JP2008210723A - ナノカーボンペースト及びナノカーボンエミッタの製造方法 - Google Patents
ナノカーボンペースト及びナノカーボンエミッタの製造方法 Download PDFInfo
- Publication number
- JP2008210723A JP2008210723A JP2007048183A JP2007048183A JP2008210723A JP 2008210723 A JP2008210723 A JP 2008210723A JP 2007048183 A JP2007048183 A JP 2007048183A JP 2007048183 A JP2007048183 A JP 2007048183A JP 2008210723 A JP2008210723 A JP 2008210723A
- Authority
- JP
- Japan
- Prior art keywords
- nanocarbon
- nano
- carbon
- paste
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ナノカーボンペースト1が、導電性粒子として酸化亜鉛2に直接または金属若しくは金属化合物を介してナノ炭素材料3が形成されてなるナノ炭素材料複合体4と、無機バインダー5と、有機バインダー6と、有機溶剤7と、を混合してなる。このナノカーボンペースト1を、基体11上の導電層12に塗布することで、ナノカーボンエミッタを製造する。
【選択図】図1
Description
本発明の第二の目的は、エミッタ材料となるナノ炭素材料を基体に容易にかつ大面積に均一に形成することで、製造コストが低減できる、ナノカーボンエミッタの製造方法を提供することにある。
図1は、本発明のナノカーボンペースト1の構成を模式的に示す断面図である。本発明のナノカーボンペースト1は、核となる導電性粒子としての酸化亜鉛粒子2と酸化亜鉛粒子2上に成長したナノ炭素材料3とからなるナノ炭素材料複合体4と、無機バインダー5と、有機バインダー6と、有機溶剤7とを混合して成る。図1では、ナノ炭素材料3が直接酸化亜鉛粒子2上に存在する場合を示しているが、ナノ炭素材料3が金属を介在させて酸化亜鉛粒子2上に存在してもよいし、酸化物をはじめとする金属化合物を介在させて酸化亜鉛粒子2上に存在してもよい。ここで、導電性粒子は酸化亜鉛粒子のほかに、鉄、ニッケル、パラジウムなどの金属粒子を用いても良い。
図2は、本発明のナノカーボンエミッタの製造工程を示す図である。
先ず、図2(a)に示す基体11上に薄膜または厚膜からなる導電層12を成膜する(図2(b)参照)。導電層11が薄膜の場合には、蒸着、スパッタ、イオンプレーティングなどの方法で基体11上に成膜する。その際、必要に応じてリソグラフィー法などを用いることにより所定形状にパターニングする工程を挿入してもよい。一方、導電層12が厚膜の場合には、印刷法などで基体11上に塗布する。所定のパターン形状となるよう同時に成形することもできる。
以上の工程により、電界放出型の電子放出素子としてのナノカーボンエミッタが完成する。
平均粒径が5μmの酸化亜鉛粒子(和光純薬工業製)を原料として用い、約300℃、約10分間の焼結により導電性粒子原料とした。遷移金属触媒微粒子としてコバルト(Co)触媒微粒子を採用し、Coの硝酸塩(Co(NO3 )2 ・6H2 O)水溶液を用いて含浸法により酸化亜鉛粒子上にCo触媒微粒子を担持した。ここで、触媒の担持量は5w%(重量%)とした。次に、電気炉中に遷移金属触媒微粒子を担持した酸化亜鉛粒子を挿入し、アルゴンで希釈したエチレンガスを流し、約650℃、30分加熱した。遷移金属触媒微粒子を担持した酸化亜鉛粒子の量は100mg、エチレンとアルゴンの流量比は1:1、総流量は30cm3/分とした。
図4は、本発明の実施例1において作製したナノ炭素材料複合体のうち、繊維状のナノ炭素材料部分の走査型電子顕微鏡像を示す図、即ち図3の拡大図である。繊維状のナノ炭素材料部分は、図4から、カーボンナノチューブ、カーボンナノフィラメントおよびカーボンナノファイバーから成ることが判明した。
図6は、本発明の実施例2において作製したナノ炭素材料複合体のうち、繊維状のナノ炭素材料部分の走査型電子顕微鏡像を示す図、即ち図5の拡大図である。繊維状のナノ炭素材料部分は、図6から、カーボンナノチューブ、カーボンナノフィラメントおよびカーボンナノファイバーから成ることが判明した。
最初に、ガラス基板上に導電層としてクロム薄膜をスパッタ法により100nm厚で成膜した。実施例1で得られたナノカーボンペーストを用いて、SUS400メッシュ版を使用してスクリーン印刷法で、スキージを用いて導電層上に印刷して塗布した。その後、空気中で370℃で30分間焼成することで脱溶剤処理及び脱有機バインダー処理を行い、更に、真空中で420℃で30分間焼成することでガラスフリットを溶融し上記生成物中のナノ炭素材料複合体同士や導電層上に固着した。これにより、カーボンナノファイバーによるナノカーボンエミッタを製造することができる。
2:酸化亜鉛粒子(導電性粒子)
3:ナノ炭素材料
4:ナノ炭素材料複合体
5:無機バインダー
6:有機バインダー
7:溶剤
11:基体
12:導電層
Claims (4)
- 導電性粒子に直接または金属若しくは金属化合物を介してナノ炭素材料が形成されてなるナノ炭素材料複合体と、バインダー材料と、溶剤と、を混合してなることを特徴とする、ナノカーボンペースト。
- 前記導電性粒子は、酸化亜鉛粒子であることを特徴とする、請求項1に記載のナノカーボンペースト。
- 基体に導電層を形成する工程と、
導電性粒子に直接または金属若しくは金属化合物を介してナノ炭素材料が形成されてなるナノ炭素材料複合体とバインダー材料と溶剤とを混合してなるナノカーボンペーストを、上記導電層上に塗布することで、上記導電層上に上記ナノ炭素材料複合体を配置する工程と、
を含むことを特徴とする、ナノカーボンエミッタの製造方法。 - 前記導電性粒子は、酸化亜鉛粒子であることを特徴とする、請求項3に記載のナノカーボンエミッタの製造方法。