JP2008504430A - マルチ構造ラミネート用の接着促進剤 - Google Patents
マルチ構造ラミネート用の接着促進剤 Download PDFInfo
- Publication number
- JP2008504430A JP2008504430A JP2007519358A JP2007519358A JP2008504430A JP 2008504430 A JP2008504430 A JP 2008504430A JP 2007519358 A JP2007519358 A JP 2007519358A JP 2007519358 A JP2007519358 A JP 2007519358A JP 2008504430 A JP2008504430 A JP 2008504430A
- Authority
- JP
- Japan
- Prior art keywords
- percent
- component
- layer
- ethylene
- propylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
表1:マトリックス/分散相の組合せ
(3)2.5” Egan Davis Standard MAC Extruders
(2)2” Egan Davis Standard MAC Extruders
DSB 11 Polyethylene Barrier Screws 30:1 L/D
Cloeren5層デュアルプランフィードブロック
Cloeren 36” Epoch(商標) III Autogauge 5.1 ダイ
(5)重量コントロール用のBarron計量ホッパー(weigh hoppers)
Electrostatic & Air Jetエッジピンナーエアーナイフおよびバキュームボックス
40” O.D.×40”長さの一次チルロール(30−40RMS)
20” O.D.×40”長さの二次チルロール(2−4RMS)
NDC Model 300 Betaトランスミッションゲージセンサー
振動フレーム
二位置単タレット水平巻取り機(50−1000fpm)
表2:押出機の条件
キャストフィルムラインを用い、一つはポリエチレンをベースとし、一つはポリプロピレンをベースとした二つのフィルムを調製した。これらのフィルムは以下の通りであった:a)4g/10分のメルトインデックス(ASTM D1238、条件190℃/2.16kg)および0.94g/ccの密度(ASTM D 792)を有するチーグラー・ナッタ産生エチレン/1−オクテンポリマー;ならびにb)8.8g/10分のメルトフローレート(ASTM D 1238、条件230℃/2.16kg)を有するホモポリマーポリプロピレン。これらのフィルムを押出しコーターで試験した。
混合物1:10wtパーセントのサンプル3および90wtパーセントのサンプル2(PP)。
混合物2:25wtパーセントのサンプル3および75wtパーセントのサンプル2(PP)。
混合物3:10wtパーセントのサンプル4および90wtパーセントのサンプル1(ZN−EO)。
混合物4:25wtパーセントのサンプル4および75wtパーセントのサンプル1(ZN−EO)。
表3:種々のフィルム組成物に対するプロセス条件
表4:三層化されたフィルム組成物の平均剥離値(10個のサンプルを試験した)
上で検討されている通りのサンプル3、上で検討されている通りのサンプル4およびサンプル5(米国特許第5,272,236号、第5,278,272号および第5,665,800号の教示により製作され、5g/10分のメルトインデックス、0.87g/ccの密度および2から3までのMw/Mnを有するエチレン/1−オクテンコポリマー)をそれぞれ個別的に用いて二つのポリプロピレン(PP)不織布基体(またはウェブ)を結合した。押出機は、上の実施例1で使用したのと同一の押出機であった。サンプル4は180°F(82℃)で押出しされ、一方、サンプル3および5は、それぞれ、215°F(102℃)および340°F(171℃)で押出しされた。
表5:不織布に対する平均剥離値(3つのサンプルを試験した)
以下の表6に示されている通りの3種類のフィルム組成物を透過型電子顕微鏡検査により調べた(PP=ポリプロピレンおよびPE=ポリエチレン)。
表6.TEMにより調べたフィルム組成物
Claims (22)
- 少なくとも2つの成分を含むラミネーション接着剤であって、前記2つの成分が:
少なくとも一つのプロピレンをベースとしたポリマーを含む成分A)であり、ASTM D1238の条件230℃/2.16kgにより測定したときに、0.5g/10分から100g/10分までの間のメルトフローレートを有する少なくとも一つのプロピレンをベースとしたポリマーを含む成分A);および
少なくとも一つのエチレンをベースとしたポリマーを含む成分B)であり、好適には0.85g/ccから0.90g/ccまでの間、より好適には0.855g/ccから0.89g/ccまでの間、最も好適には0.87g/ccから0.88g/ccまでの間の密度を有し、且つ、350°F(177℃)におけるASTM D3236により測定したときに、300cPから50,000cPまでの間、好適には1000cPから30,000cPまでの間、より好適には5000cPから25,000cPまでの間の粘度を有する少なくとも一つのエチレンをベースとしたポリマーを含む成分B);
であり、
ここで、成分A)は60パーセントから95パーセントまで、好適には70パーセントから90パーセントまで、より好適には70パーセントから80パーセントまでであり;成分B)は40パーセントから5パーセントまで、好適には30パーセントから10パーセントまで、より好適には30パーセントから20パーセントまでであって、上記パーセンテージが当該ラミネーション接着剤の総合重量をベースとした重量百分率である;
ラミネーション接着剤。 - 少なくとも2つの成分を含むラミネーション接着剤であって、前記2つの成分が:
少なくとも一つのエチレンをベースとしたポリマーを含む成分A)であり、ASTM D1238の条件190℃/2.16kgにより測定したときに、0.5g/10分から100g/10分までの間のメルトインデックスを有する少なくとも一つのエチレンをベースとしたポリマーを含む成分A);および
少なくとも一つのエチレンをベースとしたポリマーを含む成分B)であり、ASTM D−792により測定したときに、好適には0.85g/ccから0.90g/ccまでの間、より好適には0.855g/ccから0.89g/ccまでの間、最も好適には0.87g/ccから0.88g/ccまでの間の密度を有し、且つ、粘度を350°F(177℃)におけるASTM D 3236により測定したときに、300cPから50,000cPまでの間、好適には1000cPから30,000cPまでの間、より好適には5000cPから25,000cPまでの間の粘度を有する少なくとも一つのエチレンをベースとしたポリマーを含む成分B);
であり、
ここで、成分A)は60パーセントから95パーセントまで、好適には70パーセントから90パーセントまで、より好適には70パーセントから80パーセントまでであり;成分B)は40パーセントから5パーセントまで、好適には30パーセントから10パーセントまで、より好適には30パーセントから20パーセントまで、更に一層好適には30パーセントであり、上記パーセンテージが成分A)および成分B)の総合重量をベースとした重量百分率である;
ラミネーション接着剤。 - 少なくとも2つの成分を含むラミネーション接着剤であって、前記2つの成分が:
少なくとも一つのプロピレンをベースとしたポリマーを含む成分A)であり、ASTM D1238の条件230℃/2.16kgにより試験したときに、0.5g/10分から100g/10分までの間のメルトフローレートを有する少なくとも一つのプロピレンをベースとしたポリマーを含む成分A);および
少なくとも一つのプロピレンをベースとしたポリマーを含む成分B)であり、DSCを用いて測定したときに、好適には30パーセント未満、より好適には25パーセント未満、最も好適には20パーセント未満の結晶化度を有し、且つ、ASTM D1238の条件230℃/2.16kgにより測定したときに、好適には25g/10分より大きいメルトフローレートを有する少なくとも一つのプロピレンをベースとしたポリマーを含む成分B);
であり、
ここで、成分A)は60パーセントから95パーセントまで、好適には70パーセントから90パーセントまで、より好適には70パーセントから80パーセントまでであり;成分B)は40パーセントから5パーセントまで、好適には30パーセントから10パーセントまで、より好適には30パーセントから20パーセントまでであって、上記パーセンテージが成分A)および成分B)の総合重量をベースとした重量百分率である;
ラミネーション接着剤。 - 少なくとも2つの成分を含むラミネーション接着剤であって、前記2つの成分が:
少なくとも一つのエチレンをベースとしたポリマーを含む成分A)であり、ASTM D1238の条件190℃/2.16kgにより試験したときに、0.5g/10分から100g/10分までの間のメルトインデックスを有する少なくとも一つのエチレンをベースとしたポリマーを含む成分A);および
少なくとも一つのプロピレンをベースとしたポリマーを含む成分B)であり、DSCを用いて測定したときに、好適には30パーセント未満、より好適には25パーセント未満、最も好適には20パーセント未満の結晶化度を有し、且つ、ASTM D1238の条件230℃/2.16kgにより測定したときに、好適には25g/10分より大きいメルトフローレートを有する少なくとも一つのプロピレンをベースとしたポリマーを含む成分B);
であり、
ここで、成分A)は60パーセントから95パーセントまで、好適には70パーセントから90パーセントまで、より好適には70パーセントから80パーセントまでであり;成分B)は40パーセントから5パーセントまで、好適には30パーセントから10パーセントまで、より好適には30パーセントから20パーセントまでであって、上記パーセンテージが成分A)および成分B)の総合重量をベースとしたものである;
ラミネーション接着剤。 - 上記成分B)が、エチレン/C3からC20までのα−オレフィンインターポリマー、好適にはC3からC12までのα−オレフィンインターポリマー、より好適にはC8α−オレフィンコポリマーからなるグループから選択される少なくとも一つのエチレンをベースとしたポリマーを含む、請求項1または2に記載の接着剤。
- 上記成分B)がエチレン/C3からC8までのα−オレフィンインターポリマーからなるグループから選択される少なくとも一つのエチレンをベースとしたポリマーを含み、ここで、前記α−オレフィンがプロピレン、1−ブテン、2−メチル−1−プロペン、1−ペンテン、2−メチル−1−ブテン、1−ヘキセン、4−メチル−1−ペンテン、1−ヘプテンおよび1−オクテンからなるグループから選択される、請求項1または2に記載の接着剤。
- 成分A)の上記少なくとも一つのプロピレンベースのオレフィンポリマーがポリプロピレンホモポリマーおよびプロピレン/エチレンインターポリマーからなるグループから選択され、ここで、該エチレンの含有量が前記インターポリマーのうちの20重量パーセントを超えない割合を構成し、好適には<15重量パーセント、より好適には<10重量パーセント、最も好適には<5重量パーセントの割合を構成する、請求項1または3に記載の接着剤。
- 請求項1から4のいずれかに記載の組成を有するラミネーション接着剤を含むラミネート構造物であって、少なくとも三つの熱可塑性層を含み、ここで前記層が相互に共押出し、熱接合、融着及び/又は圧着されている、ラミネート構造物。
- 層1)、層2)および層3)を含むラミネート構造物であって:
層1)は、(ASTM D 1238、条件230℃/2.16kgにより測定したときに)0.5g/10分から100g/10分までの間のメルトフローレートを有する少なくとも一つの熱可塑性のプロピレンをベースとしたポリマーを含み;
層3)は少なくとも一つの熱可塑性のオレフィンをベースとしたポリマーを含み;
層2)は、層1)および層3)の間に配置され、ある接合様式において層1)と層3)との両方に緊密に接触しており、且つ、請求項1から4のいずれかに記載の組成を有するラミネーション接着剤を含んでおり;
ここで、当該ラミネート構造物が、ある接合様式において相互に緊密に接触した状態で配置された単に層1)および層3)のみから成る同等なラミネートの個別的な剥離強度と比べたときに、高められた剥離強度を有している;
ラミネート構造物。 - 層1)および層3)の両方が、(ASTM D 1238、条件230℃/2.16kgにより測定したときに)0.5g/10分から100g/10分までの間のメルトフローレートを有する熱可塑性のプロピレンをベースとしたポリマーを含む、請求項9に記載のラミネート。
- 層1)および層3)の両方がフィルム層である、請求項9に記載のラミネート。
- 層2)の成分A)がプロピレンをベースとしたポリマーであって、該ポリマーが、層1)の上記少なくとも一つの熱可塑性のプロピレンをベースとしたポリマーの粘度およびメルトフローレートと同じ粘度およびメルトフローレートを有するプロピレンホモポリマーであり;層2)の成分B)がエチレンをベースとしたポリマーであって、該ポリマーが、0.87g/ccから0.88g/ccまでの間の密度を有し、且つ、350°F(177℃)におけるASTM D3236により測定したときに、5,000cPから20,000cPまでの間の粘度を有するC8α−オレフィンコポリマーである、請求項9に記載のラミネート。
- 層1)または層3)のうちの一方の層が熱可塑性フィルム層であって、もう一方の層が不可欠な要素として不織布ウェブを含む層であり、前記不織布ウェブが、スパンボンデッド、カーデッド熱接合ステープル繊維、エアーレイド、メルトブローン不織布熱可塑性または前述のものの組合せから選択される、請求項9に記載のラミネート。
- 層1)または層3)のうちの一方の層が熱可塑性フィルム層であって、もう一方の層が不可欠な要素として熱可塑性フォームを含む層である、請求項9に記載のラミネート。
- 当該ラミネートが、単に層1)および層3)のみから成る同等なラミネートの個別的な剥離強度と比べたときに、少なくとも25パーセント、好適には50パーセント、より好適には100パーセント高められた層1)と層3)との間の180°方向の剥離強度を有している、請求項12、13または14に記載のラミネート。
- 三つの層、層1)、層2)および層3)を含むラミネート構造物であって、ここで、層2)が請求項1から4のいずれかに記載の組成を有するラミネーション接着剤を含んでおり、当該ラミネートが、単に層1)および層3)のみから成る同等なラミネートの個別的な剥離強度と比べたときに、少なくとも25パーセント、好適には50パーセント、より好適には100パーセント高められた層1)と層3)との間の180°方向の剥離強度を有している、ラミネート構造物。
- 請求項1から4のいずれかに記載の接着剤組成物を含むフィルム/不織布ラミネート。
- オムツ、トレーニングパンツ、吸水性アンダーパンツ、成人用尿漏れ防止用品および女性衛生用品からなるグループから選択されるパーソナルケア製品であって、前記パーソナルケア製品が請求項17に記載のラミネートを含んでいる、パーソナルケア製品。
- 層2)がポリオレフィンマトリックス内における分散相を含む結合層であって、ここで、前記分散相は離散した微粒子及び/又は縞の形態であってよく、且つ、該分散相の離散的な微粒子及び/又は縞は0.05ミクロン(μm)から1ミクロンまでの間の平均幅を有しており;
ここで、上記分散相が成分B)を含み、該マトリックスが成分A)を含む;
請求項9に記載のラミネート構造物。 - 当該ラミネートが層2)を層1)と層3)との間に押出しすることにより形成される、請求項9に記載のラミネート構造物。
- 上記層2)の押出し中、該押出し物の温度が層1)および層3)の溶融温度付近または溶融温度以上である、請求項20に記載のラミネート構造物。
- 上記層2)の押出し中、該押出し物の温度が340°F(171℃)から370°F(188℃)までの間であり、該押出機が15rpmから30rpmまでの速度で運転される、請求項21に記載のラミネート構造物。