JP2010519986A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2010519986A5 JP2010519986A5 JP2009552063A JP2009552063A JP2010519986A5 JP 2010519986 A5 JP2010519986 A5 JP 2010519986A5 JP 2009552063 A JP2009552063 A JP 2009552063A JP 2009552063 A JP2009552063 A JP 2009552063A JP 2010519986 A5 JP2010519986 A5 JP 2010519986A5
- Authority
- JP
- Japan
- Prior art keywords
- weight percent
- starting glass
- veneer
- veneer ceramic
- zirconium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
本発明は、下記において実施形態例を参照して、より完全に記述されるであろう。また、本発明は以下を提供する：
（項目１）
イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックであって、下記の成分：
ａ）ＳｉＯ ２ ５８．０〜７４．０重量パーセント、
ｂ）Ａｌ ２ Ｏ ３ ４．０〜１９．０重量パーセント、
ｃ）Ｌｉ ２ Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ ２ Ｏ ４．０〜１２．０重量パーセント、
ｅ）ＺｒＯ ２ ０．５〜６．０重量パーセント
を含有することを特徴とするベニアセラミック。
（項目２）
イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックであって、下記の成分：
ａ）ＳｉＯ ２ ５８．０〜７２．０重量パーセント、
ｂ）Ａｌ ２ Ｏ ３ ４．０〜１８．０重量パーセント、
ｃ）Ｌｉ ２ Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ ２ Ｏ ４．０〜１１．０重量パーセント、
ｅ）ＺｒＯ ２ ０．５〜５．５重量パーセント、
ｆ）ＴｉＯ ２ ０．２〜８．０重量パーセント
を含有することを特徴とするベニアセラミック。
（項目３）
下記のさらなる成分：
ａ）Ｌａ ２ Ｏ ３ １．０〜４．０重量パーセント、
ｂ）Ｂ ２ Ｏ ３ ０．０〜２．０重量パーセント、
ｃ）ＭｇＯ ０．０〜２．０重量パーセント、
ｄ）ＣａＯ ０．０〜２．０重量パーセント、
ｅ）ＺｎＯ ０．０〜２．０重量パーセント、
ｆ）ＢａＯ ０．０〜１．０重量パーセント
ｇ）Ｐ ２ Ｏ ５ ０．０〜２．０重量パーセント、
ｈ）フッ化物 ０．０〜３．０重量パーセント
が含有されることを特徴とする、項目１または２に記載のベニアセラミック。
（項目４）
元素Ｃｅ、Ｆｅ、Ｍｎ、Ｓｎ、Ｖ、Ｃｒ、Ｉｎの、ならびに希土類Ｐｒ、Ｎｄ、Ｓｍ、Ｅｕ、Ｔｂ、ＤｙおよびＥｒの着色もしくは蛍光添加物である酸化物が個別にまたは組み合わせて含有されることを特徴とする、前記項目の一項に記載のベニアセラミック。
（項目５）
ベータ−石英混晶の結晶化を抑制するために他の酸化アルカリ、好ましくは酸化ナトリウムが含有されることを特徴とする、項目１または２に記載のベニアセラミック。
（項目６）
項目１または２に記載のベニアセラミックによる、イットリウム安定化二酸化ジルコニウムを含む歯科修復物へのベニア形成方法であって、下記の方法ステップ：
ａ）１５３０℃で溶融したガラスを、水中でフリット化するステップと、
ｂ）前記フリット化したガラスを、核形成のため５００℃〜６８０℃の温度で２〜６時間鍛錬するステップと、
ｃ）冷却後、前記鍛錬したガラスを機械的に微粉砕するステップと、
ｄ）前記前処理した粉末を、水の添加によりペーストに変換するステップと、
ｅ）前記ペーストを、イットリウム安定化二酸化ジルコニウムを含む前記修復物に塗布するステップと、
ｆ）次いで、８００℃〜９４０℃における熱処理に掛けるステップであり、前記ベニアセラミックにおいて、主結晶相として二ケイ酸リチウムが結晶化されるステップとを特徴とする方法。
（項目７）
前記二ケイ酸リチウムに加えて、ケイ酸リチウムアルミニウム、およびリチウムチタンオキシドシリケートＬｉ ２ ＴｉＯＳｉＯ ４ も結晶化されることを特徴とする、項目６に記載の方法。
（項目８）
前記フリット化されたガラスに、固相反応により生成された二ケイ酸リチウム微粉砕物を含む結晶性添加物が添加されることを特徴とする、項目６または７に記載の方法。
（項目１）
イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックであって、下記の成分：
ａ）ＳｉＯ ２ ５８．０〜７４．０重量パーセント、
ｂ）Ａｌ ２ Ｏ ３ ４．０〜１９．０重量パーセント、
ｃ）Ｌｉ ２ Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ ２ Ｏ ４．０〜１２．０重量パーセント、
ｅ）ＺｒＯ ２ ０．５〜６．０重量パーセント
を含有することを特徴とするベニアセラミック。
（項目２）
イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックであって、下記の成分：
ａ）ＳｉＯ ２ ５８．０〜７２．０重量パーセント、
ｂ）Ａｌ ２ Ｏ ３ ４．０〜１８．０重量パーセント、
ｃ）Ｌｉ ２ Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ ２ Ｏ ４．０〜１１．０重量パーセント、
ｅ）ＺｒＯ ２ ０．５〜５．５重量パーセント、
ｆ）ＴｉＯ ２ ０．２〜８．０重量パーセント
を含有することを特徴とするベニアセラミック。
（項目３）
下記のさらなる成分：
ａ）Ｌａ ２ Ｏ ３ １．０〜４．０重量パーセント、
ｂ）Ｂ ２ Ｏ ３ ０．０〜２．０重量パーセント、
ｃ）ＭｇＯ ０．０〜２．０重量パーセント、
ｄ）ＣａＯ ０．０〜２．０重量パーセント、
ｅ）ＺｎＯ ０．０〜２．０重量パーセント、
ｆ）ＢａＯ ０．０〜１．０重量パーセント
ｇ）Ｐ ２ Ｏ ５ ０．０〜２．０重量パーセント、
ｈ）フッ化物 ０．０〜３．０重量パーセント
が含有されることを特徴とする、項目１または２に記載のベニアセラミック。
（項目４）
元素Ｃｅ、Ｆｅ、Ｍｎ、Ｓｎ、Ｖ、Ｃｒ、Ｉｎの、ならびに希土類Ｐｒ、Ｎｄ、Ｓｍ、Ｅｕ、Ｔｂ、ＤｙおよびＥｒの着色もしくは蛍光添加物である酸化物が個別にまたは組み合わせて含有されることを特徴とする、前記項目の一項に記載のベニアセラミック。
（項目５）
ベータ−石英混晶の結晶化を抑制するために他の酸化アルカリ、好ましくは酸化ナトリウムが含有されることを特徴とする、項目１または２に記載のベニアセラミック。
（項目６）
項目１または２に記載のベニアセラミックによる、イットリウム安定化二酸化ジルコニウムを含む歯科修復物へのベニア形成方法であって、下記の方法ステップ：
ａ）１５３０℃で溶融したガラスを、水中でフリット化するステップと、
ｂ）前記フリット化したガラスを、核形成のため５００℃〜６８０℃の温度で２〜６時間鍛錬するステップと、
ｃ）冷却後、前記鍛錬したガラスを機械的に微粉砕するステップと、
ｄ）前記前処理した粉末を、水の添加によりペーストに変換するステップと、
ｅ）前記ペーストを、イットリウム安定化二酸化ジルコニウムを含む前記修復物に塗布するステップと、
ｆ）次いで、８００℃〜９４０℃における熱処理に掛けるステップであり、前記ベニアセラミックにおいて、主結晶相として二ケイ酸リチウムが結晶化されるステップとを特徴とする方法。
（項目７）
前記二ケイ酸リチウムに加えて、ケイ酸リチウムアルミニウム、およびリチウムチタンオキシドシリケートＬｉ ２ ＴｉＯＳｉＯ ４ も結晶化されることを特徴とする、項目６に記載の方法。
（項目８）
前記フリット化されたガラスに、固相反応により生成された二ケイ酸リチウム微粉砕物を含む結晶性添加物が添加されることを特徴とする、項目６または７に記載の方法。
Claims (19)
- イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックであって、下記の成分：
ａ）ＳｉＯ２ ５８．０〜７４．０重量パーセント、
ｂ）Ａｌ２Ｏ３ ４．０〜１９．０重量パーセント、
ｃ）Ｌｉ２Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ２Ｏ ４．０〜１２．０重量パーセント、
ｅ）ＺｒＯ２ ０．５〜６．０重量パーセント
を含有することを特徴とするベニアセラミック。 - イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックのための出発ガラスであって、下記の成分：
ａ）ＳｉＯ ２ ５８．０〜７４．０重量パーセント、
ｂ）Ａｌ ２ Ｏ ３ ４．０〜１９．０重量パーセント、
ｃ）Ｌｉ ２ Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ ２ Ｏ ４．０〜１２．０重量パーセント、
ｅ）ＺｒＯ ２ ０．５〜６．０重量パーセント
を含有することを特徴とする出発ガラス。 - 結晶粉末、好ましくは、二ケイ酸リチウム粉末をさらに含むことを特徴とする請求項２に記載の出発ガラス。
- ＺｒＯ ２ に加えて、０．２〜８．０重量パーセントで、ＴｉＯ ２ をも含むことを特徴とする、請求項１に記載のベニアセラミック、または請求項２もしくは３に記載の出発ガラス。
- 下記の成分：
ａ）ＳｉＯ２ ５８．０〜７２．０重量パーセント、
ｂ）Ａｌ２Ｏ３ ４．０〜１８．０重量パーセント、
ｃ）Ｌｉ２Ｏ ５．０〜１７．０重量パーセント、
ｄ）Ｎａ２Ｏ ４．０〜１１．０重量パーセント、
ｅ）ＺｒＯ２ ０．５〜５．５重量パーセント、
ｆ）ＴｉＯ２ ０．２〜８．０重量パーセント
を含有することを特徴とする、請求項１もしくは４に記載のベニアセラミック、または請求項２、３、もしくは４のいずれか一項に記載の出発ガラス。 - 添加剤Ｌａ ２ Ｏ ３ 、Ｂ ２ Ｏ ３ 、Ｐ ２ Ｏ ５ 、ＣａＯ、ＭｇＯ、ＺｎＯおよびフッ化物を、最大で４．０重量パーセントまでの濃度で互いに独立して含有することを特徴とする、請求項１、４、もしくは５のいずれか一項に記載のベニアセラミック、または請求項２〜５のいずれか一項に記載の出発ガラス。
- 下記のさらなる成分：
ａ）Ｌａ２Ｏ３ １．０〜４．０重量パーセント、
ｂ）Ｂ２Ｏ３ ０．０〜２．０重量パーセント、
ｃ）ＭｇＯ ０．０〜２．０重量パーセント、
ｄ）ＣａＯ ０．０〜２．０重量パーセント、
ｅ）ＺｎＯ ０．０〜２．０重量パーセント、
ｆ）ＢａＯ ０．０〜１．０重量パーセント
ｇ）Ｐ２Ｏ５ ０．０〜２．０重量パーセント、
ｈ）フッ化物 ０．０〜３．０重量パーセント
を含有することを特徴とする、請求項６に記載のベニアセラミック、または請求項６に記載の出発ガラス。 - 元素Ｃｅ、Ｆｅ、Ｍｎ、Ｓｎ、Ｖ、Ｃｒ、Ｉｎの、ならびに希土類Ｐｒ、Ｎｄ、Ｓｍ、Ｅｕ、Ｔｂ、ＤｙおよびＥｒの着色もしくは蛍光添加物である酸化物、またはこれらの組み合わせが含有されることを特徴とする、請求項１もしくは４〜７のいずれか一項に記載のベニアセラミック、または請求項２〜７のいずれか一項に記載の出発ガラス。
- ベータ−石英混晶の結晶化を抑制するために他の酸化アルカリが含有されることを特徴とする、請求項１または５のいずれか一項に記載のベニアセラミック。
- 二ケイ酸リチウムに加えて、リチウムチタンオキシドシリケートＬｉ ２ ＴｉＯＳｉＯ ４ 、ケイ酸リチウムアルミニウム（ベータスポジュメン）、および少量のメタケイ酸リチウムもが含有されることを特徴とする、請求項１または４〜９のいずれか一項に記載のベニアセラミック。
- イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックのための出発ガラスであって、該出発ガラスは、
７１．１重量パーセント ＳｉＯ ２ 、
４．９重量パーセント Ａｌ ２ Ｏ ３ 、
１４．９重量パーセント Ｌｉ ２ Ｏ、
３．０重量パーセント Ｎａ ２ Ｏ、
５．０重量パーセント ＴｉＯ ２ 、および
１．１重量パーセント ＺｒＯ ２
を含有することを特徴とする、出発ガラス。 - イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックのための出発ガラスであって、該出発ガラスは、
６９．７重量パーセント ＳｉＯ ２ 、
４．８重量パーセント Ａｌ ２ Ｏ ３ 、
１４．６重量パーセント Ｌｉ ２ Ｏ、
２．９重量パーセント Ｎａ ２ Ｏ、
４．９重量パーセント ＴｉＯ ２ 、
１．１重量パーセント ＺｒＯ ２ 、
０．６重量パーセント ＣａＯ、および
１．４重量パーセント Ｐ ２ Ｏ ５
を含有することを特徴とする、出発ガラス。 - イットリウム安定化二酸化ジルコニウムを含む歯科修復物用ベニアセラミックのための出発ガラスであって、該出発ガラスは、
７０．５重量パーセント ＳｉＯ ２ 、
４．９重量パーセント Ａｌ ２ Ｏ ３ 、
１４．８重量パーセント Ｌｉ ２ Ｏ、
３．０重量パーセント Ｎａ ２ Ｏ、
５．０重量パーセント ＴｉＯ ２ 、
１．１重量パーセント ＺｒＯ ２ 、および
０．６重量パーセント ＣａＦ ２ 、
を含有することを特徴とする、出発ガラス。 - イットリウム安定化二酸化ジルコニウムを含む歯科修復物へのベニア形成のための、請求項１もしくは４〜１０のいずれか一項に記載のベニアセラミックの使用または請求項２、４〜７、もしくは１１〜１３のいずれか一項に記載の出発ガラスの使用。
- 請求項１もしくは４〜１０のいずれか一項に記載のベニアセラミック、または請求項２、４〜７、もしくは１１〜１３のいずれか一項に記載の出発ガラスを使用することにより、イットリウム安定化二酸化ジルコニウムを含む歯科修復物へのベニア形成方法。
- 請求項１または４〜１０のいずれか一項に記載のベニアセラミックの調製方法であって、ここで、５００℃〜６８０℃の温度範囲で核形成が行われ、そして、８００℃〜９４０℃の温度範囲で溶融および結晶化が行われる、方法。
- 請求項１もしくは４〜１０のいずれか一項に記載のベニアセラミックを使用することにより、請求項１５に記載のイットリウム安定化二酸化ジルコニウムを含む歯科修復物へのベニア形成方法であって、下記の方法ステップ：
ａ）１５３０℃で溶融したガラスを、水中でフリット化するステップと、
ｂ）前記フリット化したガラスを、核形成のため５００℃〜６８０℃の温度で２〜６時間鍛錬するステップと、
ｃ）冷却後、前記鍛錬したガラスを機械的に微粉砕するステップと、
ｄ）前記前処理した粉末を、水の添加によりペーストに変換するステップと、
ｅ）前記ペーストを、イットリウム安定化二酸化ジルコニウムを含む前記修復物に塗布するステップと、
ｆ）次いで、８００℃〜９４０℃における熱処理に掛けるステップであり、前記ベニアセラミックにおいて、主結晶相として二ケイ酸リチウムが結晶化されるステップとを特徴とする方法。 - 前記二ケイ酸リチウムに加えて、ケイ酸リチウムアルミニウム、およびリチウムチタンオキシドシリケートＬｉ２ＴｉＯＳｉＯ４も結晶化されることを特徴とする、請求項１７に記載の方法。
- 前記フリット化されたガラスに、固相反応により生成された二ケイ酸リチウム微粉砕物を含む結晶性添加物が添加されることを特徴とする、請求項１７または１８に記載の方法。