JP2012254779A - 空気入りタイヤ - Google Patents
空気入りタイヤ Download PDFInfo
- Publication number
- JP2012254779A JP2012254779A JP2012046449A JP2012046449A JP2012254779A JP 2012254779 A JP2012254779 A JP 2012254779A JP 2012046449 A JP2012046449 A JP 2012046449A JP 2012046449 A JP2012046449 A JP 2012046449A JP 2012254779 A JP2012254779 A JP 2012254779A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- styrene
- sibs
- thermoplastic elastomer
- inner liner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】カーカスプライ6の内側にインナーライナー9を備えた空気入りタイヤ1であって、インナーライナーは、タイヤ内側に配置される第1層と、カーカスプライのゴム層と接するように配置される第2層で構成され、第1層は、スチレン−イソブチレン−スチレンブロック共重合体および、そのスチレンブロック部分が不飽和結合を有する酸塩化物もしくは酸無水物で変性されたSIBS変性共重合体の少なくともいずれかを含む熱可塑性エラストマーと紫外線吸収剤または酸化防止剤の少なくともいずれかとを含む熱可塑性エラストマー組成物であり、第2層は、スチレン−イソプレン−スチレンブロック共重合体およびスチレン−イソブチレンブロック共重合体の少なくともいずれかを含む熱可塑性エラストマー組成物である。
【選択図】図1
Description
本発明はタイヤ内側にインナーライナーを備えた空気入りタイヤを図に基づいて説明する。図1は、空気入りタイヤの右半分の概略断面図である。図において空気入りタイヤ1は、トレッド部2と、該トレッド部両端からトロイド形状を形成するようにサイドウォール部3とビード部4とを有している。さらに、ビード部4にはビードコア5が埋設される。また、一方のビード部4から他方のビード部に亘って設けられ、両端をビードコア5のまわりに巻き返して係止されるカーカスプライ6と、該カーカスプライ6のクラウン部外側には、少なくとも2枚のプライよりなるベルト層7とが配置されている。
本発明においてインナーライナーは、タイヤ内側に配置され、且つ熱可塑性エラストマー組成物よりなる第1層と、前記カーカスプライのゴム層と接して配置される熱可塑性エラストマー組成物よりなる第2層で構成されている。ここで熱可塑性エラストマー組成物とは、ポリマー成分として熱可塑性エラストマーまたはゴム成分を含む組成物を意味する。但し、添加剤として配合するゴム成分、例えば、ポリイソブチレンは、本発明においては、熱可塑性エラストマー成分には含めないものとする。
本発明において前記第1層は、スチレン−イソブチレン−スチレンブロック共重合体(以下、「SIBS」ともいう。)および、そのスチレンブロック部分が不飽和結合を有する酸塩化物もしくは酸無水物で変性されたスチレン−イソブチレン−スチレンブロック共重合体(以下、「SIBS変性共重合体」ともいう。)の少なくともいずれかを含む熱可塑性エラストマー組成物で形成される。
SIBSは、分子鎖中にイソブチレンブロックを含んでいるため、そのポリマーフィルムは優れた耐空気透過性を有する。したがって、SIBSをインナーライナーに用いた場合には耐空気透過性に優れた空気入りタイヤを得ることができる。さらに、SIBSは、その分子構造において、芳香族単位以外は飽和しているため、酸化劣化が抑制される。
前記第1層は、SIBS変性共重合体を熱可塑性エラストマー成分の10質量%〜100質量%含む組成物である。ここでSIBS変性共重合体は、スチレン−イソブチレン−スチレンブロック共重合体(SIBS)のスチレンブロック部分が不飽和結合を有する酸塩化物もしくは酸無水物で変性されたものであり、分子鎖中に次の式(1)の化学構造を含んでいる。
本発明で変性に用いられる不飽和結合を有する酸塩化物とは、メタクリル酸クロライド、メタクリル酸ブロマイド、メタクリル酸ヨウダイド、アクリル酸クロライド、アクリル酸ブロマイド、アクリル酸ヨウダイド、クロトニル酸クロライドおよびクロトニル酸ブロマイドが例示される。特に、メタクリル酸クロライド、アクリル酸クロライドが好適である。
SIBSは、一般的なビニル系化合物のリビングカチオン重合法により得ることができ。例えば、特開昭62−48704号公報および特開昭64−62308号公報には、イソブチレンと他のビニル化合物とのリビングカチオン重合が可能であり、ビニル化合物にイソブチレンと他の化合物を用いることでポリイソブチレン系のブロック共重合体を製造できることが開示されている。
前記第1層はSIBS変性共重合体を主体とする熱可塑性エラストマー組成物である。即ち、熱可塑性エラストマー成分中にSIBS変性共重合体を90質量%以上含む。ここで熱可塑性エラストマーは、スチレン系熱可塑性エラストマー、ウレタン系熱可塑性エラストマーなどが好適に使用できる。
本発明において、エラストマー組成物は紫外線吸収剤が配合されている。紫外線吸収剤は、波長290nm以上の紫外線領域の光を吸収し高分子化合物の分子鎖の劣化を防止する。例えば、ベンゾフェノン系、サリチレート系およびベンゾトリアゾール系の紫外線吸収剤は高分子化合物が最も劣化を受けやすい波長320nm〜350nm付近の紫外線光を吸収する。この波長域の光を振動エネルギーまたは熱エネルギーに変換することで高分子化合物への吸収を防止する機能を有する。特に、ベンゾトリアゾール系紫外線吸収剤が幅広い紫外線光を吸収できる。ここで、紫外線吸収剤を例示すれば次のとおりである。
TINUVIN P/FL(BASF社製、分子量225、融点128〜132℃、最大吸収波長341nm)(2−(2−ヒドロキシ−ベンゾトリアゾール−2−イル)−p−クレゾール)
TINUVIN 234(BASF社製、分子量447.6、融点137〜141℃、最大吸収波長343nm)(2−[2−ヒドロキシ−3,5−ビス(α、α’ジメチルベンジル)フェニル]−2H−ベンゾトリアゾール)
TINUVIN 326/FL(BASF社製、分子量315.8、融点138〜141℃、最大吸収波長353nm)、アデカスタブLA−36((株)ADEKA製)(2−(2’−ヒドロキシ−3’−tert−ブチル−5’−メチルフェニル)−5−クロロベンゾトリアゾール)
TINUVIN 237(BASF社製、分子量338.4、融点139〜144℃、最大吸収波長359nm)(2,4−ジ−t−ブチル−6−(5−クロロベンゾトリアゾール−2−イル−)フェノール)
TINUVIN 328(BASF社製、分子量351.5、融点80〜88℃、最大吸収波長347nm)(2−(3,5−ジ−t−アミル−2−ヒドロキシフェニル)ベンゾトリアゾール)
TINUVIN 329/FL(BASF社製、分子量323、融点103〜105℃、最大吸収波長343nm)(2−(2−ヒドロキシ−ベンゾトリアゾール−2−イル)−4−tert−オクチルフェノール)。
TINUVIN 213(BASF社製、融点−40℃、最大吸収波長344nm)(5−(2−ヒドロキシ−ベンゾトリアゾール−2−イル)−4−ヒドロキシ−3−tert−ブチルベンゼンプロパン酸メチル)
TINUVIN 571(BASF社製、分子量393.6、融点−56℃、最大吸収波長343nm)(2−(2−ヒドロキシ−ベンゾトリアゾール−2−イル)−4−メチル−6−ドデシルフェノール)。
TINUVIN 1577FF(BASF社製、分子量425、融点148℃、最大吸収波長274nm)(2−[4,6−ジフェニル−1,3,5−トリアジン−2−イル]−5−(ヘキシルオキシ)フェノール)。
CHIMASSORB 81/FL(BASF社製、分子量326.4、融点48〜49℃)(2−ヒドロキシ−4−(オクチルオキシ)ベンゾフェノン)。
TINUVIN 120(BASF社製、分子量438.7、融点192〜197℃、最大吸収波長265nm)(2,4−ジ−tert−ブチルフェニル−3,5−ジ−tert−ブチル−4−ヒドロキシベンゾエート)。
CHIMASSORB 2020 FDL(BASF社製、分子量2600〜3400、融点130〜136℃)(ジブチルアミン1,3,5−トリアジン・N,N−ビス(2,2,6,6−テトラメチル−4−ピペリジル−1,6−ヘキサメチレンジアミン・N−(2,2,6,6−テトラメチル−4−ピペリジル)ブチルアミンの重縮合物)
CHIMASSORB 944 FDL(BASF社製、分子量2000〜3100、融点100〜135℃)(ポリ[{6−(1,1,3,3−テトラメチルブチル)アミノ−1,3,5−トリアジン−2,4−ジイル}{(2,2,6,6−テトラメチル−4−ピペリジル)イミノ}ヘキサメチレン{2,2,6,6−テトラメチル−4−ピペリジル)イミノ}])
TINUVIN 622 LD(BASF社製、分子量3100〜4000、融点55〜70℃)(ブタン二酸1−[2−(4−ヒドロキシ−2,2,6,6−テトラメチルピペリジノ)エチル])
TINUVIN 144(BASF社製、分子量685、融点146〜150℃)(2−ブチル−2−[3,5−ジ(tert−ブチル)−4−ヒドロキシベンジル]マロン酸ビス(1,2,2,6,6−ペンタメチル−4−ピペリジル)
TINUVIN 292(BASF社製、分子量509)(セバシン酸ビス(1,2,2,6,6−ペンタメチル−4−ピペリジニル))
TINUVIN 770 DF(BASF社製、分子量481、融点81〜85℃)(セバシン酸ビス(2,2,6,6−テトラメチルピペリジン−4−イル)。
本発明において、エラストマー組成物は酸化防止剤が配合されている。酸化防止剤は、ラジカル補足剤として機能し、主に炭素ラジカルを補足することで、高分子の分子鎖の劣化を防止できる。酸化防止剤を以下に例示する。
IRGANOX1010(BASF製)、アデカスタブAO−60((株)ADEKA製)、スミライザーBP−101(住友化学(株)製)(ペンタエリスリチル・テトラキス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート])、
IRGANOX1035(BASF製)(2,2−チオ−ジエチレンビス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート])、
IRGANOX1076(BASF製)(オクタデシル−3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート)、
IRGANOX1098(BASF製)(N,N’−ヘキサメチレンビス(3,5−ジ−t−ブチル−4−ヒドロキシ−ヒドロシンナマミド))、
IRGANOX1135(BASF製)(イソオクチル−3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート])、
IRGANOX1330(BASF製)(1,3,5−トリメチル−2,4,6−トリス(3,5−ジ−t−ブチル−4−ヒドロキシベンジル)ベンゼン)、
IRGANOX1726(BASF製)(4,6−ビス(ドデシルチオメチル)−O−クレゾール)、
IRGANOX1425(BASF製)(ビス(3,5−ジ−t−ブチル−4−ヒドロキシベンジルホスホン酸エチル)カルシウム(50%)、ポリエチレンワックス(50%))
IRGANOX1520(BASF製)(2,4−ビス[(オクチルチオ)メチル]−O−クレゾール)、
IRGANOX245(BASF製)(トリエチレングリコール−ビス[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)プロピオネート])、
IRGANOX259(BASF製)(1,6−ヘキサンジオール−ビス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート])、
IRGANOX3114(BASF製)(トリス−(3,5−ジ−t−ブチル−4−ヒドロキシベンジル)−イソシアヌレイト)、
IRGANOX5057(BASF製)(オクチル化ジフェニルアミン)、
IRGANOX565(BASF製)(2,4−ビス−(n−オクチルチオ)−6−(4−ヒドロキシ−3,5−ジ−t−ブチルアニリノ)−1,3,5−トリアジン)
サイアノックスCY1790(サンケミカル(株)製)(1,3,5−トリス(4−t−ブチル−3−ヒドロキシ−2,6−ジメチルベンジル)イソシアヌル酸)
アデカスタブAO−40((株)ADEKA製)、スミライサーBBM(住友化学(株)製)(4,4’−ブチリデンビス(3−メチル−6−t−ブチルフェノール))
アデカスタブAO−50((株)ADEKA製)、スミライザーBP-76(住友化学(株)製)(ステアリル−β−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート)
アデカスタブAO−80((株)ADEKA製)、スミライザーGA-80(住友化学(株)製)(3,9−ビス[1,1−ジメチル−2−[β−(3−t−ブチル−4−ヒドロキシ−5−メチルフィエニル)プロピオニルオキシ]エチル]2,4,8,10−テトラオキサスピロ[5,5]−ウンデカン)。
リン系酸化防止剤は、過酸化物分解剤として使用され、熱加工成型時の酸化防止機能に優れており、例えば、以下のものがある
IRGAFOS12(BASF製、分子量1462.9)(6,6’,6’’−[ニトリロトリス(エチレンオキシ)]トリス(2,4,8,10−テトラ−tert−ブチルベンゾ[d,f][1,3,2]ジオキサホスフェピン))、
IRGAFOS38(BASF製、分子量514)(亜リン酸エチルビス(2,4−ジ−tert−ブチル−6−メチルフェニル))、
IRGAFOS168(BASF製、分子量646)、アデカスタブ2112((株)ADEKA製)、スミライザーP−16(住友化学(株)製)(トリス(2,4−ジ−t−ブチルフェニル)フォスファイト)
アデカスタブPEP−8((株)ADEKA製)(ジステアリルペンタエリスリトールジフォスファイト)
アデカスタブPEP−36((株)ADEKA製)(サイクリックネオペンタンテトライルビス(2,6−ジ−t−ブチル−4−メチルフェイニル)フォスファイト)。
IRGASTAB FS 042(BASF製)(N,N−ジオクタデシルヒドロキシルアミン)。
IRGANOX B 225(BASF製)(IRGAFOS168:IRGANOX1010=1:1)
IRGANOX215(BASF製)(IRGAFOS168:IRGANOX1010=2:1)
IRGANOX220(BASF製)(IRGAFOS168:IRGANOX1010=3:1)
IRGANOX921(BASF製)(IRGAFOS168:IRGANOX1076=2:1)。
本発明において酸化防止剤は酸素吸収剤を包含する概念である。酸素吸収剤は空気中の酸素捕捉能がある一般的な酸素吸収剤を用いることができ、例えば、鉄粉の酸化反応を利用して空気中の酸素を吸収する鉄粉末酸素吸収剤をあげることができ、通常、表面積が0.5m2/g以上の鉄粉100重量部に対し、0.1〜50重量部のハロゲン化金属、例えば塩化ナトリウム、臭化ナトリウム、塩化カルシウム、塩化マグネシウムなどのアルカリ金属またはアルカリ土類金属の塩素、臭素、ヨウ素などのハロゲン化物を組合せて用いる。これは両者の混合物として、また鉄粉表面をハロゲン化金属で被覆したものでもよい。なお、本発明に用いる酸素吸収剤にはさらにゼオライトなどの多孔性粒子に水分を含浸させたものをさらに組合せて前記酸素による鉄の酸化をさらに促進させることができる。特に、炭素ラジカルのラジカルトラップ剤としてヒンダードフェノール系酸化防止剤が好ましい。
第1層の厚さは、0.05〜0.6mmである。第1層の厚さが0.05mm未満であると、第1層と第2層よりなるポリマー積層体をインナーライナーに適用した生タイヤの加硫時に、第1層がプレス圧力で破れてしまい、得られたタイヤにおいてエアーリーク現象が生じる虞がある。一方、第1層の厚さが0.6mmを超えるとタイヤ重量が増加し、低燃費性能が低下する。第1層の厚さは、さらに0.05〜0.4mmであることが好ましい。第1層は、押出成形、またはカレンダー成形といった熱可塑性樹脂、もしくは熱可塑性エラストマーをフィルム化する通常の方法が採用できる。
前記第2層は、スチレン−イソプレン−スチレンブロック共重合体(以下、「SIS」ともいう。)およびスチレン−イソブチレンブロック共重合体(以下、「SIB」ともいう。)の少なくともいずれかを含む熱可塑性エラストマー組成物である。
本発明では第2層をSISとSIBSの混合物、またはSIBとSIBSの混合物で構成することができる。この場合、SIBSの配合量は、熱可塑性エラストマー成分の10〜80質量%、好ましくは30〜70質量%の範囲で調整される。SIBSが10質量%より少ないと第1層との接着性が低下し、SIBSが80質量%を超えるとカーカスプライとの接着性が低下する傾向がある。
本発明において、前記第1層及び第2層の少なくともいずれかは、熱可塑性エラストマー成分100質量に対し、粘着付与剤が0.1〜100質量部は配合される。ここで粘着付与剤とは、熱可塑性エラストマー組成物の粘着性を増進するための配合剤をいい、例えば次の粘着付与剤が例示される。
本発明において、インナーライナーは前記第1層と第2層で構成されるポリマー積層体が使用される。ここで第1層、第2層は熱可塑性エラストマーの組成物であり、加硫温度、例えば150℃〜180℃において、金型中で軟化状態にある。軟化状態とは分子運動性が向上し固体と液体の中間状態を意味する。また、熱可塑性エラストマー組成物が軟化状態では、固体状態よりも反応性が向上するため、隣接する部材と粘着、または接着する。そのため熱可塑性エラストマー組成物の形状変化、隣接部材との粘着、および隣接部材との融着を防止するために、タイヤの製造の際には冷却工程を設けることが好ましい。冷却工程は、タイヤ加硫後に、10〜300秒間、50〜120℃に急冷しブラダー部内を冷却することができる。冷却媒体としては、空気、水蒸気、水およびオイルより選択される1種以上が使用される。かかる冷却工程を採用することで、インナーライナーを0.05〜0.6mmの範囲の薄いインナーライナーを形成することが容易となる。
本発明の空気入りタイヤは、一般的な製造方法を用いることができる。まず前記ポリマー積層体PLを用いてインナンーライナーを製造する。空気入りタイヤ1の生タイヤに前記インナーライナーを適用して他の部材とともに加硫成形することによって製造することができる。ポリマー積層体PLを生タイヤに配置する際は、ポリマー積層体PLの第2層であるSIS層PL2またはSIB層PL3が、カーカスプライ6に接するようにタイヤ半径方向外側に向けて配置する。このように配置すると、タイヤ加硫工程において、SIS層PL2またはSIB層PL3とカーカス61との接着強度を高めることができる。得られた空気入りタイヤは、インナーライナーとカーカスプライ6のゴム層とが良好に接着しているため、優れた耐空気透過性および耐久性を有することができる。
本発明の第1層および第2層よりなるポリマー積層体の製造に用いた熱可塑性エラストマー(SIB、SIBS、SIS及びSIBS変性共重合体)、紫外線吸収剤、酸化防止剤は以下のとおり調整した。
攪拌機付き2L反応容器に、メチルシクロヘキサン(モレキュラーシーブスで乾燥したもの)589mL、n−ブチルクロライド(モレキュラーシーブスで乾燥したもの)613ml、クミルクロライド0.550gを加えた。反応容器を−70℃に冷却した後、α−ピコリン(2−メチルピリジン)0.35mL、イソブチレン179mLを添加した。さらに四塩化チタン9.4mLを加えて重合を開始し、−70℃で溶液を攪拌しながら2.0時間反応させた。次に反応容器にスチレン59mLを添加し、さらに60分間反応を続けた後、大量のメタノールを添加して反応を停止させた。反応溶液から溶剤などを除去した後に、重合体をトルエンに溶解して2回水洗した。このトルエン溶液をメタノール混合物に加えて重合体を沈殿させ、得られた重合体を60℃で24時間乾燥することによりスチレン−イソブチレンジブロック共重合体を得た(スチレン成分含有量:15質量%、重量平均分子量:70,000)。
カネカ(株)社製の「シブスターSIBSTAR 102T(ショアA硬度25、スチレン成分含有量25質量%、重量平均分子量:100,000)」を用いた。
クレイトンポリマー社製のD1161JP(スチレン成分含有量15質量%、重量平均分子量:150,000)を用いた。
2リットルのセパラブルフラスコにスチレン―イソブチレンブロック共重合体75g(スチレン含量30%、スチレンユニットのモル数0.216モル)を入れて、容器内を窒素で置換した。注射器を用いて、モレキュラーシーブスで乾燥したn−ヘキサン1200mL及びモレキュラーシーブスで乾燥したn−ブチルクロリド1800ミリリットルを加えた。
(株)ADEKA社製のベンゾトリアゾール系紫外線吸収剤として「アデカスタブLA−36」(2−(2’−ヒドロキシ−3’−ter−ブチル−5’−メチルフェニル)−5−クロロベンゾトリアゾール)を用いた。この紫外線吸収剤は融点が138〜141℃、分子量315.8、最大吸収波長が353nmである。
BASF社製のヒンダードフェノール系酸化防止剤として「IRGANOX 1010」(ペンタエリスリチル・テトラキス(3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート)を用いた。この酸化防止剤の融点は110〜125℃であり、比重が1.15、分子量が117.7である。
(注2)ポリイソブチレン:新日本石油(株)社製、「テトラックス3T」(粘度平均分子量30,000、重量平均分子量、49,000)。
表1、表2の実施配合、比較配合に基づき、SIBS変性共重合体、SIBS、SISおよびSIBなどの熱可塑性エラストマー組成物を、2軸押出機(スクリュ径:φ50mm、L/D:30、シリンダ温度:220℃)にてペレット化した。その後、Tダイ押出機(スクリュ径:φ80mm、L/D:50、ダイリップ幅:500mm、シリンダ温度:220℃、フィルムゲージ:第1層は0.25mm、第2a層及び第2b層は、いずれも0.05mm)にてインナーライナーを作製した。
空気入りタイヤは、図1に示す基本構造を有する195/65R15サイズのものを製造した。上記ポリマー積層体をインナーライナーに用いて生タイヤを製造し、170℃で20分間プレス加硫を行った。加硫タイヤを加硫金型から取り出すことなく、110℃で3分間冷却した後に加硫金型から取り出した。冷却媒体としては水を使用した。
比較例1〜3は、第1層にSIBSを、第2層にSISを用いたインナーライナーの例である。比較例4は、第1層にSIBS変性共重合体を、第2層にSISを用いたインナーライナーの例である。比較例5、6は、第1層にSIBSとSIBS変性共重合体の混合物を、第2層にSISを用いたインナーライナーの例である。比較例7は、第1層にSIBSを、第2層としてSIS(第2a層)と、SIB(第2b層)の複合層を用いたインナーライナーの例である。
第1層及び第2層に紫外線吸収剤または酸化防止剤のいずれかが、若しくは両者の合計が熱可塑性エラストマー100質量%に対し、0.5〜40質量%となるように混合した例である。
前述の如く製造された空気入りタイヤに関し、以下の性能試験をおこなった。
インナーライナー内部について、スガ試験機(株)製サンシャインスーパーロングライフウェザーメーターを用いて、次の条件で耐候性試験を行った。槽内温度63℃、湿度50%、60℃中、12分間降雨の条件で60時間照射し、試験後のインナーライナーの亀裂個数を求めた。比較例1を基準として、他の比較例、実施例との亀裂個数の相対値を求め、以下の式に基づき耐候性指数を算出した。数値が大きいほど耐候性に優れている
耐候性指数=(比較例1の亀裂個数)/(各実施例の亀裂個数)×100。
耐久走行試験は、インナーライナーが割れたり剥がれたりするかどうかで評価した。試作タイヤをJIS規格リム15×6JJに組み付け、タイヤ内圧は150KPaで通常よりも低内圧に設定し、荷重は600kg、速度100km/h、走行距離20,000kmでタイヤの内部を観察し、亀裂、剥離の数を測定した。比較例1を基準として、各比較例、実施例の亀裂成長性を指数で表示した。指数の値が大きいほど、屈曲亀裂成長が小さいことを示す
屈曲亀裂成長指数=(比較例1の亀裂の数)/(各実施例の亀裂の数)×100。
屈曲亀裂成長試験と同様な条件で、走行する前と20,000km走行した後において、空気入りタイヤのインナーライナーを粘弾性スペクトロメータVES((株)岩本製作所)を用いて、温度70℃、初期歪10%、動歪2%の条件下で動的弾性率(E’)の上昇率を評価した。
弾性率の変化率=(走行後の弾性率)/(走行前の弾性率)×100
弾性率変化指数=(比較例1の弾性率の変化率)/(各実施例の弾性率の変化率)×100。
耐久走行試験は、酸素注入下でタイヤが損傷するまでの走行距離を測定した。試作タイヤを酸素90%、相対湿度70%雰囲気下で336時間放置し、その後、リム組みを行い100%酸素注入し、内圧350kPaで酸素90%、相対湿度70%の雰囲気下において336時間放置する。その後、JIS規格リム15×6JJに組み付け、100%酸素を注入しタイヤ内圧は280kPaに設定しタイヤを準備する。
耐久走行速度指数=(各実施例の故障時の走行速度)/(比較例1の故障時の走行速度)×100。
判定Aは、次の条件をすべて満たしたものをいう
(a)耐候性指数が100以上
(b)屈曲亀裂成長指数が100以上
(c)弾性率変化指数が100以上
(d)耐久走行速度指数が100より大きい。
(a)耐候性指数が100以下
(b)屈曲亀裂成長指数が100以下
(c)弾性率変化指数が100以下
(d)耐久走行速度指数が100より大きい。
Claims (5)
- 一対のビード部の間に装架されたカーカスプライのタイヤ内側にインナーライナーを備えた空気入りタイヤであって、
前記インナーライナーは、タイヤ内側に配置される第1層と、前記カーカスプライのゴム層と接するように配置される第2層で構成されており、
前記第1層は、スチレン−イソブチレン−スチレンブロック共重合体および、そのスチレンブロック部分が不飽和結合を有する酸塩化物もしくは酸無水物で変性されたSIBS変性共重合体の少なくともいずれかを含む熱可塑性エラストマーと紫外線吸収剤および酸化防止剤の少なくともいずれかを含む熱可塑性エラストマー組成物であり、
前記第2層は、スチレン−イソプレン−スチレンブロック共重合体およびスチレン−イソブチレンブロック共重合体の少なくともいずれかを含む熱可塑性エラストマー組成物であることを特徴とする空気入りタイヤ。 - 前記第1層は、紫外線吸収剤および酸化防止剤の少なくともいずれかが熱可塑性エラストマー成分の0.5質量%〜40質量%配合されている請求項1記載の空気入りタイヤ。
- 前記第1層および前記第2層のいずれかの熱可塑性エラストマー組成物は、SIBS変性共重合体が熱可塑性エラストマー成分の5質量%〜100質量%配合されている請求項1記載の空気入りタイヤ。
- 前記第1層の熱可塑性エラストマー組成物は、スチレン−イソブチレン−スチレンブロック共重合体とSIBS変性共重合体の混合物である請求項1記載の空気入りタイヤ。
- 前記第1層および前記第2層のいずれかの熱可塑性エラストマー組成物は、粘着付与剤が配合されている請求項1記載の空気入りタイヤ。