JP2017008323A - 弾性体、その調製のための方法および使用 - Google Patents
弾性体、その調製のための方法および使用 Download PDFInfo
- Publication number
- JP2017008323A JP2017008323A JP2016153755A JP2016153755A JP2017008323A JP 2017008323 A JP2017008323 A JP 2017008323A JP 2016153755 A JP2016153755 A JP 2016153755A JP 2016153755 A JP2016153755 A JP 2016153755A JP 2017008323 A JP2017008323 A JP 2017008323A
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- mol
- crystallinity
- molecular weight
- cyclic olefin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本開示の分野:本開示は、弾性体、弾性体の調製のための方法、および弾性体の使用、特にゴルフボールのコアの生産において、およびゴム調剤物においてのものに関する。
(結晶化度およびガラス転移温度(Tg))-
環状オレフィンモノマー(単量体)のROMPによって本明細書において生成される共重合体の結晶化度の程度は以下の通りに定まる。環状オレフィンモノマーのROMPによって本明細書において生成される共重合体のガラス転移温度(Tg)は以下の通りに定まる:
Xc=100*A/ΔHf
双方のAおよびΔHfはJ/gの単位においてであり、およびXcは%で表される。
ここに請求されるポリマーについて、シス-1,4-ポリブタジエンのための融合の報告された熱は、パーセント結晶化度の決定のための最適な既知の値である。この値は、170.4J/gである[L. Mandelkern(マンデルケルン)およびR. G. Alamo(アラモ)、"Thermodynamic Quantities Governing Melting(サーモダイナミック・クオンティティーズ・ガバーニング・メルティング)"、J. E. Mark(マーク)での、ed.(編集)、 Physical Properties of Polymers Handbook(フィジカル・プロパティーズ・オブ・ポリマーズ・ハンドブック)(AIP Press(AIPプレス社):Woodbury(ウッドベリー)、NY(米国ニューヨーク州)、1996年)]。
1.3kg(1.6L)のオレフィンフリーのシクロヘキサン、0.75kg(0.97L、11.0モル)のシクロペンテン、および0.51kg(0.57L、3.1モル)の1,5,9-シクロドデカトリエンから構成するバッチ混合物を、1-ガロン(米3.7853 リットル、英4.546 リットル)の容量の反応器中にチャージし、窒素を用いてパージして、撹拌した(49.5%の固体)。100mLの無水エタノール中での0.90gのトランス-β-ハイドロムコン酸の溶液(6.2mmol(ミリモル))を容器中にチャージし、そして反応器の内容を40℃にまで加熱した。50mLの脱気したトルエン中での0.21g(0.25mmol)のGrubbs 2nd Generation(グラブスの第2世代の)ルテニウム開環複分解重合触媒から構成する溶液を、反応器に加えた。20分以内に、モノマーの重合が起こり始め、そして43℃までの反応温度の増加が観察された。結果として生じる生成物を次いで追加の2時間一定の40℃の温度で撹拌した。このとき、4mLのエチルビニルエーテルを、重合を停止させるために加えた。追加的に12時間撹拌後、次いでインターポリマー溶液をイソプロパノール/BHT(ブチル化ヒドロキシトルエン)の混合物中に凝固させ、白色の、弾性固形物質を生成させた。結果として生じる弾性インターポリマーは、以下の特徴を持っていた。すなわち、非晶質、Mn=49.2kg/モル、Mw/Mn=1.6、Tg=-97.7℃。共重合体組成は、45:55モルパーセントのブテニル:ペンテニル単位であった。この例において利用される触媒は商業的に“Grubbs Second Generation Catalyst”と称される。この触媒は、Materia Inc.(マテリア社)(Pasadena(パサデナ)、CA(カリフォルニア州)USA(米国))によって製造され、そして触媒はSigma-Aldrich(シグマ-アルドリッチ社)(St. Louis(セント・ルイス)、MO(ミズーリ州)USA)によって販売される。触媒の化学名は、(1,3-ビス(2,4,6-トリメチルフェニル)-2-イミダゾリジニリデン)ジクロロ(フェニルメチレン)(トリシクロヘキシルホスフィン)ルテニウムである。
1.1kg(1.4L)の脱オレフィン化(deolefinated)シクロヘキサン、0.73kg(0.95L、10.9モル)のシクロペンテン、および0.51kg(0.57、3.1モル)Lの1,5,9-シクロドデカトリエンから構成するバッチ混合物を、1-ガロンの容量の反応器中にチャージし、窒素を用いてパージして、撹拌した(52.6%の固体)。100mLの無水エタノール中での0.90gのトランス-β-ハイドロムコン酸の溶液(6.2mmol)を容器中にチャージし、そして反応器の内容を55℃にまで加熱した。50mLの脱気したトルエン中での0.49g(0.6mmol)のGrubbs 2nd Generation(グラブスの第2世代の)ルテニウム複分解重合触媒から構成する溶液を、反応器に加えた。10分以内に、モノマーの重合が起こり始め、そして71℃までの反応温度の増加が観察された。結果として生じるポリマー溶液を次いで40℃にまで冷却し、そして追加の2時間撹拌した。このとき、50mLのシクロヘキセン中でのエチルビニルエーテルの5mLの溶液を、重合を停止させるために加えた。追加的に12時間撹拌後、次いでポリマーをイソプロパノール/BHT(ブチル化ヒドロキシトルエン)の混合物中に凝固させることによって分離し、弾性固形物質を生成させた。結果として生じるポリマーは、以下の特徴を持っていた。すなわち、Mn=58.5kg/モル、Mw/Mn=1.67、Tg=-95.6℃であり、および非晶質であった。インターポリマー組成は、53:47パーセントのブテニル:ペンテニル単位であった。この例において利用される触媒は商業的に“Grubbs Second Generation Catalyst”と称される。この触媒は、Materia Inc.(Pasadena、CA、USA)によって製造され、そして触媒はSigma-Aldrich(St. Louis、MO USA)によって販売される。触媒の化学名は、(1,3-ビス(2,4,6-トリメチルフェニル)-2-イミダゾリジニリデン)ジクロロ(フェニルメチレン)(トリシクロヘキシルホスフィン)ルテニウムである。
例1のポリマーを、ゴルフボールコア調剤物において調合し、および硬化させた。調剤物は、ゴムの百分率当り100部(phr)のポリマー、23phrの亜鉛ジアクリレート、20phrの酸化亜鉛、0.2phrの酸化防止剤(Ciba Irganox(チバ・イルガノックス)1076)、および0.5phrの過酸化物(t-ブチルペルオキシジイソプロピル-ベンゼン;Vulcup(バルカップ)R、Geo Specialty Chemicals(ゲオ・スペシャルティ・ケミカルズ社)からのもの)を含有した。過酸化物以外のすべての原材料を、300グラムのバッチにおいて、Brabender Plasticorder(ブラベンダー・プラスチコーダー)の内部混合機(internal mixer)で5分間60rpmの混合速度で混ぜた。初期の温度は75℃で、そしてバッチの最終的な温度は105℃であった。過酸化物をその後、60℃で2つのロールミルを用いて調合物に加えた。1.54インチ(39.1mm)に等しい直径を有する球状のコアを、モルド(型)において160℃で20分間硬化させることによって、最終的な混合物から形成した。反発係数(COR)は、エアカノンを用いてコアについて定めた。この試験において、コアは鋼板に衝撃を与える前に、1秒につきおよそ143フィート(45.6m/s)の初速度を持つ。34の圧縮値および0.68のCORがこの例について測定された。
例2のポリマーを、ゴルフボールコア調剤物において調合し、および硬化させた。調剤物は、ゴムの百分率当り100部(phr)の重合体、23phrの亜鉛ジアクリレート、20phrの酸化亜鉛、0.2phrの酸化防止剤(Ciba Irganox 1076)、および0.5phrの過酸化物(t-ブチルペルオキシジイソプロピル-ベンゼン;Vulcup R、Geo Specialty Chemicalsからのもの)を含有した。過酸化物以外のすべての原材料を、300グラムのバッチにおいて、Brabender Plasticorderの内部混合機で5分間60rpmの混合速度で混ぜた。初期の温度は75℃で、そしてバッチの最終的な温度は105℃であった。過酸化物をその後、60℃で2つのロールミルを用いて調合物に加えた。1/54インチ(39.1mm)に等しい直径を有する球状のコアを、モルドにおいて160℃で20分間硬化させることによって、最終的な混合物から形成した。反発係数(COR)は、エアカノンを用いてコアについて定めた。この試験において、コアは鋼板に衝撃を与える前に、1秒につきおよそ143フィート(45.6m/s)の初速度を持つ。32の圧縮値および0.69のCORがこの例について測定された。
Claims (21)
- 少なくとも2つの環状オレフィン単量体を備える弾性共重合体であって、その共重合体は、少なくとも2つの環状オレフィン単量体の開環複分解重合によって調製され、および共重合体は、結晶化度を持たず、−80℃よりも低いガラス転移温度(Tg)、および少なくとも40kg/モルの数平均分子量(Mn)を持つことによって特徴付けられ、各々の特性は本明細書に記載の試験手順によって定まる、弾性共重合体。
- 少なくとも1種の官能基を持つ、請求項1記載の弾性共重合体。
- 少なくとも1種の官能基は、カルボン酸、ニトリル、アミン、アミド、エステル、スルホン酸塩、カルボン酸の金属塩、コハク酸無水物、水酸基、およびその組合せからなる群より選ばれる、請求項2記載の弾性共重合体。
- 少なくとも1種のオレフィン単量体は、シクロプロペン、シクロブテン、ベンゾシクロブテン、シクロペンテン、ジシクロペンタジエン、ノルボルネン、ノルボルナジエン、シクロヘプテン、シクロオクテン、7−オキサノルボルネン、7−オキサノルボルナジエン、シクロデセン、1,3−シクロオクタジエン、1,5−シクロオクタジエン、1,3−シクロヘプタジエン、[2.2.1]ビシクロヘプテン、[2.2.2]ビシクロオクテン、シクロヘキセニルノルボルネン、ノルボルネンジカルボキシ無水物、シクロドデセン、1,5,9−シクロドデカトリエン、およびその混合物からなる群より選ばれる、請求項1記載の弾性共重合体。
- ガラス転移温度(Tg)は−80℃よりも低いものから約−130℃まで及ぶ、請求項1記載の弾性共重合体。
- 数平均分子量(Mn)は少なくとも約40kg/モルから約500kg/モルまで及ぶ、請求項1記載の弾性共重合体。
- 弾性共重合体は、結晶化度を持たず、−80℃よりも低いものから約−130℃まで及ぶガラス転移温度(Tg)を持ち、および少なくとも約40kg/モルから約500kg/モルまで及ぶ数平均分子量(Mn)を持つ、請求項1記載の弾性共重合体。
- 数平均分子量(Mn)は約60kg/モルから約200kg/モルまで及ぶ、請求項1記載の弾性共重合体。
- 請求項1の弾性共重合体を調製するための方法であって、少なくとも2つの環状オレフィン単量体を、開環複分解重合触媒の存在下に、開環複分解重合する工程、および重合を停止する工程を具え、そこでは、少なくとも1種の環状オレフィン単量体は、約15から約85までのモル%の量において存在し、および他の環状オレフィン単量体(群)は約85から約15までのモル%の残りの量において存在する、方法。
- 少なくとも2つの環状オレフィン単量体を備える弾性共重合体を含むゴルフボールのコアであって、その共重合体は、少なくとも2つの環状オレフィン単量体の開環複分解重合によって調製され、および共重合体は、0から約30%までの結晶化度、−80℃よりも低いガラス転移温度(Tg)、および少なくとも40kg/モルの数平均分子量(Mn)を持つことによって特徴付けられ、各々の特性は本明細書に記載の試験手順によって定まる、ゴルフボールのコア。
- 弾性共重合体は、0%の結晶化度、−80℃よりも低いものから約−130℃まで及ぶガラス転移温度(Tg)を持ち、および少なくとも約40kg/モルから約500kg/モルまで及ぶ数平均分子量(Mn)を持つ、請求項10記載のゴルフボールのコア。
- 共重合体は−80℃よりも低いものから約−130℃まで及ぶガラス転移温度(Tg)を持つ、請求項10記載のゴルフボールのコア。
- 共重合体は少なくとも40kg/モルから約500kg/モルまでの数平均分子量を持つ、請求項10記載のゴルフボールのコア。
- 共重合体は0から約20%までの結晶化度を持つ、請求項10記載のゴルフボールのコア。
- 共重合体は0%の結晶化度を持つ、請求項10記載のゴルフボールのコア。
- 共重合体は、0%の結晶化度、−80℃よりも低いものから約−130℃までのガラス転移温度(Tg)、および少なくとも40kg/モルから約200kg/モルまでの数平均分子量(Mn)を持つ、請求項10記載のゴルフボールのコア。
- 少なくとも2つの環状オレフィン単量体を備える弾性合成物を含む、ゴム組成物であって、その共重合体は、少なくとも2つの環状オレフィン単量体の開環複分解重合によって調製され、および共重合体は、0から約30%までの結晶化度、−80℃よりも低いガラス転移温度(Tg)、および少なくとも40kg/モルの数平均分子量(Mn)を持つことによって特徴付けられ、各々の特性は本明細書に記載の試験手順によって定まる、ゴム組成物。
- 弾性共重合体は、0%の結晶化度、−80℃よりも低いものから約−130℃まで及ぶガラス転移温度(Tg)を持ち、および少なくとも約40kg/モルから約500kg/モルまで及ぶ数平均分子量(Mn)を持つ、請求項17記載のゴム組成物。
- 共重合体は0から約20%までの結晶化度を持つ、請求項17記載のゴム組成物。
- 共重合体は0%の結晶化度を持つ、請求項17記載のゴム組成物。
- タイヤの構成要素である、請求項17記載のゴム組成物。