JP2008179707A - 帯電防止性アクリル系樹脂組成物およびフィルム、シート - Google Patents
帯電防止性アクリル系樹脂組成物およびフィルム、シート Download PDFInfo
- Publication number
- JP2008179707A JP2008179707A JP2007014613A JP2007014613A JP2008179707A JP 2008179707 A JP2008179707 A JP 2008179707A JP 2007014613 A JP2007014613 A JP 2007014613A JP 2007014613 A JP2007014613 A JP 2007014613A JP 2008179707 A JP2008179707 A JP 2008179707A
- Authority
- JP
- Japan
- Prior art keywords
- antistatic
- film
- acrylic
- weight
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本発明は帯電防止剤の滲出による被着体の汚染や帯電防止効果の減衰が少なく、物性や成形加工性の優れた帯電防止アクリル系樹脂組成物及びフィルム、シートを提供することを目的とする。
【解決手段】
上記目的を達成するため、本発明の帯電防止性アクリル系樹脂組成物は、10〜80重量%のアクリル樹脂(a1)と90〜20重量%のアクリル系ゴム状粒子(a2)とからなるアクリル系ポリマー混合物(A)に帯電防止剤として熱可塑性ポリアミドエラストマー樹脂(B)を添加してなる帯電防止性アクリル系樹脂組成物としたことであり(請求項1)、また、アクリル系樹脂組成物の熱可塑性ポリアミドエラストマー(B)がメルトインデックス(MI)を15g/10min以下としたことであり(請求項2)、さらに、上記の帯電防止性アクリル系樹脂組成物から形成されるフィルムおよびシートとしたことである(請求項3)。
【選択図】 なし
Description
本発明で使用するアクリル樹脂(a1)とアクリル系ゴム状粒子(a2)の比率は、10〜80重量%のアクリル樹脂(a1)と90〜20重量%のアクリル系ゴム状粒子(a2)からなることが必要で、より少量の帯電防止剤の添加で帯電防止性能が得られるようにするには、10〜50重量%のアクリル樹脂(a1)と90〜50重量%のアクリル系ゴム状粒子(a2)であることがより好ましい。
また、アクリル系ゴム状粒子(a2)は、特に限定されないがアクリル酸エステルとこれと共重合可能な多官能性単量体および他の単官能性単量体からなる単量体混合物によって形成されるゴム弾性を有する層を含む樹脂組成物等が挙げられる。
さらに、前記熱可塑性ポリアミドエラストマー樹脂(B)の構成成分中に、炭素原子数20〜48の重合脂肪酸及びこれらのエステル誘導体に由来する成分を1質量%〜40質量%含有することは透明性の点から好ましい構成である。
なお、メルトインデックス(MI値)は、メルトインデクサーを用いて、試料を特定温度(190℃)で加熱後、21.18N(2.16kgf)の荷重下で一定時間の間にオリフィスを通過した溶融試料の質量を測定し、これを10分当たりのg数に換算した値である。
250℃に到達した時点から800Paまで徐々に減圧し、1時間この温度に保持した後、エステル化触媒としてテトラブトキシジルコニウムを添加し、再び減圧を開始し、最終的には130〜270Paまで減圧することにより反応を進め、3時間後、熱可塑性ポリアミドエラストマー樹脂(B)を得た。
アクリル系ポリマー混合物(A)として、アクリル系樹脂(a1)20重量%とアクリル系ゴム粒子(a2)80重量%であるパラペットSA−FW001(クラレ社製)(以下、これを[A1]と記す。)を64重量部と、アクリル系樹脂(a1)50重量%とアクリル系ゴム粒子(a2)50重量%であるパラペットGR−F(クラレ社製)(以下、これを[A2]と記す。)16重量部と、帯電防止剤として上記の製造方法によりMIを3.3に調整した熱可塑性ポリアミドエラストマー(以下、これを[B1]と記す。)を20重量部とに、酸化防止剤AO−60(ADEKA社製)0.1重量部および滑剤としてモンタン酸エステルであるリコワックスE(クラリアントジャパン社製)0.3重量部をドライブレンドした後に、バンバリーミキサーで混練し180℃に設定したカレンダー成形機にて厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表1に記す。
表1から明らかなように、実施例1は、帯電防止性能、成形性、引張試験による評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
アクリル系ポリマー混合物(A)として、[A1]72重量部と[A2]18重量部にし、帯電防止剤として前記の製造方法と同様にしてMIを13.1に調整した熱可塑性ポリアミドエラストマー(以下、これを[B2]と記す。)を10重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表1に記す。
表1から明らかなように、実施例2も、帯電防止性能、成形性、引張試験による評価、tanδによる評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
アクリル系ポリマー混合物(A)として、[A1]89.5重量部とアクリル系樹脂100重量%のGF(クラレ社製)(以下、これを[A3]と記す。)9.5重量部にし、熱可塑性ポリアミドエラストマー[B2]を5重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表1に記す。
表1から明らかなように、実施例3も、帯電防止性能、成形性による評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
アクリル系ポリマー混合物(A)として、[A1]72重量部と[A3]18重量部にし、熱可塑性ポリアミドエラストマー[B1]を10重量部とすること以外は実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表1に記す。
表1から明らかなように、実施例4も、帯電防止性能、成形性による評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
アクリル系ポリマー混合物(A)として、[A1]36重量部と[A3]54重量部にし、熱可塑性ポリアミドエラストマー[B1]を10重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表1に記す。
表1から明らかなように、実施例5も、帯電防止性能、成形性による評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
アクリル系ポリマー混合物(A)として[A1]19.8重量部と[A2]79.2重量部にし、熱可塑性ポリアミドエラストマー[B1]を1重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表2に記す。
表1から明らかなように、実施例6も、帯電防止性能、成形性による評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
アクリル系ポリマー混合物(A)として[A1]18重量部と[A2]72重量部にし、帯電防止剤として前記の製造方法と同様にしてMIを19.3に調整した熱可塑性ポリアミドエラストマー(以下、これを[B3]と記す。)を10重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表2に記す。
表1から明らかなように、実施例7も、帯電防止性能、成形性による評価が共に優れており、マスキングテープ、マーキングフィルムなどの産業用途、ダイシング用粘着テープ、バックグラインド用粘着テープなど半導体製造用途、保護フィルムなどの基材フィルム、シートに使用することができる。
[帯電防止性能の評価]
フィルム、シートを100mm角にカットして、温度20℃で63%RHの恒温室にて、超高抵抗計(アドバンテスト社製 R8340A)を用いて、表面固有抵抗値の測定を行い以下の基準にて評価した。
評価基準
◎:表面固有抵抗値が1011Ω未満
○:表面固有抵抗値が1011以上〜1014Ω未満
×:表面固有抵抗値が1014Ω以上
[成形性の評価]
カレンダーロールでの加工において、ロールへの粘着性を以下の基準にて評価した。
評価基準
◎:容易に剥離できる。
○:特に問題なく、剥離できる。
△:粘着傾向はみられるが、剥離できる。
×:ロールに粘着し剥離できない。
アクリル系ポリマー混合物(A)として[A3]90重量部と熱可塑性ポリアミドエラストマー[B1]を10重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表2に記す。
比較例1では十分な帯電防止性能が得られていないことがわかる。
アクリル系ポリマー混合物(A)として[A2]30重量部と[A3]45重量部と帯電防止剤としてポリアミド系共重合体をベースとしたIRGASTAT P22(以下、これを[B4]と記す。)25重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表2に記す。
比較例2では十分な帯電防止性能は得られているが、ロールに粘着して成形性に問題があった。
アクリル系ポリマー混合物(A)として[A1]9重量部と[A2]81重量部にし、帯電防止剤として[B4]を10重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表2に記す。
比較例3ではロールに粘着し安定した成型加工が出来ないだけでなく、十分な帯電防止性能が得られていないことがわかる。
アクリル系ポリマー混合物(A)の替わりにオレフィン系樹脂であるEG8003(ダウケミカル社製)(以下、これを[C1]と記す。)90重量部と熱可塑性ポリアミドエラストマー[B1]を10重量部とすること以外は、実施例1と同様にして厚さ100μmのフィルムを得た。得られたフィルムの評価結果を表2に記す。
比較例4ではロールに粘着し安定した成型加工が出来ないだけでなく、十分な帯電防止性能が得られていないことがわかる。
A1:パラペットSA−FW001(a1/a2=20/80 クラレ社製)
A2:パラペットGR−F(a1/a2=50/50 クラレ社製)
A3:GF(a1が100% クラレ社製)
B1:熱可塑性ポリアミドエラストマー
B2:熱可塑性ポリアミドエラストマー
B3:熱可塑性ポリアミドエラストマー
a1/a2:アクリル樹脂/アクリル系ゴム状粒子
Claims (3)
- 10〜80重量%のアクリル樹脂(a1)と90〜20重量%のアクリル系ゴム状粒子(a2)とからなるアクリル系ポリマー混合物(A)に帯電防止剤として熱可塑性ポリアミドエラストマー樹脂(B)を添加してなることを特徴とする帯電防止性アクリル系樹脂組成物
- 請求項1記載の熱可塑性ポリアミドエラストマー(B)のメルトインデックス(MI)が15g/10min以下であることを特徴とする帯電防止性アクリル系樹脂組成物。
- 請求項1または2に記載の帯電防止性アクリル系樹脂組成物から形成されることを特徴とするフィルムおよびシート。