JP2010248411A - 表面処理蛍光体含有硬化性シリコーン樹脂組成物及び発光装置 - Google Patents
表面処理蛍光体含有硬化性シリコーン樹脂組成物及び発光装置 Download PDFInfo
- Publication number
- JP2010248411A JP2010248411A JP2009100921A JP2009100921A JP2010248411A JP 2010248411 A JP2010248411 A JP 2010248411A JP 2009100921 A JP2009100921 A JP 2009100921A JP 2009100921 A JP2009100921 A JP 2009100921A JP 2010248411 A JP2010248411 A JP 2010248411A
- Authority
- JP
- Japan
- Prior art keywords
- phosphor
- silicone resin
- group
- resin composition
- curable silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【効果】本発明によれば、LEDチップの封止材として、硫化物系蛍光体又はシリケート系蛍光体に表面処理を施した蛍光体を含有する硬化性シリコーン樹脂組成物の硬化物を用いたことで、従来は、時間の経過とともに蛍光体の分解により、信頼性が低下していた発光装置に対し、長期信頼性が確保できる蛍光体含有シリコーン樹脂組成物及び発光装置を得ることができる。
【選択図】図1
Description
請求項1:
少なくとも一部が表面処理された無機蛍光体を含有することを特徴とする硬化性シリコーン樹脂組成物。
請求項2:
無機蛍光体が、硫化物系又はシリケート系蛍光体であることを特徴とする請求項1記載の硬化性シリコーン樹脂組成物。
請求項3:
無機蛍光体が、ハイドロアルコキシシラン又はそのオリゴマーで表面処理されていることを特徴とする請求項1又は2記載の硬化性シリコーン樹脂組成物。
請求項4:
発光ダイオード(LED)チップの封止用である請求項1〜3のいずれか1項記載の硬化性シリコーン樹脂組成物。
請求項5:
LEDチップを少なくとも一部が表面処理された無機蛍光体を含有するシリコーン樹脂組成物の硬化物により封止してなることを特徴とする発光装置。
請求項6:
無機蛍光体が、硫化物系又はシリケート系蛍光体であることを特徴とする請求項5記載の発光装置。
請求項7:
無機蛍光体が、ハイドロアルコキシシラン又はそのオリゴマーで表面処理されていることを特徴とする請求項5又は6記載の発光装置。
図1は、本発明の代表的な発光装置の基本構成の断面図である。本発明の発光装置は、LEDチップ1とシリコーン樹脂封止部5を備える発光装置であって、シリコーン樹脂封止部5中にLEDチップ1の発光の一部を異なる波長に変換する無機蛍光体3が含有され、該無機蛍光体の少なくとも一部が予め表面処理されているものである。
(a)1分子中にケイ素原子と結合するアルケニル基を2個以上含有するオルガノポリシロキサン、
(b)1分子中に2個以上のケイ素原子に結合した水素原子(SiH基)を有するオルガノハイドロジェンポリシロキサン:(a)成分中のケイ素原子と結合するアルケニル基に対して、(b)成分のケイ素原子に結合した水素原子がモル比で0.1〜5.0となる量、
(c)触媒量の白金族系触媒
を必須成分とする付加硬化型シリコーン樹脂組成物が挙げられる。
R1 aSiO(4-a)/2 (1)
(式中、R1は互いに同一又は異種の炭素数1〜10、好ましくは1〜8の非置換又は置換の一価炭化水素基であり、aは1.5〜2.8、好ましくは1.8〜2.5、より好ましくは1.95〜2.05の範囲の正数である。)
R2 bHcSiO(4-b-c)/2 (2)
(式中、R2は炭素数1〜10の非置換又は置換の一価炭化水素基であり、このR2としては、上記式(1)中のR1と同様の基が挙げられる。また、bは0.7〜2.1、cは0.001〜1.0で、かつb+cが0.8〜3.0を満足する正数であり、好ましくは、bは1.0〜2.0、cは0.01〜1.0、かつb+cは1.5〜2.5である。)
硫化物系蛍光体である硫化カルシウム系蛍光体100部に下記式
実施例1と同様にして、シリケート系蛍光体であるSr3SiO5:Eu2+にハイドロトリアルコキシシランを用いて表面処理を施し、表面処理シリケート系蛍光体を得た。
実施例1において、表面処理を施さない硫化物系蛍光体を使用する以外は、実施例1と同様の方法で蛍光体含有硬化性シリコーン樹脂組成物を調製し、比較例1とした。
実施例1において、表面処理剤としてシランカップリング剤であるトリメトキシシランを用いて表面処理を施す以外は、実施例1と同様の方法で表面処理蛍光体含有硬化性シリコーン樹脂組成物を調製し、比較例2とした。
2 導電性ワイヤー
3 蛍光体
4 パッケージ
5 シリコーン樹脂封止部
Claims (7)
- 少なくとも一部が表面処理された無機蛍光体を含有することを特徴とする硬化性シリコーン樹脂組成物。
- 無機蛍光体が、硫化物系又はシリケート系蛍光体であることを特徴とする請求項1記載の硬化性シリコーン樹脂組成物。
- 無機蛍光体が、ハイドロアルコキシシラン又はそのオリゴマーで表面処理されていることを特徴とする請求項1又は2記載の硬化性シリコーン樹脂組成物。
- 発光ダイオード(LED)チップの封止用である請求項1〜3のいずれか1項記載の硬化性シリコーン樹脂組成物。
- LEDチップを少なくとも一部が表面処理された無機蛍光体を含有するシリコーン樹脂組成物の硬化物により封止してなることを特徴とする発光装置。
- 無機蛍光体が、硫化物系又はシリケート系蛍光体であることを特徴とする請求項5記載の発光装置。
- 無機蛍光体が、ハイドロアルコキシシラン又はそのオリゴマーで表面処理されていることを特徴とする請求項5又は6記載の発光装置。