JP2016186034A - 親水性活性エネルギー線硬化型コーティング樹脂組成物 - Google Patents
親水性活性エネルギー線硬化型コーティング樹脂組成物 Download PDFInfo
- Publication number
- JP2016186034A JP2016186034A JP2015067019A JP2015067019A JP2016186034A JP 2016186034 A JP2016186034 A JP 2016186034A JP 2015067019 A JP2015067019 A JP 2015067019A JP 2015067019 A JP2015067019 A JP 2015067019A JP 2016186034 A JP2016186034 A JP 2016186034A
- Authority
- JP
- Japan
- Prior art keywords
- group
- resin composition
- ethylene oxide
- active energy
- energy ray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
項1. ポリグリセリンエチレンオキサイド変性(メタ)アクリレート化物と、エチレンオキサイド基を有するリン酸エステル化合物とを含有することを特徴とする活性エネルギー線硬化型コーティング樹脂組成物であって、ポリグリセリンエチレンオキサイド変性(メタ)アクリレート化物が一般式(A)
で表される活性エネルギー線硬化型コーティング樹脂組成物。
項2. エチレンオキサイド基を有するリン酸エステル化合物が一般式(B)
で表される化合物又はその塩である、項1に記載の活性エネルギー線硬化型コーティング樹脂組成物。
項3. さらに硬化性モノマーまたはオリゴマーを含有する項1または2に記載の活性エネルギー線硬化型コーティング樹脂組成物。
項4. 項1〜3のいずれかに記載の活性エネルギー線硬化型コーティング樹脂組成物を硬化してなる硬化膜。
項5. 水滴接触角が10度以下である、項4に記載の硬化膜。
ジグリセリンエチレンオキサイド付加物(付加モル数8モル)15重量部、2−(イソシアネートエチル)アクリレート(昭和電工(株)製 カレンズAOI)16.4重量部、メチルエチルケトン24重量部をフラスコに入れ、50℃で反応溶液の撹拌を5時間続行した。反応の終了をFT−IRを用いて−N=C=O吸収(2275〜2250cm−1)の消失により確認した。a+b+c=8、d=2、1分子あたりアクリレート4モル。
ジグリセリンエチレンオキサイド付加物(付加モル数22モル)15重量部、2−(イソシアネートエチル)アクリレート(昭和電工(株)製 カレンズAOI)7.5重量部、メチルエチルケトン24重量部をフラスコに入れ、50℃で反応溶液の撹拌を5時間続行した。反応の終了をFT−IRを用いて−N=C=O吸収(2275〜2250cm−1)の消失により確認した。a+b+c=22、d=2、1分子あたりアクリレート4モル。
ポリオキシアルキレンアルキルエーテルリン酸エステルアミン塩(丸菱油化工業(株)製 エリミナ208)15重量部、2−(イソシアネートエチル)アクリレート(昭和電工(株)製 カレンズAOI)1.5重量部、メチルエチルケトン35重量部をフラスコに入れ、50℃で反応溶液の撹拌を5時間続行した。反応の終了をFT−IRを用いて−N=C=O吸収(2275〜2250cm−1)の消失により確認した。
ジ(C12〜15)パレス‐6リン酸 (日光ケミカルズ(株)製 NIKKOL DDP-6)15重量部、2−(イソシアネートエチル)アクリレート(昭和電工(株)製 カレンズAOI)2重量部、メチルエチルケトン30重量部をフラスコに入れ、50℃で反応溶液の撹拌を6時間続行した。反応の終了をFT−IRを用いて−N=C=O吸収(2275〜2250cm−1)の消失により確認した。p=6。
(C12〜C15)パレス‐3リン酸 (東邦化学工業(株)製 フォスファノールRS-410)
15重量部、2−(イソシアネートエチル)アクリレート(昭和電工(株)製 カレンズAOI)2.7重量部、メチルエチルケトン30重量部をフラスコに入れ、50℃で反応溶液の撹拌を6時間続行した。反応の終了をFT−IRを用いて−N=C=O吸収(2275〜2250cm−1)の消失により確認した。p=3。
樹脂組成物は表1、表2に示す配合で全量を10gとなるように調液した。
<防曇性>
(i) 呼気防曇性
常温で呼気を吹きかけ、曇りの有無を目視で評価した。曇りが認められないものを○、曇りが認められたものを×とした。
(ii) 蒸気防曇性
塗膜表面に50℃蒸気を1分間当てながら曇りの有無を目視で評価した。曇りが認められないものを○、曇りが認められたものを×とした。
水の接触角を協和界面科学社製DropMaster700を用いて25℃で測定した。水の接触角が10度以下のものを○、水の接触角が10度超えのものを×とした。
<耐スチールウール性(耐SW性)>
スチールウール(#0000)を用い、500g/cm2荷重をかけ、塗膜を10往復擦った。試験後の塗膜を観察し、以下の基準に基づき評価した。
傷の本数が0本=◎
傷の本数が1〜10本=○
傷の本数が11〜30本=△
傷の本数が30本より多い=×
<塗液外観>
透明ガラス瓶に入れた塗液の外観を目視で観察し、以下の基準に基づき評価した。
塗液が均一で透明=○
塗液が微濁=△
塗液が相分離し、凝集物がある=×
<塗膜外観>
硬化後の塗膜の外観を目視で観察し、以下の基準に基づき評価した。
塗膜表面が平滑でブツが認められない=◎
塗膜表面にごくわずかにブツが認められる=○
塗膜表面にブツが認められる=△
塗膜表面に顕著なブツがあり凹凸が発生している=×
<ヘイズ値>
ヘイズメーター(日本電色(株)製 NDH-5000)を用いて塗膜のヘイズ値を測定した。ヘイズ値が1未満を○、1以上5未満を△、5以上を×とした。
Claims (5)
- ポリグリセリンエチレンオキサイド変性(メタ)アクリレート化物と、エチレンオキサイド基を有するリン酸エステル化合物とを含有することを特徴とする活性エネルギー線硬化型コーティング樹脂組成物であって、ポリグリセリンエチレンオキサイド変性(メタ)アクリレート化物が一般式(A)
で表される活性エネルギー線硬化型コーティング樹脂組成物。 - さらに硬化性モノマーまたはオリゴマーを含有する請求項1または2に記載の活性エネルギー線硬化型コーティング樹脂組成物。
- 請求項1〜3のいずれかに記載の活性エネルギー線硬化型コーティング樹脂組成物を硬化してなる硬化膜。
- 水滴接触角が10度以下である、請求項4に記載の硬化膜。