JP2009160659A - ろう付け材及びそれで得られる製品 - Google Patents

ろう付け材及びそれで得られる製品 Download PDF

Info

Publication number
JP2009160659A
JP2009160659A JP2009099110A JP2009099110A JP2009160659A JP 2009160659 A JP2009160659 A JP 2009160659A JP 2009099110 A JP2009099110 A JP 2009099110A JP 2009099110 A JP2009099110 A JP 2009099110A JP 2009160659 A JP2009160659 A JP 2009160659A
Authority
JP
Japan
Prior art keywords
brazing
iron
brazing material
product
base material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2009099110A
Other languages
English (en)
Other versions
JP5345442B2 (ja
JP2009160659A6 (ja
Inventor
Per Erik Sjodin
ペル エーリック シェーディン、
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Alfa Laval Corporate AB
Original Assignee
Alfa Laval Corporate AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=20284387&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JP2009160659(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Alfa Laval Corporate AB filed Critical Alfa Laval Corporate AB
Publication of JP2009160659A publication Critical patent/JP2009160659A/ja
Publication of JP2009160659A6 publication Critical patent/JP2009160659A6/ja
Application granted granted Critical
Publication of JP5345442B2 publication Critical patent/JP5345442B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

【課題】主に製品の母材と同じ組成を有するろう付け材を用いたろう付けにより物品を接合可能とする。
【解決手段】ろう付けによって物品を接合するための鉄を母材とするろう付け材は、鉄を別として、質量％で、０〜４０％、好ましくは９〜３０％のＣｒ、０〜１６％、好ましくは０〜８％、より好ましくは０〜５％のＭｎ、０〜２５％のＮｉ、０〜１％のＮ、及び最大７％のＭｏ６％未満のＳｉ及び／または０〜２％、好ましくは０〜１．５％のＢ、及び／または０〜１５％のＰを含む合金であって、Ｂ、Ｐ、Ｓｉの組み合わせまたは個別の添加により、ろう付け材が完全に溶融される温度である液相線温度が低下される合金に相当する。ろう付け製品は、Ｂ及び／またはＰ及び／またはＳｉを液相線温度を低下させる成分として合金化した、鉄を母材とするろう付け材によって、鉄を母材とする物品をろう付けすることによって製造される。
【選択図】なし

Description

本発明はろう付けによって物品を接合するための鉄を母材とするろう付け材に関する。
本発明はまた、本発明による鉄を母材とするろう付け材によって鉄を母材とする物品をろ
う付けして製造されるろう付け製品を含む。
鋼または鉄を母材とする異なった物品は、通常Ｎｉ−，Ａｇ−またはＣｕ−ろう付け材
でろう付けされる。
ろう付けは、お互いに接合または固定される物品の母材の液相線よりも低温において、
固定または接合するプロセスである。
ろう付け材は、ろう付けプロセスの間で完全にまたは部分的に溶融する接合または固定
のための材料を含む。
ＵＳ４１３５６５６はＮｉを母材とした合金に関し、これは質量％で１９−２３％のＭ
ｎ、５−８％のＳｉ，４−６％のＣｕ、０．６−１．８％のＢと他より少ない元素を別と
して残りＮｉを含む。ＵＳ４３１４６６１は他の種類のＮｉを母材とした合金が記載され
、これは原子％で０−４％のＦｅ、０−２１％のＣｒ，０−１９％のＢ、０−１２％のＳ
ｉ、０−２２％のＰと残りのＮｉを含む。
Ｃｕでろう付けするときは、一般に純粋または殆ど純粋なＣｕを用いる。純Ｃｕろう付
け材はくっきりと明確な融点を持つが、一方、ニッケルを母材とするろう付け材は合金で
あることによってしばしば溶融間隔を持つ。
板状熱交換器においてステンレルスチール板を接合する時には、Ｃｕろう付け材がしば
しば用いられる。しかしながら、銅は全ての用途には適していない。銅のろう付け材の食
品用途での使用は許されていないが、地域暖房用や水道設備用の板状熱交換器に用いられ
る。
ニッケルのろう付け材で接合した熱交換器は多くの用途に用いられ、また限られた数の
食品用途に許されている。
もし、ニッケル合金を含むろう付け材が鉄、または非ニッケルを母材とする物品の接合
に用いられると、ろう付け接合部の組成が、接合された物品の組成とは大きな相違がある
。これは化学的特性または機械的特性に好ましくない相違となり得る。
本発明は、製品を製造するために用いる母材の組成と主として同じ組成を有し液相線温
度を低下させる添加成分を含むろう付け材を用いて、ろう付けすることによって物品を接
合する可能性を提供する。
したがって、本発明は、本発明によるろう付け材を用いて食品用途の要求に適合できる
板状熱交換器としての装置を製造する可能性を提供する。本発明は、主として、ろう付け
材が、鉄を別として、質量％として、０〜４０％、好ましくは９〜３０％のＣｒ、０〜１
６％、好ましくは０〜８％、より好ましくは０〜５％のＭｎ、０〜２５％のＮｉ、０〜１
％のＮ、最大７％のＭｏ及び６％未満のＳｉ及び／または０〜２％、好ましくは０〜１．
５％のＢ、及び／または０〜１５％のＰを含む合金からなり、ボロン、リン及びシリコン
の組み合わせまたは個別の添加により、ろう付け材が完全に溶融される温度である液相線
温度が低下されることを特徴とする。
ろう付け材における鉄の含有率は、好ましくは少なくとも５０％である。本発明のろう
付け材は、常にＦｅとＣｒを含まなければならない。
融点の好ましい低下を達成するために、Ｂ及び／またはＰ及び／またはＳｉの効果的な
実用的な量は、上記の範囲にしなければならない。例えばＳｉは、炭化ケイ素または窒化
ケイ素の状態や、酸素と結合されて、または他の方法で焼結されるため、Ｓｉの分析値は
かなり高くなるかもしれない。同様な理由によってＢまたはＰの分析値も高くなるかもし
れない。
鉄を母材とするろう付け材は合金成分としてＴｉ、Ｗ、Ａｌ、Ｃｕ、Ｎｂ，Ｔａ、Ｖそ
の他を含んでも良い。組成の変化は少量で不可避の量のＣ、Ｏ及びＳの混在物の影響であ
ろう。
融点低下成分はろう付け材に次式による量で好ましく添加される。
インデックス＝Ｐ％＋１．１×Ｓｉ％＋３×Ｂ％
ここで該インデックスの値は４．５〜１８にすべきである。
鉄を母材とするろう付け材は上記組成のインゴットのガスまたは水による微粒化または
このようなインゴットの粉砕で好ましくは製造される。他の製造方法は溶融スピニングで
ある。
本発明はまた鉄を母材とする物品と共にろう付けして作られた製品を含み、該製品が該
物品をＢ及び／またはＰ及び／またはＳｉのような液相線を低下させる成分を含む合金の
鉄を母材とするろう付け材でろう付けしたものであることを特徴とするものである。鉄を
母材とするろう付け材は主請求項に記載の組成が好ましい。
ろう付け製品中の鉄を母材とする物品と鉄を母材とするろう付け材の両方が好ましくは
９〜３０％のＣｒを含む。
ろう付け製品は好ましくはろう付けされた板状熱交換器であり、それは少なくとも二つ
の熱交換流体のためのもので、それは鉄を母材とする薄い壁を有する熱交換板の幾つかを
、鉄を母材とするろう付け材によってろう付けして製造された少なくとも一つの板状パッ
ケージを含む。熱交換板は相対で熱交換流体のための内部スペースの輪郭を定める。鉄を
母材とする板材と比べて、内部または周囲において局部的に高いB、P、Si量を有するろう
付け接合部は、鉄を母材とするろう付け材の組成に近い冶金組成を持つ。
鉄を母材とするろう付けには、前記したように伝統的にCu−またはNi-ろう付け材が用
いられていた。驚くべきことに、今や、接合したい物品の材料と同じ組成の母材から開始
できることが見つけられた。このような材料をシリコン及び／またはホウ素及び／または
リンと合金化することによってうまく機能するろう付け材が得られる。鉄とSi、B及びPの
二相ダイアグラムの検討によって、Fe-Si合金が約１９％のSiで1212℃の最低融点を持つ
ことを見出すであろう。Ｆｅ−Ｂ合金については、約４％のＢで１１７４℃の融点の最低
がある。Ｆｅ−Ｐ系では約１０％のＰで１０４８℃の融点の最低がある。
多くの場合、純鉄材料は用いられないで、鉄を別として、比較的大量のＣｒまたはＮｉ
を含む合金が用いられる。また多くの合金にＭｏとＭｎが含まれる。このような合金に異
なった量のホウ素及び／またはリン及び／またはシリコンを添加する効果を、相ダイアグ
ラムを用いて理論的に確立する試みは、次元数が合金の成分の数と同じとなるので、ほと
んど不可能である。
ろう付けの接合を得るためには、ろう付け材の液相線温度が１２３０℃以下、好ましく
は１２００℃以下であるべきである。
驚くべきことに、比較的少量のシリコン、ホウ素またリンを組み合わせてまたは単独で
添加すると、液相線温度が低下し、好ましいろう付け材が得られることが見出された。
下の表に、本発明によるろう付け材の、組成の異なる例が示されている。
Figure 2009160659
各試料は１１９０℃でろう付けされた。試料のろう付け試験の目視による検査の結果で
は全ての試料は溶融し、ろう付け接合物が得られ、またすべての接合物で機械強度が得ら
れた。
本発明のろう付け材は好ましくは粉または箔状で製造される。粉は、インゴットを製造
しこれを破砕した後に、粉砕して調製されても良い。材料の壊れやすい性質はこの製造方
法で利用される。インゴットキャスティングの欠点は、融解間隔がはっきりしないか広い
という不均一性物質となる偏析の危険がありことである。より小さなインゴット及び／ま
たは急冷は偏析の危険を減らす。インゴットキャスティングにおいては、真空キャスティ
ングまたはガスシールキャスティングによって、空気との接触を最小にすることが重要で
ある。機械的処理によって、ろう付け材のエネルギー含有量が増加しそれに伴ってその反
応性も増加する。
均一組成の粉末を製造する他の方法は水またはガスによる微粒化である。粉末の性質は
製造方法によって変化する。破砕され粉砕された粒子は角があり先がとがっている。水で
微粉化されたものは団塊状（ｎｏｄｕｌａｒ）であり、ガスで微粉化されたものはほとん
ど球状である。この粒子形状の相違はろう付けに使用する際にろう付け材に多少の性質の
変化を与える。異なった微粉化法の選択、破砕／粉砕の程度及びふるい分けとの組み合わ
せによって粒子サイズ分布が調整できるであろう。水微粉化においては、ガス微粉化より
も酸素ポテンシャルが高くなるので、一般に酸素含有率が高くなるであろう。高い酸素含
有率は、材料の酸化物の形成をもたらし、ろう付け接合の機械的性質に悪い影響を与える
であろう。ろう付け材中の有効なＳｉ及び／またはＢ及び／またはＰの割合は低くなるで
あろう。これはこのために融解範囲が移動することを意味する。
金属溶融物からの溶融スピニングによる箔の製造は、冷えた表面で金属溶融物が直接冷
却され、例えば箔が形成されるような方法で行われる。通常の連続箔製造においては、冷
却表面は銅または銅合金で作られた冷却ロールよりなる。非晶性の箔を得ることができる
が、この場合、通常はホウ素が加えられる。
本発明によるろう付け材は異なった方法で望ましいろう付け場所に適用できる。記載さ
れたいかなる方法によって得られた粉末ろう付け材も、適当な方法で適用するためにバイ
ンダー中に懸濁させても良い。

Claims (7)

  1. ろう付けによって物品を接合するための鉄を母材とするろう付け材であって、該ろう付
    け材が、鉄を別として、質量％で、０〜４０％、好ましくは９〜３０％のＣｒ、０〜１６
    ％、好ましくは０〜８％、より好ましくは０〜５％のＭｎ、０〜２５％のＮｉ、０〜１％
    のＮ、最大７％のＭｏ及び６％未満のＳｉ及び／または０〜２％、好ましくは０〜１．５
    ％のＢ、及び／または０〜１５％のＰを含む合金からなり、該Ｂ、Ｐ、Ｓｉの組み合わせ
    または個別の添加により、ろう付け材が完全に溶融される温度である液相線温度が低下さ
    れることを特徴とするろう付け材。
  2. 融点低下成分がろう付け材に次式
    インデックス＝Ｐ％＋１．１×Ｓｉ％＋３×Ｂ％
    ここで該インデックスの値は４．５〜１８である
    による量で添加されることを特徴とする請求項１記載の鉄を母材とするろう付け材。
  3. ガス微粉化もしくは水微粉化もしくは上記組成のインゴットの破砕または溶融物のスピ
    ニングによって製造されることを特徴とする請求項１または２記載の鉄を母材とするろう
    付け材。
  4. ０〜２０％のＨｆ及び／または０−２％のＣを含むことを特徴とする先の請求項のいず
    れか記載の鉄を母材とするろう付け材。
  5. 鉄を母材とする物品をろう付けすることによって製造されるろう付け製品であって、Ｂ
    及び／またはＰ及び／またはＳｉを液相線温度を低下させる成分として合金化した鉄を母
    材とするろう付け材によって接合されることを特徴とするろう付け製品。
  6. 鉄を母材とする物品と鉄を母材とするろう付け材が９−３０％のＣｒを含むことを特徴
    とする請求項５記載のろう付け製品。
  7. 請求項６記載のろう付け製品であって、該製品は少なくとも二つの熱交換流体のための
    板状熱交換器であって、鉄を母材とする薄い壁を有する熱交換板の幾つかを、鉄を母材と
    するろう付け材によってろう付けして製造された少なくとも一つの板状パッケージを含み
    、該熱交換板は相対で熱交換流体のための内部スペースの輪郭を定め、得られたろう付け
    接合部が、鉄を母材とする板材と比べて、内部または周囲において局部的に高いB、P、Si
    量を有し、鉄を母材とするろう付け材の組成に近い冶金組成を持つことを特徴とするろう
    付け製品。
JP2009099110A 2001-06-05 2009-04-15 ろう付け材及びそれで得られる製品 Expired - Lifetime JP5345442B2 (ja)