JP2016500642A - 誘導調理機器のためのガラスプレート - Google Patents
誘導調理機器のためのガラスプレート Download PDFInfo
- Publication number
- JP2016500642A JP2016500642A JP2015538546A JP2015538546A JP2016500642A JP 2016500642 A JP2016500642 A JP 2016500642A JP 2015538546 A JP2015538546 A JP 2015538546A JP 2015538546 A JP2015538546 A JP 2015538546A JP 2016500642 A JP2016500642 A JP 2016500642A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass plate
- weight content
- content
- plate according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Fe2O3(全鉄分) 0.8〜1.8%
CoO 0.02〜0.06%
Se 0〜0.005%
Cr2O3 0〜0.1%
・強化前のガラスのc/a比が1kgの荷重下でのビッカース押し込み試験後に最大で3.0であること。cは放射状の割れの長さであり、aはビッカース圧痕の対角線の半分である。
・σ/(e・E・α)比が少なくとも20K・mm-1、場合によっては25又は30K・mm-1であること。σは強化によってガラスのバルクに生じる最大応力(Pa)であり、eはガラスの厚さ(mm)であり、Eはヤング率(Pa)であり、そしてαはガラスの線熱膨張係数(K-1)である。
1.ガラスのヤング率(Pa)と線熱膨張係数(K-1)との積E・αが0.1MPa・K-1と0.8MPa・K-1の間、特に0.2MPa・K-1と0.5MPa・K-1の間であり、とりわけ0.2MPa・K-1と0.4MPa・K-1の間である。積E・αが小さすぎると熱テンパー処理が難しくなるのに対して、積E・αが大きすぎると耐熱衝撃性が低くなる。
2.ガラスの歪点が少なくとも500℃、特に600℃、場合によっては630℃である。この温度は好ましくは最高でも800℃以下、特に700℃以下である。歪点は、ガラスの粘度が1014.5ポアズ(1ポアズ=0.1Pa・s)である温度に相当する。高い歪点は、調理機器の操作中にガラスの強化が損なわれるのを防止することを可能にする。
3.ガラスの線熱膨張係数は最大で50×10-7/Kであり、特に30×10-7/Kと45×10-7/Kの間、場合によっては32(又は35)×10-7/Kと45×10-7/Kの間である。熱膨張係数が大きいと、申し分のない耐熱衝撃性が得られなくなる。反対に、熱膨張係数が小さすぎると、ガラスを充分に強化することが難しくなる。
4.強化前のガラスのc/a比は最大で2.8、特に2.7又は2.5であり、場合によっては0.5又は0.2又は0.1である。この比はゼロであるのが一層好ましい。驚くべきことに、この特性は、ガラスが強化される前に測定されるという事実にもかかわらず、本発明による調理機器を実際に使用する際のプレートの強度に決定的な影響をもたらすことになる。
5.ガラスのσ/(e・E・α)比は少なくとも20、特に30K・mm-1である。σ/(e・E・α)比は通常、最大で200K・mm-1、場合によっては100K・mm-1である。この特性は、調理機器使用中にプレートが破断するリスクを防止するのに大きな影響をもたらすことが観察されている。
6.強化によってガラスのバルクに生じる最大応力は好ましくは少なくとも20MPa、特に25又は30MPa、そして場合によっては40MPaである。
SiO2 49〜75%、特に52〜75%
Al2O3 15〜30%、特に18〜27%
Li2O 1〜8%、特に2.5〜5.5%
K2O 0〜5%、特に0〜3%
Na2O 0〜5%、特に0〜3%
ZnO 0〜5%、特に0〜3.5%
MgO 0〜5%、特に0〜3%
CaO 0〜5%、特に0〜2.5%
BaO 0〜5%、特に0〜3.5%
SrO 0〜5%、特に0〜2%
TiO2 0〜6%、特に0〜3%
ZrO2 0〜5%、特に0〜3%
P2O5 0〜10%、特に0〜8%
B2O3 0〜5%、特に0〜3%
SiO2 70〜85%、特に75〜85%
B2O3 8〜16%、特に10〜15%又は9〜12%
Al2O3 0〜5%、特に0〜3%又は2〜5%
K2O 0〜2%、特に0〜1%
Na2O 1〜8%、特に2〜6%
SiO2 45〜68%、特に55〜65%
Al2O3 8〜20%、特に14〜18%
B2O3 4〜18%、特に5〜10%
RO 5〜30%、特に5〜17%
R2O 最大で10%、特に1%
・プレートの厚さe(mmで表す)。
・EN410:1998標準規格で規定された光透過率(「TL」で示す)。
・ISO 11664−1及び−2標準規格に規定されたようにD65光源及びCIE 1931の標準観測者を踏まえた色座標L*、a*、b*。
・波長430、530及び630nmの透過率。
Claims (15)
- 誘導調理機器のための強化ガラス製のプレートであって、その化学組成が下記の着色剤を下記に規定される重量による範囲内で変動する含有量で含む、誘導調理機器のための強化ガラス製のプレート。
Fe2O3(全鉄分) 0.8〜1.8%
CoO 0.02〜0.06%
Se 0〜0.005%
Cr2O3 0〜0.1% - 前記ガラスの線熱膨張係数が最大で50×10-7/Kであり、特に30×10-7/Kと45×10-7/Kの間に含まれる、請求項1に記載のガラスプレート。
- 前記ガラスの化学組成がリチウムアルミノケイ酸塩タイプ、ホウケイ酸塩タイプ、又はアルミノホウケイ酸塩タイプのものである、請求項1又は2に記載のガラスプレート。
- 前記ガラスの化学組成が、重量含有量49〜75%のシリカSiO2と、重量含有量15〜30%のアルミナAl2O3と、重量含有量1〜8%の酸化リチウムLi2Oとを含む、請求項3に記載のガラスプレート。
- 前記ガラスの化学組成が、下記に規定する重量範囲内で変動する下記の成分を含む、請求項4に記載のガラスプレート。
SiO2 49〜75%、特に52〜75%
Al2O3 15〜30%、特に18〜27%
Li2O 1〜8%、特に2.5〜5.5%
K2O 0〜5%、特に0〜3%
Na2O 0〜5%、特に0〜3%
ZnO 0〜5%、特に0〜3.5%
MgO 0〜5%、特に0〜3%
CaO 0〜5%、特に0〜2.5%
BaO 0〜5%、特に0〜3.5%
SrO 0〜5%、特に0〜2%
TiO2 0〜6%、特に0〜3%
ZrO2 0〜5%、特に0〜3%
P2O5 0〜10%、特に0〜8%
B2O3 0〜5%、特に0〜3% - 前記ガラスの化学組成が、重量含有量70〜85%のシリカSiO2と、重量含有量8〜20%の酸化ホウ素B2O3と、合計重量含有量が1〜10%の少なくとも1種のアルカリ金属酸化物とを含む、請求項1から3までの1項に記載のガラスプレート。
- 前記ホウケイ酸塩ガラスの化学組成が、下記に規定する重量範囲内で変動する下記の成分を含む、請求項6に記載のガラスプレート。
SiO2 70〜85%
B2O3 8〜16%
Al2O3 0〜5%
K2O 0〜2%
Na2O 1〜8% - 前記アルミノホウケイ酸塩ガラスの化学組成が、重量含有量45〜68%のシリカSiO2と、重量含有量8〜20%のアルミナAl2O3と、重量含有量4〜18%の酸化ホウ素B2O3と、合計含有量が5〜30%の、MgO、CaO、SrO及びBaOから選択されるアルカリ土類酸化物とを含み、アルカリ金属酸化物の合計重量含有量が10%を超えず、特に1%を超えない、請求項1から3までの1項に記載のガラスプレート。
- Fe2O3(全鉄分)の重量含有量が0.9〜1.7%である、請求項1から8までの1項に記載のガラスプレート。
- CoOの重量含有量が0.03〜0.05%である、請求項1から9までの1項に記載のガラスプレート。
- Cr2O3の重量含有量がゼロである、請求項1から10までの1項に記載のガラスプレート。
- TiO2の重量含有量が最大で1%、特に0.5%である、請求項1から11までの1項に記載のガラスプレート。
- 前記ガラスが熱的に強化されている、請求項1から12までの1項に記載のガラスプレート。
- 請求項1から13までの1項に記載のガラスプレートの下側に配置された少なくとも1つのインダクタを含む誘導調理機器。
- 白色光を発光する少なくとも1つのデバイスを含む、請求項14に記載の調理機器。