JP2014114174A - 水硬性組成物 - Google Patents
水硬性組成物 Download PDFInfo
- Publication number
- JP2014114174A JP2014114174A JP2012267364A JP2012267364A JP2014114174A JP 2014114174 A JP2014114174 A JP 2014114174A JP 2012267364 A JP2012267364 A JP 2012267364A JP 2012267364 A JP2012267364 A JP 2012267364A JP 2014114174 A JP2014114174 A JP 2014114174A
- Authority
- JP
- Japan
- Prior art keywords
- less
- group
- dispersant
- monomer
- hydraulic composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】特定の分散剤(A)と、特定の多糖誘導体と、アルミニウム粉末と、水硬性粉体と、水と、骨材とを含有し、分散剤(A)を、水硬性粉体100質量部に対して、0.09質量部以上0.40質量部以下含有する、水硬性組成物。
【選択図】なし
Description
東日本高速道路株式会社(NEXCO東日本)、"建設技術の紹介 トンネル覆工コンクリート"、[online]、2010年11月11日掲載、[2012年9月28日検索]、インターネット<URL:http://www.e-nexco.co.jp/dotodo/construction/concret/index.html> 株式会社鴻池組、"トンネル急速覆工 K-NTL工法"、[online]、[2012年9月28日検索]、インターネット<URL:http://www.konoike.co.jp/solution/detail/000409.html>
分散剤(A)を、水硬性粉体100質量部に対して、0.09質量部以上0.40質量部以下含有し、
分散剤(A)が、下記一般式(a1)で表される単量体(a1)由来の構成単位と下記一般式(a2)で表される単量体(a2)由来の構成単位を含み、単量体(a1)と単量体(a2)のモル比(a1)/(a2)が1/99以上30/70以下である共重合体であり、
多糖誘導体が、多糖類又はそのアルキル化誘導体若しくはヒドロキシアルキル化誘導体の一部又は全部の水酸基の水素原子が、炭素数8以上40以下の炭化水素鎖を部分構造として有する疎水性置換基と、スルホン酸基及びスルホン酸基の塩からなる群から選ばれる一種以上の基を部分構造として有するイオン性親水性基と、で置換されてなる多糖誘導体である、
水硬性組成物に関する。
R1a、R2a:水素原子又はメチル基
m1:0以上2以下の数
A1O:炭素数2又は炭素数3のアルキレンオキシ基
n1:平均付加モル数であり、100以上300以下の数
X1:水素原子又は炭素数1以上3以下のアルキル基
R3a、R4a、R5a:水素原子、メチル基又は(CH2)m2COOM2
M1、M2:水素原子、アルカリ金属、アルカリ土類金属(1/2原子)、アンモニウム、アルキルアンモニウム又は置換アルキルアンモニウム
m2:0以上2以下の数
を示す。〕
分散剤(A)は、前記一般式(a1)で表される単量体(a1)由来の構成単位と前記一般式(a2)で表される単量体(a2)由来の構成単位を含み、単量体(a1)と単量体(a2)のモル比(a1)/(a2)が1/99以上30/70以下である共重合体〔以下、共重合体(A)という〕からなる。
本発明で使用される多糖誘導体は、多糖類又はそのアルキル化若しくはヒドロキシアルキル化誘導体の一部又は全部の水酸基の水素原子が、炭素数8以上40以下の炭化水素鎖を部分構造として有する疎水性置換基〔以下、疎水性置換基という〕と、スルホン酸基及びスルホン酸基の塩からなる群から選ばれる一種以上の基を部分構造として有するイオン性親水性基〔以下、イオン性親水性置換基という〕で置換されてなる。
(i)直鎖又は分岐鎖のアルキル基を有するアルキルグリセリルエーテル基、
(ii)直鎖又は分岐鎖のアルケニル基を有するアルケニルグリセリルエーテル基、
(iii)ヒドロキシル基が置換されていてもよく、オキシカルボニル基が挿入されていてもよい、直鎖又は分岐鎖のアルキル基、
(iv)ヒドロキシル基が置換されていてもよく、オキシカルボニル基が挿入されていてもよい、直鎖又は分岐鎖のアルケニル基、並びに、
(v)ヒドロキシル基が置換されていてもよく、オキシカルボニル基が挿入されていてもよい、直鎖又は分岐鎖のアシル基
本発明に係るアルミニウム粉末は、表面が処理された市販のアルミニウム粉末を使用できる。表面処理は、アスファルト、合成樹脂、油脂類、高級パラフィン炭化水素類、高級脂肪酸をアルミ粉末表面にコートすることや過酸化水素水で表面を酸化させることなどが挙げられる。アルミニウム粉末を水硬性組成物中に混練した後、2時間から4時間のあいだに水硬性組成物の膨張が始まるアルミニウム粉末を使用することが好ましい。
本発明の水硬性組成物に使用される水硬性粉体は、水和反応により硬化する物性を有する粉体のことであり、セメント、石膏等が挙げられる。好ましくは普通ポルトランドセメント、ビーライトセメント、中庸熱セメント、早強セメント、超早強セメント、耐硫酸セメント、及びメーソンリーセメントから選ばれるセメントである。また、セメントに、高炉スラグ、フライアッシュ、シリカフューム、石粉(炭酸カルシウム粉末)等が添加されたものでもよい。
骨材としては、細骨材及び粗骨材から選ばれる骨材が挙げられる。細骨材として、JIS A0203−2302で規定されるものが挙げられる。細骨材としては、川砂、陸砂、山砂、海砂、石灰砂、珪砂及びこれらの砕砂、高炉スラグ細骨材、フェロニッケルスラグ細骨材、軽量細骨材(人工及び天然)及び再生細骨材等が挙げられる。また、粗骨材として、JIS A0203−2303で規定されるものが挙げられる。例えば粗骨材としては、川砂利、陸砂利、山砂利、海砂利、石灰砂利、これらの砕石、高炉スラグ粗骨材、フェロニッケルスラグ粗骨材、軽量粗骨材(人工及び天然)及び再生粗骨材等が挙げられる。細骨材、粗骨材は種類の違うものを混合して使用しても良く、単一の種類のものを使用しても良い。
本発明の水硬性組成物は、分散剤(A)を、水硬性粉体100質量部に対して、0.09質量部以上0.40質量部以下含有する。水硬性組成物の膨張率を得る観点から、分散剤(A)の含有量は、水硬性粉体100質量部に対して、0.10質量部以上が好ましく、0.14質量部以上がより好ましく、そして、0.20質量部以下が好ましく、更に0.18質量部以下がより好ましく、更に0.17質量部以下が更に好ましい。
分散剤(B):下記一般式(b1)で表される単量体(b1)由来の構成単位と下記一般式(b2)で表される単量体(b2)由来の構成単位とを含み、単量体(b1)と単量体(b2)のモル比(b1)/(b2)が30/70を超え50/50以下である共重合体〔以下、共重合体(B)という〕。
R1b、R2b:水素原子又はメチル基
m3:0以上2以下の数
A2O:炭素数2又は炭素数3のアルキレンオキシ基
n2:平均付加モル数であり、100以上300以下の数
X2:水素原子又は炭素数1以上3以下のアルキル基
R3b、R4b、R5b:水素原子、メチル基又は(CH2)m4COOM4
M3、M4:水素原子、アルカリ金属、アルカリ土類金属(1/2原子)、アンモニウム、アルキルアンモニウム又は置換アルキルアンモニウム
m4:0以上2以下の数
を示す〕
・AE剤:樹脂石鹸、飽和又は不飽和脂肪酸、ヒドロキシステアリン酸ナトリウム、ラウリルサルフェート、アルキルベンゼンスルホン酸又はその塩、アルカンスルホネート、ポリオキシアルキレンアルキル(又はアルキルフェニル)エーテル、ポリオキシアルキレンアルキル(又はアルキルフェニル)エーテル硫酸エステル又はその塩、ポリオキシアルキレンアルキル(又はアルキルフェニル)エーテルリン酸エステル又はその塩、蛋白質材料、アルケニルコハク酸、α−オレフィンスルホネート等。
・起泡剤
・早強剤又は促進剤:塩化カルシウム、亜硝酸カルシウム、硝酸カルシウム、臭化カルシウム、沃化カルシウム等の可溶性カルシウム塩、塩化鉄、塩化マグネシウム等の塩化物等、水酸化カリウム、炭酸塩、蟻酸又はその塩等。
・防水剤:樹脂酸又はその塩、脂肪酸エステル、油脂、シリコーン、パラフィン、アスファルト、ワックス等。
・消泡剤:ジメチルポリシロキサン系、ポリアルキレングリコール脂肪酸エステル系、鉱油系、油脂系、オキシアルキレン系、アルコール系、アミド系等。
・防錆剤:亜硝酸塩、燐酸塩、酸化亜鉛等。
・水溶性高分子:分散剤(A)〜(C)及び多糖誘導体以外の水溶性高分子であり、β−1,3−グルカン、キサンタンガム等の天然物系、ポリアクリル酸アミド、ポリエチレングリコール、オレイルアルコールのエチレンオキシド付加物もしくはこれとビニルシクロヘキセンジエポキシドとの反応物等の合成系等。
本発明のトンネルの覆工方法は、本発明の水硬性組成物を、トンネル内に配設された覆工用型枠に打設する。例えば、トンネルを掘削後に補強された岩盤の内側に覆工用型枠をトンネル内に配設し、岩盤と覆工用型枠の間に本発明の水硬性組成物を充填し、例えば3〜4日養生後に型枠をはずす方法が挙げられる。本発明のトンネルの覆工方法では、スランプフロー値が550mm以上、更に600mm以上、そして、700mm以下、更に650mm以下の水硬性組成物を用いることが好ましい。ここで、スランプフロー値は、JIS A 1150 コンクリートのスランプフロー試験方法により測定されたものである。
製造した水硬性組成物(コンクリート)の配合を表1に示す。
・水(W):水道水に分散剤及び多糖誘導体を添加した練り混ぜ水
・セメント(C):普通ポルトランドセメント(太平洋セメント(株)製普通ポルトランドセメントと、住友大阪セメント(株)製普通ポルトランドセメントとを、等量(質量比)混合したもの)、密度=3.16g/cm3
・細骨材1(S1):川砂(岐阜県 揖斐川産)、密度=2.61g/cm3
・細骨材2(S2):砕砂(兵庫県 西島産)、密度=2.54g/cm3
・細骨材3(S3):石灰砕砂(高知県 鳥形山産)、密度=2.65g/cm3
・粗骨材1(G1):石灰砕石2010(高知県 鳥形山産)、密度=2.72g/cm3
・細骨材2(G2):石灰砕石1005(高知県 鳥形山産)、密度=2.72g/cm3
(2−1)分散剤
下記表2に用いた分散剤を示す。分散剤(A)、(B)、(C)は以下の通りである。
・分散剤(A):〔一般式(a1)において、R1aが水素原子、R2aがメチル基、m1が0、A1Oがエチレンオキシ基、n1が120、X1がメチル基の単量体〕と〔一般式(a2)において、R3a及びR5aが水素原子、R4aがメチル基、M1が水素原子の単量体〕の共重合体である分散剤A1、モル比(a1)/(a2)が20/80、重量平均分子量70,000
・分散剤(B):〔一般式(b1)において、R1bが水素原子、R2bがメチル基、m3が0、A2Oがエチレンオキシ基、n2が120、X2がメチル基の単量体〕と〔一般式(b2)において、R3b及びR5bが水素原子、R4bがメチル基、M3が水素原子の単量体〕の共重合体である分散剤B1、モル比(b1)/(b2)が35/65、重量平均分子量80,000
・分散剤(C):〔一般式(a1)において、R1aが水素原子、R2aがメチル基、m1が0、A1Oがエチレンオキシ基、n1が9、X1がメチル基の単量体〕と〔一般式(a2)において、R3a及びR5aが水素原子、R4aがメチル基、M1が水素原子の単量体〕の共重合体である分散剤C1、モル比(a1)/(a2)が53/47、重量平均分子量70,000
分散剤の重量平均分子量は以下の方法による。
使用カラム:東ソー(株)製
TSKguardcolumn PWxl
TSKgel G4000PWxl+G2500PWxl
溶離液:0.2mol/Lリン酸バッファー(伸陽化学工業(株)製)/高速液体クロマトグラフ用アセトニトリル(和光純薬工業(株)製)=9/1(vol%)
流速:1.0mL/min.
カラム温度:40℃
検出:RI
注入量:10μL(0.5質量%水溶液)
標準物質:ポリエチレングリコール、重量平均分子量(Mw)875000、540000、235000、145000、107000、24000
検量線次数:三次式
装置:HLC-8320GPC(東ソー(株)製)
ソフトウエア:EcoSEC-WS(東ソー(株)製)
多糖誘導体として、下記合成例により得られた多糖誘導体1を用いた。
<合成例>
(i)攪拌機、温度計及び冷却管を備えた1000mlのガラス製セパラブル反応容器に、重量平均分子量約80万、ヒドロキシエチル基の置換度1.8のヒドロキシエチルセルロース(HEC−QP4400、ユニオンカーバイド社製)50g、88質量%イソプロピルアルコール400g及び48質量%水酸化ナトリウム水溶液3.5gを加えてスラリー液を調製し、窒素雰囲気下室温で30分間攪拌した。これにステアリルグリシジルエーテル4.0gを加え、80℃で7時間反応させて疎水化を行った。疎水化反応終了後、反応液を酢酸で中和し、反応生成物をろ別した。反応生成物を80質量%アセトン500gで2回、次いでアセトン500gで2回洗浄し、減圧下70℃で1昼夜乾燥し、疎水化されたヒドロキシエチルセルロース誘導体49.4gを得た。
アルミニウム粉末は、(株)フローリック製セルメックを用いた。
60リットルの強制二軸ミキサーを用いて、コンクリートを50リットル製造した。分散剤及び多糖誘導体と水とを混合し固形分20質量%の混和剤を調製し、さらに予め練混水に溶解した。セメントと骨材と混練水の練り混ぜは、環境温度20℃にて90秒間行った。練り混ぜ終了後、直ちに、スランプフロー値(これを「直後」のスランプフロー値とする)、コンクリート空気量(これを「直後」の空気量とする)、分離抵抗性の3種の評価項目を測定した。これら3つの評価項目の測定後、前記ミキサーにコンクリートを全量戻して混練開始から25分後まで静置した。その後、表3に示す量のアルミニウム粉末をミキサー内のコンクリートに添加して、再び30秒間混練して目的とするコンクリートを得た。ここで調製したコンクリートは、主にトンネル覆工に用いる水硬性組成物を想定して設計したものである。
1.スランプフロー値(mm)
JIS A 1150 コンクリートのスランプフロー試験方法に従った。上端内径100mm、下端内径200mm、高さ300mmのスランプコーンを用いた。
上記1.にて測定したスランプフロー値から、90分後と120分後の流動性の変化を120−90分流動性保持率として以下の方法により算出した。その際、スランプコーン下端内径が200mmであるため、スランプフロー値から200mmを引いて計算した。
120−90分流動性保持率(%)=(120分後のスランプフロー値−200)÷(90分後のスランプフロー値−200)×100
コンクリート製造から90分後程度までに打設及び施工が完了すると仮定して、打設・施工完了後における型枠からの漏れ防止及び型枠に対する圧力の軽減を期待する基準値として、上記で算出される120−90分流動性保持率の値が小さいこと、即ち流動性の低下が大きいことが、漏れ防止及び型枠への圧力軽減の観点から好ましい。具体的には、この評価における120−90分流動性保持率は70%未満が好ましく、60%未満がより好ましい。
JIS A 1128 フレッシュコンクリートの空気量の圧力による試験方法−空気室圧力法に従った。
ワーカービリティー、凍結融解抵抗性の観点から、設定空気量4.5%との差の絶対値が1.5%以下(4.5%±1.5%以内)が好ましく、設定空気量4.5%との差の絶対値が1.0%以下(空気量が4.5%±1.0%以内)がより好ましい。
アルミニウム粉末添加前のコンクリートについて、目視(肉眼)による観察評価にて行った。施工性、強度発現性、耐久性等を考慮して、○:骨材分離および水の分離なし、×:骨材分離および水の分離あり、とした。
JIS A 1147 コンクリートの凝結時間試験方法に従った。
内径125mm×250mmの鋼製型枠に、水硬性組成物を230mmの高さまで詰め、高感度変位計を用いて自動測定した。
地山、或いは一次覆工コンクリートとの優れた一体性付与の観点から、膨張率は0.50%以上が好ましく、2.00%以上がより好ましい。
Claims (6)
- 分散剤(A)と、多糖誘導体と、アルミニウム粉末と、水硬性粉体と、水と、骨材とを含有し、
分散剤(A)を、水硬性粉体100質量部に対して、0.09質量部以上0.40質量部以下含有し、
分散剤(A)が、下記一般式(a1)で表される単量体(a1)由来の構成単位と下記一般式(a2)で表される単量体(a2)由来の構成単位を含み、単量体(a1)と単量体(a2)のモル比(a1)/(a2)が1/99以上30/70以下である共重合体であり、
多糖誘導体が、多糖類又はそのアルキル化誘導体若しくはヒドロキシアルキル化誘導体の一部又は全部の水酸基の水素原子が、炭素数8以上40以下の炭化水素鎖を部分構造として有する疎水性置換基と、スルホン酸基及びスルホン酸基の塩からなる群から選ばれる一種以上の基を部分構造として有するイオン性親水性基と、で置換されてなる多糖誘導体である、
水硬性組成物。
〔式中、
R1a、R2a:水素原子又はメチル基
m1:0以上2以下の数
A1O:炭素数2又は炭素数3のアルキレンオキシ基
n1:平均付加モル数であり、100以上300以下の数
X1:水素原子又は炭素数1以上3以下のアルキル基
R3a、R4a、R5a:水素原子、メチル基又は(CH2)m2COOM2
M1、M2:水素原子、アルカリ金属、アルカリ土類金属(1/2原子)、アンモニウム、アルキルアンモニウム又は置換アルキルアンモニウム
m2:0以上2以下の数
を示す。〕 - 更に下記分散剤(B)を含有し、分散剤(A)と分散剤(B)の質量比、分散剤(A)/分散剤(B)が、30/70以上90/10以下である請求項1に記載の水硬性組成物。
分散剤(B):下記一般式(b1)で表される単量体(b1)由来の構成単位と下記一般式(b2)で表される単量体(b2)由来の構成単位とを含み、単量体(b1)と単量体(b2)のモル比(b1)/(b2)が30/70を超え50/50以下である共重合体。
〔式中、
R1b、R2b:水素原子又はメチル基
m3:0以上2以下の数
A2O:炭素数2又は炭素数3のアルキレンオキシ基
n2:平均付加モル数であり、100以上300以下の数
X2:水素原子又は炭素数1以上3以下のアルキル基
R3b、R4b、R5b:水素原子、メチル基又は(CH2)m4COOM4
M3、M4:水素原子、アルカリ金属、アルカリ土類金属(1/2原子)、アンモニウム、アルキルアンモニウム又は置換アルキルアンモニウム
m4:0以上2以下の数
を示す〕 - 多糖誘導体を、水硬性粉体100質量部に対して、0.0010質量部以上0.0200質量部以下含有する請求項1又は2に記載の水硬性組成物。
- アルミニウム粉末を、10g/m3以上100g/m3以下含有する請求項1〜3のいずれかに記載の水硬性組成物。
- 請求項1〜4のいずれかに記載の水硬性組成物を、トンネル内に配設された覆工用型枠に打設する、トンネルの覆工方法。
- 水硬性組成物のスランプフロー値が550mm以上700mm以下である請求項5に記載のトンネル覆工方法。