JP2014185355A - 溶融Alめっき鋼線並びに撚り線およびその製造方法 - Google Patents
溶融Alめっき鋼線並びに撚り線およびその製造方法 Download PDFInfo
- Publication number
- JP2014185355A JP2014185355A JP2013059411A JP2013059411A JP2014185355A JP 2014185355 A JP2014185355 A JP 2014185355A JP 2013059411 A JP2013059411 A JP 2013059411A JP 2013059411 A JP2013059411 A JP 2013059411A JP 2014185355 A JP2014185355 A JP 2014185355A
- Authority
- JP
- Japan
- Prior art keywords
- wire
- steel wire
- plated steel
- plating
- molten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】直径0.09〜0.50mmの鋼芯線を芯材に持つ溶融Alめっき鋼線であって、その長手方向における平均径DA(mm)および最小径DMIN(mm)が下記(1)式を満たすように溶融Alめっき付着量が均一化されている溶融Alめっき鋼線。
(DA−DMIN)/DA≦0.10 …(1)
【選択図】図4
Description
(DA−DMIN)/DA≦0.10 …(1)
(DA−DMIN)/DA≦0.10 …(1)
上述のように、ここでは最小径DMINとしてチャック間距離100mmにおける値を採用しているが、撚り線製造時に最も破断しやすい箇所は長手方向全長において最も径の細い位置である。したがって、長手方向全長の線径測定データに基づくDAおよびDMINが(1)式を満たす場合には、その溶融Alめっき鋼線は全長にわたって撚り線製造時のねじり破断が回避される性能を有していると判断することができる。
図7にその手法を模式的に例示する。めっき浴立ち上がり部5から鉛直に引き上げられる鋼線3に接触するように接触部材31が設けられている。接触部材31の鋼線3との接触部は例えば耐熱クロス等により構成することができる。鋼線3が接触部材31との接触状態を保ちながら引き上げられることにより、鋼線3の微小振動が抑制され、(1)式の条件を満たす線径変動の少ない溶融Alめっき鋼線が製造できる。
なお、得られた溶融Alめっき鋼線の径については前述の通り、平均径DAは各溶融Alめっき鋼線の全長約100〜8000mの測定データに基づく値を採用し、最小径DMINは実際にねじり試験に供した線材のチャック間距離100mmの測定データに基づく値を採用した。
2 大気環境
3 鋼線
4 遮蔽体
5 めっき浴立ち上がり部
6 遮蔽体内部の浴面部分
7 開口部
8 気相空間
10 浴面
21 中心素線
22 周辺素線
23、24 供給ボビン
25 回転盤
30 撚り線
31 接触部材
41a、41b チャック
42 線材試料
43 錘
50 めっき浴槽
51 送出装置
52 巻取装置
53 冷却装置
56 不活性ガス供給管
57 不活性ガス供給装置
58 リール
61 不活性ガス吐出ノズル
62 酸素含有ガス吐出口
63 酸素含有ガス供給管
64 酸素含有ガス供給装置
Claims (4)
- 直径0.05〜0.50mmの鋼芯線を芯材に持つ溶融Alめっき鋼線であって、その長手方向における平均径DA(mm)および最小径DMIN(mm)が下記(1)式を満たすように溶融Alめっき付着量が均一化されている溶融Alめっき鋼線。
(DA−DMIN)/DA≦0.10 …(1) - 当該溶融Alめっき鋼線は溶融Alめっき後に伸線加工を受けていないものである請求項1に記載の溶融Alめっき鋼線。
- 請求項1または2に記載の溶融Alめっき鋼線を素線に用いて、当該溶融Alめっき鋼線にねじれが加えられた状態で他の素線とともに撚り合わされた撚り線。
- 請求項1または2に記載の溶融Alめっき鋼線を素線に用いて、当該溶融Alめっき鋼線にねじれが加わる手法にて他の素線とともに巻取る撚り線の製造方法。