JP2013244151A - 識別情報記録部の識別情報を蛍光により確認できる義歯を製造する方法及び義歯に蛍光により確認できる識別情報を付与する組成物キット - Google Patents
識別情報記録部の識別情報を蛍光により確認できる義歯を製造する方法及び義歯に蛍光により確認できる識別情報を付与する組成物キット Download PDFInfo
- Publication number
- JP2013244151A JP2013244151A JP2012119384A JP2012119384A JP2013244151A JP 2013244151 A JP2013244151 A JP 2013244151A JP 2012119384 A JP2012119384 A JP 2012119384A JP 2012119384 A JP2012119384 A JP 2012119384A JP 2013244151 A JP2013244151 A JP 2013244151A
- Authority
- JP
- Japan
- Prior art keywords
- identification information
- weight
- denture
- meth
- fluorescence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】義歯の義歯床の表面を削り取った識別情報記録部に、テトラヒドロフルフリル(メタ)アクリレートと2−ヒドロキシエチルメタクリレートとの単量体混合物とジ(メタ)アクリレートモノマーと光重合触媒とから成る歯科用プライマーを塗布し、光照射して重合させ、次に当該部位に、(メタ)アクリレートモノマーと特定平均粒子径のシリカ粉末と蛍光剤と光重合触媒とから構成され、硬化後に60〜98%の透過率を有する歯科用組成物を当該部位に充填し、光照射して重合硬化させた後に表面を研磨することにより波長が310〜430nmにピークを有する光を照射すると識別情報記録部の識別情報を蛍光により確認できる義歯を製造する。
【選択図】なし
Description
義歯の義歯床の表面に識別情報記録部を削り取り、この識別情報記録部に、
テトラヒドロフルフリル(メタ)アクリレートと2−ヒドロキシエチルメタクリレートとの重量割合が1:1〜1:3から成る単量体混合物:60〜90重量%と,ジ(メタ)アクリレートモノマー:10〜40重量%とから成る単量体混合物100重量部に対して,光重合触媒:0.04〜0.5重量部を添加した歯科用プライマーを塗布し、光照射して重合させ、
次に当該部位に、(メタ)アクリレートモノマー:88〜97重量%,平均粒子径0.01〜1μmのシリカ粉末:1〜10重量%,蛍光剤:0.1〜2重量%,光重合触媒:0.2〜0.6重量%から構成され、硬化後に60〜98%の透過率を有する歯科用組成物を当該部位に充填し、光照射して重合硬化させた後に表面を研磨することにより、
波長が310〜430nmにピークを有する光を照射すると識別情報記録部の識別情報を蛍光により確認できる義歯を製造する方法と、
(メタ)アクリレートモノマー:88〜97重量%,平均粒子径0.01〜1μmのシリカ粉末:1〜10重量%,蛍光剤:0.1〜2重量%,光重合触媒:0.2〜0.6重量%から構成され、硬化後に60〜98%の透過率を有する歯科用組成物と、
テトラヒドロフルフリル(メタ)アクリレートと2−ヒドロキシエチルメタクリレートとの重量割合が1:1〜1:3から成る単量体混合物:60〜90重量%と,ジ(メタ)アクリレートモノマー:10〜40重量%とから成る単量体混合物100重量部に対して,光重合触媒:0.04〜0.5重量部を添加した歯科用プライマーと
から成る義歯に蛍光により確認できる識別情報を付与する組成物キット
とである。
本発明に係る組成物キットの歯科用組成物で使用する(メタ)アクリレートモノマーは、従来から歯科用材料で使用されてきた物質が使用可能である。具体的には、1つの不飽和二重結合を有する(メタ)アクリレートモノマーとして、メチルメタクリレート、エチルメタクリレート、イソプロピルメタクリレート、2−ヒドロキシエチルメタクリレート、3−ヒドロキシプロピルメタクリレート、n−ブチルメタクリレート、イソブチルメタクリレート、ヒドロキシプロピルメタクリレート、テトラヒドロフルフリルメタクリレート、グリシジルメタクリレート、2−メトキシエチルメタクリレート、2−エチルヘキシルメタクリレート、ベンジルメタクリレートの各モノマー、及びこれらのアクリレートの各モノマーが例示できる。
また、不飽和二重結合を4個以上含有する(メタ)アクリレートモノマーとしては、1,3,5−トリス[1,3−ビス((メタ)アクリロイルオキシ)−2−プロポキシカルボニルアミノヘキサン]−1,3,5−(1H,3H,5H)トリアジン−2,4,6−トリオンのモノマー及びこのアクリレートの各モノマーが使用できる。
本発明に係る組成物キットの歯科用組成物においては、(メタ)アクリレートモノマーの不飽和二重結合の数等に関係なく、これ等は夫々1種又は2種以上を混合して用いることができる。これらの(メタ)アクリレートモノマーは、後述する特定のシリカ粉末と組み合わせた時に硬化した後の透過率が60〜98%(濁度計にて測定する)となるように後述するシリカ粉末との組合せを適宜選択して使用すると、義歯の義歯床に使用した際に識別情報が目立たず外部から簡単に視認されない。
光重合型開始剤は、紫外線又は可視光線等の活性光線を照射することにより重合反応が達せられる。光源としては超高圧、高圧、中圧及び低圧の各種水銀灯、ケミカルランプ、カーボンアーク灯、メタルハライドランプ、蛍光ランプ、タングステンランプ、キセノンランプ、アルゴンイオンレーザー、発光ダイオードを使用した歯科用光照射装置等が使用される。
次に、歯科用プライマーが塗布・重合された部位に歯科用組成物を充填する。充填操作は、例えばシリンジ等に充填された歯科用組成物をそのシリンジのノズルから押し出して義歯の義歯床の表面の切削された部位に充填すればよい。
次に、充填された歯科用組成物に歯科用プライマーと同様に光照射を行い重合硬化させる。そして硬化後の表面を研磨することで識別情報を含んだ義歯が作製される。
しかし、識別情報を確認する状況、即ち、不運にも使用者が災害に遭遇し、義歯が残った場合には、義歯の義歯床の表面に対して波長310〜430nmにピークを有する光を照射することによって識別情報を確認することができるのである。
表中の略語はそれぞれ以下の通りである。
UTMA:1,3,5−トリス[1,3−ビス((メタ)アクリロイルオキシ)−2−プロポキシカルボニルアミノヘキサン]−1,3,5−(1H,3H,5H)トリアジン−2,4,6−トリオン
NPG:ネオペンチルグリコールジメタクリレート
3G:トリエチレングリコールジメタアクリレート
TMPT:トリメチロールプロパントリメタクリレート
TF:2,5−ビス(5’−t−ブチルベンゾオキサゾリル−2’)チオフェン
DME:4−ジメチルアミノ安息香酸メチル
DMI:4−ジメチルアミノ安息香酸イソアミル
HEMA:2−ヒドロキシエチルメタクリレート
<透過率>
実施例及び比較例に記載された歯科用組成物を直径20mm×高さ0.5mmの金型に充填し、歯科用光照射装置(商品名 ラボライトLVIII,ジーシー社製)にて片面3分間ずつ光照射して、重合を行い、試験体を作製した。その後、濁度計(商品名 濁度計WA6000,日本電色工業製)を使用して透過率の測定を行った。
歯科用補綴物材料として、説明書の指示に従い重合を行い、20mm×20mm×2mmの大きさに切断された義歯床用レジン(商品名 アクロン,ジーシー社製)を使用した。表面を削り、その部位に実施例及び比較例に記載された歯科用プライマーを筆を用いて塗布した塗布後に、光照射器を用いて光照射し重合させ、次いで歯科用組成物の充填を行い、光照射器を用いて光照射し重合させ、官能評価にて充填性がよければ○、悪ければ×と評価した。
義歯の義歯床として、説明書の指示に従い重合を行い、50mm×50mm×4mmの大きさに切断された義歯床用レジン(商品名 アクロン,ジーシー社製)を使用した。表面を削り、その部位に実施例及び比較例に記載された歯科用プライマー及び歯科用組成物を適用し、それぞれに対して前記ラボライトLVIIIにて各3分間重合硬化後、重合硬化表面を研磨して識別情報を含んだレジン製の歯科用補綴物を作製した。識別状況を目視にて確認し、重合硬化後の充填物が識別できなければ○、目視にて識別が容易にできれば×と評価した。
前記識別試験で作製された歯科用補綴物の記録場所に対して、励起波長が310〜430nmにピークを有する光を照射した。記録された識別情報の確認を目視にて行い、識別情報が明確に判別できれば○、確認が難しければ×として評価した。
Claims (3)
- 義歯の義歯床の表面に識別情報記録部を削り取り、この識別情報記録部に、
テトラヒドロフルフリル(メタ)アクリレートと2−ヒドロキシエチルメタクリレートとの重量割合が1:1〜1:3から成る単量体混合物:60〜90重量%と,ジ(メタ)アクリレートモノマー:10〜40重量%とから成る単量体100重量部に対して,光重合触媒:0.04〜0.5重量部を添加した歯科用プライマーを塗布し、光照射して重合させ、
次に当該部位に、(メタ)アクリレートモノマー:88〜97重量%,平均粒子径0.01〜1μmのシリカ粉末:1〜10重量%,蛍光剤:0.1〜2重量%,光重合触媒:0.2〜0.6重量%から構成され、硬化後に60〜98%の透過率を有する歯科用組成物を当該部位に充填し、光照射して重合硬化させた後に表面を研磨することにより、
波長が310〜430nmにピークを有する光を照射すると識別情報記録部の識別情報を蛍光により確認できる義歯を製造する方法。 - 照射する光の波長が、350〜420nmにピークを有する光である請求項1に記載の義歯を製造する方法。
- (メタ)アクリレートモノマー:88〜97重量%,平均粒子径0.01〜1μmのシリカ粉末:1〜10重量%,蛍光剤:0.1〜2重量%,光重合触媒:0.2〜0.6重量%から構成され、硬化後に60〜98%の透過率を有する歯科用組成物と、
テトラヒドロフルフリル(メタ)アクリレートと2−ヒドロキシエチルメタクリレートとの重量割合が1:1〜1:3から成る単量体混合物:60〜90重量%と,ジ(メタ)アクリレートモノマー:10〜40重量%とから成る単量体100重量部に対して,光重合触媒:0.04〜0.5重量部を添加した歯科用プライマーと
から成る義歯に蛍光により確認できる識別情報を付与する組成物キット。