製造方法。
- ビフェノール化合物とビスクロロメチルビフェニル化合物とを反応させるにあたり、先ず無触媒又は酸触媒の存在下にて反応させて、ビスクロロメチルビフェニル化合物の80wt%以上を反応させた後、アルカリ金属水酸化物を加えて中和反応させて全塩素量が1000ppm以下である多価ヒドロキシ樹脂を得て、この多価ヒドロキシ樹脂とエピクロルヒドリンを反応させることを特徴とするエポキシ樹脂の製造方法。