JP2012204246A - 非水二次電池電極用バインダー樹脂組成物 - Google Patents
非水二次電池電極用バインダー樹脂組成物 Download PDFInfo
- Publication number
- JP2012204246A JP2012204246A JP2011069466A JP2011069466A JP2012204246A JP 2012204246 A JP2012204246 A JP 2012204246A JP 2011069466 A JP2011069466 A JP 2011069466A JP 2011069466 A JP2011069466 A JP 2011069466A JP 2012204246 A JP2012204246 A JP 2012204246A
- Authority
- JP
- Japan
- Prior art keywords
- secondary battery
- ethylenically unsaturated
- meth
- acrylate
- binder resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】無水マレイン化ポリブタジエン(BP)の酸無水物環を、水酸基を有する化合物(A)によって開環してなるマレイン化ポリブタジエン(B)の存在下、水性媒体中でエチレン性不飽和単量体(C)を乳化重合してなる樹脂微粒子分散体を含む非水二次電池電極用バインダー樹脂組成物。
【選択図】なし
Description
二次電池の電極は、電極活物質、導電助剤、更にはこれらを集電体に結着するバインダーより構成される。二次電池電極用バインダー樹脂には従来、正極、負極共にポリフッ化ビニリデンなどのフッ素樹脂をN−メチルピロリドン等の有機溶剤に溶解させて使用されてきた(非特許文献1、2)。この有機溶媒系バインダー組成物に活物質を分散させたスラリーを電極基体に塗布して、有機溶媒を除去して製造した電極を用いると電池の初期容量を大きくすることができるが、この電極を用いた電池で充放電を繰り返すと電極に固定された活物質が脱落しやすいという問題がある。また、電極作製時の臭気等、人体や環境に対する悪影響も懸念されている。このような問題を解決するために、特許文献1〜3では、乳化重合法により水を溶媒として製造されたスチレン・ブタジエン共重合ゴムのエマルジョン水分散液に、増粘剤としてカルボキシルメチルセルロースを添加した水系バインダー樹脂組成物が開示されている。この水系バインダー樹脂組成物は、有機溶剤系バインダー樹脂組成物に対して、活物質の密着性に優れているが、遊離してくる界面活性剤成分が電極の耐電解液性や電池の充放電サイクル特性を低下させる問題がある。そこで、特許文献4では、エチレン性不飽和カルボン酸を含むエチレン性不飽和単量体を共重合して得られる高酸価の樹脂を乳化剤として、乳化重合したエマルジョンを含む水系バインダー組成物が開示されている。このエマルジョンを水系バインダー樹脂として使用する事で、電池特性に悪影響を及ぼす遊離成分が減少し、電池の充放電サイクル特性が確かに向上するがまだ十分とは言いがたい。
アルコキシシリル基含有エチレン性不飽和単量体、N−メチロール基含有エチレン性不飽和単量体、エポキシ基含有エチレン性不飽和単量体及び1分子中に2つ以上のエチレン性不飽和基を有する単量体からなる群より選ばれる少なくとも1種の単量体0.1〜10重量%を含む、第1ないし第3いずれか発明の非水二次電池電極用バインダー樹脂組成物に関する。
本発明で使用する樹脂微粒子分散体は、水酸基を有する化合物(A)によって酸無水物環が開環されてなるマレイン化ポリブタジエン(B)を乳化剤として、エチレン性不飽和単量体(C)を乳化重合する事により得る事ができる。マレイン化ポリブタジエン(B)はビニル基を多数有しているため、粒子核となるエチレン性不飽和単量体(C)が重合時にグラフトされる。したがって、電池特性に悪影響を及ぼす遊離成分が大幅に低減さる。さらに、マレイン化ポリブタジエン(B)の柔軟な骨格から活物質や集電体への密着性ならびに電極の可とう性にも優れ、電池の充放電サイクル特性が飛躍的に向上する。
このマレイン化ポリブタジエン(B)の前駆体、すなわち、無水マレイン化ポリブタジエン(BP)は、触媒としてのクメンヒドロペルオキシド等の有機過酸化物存在下、1,2−ポリブタジエンと無水マレイン酸を有機溶媒中で付加反応させる事により得る事ができる。また、すでに1,2−ポリブタジエンがマレイン化された市販品を使用しても構わない。無水マレイン化ポリブタジエン(BP)の市販品としては、例えば、日本曹達株式会社製、BN−1015、SARTOMER社製、Ricon130MA8、130MA13、130MA20、131MA5、131MA10、131MA17、131MA20、184MA6、156MA17等が挙げられる。
酸無水物価(mgKOH/g)=[0.02(mol/L)×(ブランクの滴定量−試料の滴定量)(mL)×F]/試料固形量(g)×56.11(mmol/g)
F:0.02mol/L過塩素酸の力価
なお、本発明においては、水も「水酸基を有する化合物(A)」に含まれるものとする。
水、ブチルアルコール、ヘキシルアルコール、オクタノール、デシルアルコール、イソプロピルアルコール、イソブチルアルコール、イソヘプチルアルコール、2−エチルヘキシルアルコール、イソオクチルアルコール、3,5,5−トリメチルヘキシルアルコール、イソノニルアルコール、イソデシルアルコール、イソウンデシルアルコール、イソドデシルアルコール、イソトリデシルアルコール、シクロヘキサノール、ベンジルアルコール、メチルグリコール、メチルジグリコール、メチルトリグリコール、イソプロピルグリコール、ブチルグリコール、ブチルジグリコール、ブチルトリグリコール、イソブチルグリコール、イソブチルジグリコール、ヘキシルグリコール、ヘキシルジグリコール、2−エチルヘキシルグリコール、2−エチルヘキシルジグリコール、アリルグリコール、フェニルグリコール、ベンジルグリコール、ベンジルジグリコール、メチルプロピレングリコール、メチルプロピレンジグリコール、メチルプロピレントリグリコール、プロピルプロピレングリコール、プロピルプロピレンジグリコール、フェニルプロピレングリコール、ポリオキシエチレンモノアルキルエーテル(市販品としては例えば花王社製エマルゲンLS−106、LS−110、LS−114、MS−110、A−60、A−90、A−500、B−66、PP−290)、ポリオキシエチレンモノアルキレンアルキルエーテル(市販品としては例えば花王社製エマルゲン102、103、104、105、108、109、120、123、130、147、150、210、220、306、320、350、404、408、409、420、430、705、707、709、1108、4085)、ポリオキシエチレンモノアルキレンアルケニルエーテル(市販品としては例えば、花王社製ラムテルPD−420、430、450)、ポリオキシエチレンモノアルキルエステル(市販品としては例えば、日本油脂社製ノニオンL−2、L−4、S−2、S−4、S−6、S−10、S−15、S−15.4、S−40、O−2、O−3、O−4、O−6)
2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、
2−ヒドロキシブチル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、2−ヒドロキシー3−アクリロキシプロピルメタクリレート、ペンタエリスリトールトリアクリレート、ポリエチレングリコールモノ(メタ)アクリレート(市販品としては例えば日本油脂社製PE−90、200、350、AE−90、200、400)、ポリプロピレングリコールモノ(メタ)アクリレート(市販品としては例えば日本油脂社製PP−500、800、1000)、ポリエチレングリコール・プロピレングリコールモノメタクリレート(市販品としては、例えば、50PEP−300、70PEP−350B)、乳酸、3−ヒドロキシブタン酸、5-ヒドロキシ-2-プロピルペンタン酸、2−ヒドロキシステアリン酸、ヒドロキシメタンスルホン酸、ヒドロキシテトラデカンスルホン酸等が挙げられるが、特にこれらに限定されるものではない。これらは1種類または2種以上を併用して用いることができる。
エチレン性不飽和基を有する化合物としては、アリルグリコール、アリル基を有するポリオキシエチレンモノアルキレンアルキルエーテル(市販品としては例えば株式会社ADEKA製アデカリアソープER−10、ER−20、ER−30、ER−40)、ポリオキシエチレンモノアルキレンアルケニルエーテル(市販品としては例えば、花王社製ラムテルPD−420、430、450)、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、2−ヒドロキシブチル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、2−ヒドロキシー3−アクリロキシプロピルメタクリレート、ペンタエリスリトールトリアクリレート、ポリエチレングリコールモノ(メタ)アクリレート(市販品としては例えば日本油脂社製PE−90、200、350、AE−90、200、400)、ポリプロピレングリコールモノ(メタ)アクリレート(市販品としては例えば日本油脂社製PP−500、800、1000)、ポリエチレングリコール・プロピレングリコールモノメタクリレート(市販品としては、例えば、50PEP−300、70PEP−350B)
等が挙げられる。
水酸基を有する化合物(A)で酸無水物環を開環されたマレイン化ポリブタジエン(B)は、水性媒体への親和性を高める目的で塩基性化合物により中和することができる。中和する際、アンモニアもしくはトリメチルアミン、トリエチルアミン、ブチルアミンなどのアルキルアミン類;
2−ジメチルアミノエタノール、2−ジエチルアミノエタノール、ジエタノールアミン、トリエタノールアミン、アミノメチルプロパノールなどのアルコールアミン類;
水酸化カリウム、水酸化ナトリウムなどの水酸化物塩;
モルホリン
等の塩基性化合物で中和することができる。
メチル(メタ)アクリレート、エチル(メタ)アクリレート、プロピル(メタ)アクリレート、n−ブチル(メタ)アクリレート、tーブチル(メタ)アクリレート、ペンチル(メタ)アクリレート、ヘプチル(メタ)アクリレート、ヘキシル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、オクチル(メタ)アクリレート、ノニル(メタ)アクリレート、デシル(メタ)アクリレート、ウンデシル(メタ)アクリレート、ドデシル(メタ)アクリレート、トリデシル(メタ)アクリレート、テトラデシル(メタ)アクリレート等の直鎖または分岐アルキル基含有エチレン性不飽和単量体;
シクロヘキシル(メタ)アクリレート、イソボニル(メタ)アクリレート等の脂環式アルキル基含有エチレン性不飽和単量体;
トリフルオロエチル(メタ)アクリレート、ヘプタデカフルオロデシル(メタ)アクリレート等のフッ素化アルキル基含有エチレン性不飽和単量体;
ベンジル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート、フェニル(メタ)アクリレート、スチレン、α−メチルスチレン、o−メチルスチレン、p−メチルスチレン、m−メチルスチレン、ビニルナフタレン等の芳香族エチレン性不飽和単量体;
(メタ)アクリロニトリルなどのニトリル基含有エチレン性不飽和単量体;
(メタ)アクリルアミド、N−メトキシメチル−(メタ)アクリルアミド、N−エトキシメチル−(メタ)アクリルアミド、N−プロポキシメチル−(メタ)アクリルアミド、N−ブトキシメチル−(メタ)アクリルアミド、N−ペントキシメチル−(メタ)アクリルアミド、N,N−ジ(メトキシメチル)アクリルアミド、N−エトキシメチル−N−メトキシメチルメタアクリルアミド、N,N−ジ(エトキシメチル)アクリルアミド、N−エトキシメチル−N−プロポキシメチルメタアクリルアミド、N,N−ジ(プロポキシメチル)アクリルアミド、N−ブトキシメチル−N−(プロポキシメチル)メタアクリルアミド、N,N−ジ(ブトキシメチル)アクリルアミド、N−ブトキシメチル−N−(メトキシメチル)メタアクリルアミド、N,N−ジ(ペントキシメチル)アクリルアミド、N−メトキシメチル−N−(ペントキシメチル)メタアクリルアミド、N,N−ジメチルアミノプロピルアクリルアミド、N,N−ジエチルアミノプロピルアクリルアミド、N,N−ジメチルアクリルアミド、N,N−ジエチルアクリルアミド、ダイアセトン(メタ)アクリルアミド等のアミド基含有エチレン性不飽和単量体;
2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、グリセロールモノ(メタ)アクリレート、4−ヒドロキシビニルベンゼン、1−エチニル−1−シクロヘキサノール、アリルアルコール等のヒドロキシル基含有エチレン性不飽和単量体;
スチレンスルホン酸、スチレンスルホン酸ナトリウム、スチレンスルホン酸アンモニウム、2−アクリルアミド2−メチルプロパンスルホン酸、2−アクリルアミド2−メチルプロパンスルホン酸ナトリウム、メタリルスルホン酸、メタリルスルホン酸、メタリルスルホン酸ナトリウム、アリルスルホン酸、アリルスルホン酸ナトリウム、アリルスルホン酸アンモニウム、ビニルスルホン酸、アリルオキシベンゼンスルホン酸、アリルオキシベンゼンスルホン酸ナトリウム、アリルオキシベンゼンスルホン酸アンモニウム等のスルホン酸基含有エチレン性不飽和単量体;
ポリエチレングリコール(メタ)アクリレート、メトキシポリエチレングリコール(メタ)アクリレート、エトキシポリエチレングリコール(メタ)アクリレート、プロポキシポリエチレングリコール(メタ)アクリレート、n−ブトキシポリエチレングリコール(メタ)アクリレート、n−ペンタキシポリエチレングリコール(メタ)アクリレート、フェノキシポリエチレングリコール(メタ)アクリレート、ポリプロピレングリコール(メタ)アクリレート、メトキシポリプロピレングリコール(メタ)アクリレート、エトキシポリプロピレングリコール(メタ)アクリレート、プロポキシポリプロピレングリコール(メタ)アクリレート、n−ブトキシポリプロピレングリコール(メタ)アクリレート、n−ペンタキシポリプロピレングリコール(メタ)アクリレート、フェノキシポリプロピレングリコール(メタ)アクリレート、ポリテトラメチレングリコール(メタ)アクリレート、メトキシポリテトラメチレングリコール(メタ)アクリレート、フェノキシテトラエチレングリコール(メタ)アクリレート、ヘキサエチレングリコール(メタ)アクリレート、メトキシヘキサエチレングリコール(メタ)アクリレートなどのポリエーテル鎖を有するエチレン性不飽和単量体;
γ−メタクリロキシプロピルトリメトキシシラン、γ−メタクリロキシプロピルトリエトキシシラン、γ−メタクリロキシプロピルトリブトキシシラン、γ−メタクリロキシプロピルメチルジメトキシシラン、γ−メタクリロキシプロピルメチルジエトキシシラン、γ−アクリロキシプロピルトリメトキシシラン、γ−アクリロキシプロピルトリエトキシシラン、γ−アクリロキシプロピルメチルジメトキシシラン、γ−メタクリロキシメチルトリメトキシシラン、γ−アクリロキシメチルトリメトキシシラン、ビニルトリメトキシシラン、ビニルトリエトキシシラン、ビニルトリブトキシシラン、ビニルメチルジメトキシシラン等のアルコキシシリル基含有エチレン性不飽和単量体;
N−メチロール(メタ)アクリルアミド、N,N−ジメチロール(メタ)アクリルアミド、アルキルエーテル化N−メチロール(メタ)アクリルアミド等のメチロール基含有エチレン性不飽和単量体;
グリシジル(メタ)アクリレート、3,4−エポキシシクロヘキシル(メタ)アクリレート等のエポキシ基含有エチレン性不飽和単量体;
アリル(メタ)アクリレート、ビニル(メタ)アクリレート、エチレングリコールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、ポリエチレングリコール(メタ)アクリレート、1,4−ブタンジオールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、1,9−ノナンジオールジ(メタ)アクリレート、1,10−デカンジオールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、グリセリンジメタクリレート、ジメチロールトリシクロデカンジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ペンタエリストールテトラ(メタ)アクリレート、ジビニルベンゼン、アジピン酸ジビニル、イソフタル酸ジアリル、フタル酸ジアリル、マレイン酸ジアリル等の2個以上のエチレン性不飽和基を有するエチレン性不飽和単量体が挙げられるが、特にこれらに限定されるものではない。これらは1種類または2種以上を併用して用いることができる。
2,2’−アゾビスイソブチロニトリル、2,2’−アゾビス−2,4−ジメチルバレロニトリル、2,2’−アゾビス(4−メトキシ−2,4−ジメチルバレロニトリル)、1,1’−アゾビス−シクロヘキサン−1−カルボニトリルなどのアゾビス化合物を挙げることができる。これらは1種類または2種類以上を混合して使用することができる。これら重合開始剤は、エチレン性不飽和単量体100重量部に対して、0.1〜10.0重量部の量を用いるのが好ましい。
アルキルエーテル系(市販品としては、例えば、第一工業製薬株式会社製アクアロンKH−05、KH−10、KH−20、株式会社ADEKA製アデカリアソープSR−10N、SR−20N、花王株式会社製ラテムルPD−104など)、スルフォコハク酸エステル系(市販品としては、例えば、花王株式会社製ラテムルS−120、S−120A、S−180P、S−180A、三洋化成株式会社製エレミノールJS−2など)、アルキルフェニルエーテル系もしくはアルキルフェニルエステル系(市販品としては、例えば、第一工業製薬株式会社製アクアロンH−2855A、H−3855B、H−3855C、H−3856、HS−05、HS−10、HS−20、HS−30、株式会社ADEKA製アデカリアソープSDX−222、SDX−223、SDX−232、SDX−233、SDX−259、SE−10N、SE−20N、など)、(メタ)アクリレート硫酸エステル系(市販品としては、例えば、日本乳化剤株式会社製アントックスMS−60、MS−2N、三洋化成工業株式会社製エレミノールRS−30など)、リン酸エステル系(市販品としては、例えば、第一工業製薬株式会社製H−3330PL、株式会社ADEKA製アデカリアソープPP−70など)等のアニオン系反応性界面活性剤;
アルキルエーテル系(市販品としては、例えば、株式会社ADEKA製アデカリアソープER−10、ER−20、ER−30、ER−40、花王株式会社製ラテムルPD−420、PD−430、PD−450など)、アルキルフェニルエーテル系もしくはアルキルフェニルエステル系(市販品としては、例えば、第一工業製薬株式会社製アクアロンRN−10、RN−20、RN−30、RN−50、株式会社ADEKA製アデカリアソープNE−10、NE−20、NE−30、NE−40など)、(メタ)アクリレート硫酸エステル系(市販品としては、例えば、日本乳化剤株式会社製RMA−564、RMA−568、RMA−1114など)等のノニオン系反応性界面活性剤;
オレイン酸ナトリウムなどの高級脂肪酸塩類、ドデシルベンゼンスルホン酸ナトリウムなどのアルキルアリールスルホン酸塩類、ラウリル硫酸ナトリウムなどのアルキル硫酸エステル塩類、ポリエキシエチレンラウリルエーテル硫酸ナトリウムなどのポリオキシエチレンアルキルエーテル硫酸エステル塩類、ポリオキシエチレンノニルフェニルエーテル硫酸ナトリウムなどのポリオキシエチレンアルキルアリールエーテル硫酸エステル塩類、モノオクチルスルホコハク酸ナトリウム、ジオクチルスルホコハク酸ナトリウム、ポリオキシエチレンラウリルスルホコハク酸ナトリウムなどのアルキルスルホコハク酸エステル塩およびその誘導体類、ポリオキシエチレンジスチレン化フェニルエーテル硫酸エステル塩類
等のアニオン性非反応性界面活性剤;
ポリオキシエチレンラウリルエーテル、ポリオキシエチレンステアリルエーテルなどのポリオキシエチレンアルキルエーテル類、ポリオキシエチレンオクチルフェニルエーテル、ポリオキシエチレンノニルフェニルエーテルなどのポリオキシエチレンアルキルフェニルエーテル類、ソルビタンモノラウレート、ソルビタンモノステアレート、ソルビタントリオレエートなどのソルビタン高級脂肪酸エステル類、ポリオキシエチレンソルビタンモノラウレートなどのポリオキシエチレンソルビタン高級脂肪酸エステル類、ポリオキシエチレンモノラウレート、ポリオキシエチレンモノステアレートなどのポリオキシエチレン高級脂肪酸エステル類、オレイン酸モノグリセライド、ステアリン酸モノグリセライドなどのグリセリン高級脂肪酸エステル類、ポリオキシエチレン・ポリオキシプロピレン・ブロックコポリマー、ポリオキシエチレンジスチレン化フェニルエーテル
等のノニオン性非反応性界面活性剤;
等が挙げられる。
本発明の非水二次電池電極用バインダー樹脂組成物は、二次電池の正極、及び負極に使用することができる。その他、エネルギーデバイス、即ち、キャパシタ、太陽電池などにも使用することができる。
[製造例1]
1,2−ポリブタジエン,NISSO−PB B−1000(日本曹達社製、数平均分子量(以下、Mnと記す)1100、1,2−結合含有量90.5%)173.8部、無水マレイン酸26.2部、反応溶媒としてシクロヘキサノン500.0部、反応触媒としてクメンハイドロパーオキサイド1部を反応容器に仕込み、窒素雰囲気下、攪拌しながら140℃で4時間反応させた。反応液をガスクロマトグラフィー(以下、GCと記す)により分析した結果、未反応の無水マレイン酸は1%以下であり、反応が完結している事が確認された。次いで、反応液を大量のメタノール中に投入してポリマーを析出させ、濾過、洗浄後、60℃で5時間乾燥し、酸無水物環を含有するポリブタジエン樹脂197.0部を得た。得られた樹脂の酸無水物価は75.0mgKOH/gであった。
NISSO−PB B−1000 147.2部と無水マレイン酸52.8部を用いる以外は、製造例1と同様の方法で酸無水物環を含有するポリブタジエン樹脂198.1部を得た。得られた樹脂の酸無水物価は151.1mgKOH/gであった。
NISSO−PB B−1000 191.3部と無水マレイン酸8.7部を用いる以外は、製造例1と同様の方法で酸無水物環を含有するポリブタジエン樹脂197.6部を得た。得られた樹脂の酸無水物価は22.3mgKOH/gであった。
NISSO−PB B−1000 129.2部と無水マレイン酸70.8部を用いる以外は、製造例1と同様の方法でマレイン化ポリブタジエン樹脂197.6部を得た。得られた樹脂の酸無水物価は202.5mgKOH/gであった。
[製造例5]
反応容器に製造例1で得た無水マレイン化ポリブタジエン100.0部、水276.2部、中和剤のジメチルアミノエタノール23.8部を加えて、攪拌しながら70℃で6時間反応させた。冷却後、水に溶解したマレイン化ポリブタジエン水溶液が得られた。更にイオン交換水を加えてマレイン化ポリブタジエン水溶液の固形分を20.0%に調整した。
表1に示す配合組成で、製造例1と同様の方法で合成し、固形分20.0%のマレイン化ポリブタジエン水溶液を調製した。中和剤のジメチルアミノエタノールは、開環したマレイン化ポリブタジエン(B)のカルボキシル基に対して当量になるように添加した。
反応容器に4−ヒドロキシブチルアクリレート38.8部、メチルエチルケトン111.2部、製造例2で得た無水マレイン化ポリブタジエン100.0部、触媒としてジメチルベンジルアミン1.3部を加えて攪拌しながら、70℃で8時間反応させた。反応後、トリエチルアミン27.2部とイオン交換水300.0部を加え、攪拌しながらストリッピングをおこないメチルエチルケトンを除いた。さらにイオン交換水を加えて、固形分20.0%のマレイン化ポリブタジエン水溶液を調製した。
表2に示す組成比で、製造例11と同様の方法で合成し、固形分20.0%のマレイン化ポリブタジエン水溶液を調製した。中和剤のトリエチルアミンは、開環したマレイン化ポリブタジエン(B)のカルボキシル基に対して当量になるように添加した。
[製造例19]
攪拌器、温度計、2つの滴下ロート、還流器を備えた別の反応容器に、製造例5で得たマレイン化ポリブタジエン水溶液500.0部、イオン交換水56.7部を加えて、攪拌しながら、窒素還流下で温度70℃まで昇温した。
別途、スチレン60.4部、2−エチルヘキシルアクリレート37.6部、3−メタクリロキシプロピルトリメトキシシラン2.0部を滴下槽1に、又、過硫酸アンモニウム10%水溶液15.0部を滴下槽2に仕込んだ。滴下槽1、2の内容物を2時間かけて滴下し、重合を行った。滴下終了後、内温を70℃に保ったまま1時間攪拌を続け、固形分測定にて転化率が98%超えたことを確認後、温度を室温まで冷却し、樹脂微粒子水分散体を得た。得られた樹脂微粒子分散体の固形分は30.0%、平均粒子径は115.6nmであった。尚、平均粒子径は、樹脂微粒子分散体を500倍に水希釈し、該希釈液約5mlを動的光散乱測定法(測定装置はマイクロトラック(株)日機装製)により測定した。この時得られた体積粒子径分布データ(ヒストグラム)のピークを平均粒子径とした。
表3に示す配合組成で、製造例19と同様の方法で合成し、樹脂微粒子水分散体を得た。あらかじめ反応容器に仕込んでおくイオン交換水の量は、樹脂微粒子分散体の仕上がり固形分が30.0%なるように調整して加えた。
攪拌器、温度計、滴下ロート、還流器を備えた反応容器に、イオン交換水194.6部と界面活性剤としてドデシルベンゼンスルホン酸ナトリウム0.2部とを仕込み、別途、スチレン118.8部、2−エチルヘキシルアクリレート75.2部、アクリル酸2.0部、3−メタクリロキシプロピルトリメトキシシラン4.0部、イオン交換水87.0部及び界面活性剤としてドデシルベンゼンスルホン酸ナトリウム3.8部をあらかじめ混合しておいたプレエマルジョンのうちの5%を更に加えた。内温を70℃に昇温し十分に窒素置換した後、過硫酸カリウムの5%水溶液24.0部の10%を添加し重合を開始した。反応系内を70℃で5分間保持した後、内温を70℃に保ちながらプレエマルジョンの残りと過硫酸カリウムの5%水溶液の残りを3時間かけて滴下し、更に2時間攪拌を継続した。固形分測定にて転化率が98%超えたことを確認後、温度を室温まで冷却し、樹脂微粒子水分散体を得た。得られた樹脂微粒子分散体の固形分は45.1%、平均粒子径は120.3nmであった。
攪拌器、温度計、2つの滴下ロート、還流器を備えた別の反応容器に、水溶性のスチレンアクリル樹脂であるジョンクリル61J(BASF社製、酸価213、固形分30%水溶液)333.3部、イオン交換水223.3部を加えて、攪拌しながら、窒素還流下で温度70℃まで昇温した。別途、スチレン60.4部、2−エチルヘキシルアクリレート37.6部、3−メタクリロキシプロピルトリメトキシシラン2.0部を滴下槽1に、又、過硫酸アンモニウム10%水溶液15.0部を滴下槽2に仕込んだ。滴下槽1、2の内容物を2時間かけて滴下し、重合を行った。滴下終了後、内温を70℃に保ったまま1時間攪拌を続け、固形分測定にて転化率が98%超えたことを確認後、温度を室温まで冷却し、樹脂微粒子水分散体を得た。得られた樹脂微粒子分散体の固形分は30.0%、平均粒子径は104.2nmであった。
(正極の作製)
正極活物質であるリン酸鉄リチウム(LiFePO4)90部、導電性材料としてアセチレンブラック5部、増粘剤としてカルボキシメチルセルロース2部、製造例19で得られた樹脂微粒子水分散体を固形分として3部に、イオン交換水を固形分50%となるように加えた後、混練して二次電池電極用組成物を調整した。この二次電池電極用組成物を集電体となる厚さ20μmのアルミ箔上にドクターブレードを用いて塗布した後、減圧加熱乾燥し、ロールプレスによる圧延処理を行い、厚さ50μmの正極合剤層を有する正極を作製した。
負極活物質としてメソフェーズカーボン97部、増粘剤としてカルボキシメチルセルロース1部、製造例19で得られた樹脂微粒子水分散体を固形分として2部に、イオン交換水を固形分50%となるように加えた後、混練して二次電池電極用組成物を調整した。この二次電池電極用組成物を集電体となる厚さ20μmの銅箔上にドクターブレードを用いて塗布した後、減圧加熱乾燥し、ロールプレスによる圧延処理を行い、厚さ50μmの負極合剤層を有する負極を作製した。
表4に示す配合組成で、実施例1と同様の方法で調製し、二次電池電極用組成物(正極用及び負極用)及び、正・負極電池電極を得た。尚、比較例3では、樹脂微粒子分散体にBM−400B(日本ゼオン社製 SBRエマルジョン)を使用した。
(正極の作製)
正極活物質であるリン酸鉄リチウム(LiFePO4)を90部、導電性材料としてアセチレンブラック5部、KFポリマーW#1100(株式会社クレハ製 ポリフッ化ビニリデン)を固形分として5部に、N−メチル−2−ピロリドンを固形分50%となるように加えた後、混練して二次電池電極用組成物を調整した。この二次電池電極用組成物を集電体となる厚さ20μmのアルミ箔上にドクターブレードを用いて塗布した後、減圧加熱乾燥し、ロールプレスによる圧延処理を行い、厚さ50μmの正極合剤層を有する正極を作製した。
負極活物質としてメソフェーズカーボン97部、ポリフッ化ビニリデン(KFポリマーW#1100、株式会社クレハ製)を固形分として3部に、N−メチル−2−ピロリドンを固形分50%となるように加えた後、混練して二次電池電極用組成物を調整した。この二次電池電極用組成物を集電体となる厚さ20μmの銅箔上にドクターブレードを用いて塗布した後、減圧加熱乾燥し、ロールプレスによる圧延処理を行い、厚さ50μmの負極合剤層を有する負極を作製した。
上記で作製した正極を、直径16mmに打ち抜き作用極とし、金属リチウム箔を対極として、作用極及び対極の間に多孔質ポリプロピレンフィルムからなるセパレーターを挿入積層し、電解液(エチレンカーボネートとジエチルカーボネートを1:1(体積比)の割合で混合した混合溶媒にLiPF6を1Mの濃度で溶解させた非水電解液)を満たしてコインセルを組み立てた。コインセルの組み立てはアルゴンガス置換したグロ−ブボックス内で行い、セル組み立て後、所定の電池特性評価を行った。
上記で作製した負極を、直径16mmに打ち抜き作用極とし、金属リチウム箔を対極として、作用極及び対極の間に多孔質ポリプロピレンフィルムからなるセパレーターを挿入積層し、電解液(エチレンカーボネートとジエチルカーボネートを1:1(体積比)の割合で混合した混合溶媒にLiPF6 を1Mの濃度で溶解させた非水電解液)を満たしてコインセルを組み立てた。コインセルの組み立てはアルゴンガス置換したグロ−ブボックス内で行い、セル組み立て後、所定の電池特性評価を行った。
(密着性)
電極表面にナイフを用いて、合剤層から集電体に達する深さまでの切込みを2mm間隔で縦横それぞれ6本入れて碁盤目の切込みを入れた。この切り込みに粘着テープを貼り付けて直ちに引き剥がし、活物質の脱落の程度を目視判定で判定した。評価基準を下記に示す。
◎:「剥離なし」
○:「わずかに剥離(実用上問題のないレベル)」
○△:「半分程度剥離(問題はあるが使用可能レベル)」
△:「ほとんどの部分で剥離」
×:「完全に剥離」
作成した電極をエチレンカーボネートとジエチルカーボネートを1:1(体積比)の割合で混合した混合溶媒に60℃、24時間浸漬し、浸漬前後での膜の膨潤状態、樹脂の溶出状態を下記の通り算出し、比較評価した。
膨潤率 (%)=〔(浸漬後重量)/(浸漬前重量)〕×100
溶出率 (%)=〔1−(浸漬乾燥後重量)/(浸漬前重量)〕×100
膨潤率はその値が100%に近いほど、溶出率は0%に近いほど耐電解液性が高いことを示す。
○:「膨潤率が110%未満。全く問題なし。」
△:「膨潤率が110%以上、120%未満。実用上使用可。」
×:「膨潤率が120%以上。実用上問題あり。」
△:「溶出率が1.0%以上、3.0%未満。実用上使用可。」
×:「溶出率が3.0%以上。実用上問題あり。」
上記で作製したリチウム二次電池電極評価用セルの充放電サイクル試験を行った。1回目の放電容量を100%として70℃、100時間後の放電容量を測定し変化率とした(100%に近いほど良好)。
◎:「変化率が99%以上。特に優れている。」
○:「変化率が95%以上、99%未満。全く問題なし。」
○△:「変化率が90%以上、95%未満。実用上問題なし。」
△:「変化率が80%以上、90%未満。実用上問題はあるが使用可。」
×:「変化率が80%未満。実用上問題あり、使用不可。」
Claims (8)
- 無水マレイン化ポリブタジエン(BP)の酸無水物環を、水酸基を有する化合物(A)によって開環してなるマレイン化ポリブタジエン(B)の存在下、水性媒体中でエチレン性不飽和単量体(C)を乳化重合してなる樹脂微粒子分散体を含む非水二次電池電極用バインダー樹脂組成物。
- 無水マレイン化ポリブタジエン(BP)の酸無水物価が、25〜200mgKOH/gである請求項1記載の非水二次電池電極用バインダー樹脂組成物。
- エチレン性不飽和単量体(C)の合計100重量部に対する、マレイン化ポリブタジエン(B)の量が、5〜150重量部である請求項1又は2記載の非水二次電池電極用バインダー樹脂組成物。
- エチレン性不飽和単量体(C)の合計100重量%中、
アルコキシシリル基含有エチレン性不飽和単量体、N−メチロール基含有エチレン性不飽和単量体、エポキシ基含有エチレン性不飽和単量体及び1分子中に2つ以上のエチレン性不飽和基を有する単量体からなる群より選ばれる少なくとも1種の単量体0.1〜10重量%を含む、請求項1ないし3いずれか記載の非水二次電池電極用バインダー樹脂組成物。 - 水酸基を有する化合物(A)が、エチレン性不飽和基を有する化合物である請求項1ないし4いずれか記載の非水二次電池電極用バインダー樹脂組成物。
- 請求項1ないし5いずれか記載の非水二次電池電極用バインダー樹脂組成物を用いてなる非水系二次電池電極。
- 請求項6記載の非水系二次電池電極を用いてなる非水系二次電池。
- リチウムイオン二次電池であることを特徴とする請求項7記載の非水系二次電池。