JP2008075007A - マーキング用粘着シート - Google Patents
マーキング用粘着シート Download PDFInfo
- Publication number
- JP2008075007A JP2008075007A JP2006257181A JP2006257181A JP2008075007A JP 2008075007 A JP2008075007 A JP 2008075007A JP 2006257181 A JP2006257181 A JP 2006257181A JP 2006257181 A JP2006257181 A JP 2006257181A JP 2008075007 A JP2008075007 A JP 2008075007A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- adhesive sheet
- modified
- marking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】非塩化ビニル系樹脂基材の一方の面に粘着剤層を有すると共に、他方の面に、(A)重量平均分子量が15,000〜80,000のポリエステル変性アクリルポリオール樹脂と、(B)硬化剤としてポリイソシアネート系化合物を含む、架橋化されたアクリルウレタン系コーティング層を有するマーキング用粘着シートである。
【選択図】なし
Description
一方、最近、前記用途の中で表示・標識用粘着シートや装飾用粘着シートなどのマーキング用粘着シートの分野においては、塗装製品の生産性の向上や製造コストの低減を図るために、塗装代替用としての粘着シートの需要が増加してきている。例えば表示・標識用として、危険表示用テープ、ラインテープ、マーキングテープなどが用いられ、また装飾用として、看板、ショーウインドや建造物の内外装、マーキングシート・ステッカーによる車やオートバイの装飾、自動車ドアサッシュ部の装飾などに粘着シートが用いられている。
このような塗装代替用粘着シートが適用される被着体としては様々なものがあり、例えば金属板、塗装金属板、ガラス、セラミックス、石材、木質材料、プラスチック、紙類などが挙げられる。
塗装代替用粘着シートにおいては、その貼付製品は屋外で使用されることが多く、基材及び粘着剤共に、耐候性に優れることが必要であり、粘着剤としては、通常耐候性が良好なアクリル系粘着剤が用いられる。一方、基材は、耐候性に優れると共に、収縮率が小さく、かつ貼付作業性の面からは、あまり硬質でないものが好ましく、したがって、例えば塩化ビニル系樹脂、ポリエステル、ポリオレフィン、ポリアクリレート、ポリカーボネート、ポリ四フッ化エチレン、熱可塑性ポリウレタンなどからなるフィルム基材が用いられるが、経済性などの点で、これまで塩化ビニル系樹脂からなるフィルム基材が多用されてきた。
しかしながら、現在、環境対応の面より、マーキング用粘着シートにおいては、塩化ビニル系樹脂基材から、非塩化ビニル系樹脂基材への移行傾向が多く見られる。屋外で用いられる外装用のマーキング用粘着シートには、耐候性が求められるが、例えばポリエステル系フィルムやポリオレフィン系フィルムは、耐候性に劣り、基材のクラッキングや白化、着色基材の場合であれば色の劣化などが発生しやすい。
ところで、自動車に用いられるマーキング用粘着シートに対しては、耐候性以外に、基材の光沢度、耐擦傷性、耐薬品浸漬性(耐ガソリン浸漬性)などが要求されるものの、ポリエステル系基材などにおいては、これらを同時に満たすことは困難である。
一方、ゴルフボール分野においては、耐衝撃・耐摩耗性を有すると共に、耐候性にも優れるゴルフボール用塗料組成物が開示されている(例えば、特許文献1参照)。しかしながら、この塗料組成物はゴルフボール用であって、マーキング用粘着シートに用いられるものではない。
すなわち、本発明は、
[1]非塩化ビニル系樹脂基材の一方の面に粘着剤層を有すると共に、他方の面に、(A)重量平均分子量が15,000〜80,000のポリエステル変性アクリルポリオール樹脂と、(B)硬化剤としてポリイソシアネート系化合物を含む、架橋化されたアクリルウレタン系コーティング層を有することを特徴とするマーキング用粘着シート、
[2](A)成分のポリエステル変性アクリルポリオール樹脂のガラス転移温度が42〜60℃である上記[1]項に記載のマーキング用粘着シート、
[3]架橋化されたアクリルウレタン系コーティング層が、平均粒径1〜5μmの無機粒子及び/又は有機粒子を含む上記[1]又は[2]項に記載のマーキング用粘着シート、
[4](B)成分のポリイソシアネート系化合物が、脂肪族、脂環式、芳香族及び芳香脂肪族イソシアネート、並びにこれらのアダクト変性体、ビュレット変性体、イソシアヌレート変性体、ウレトンイミン変性体、ウレトジオン変性体、カルボジイミド変性体及び弾性変性ポリイソシアネートの中から選ばれる少なくとも1種である上記[1]〜[3]項のいずれかに記載のマーキング用粘着シート、
[5](B)成分のイソシアネート基と(A)成分の水酸基とのモル比[NCO]/[OH]が0.5〜1.5である上記[1]〜[4]項のいずれかに記載のマーキング用粘着シート、及び
[6]架橋化されたアクリルウレタン系コーティング層の厚さが、1〜8μmである上記[1]〜[5]項のいずれかに記載のマーキング用粘着シート、
を提供するものである。
本発明のマーキング用粘着シートにおいて用いられる非塩化ビニル系樹脂基材(以下、基材ともいう)としては、該粘着シートが塗装代替用として使用されるため、収縮率が小さく、かつ貼付作業性の面から、あまり硬質でないものが好ましい。したがって、ポリエチレンテレフタレートや非晶質ポリエチレンテレフタレートなどのポリエステル系樹脂、ポリエチレン、ポリプロピレン、プロピレン−エチレン共重合体などのポリオレフィン系樹脂、アクリル系樹脂、ポリカーボネート系樹脂、フッ素系樹脂、熱可塑性ウレタン系樹脂、ポリエステル系熱可塑性エラストマー、ポリオレフィン系熱可塑性エラストマー及びこれらの混合物などを用いて得られたシート基材を用いることができる。
これらの非塩化ビニル系樹脂基材は、その上に設けられる粘着剤層やアクリルウレタン系コーティング層との密着性を向上させる目的で、所望により片面又は両面に、酸化法や凹凸化法などにより表面処理を施すことができる。上記酸化法としては、例えばコロナ放電処理、プラズマ処理、クロム酸処理(湿式)、火炎処理、熱風処理、オゾン・紫外線照射処理などが挙げられ、また、凹凸化法としては、例えばサンドブラスト法、溶剤処理法などが挙げられる。これらの表面処理法は基材の種類に応じて適宜選ばれるが、一般にはコロナ放電処理法が効果及び操作性などの面から、好ましく用いられる。また、片面又は両面にプライマー処理を施したものも用いることができる。
この基材の厚さは、粘着シートの用途にもよるが、通常10〜300μmの範囲、好ましくは30〜200μmの範囲で選定される。
前記各種の粘着剤の中では、耐候性などの面から、アクリル系粘着剤が好ましい。
このアクリル系粘着剤を用いて形成された粘着剤層は、重量平均分子量50万〜200万程度、好ましくは70万〜170万のアクリル系樹脂を含み、かつ架橋処理されたアクリル系粘着剤からなる層であることが好適である。重量平均分子量が上記範囲にあれば、粘着力及び保持力のバランスがとれたマーキング用粘着シートが得られる。
なお、上記重量平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)法により測定したポリスチレン換算の値である。
ここで、エステル部分のアルキル基の炭素数が1〜20の(メタ)アクリル酸エステルの例としては、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸プロピル、(メタ)アクリル酸ブチル、(メタ)アクリル酸ペンチル、(メタ)アクリル酸ヘキシル、(メタ)アクリル酸シクロヘキシル、(メタ)アクリル酸2−エチルヘキシル、(メタ)アクリル酸イソオクチル、(メタ)アクリル酸デシル、(メタ)アクリル酸ドデシル、(メタ)アクリル酸ミリスチル、(メタ)アクリル酸パルミチル、(メタ)アクリル酸ステアリルなどが挙げられる。これらは単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
該アクリル系粘着剤において、樹脂成分として用いられる(メタ)アクリル酸エステル系共重合体は、その共重合形態については特に制限はなく、ランダム、ブロック、グラフト共重合体のいずれであってもよい。
該アクリル系粘着剤としては、架橋処理されたものが好ましく、この架橋処理に用いられる架橋剤としては特に制限はなく、従来アクリル系粘着剤において架橋剤として慣用されているものの中から、任意のものを適宜選択して用いることができる。このような架橋剤としては、例えばポリイソシアネート化合物、エポキシ化合物、メラミン樹脂、尿素樹脂、ジアルデヒド類、メチロールポリマー、金属キレート化合物、金属アルコキシド、金属塩などが挙げられるが、ポリイソシアネート化合物やエポキシ化合物が好ましく用いられる。
本発明においては、この架橋剤は1種を単独で用いてもよいし、2種以上を組み合わせて用いてもよい。また、その使用量は、架橋剤の種類にもよるが、前記(メタ)アクリル酸エステル系共重合体100質量部に対し、通常0.01〜20質量部、好ましくは、0.1〜10質量部の範囲で選定される。
また、このアクリル系粘着剤には、所望により粘着付与剤、酸化防止剤、紫外線吸収剤、光安定剤、軟化剤、シランカップリング剤、充填剤などを添加することができる。
前記(A)成分のポリエステル変性アクリルポリオール樹脂は、アクリル系重合体からなる主鎖とポリエステルからなる側鎖から構成されている。
当該ポリエステル変性アクリルポリオール樹脂においては、側鎖のポリステル部分の含有量は、コーティング層の耐擦過性、延伸時の耐クラック性、耐汚染性、耐候性などの観点から、2〜50質量%が好ましく、10〜30質量%がより好ましい。
また、当該ポリエステル変性アクリルポリオール樹脂は、重量平均分子量Mwが15,000〜80,000の範囲にあることを要す。重量平均分子量が上記の範囲にあれば、耐擦過性、耐薬品浸漬性、耐ブロッキング性などが良好となる。好ましい重量平均分子量は16,000〜75,000、より好ましくは17,000〜70,000である。また、ガラス転移温度が42〜60℃の範囲にあることが好ましい。このガラス転移温度が上記範囲にあれば耐擦過性などが良好となる。より好ましいガラス転移温度は42〜55℃である。
なお、この重量平均分子量は、GPC法により測定したポリスチレン換算の値であり、ガラス転移温度はSeiko Instruments社製、示差走査熱量計(DSC)装置を用いて測定した値である。
さらに、水酸基価が30〜180mgKOH/gの範囲にあることが好ましい。この水酸基価が30mgKOH/g以上であれば十分な架橋が可能となり、コーティング層の耐擦過性や延伸時における耐クラック性が良好となる。また、水酸基価が180mgKOH/g以下であれば、塗工液は適度の粘度を有し、塗工性、ポットライフが良好となる。より好ましい水酸基価は50〜150mgKOH/gである。
なお、前記水酸基価は、JIS K 0070 7.1に準じて測定した値である。
当該ポリエステル変性アクリルポリオール樹脂の側鎖であるポリエステル部分は、一般式(I)及び/又は(II)
で表される構造を有することが好ましい。
当該ポリエステル変性アクリルポリオール樹脂は、例えば(1)アクリル系重合体の主鎖にラクトンなどの側鎖を構成する成分を付加させたもの、(2)ポリエステルが付加されたアクリル系モノマー(以下、ポリエステル含有アクリル系モノマーと略記する。)を単独重合させたもの、(3)ポリエステル含有アクリル系モノマーと他のアクリル系モノマーとを共重合させたものなどを挙げることができる。
本発明においては、当該ポリエステル変性アクリルポリオール樹脂を、少なくとも2種のアクリル系モノマーから構成される共重合体とすることが好ましい。また、アクリル系モノマーとして、ポリエステル含有アクリル系モノマーを含んでいることが好ましい。
本発明においては、ポリエステル含有アクリル系モノマーの量を、コーティング層の耐擦過性、延伸時の耐クラック性、塗装作業性などの観点から、モノマーの全質量に対して5〜50質量%とすることが好ましく、より好ましくは10〜30質量%である。
本発明においては、ポリエステル含有アクリル系モノマーとして、水酸基末端ラクトン変性(メタ)アクリレートを用いることが好ましい。水酸基末端ラクトン変性(メタ)アクリレートとしては、例えば、水酸基含有アクリル系モノマーにラクトン化合物を触媒を用いて1〜10モル程度開環付加させたものが挙げられる。ラクトン化合物の例としては、ε−カプロラクトン、β−プロピオラクトン、γ−ブチロラクトン、δ−バレロラクトンなどを挙げることができる。具体的には、ダイセル化学工業株式会社製の「プラクセルFMシリーズ(プラクセルFM−3等)」(カプロラクトン変性メタクリレート)、「プラクセルFAシリーズ」(カプロラクトン変性アクリレート)等を用いることができる。
また、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、3−ヒドロキシプロピル(メタ)アクリレート、2−ヒドロキシブチル(メタ)アクリレート、3−ヒドロキシブチル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、N−メチロール化アクリルアミド、カーボネート変性メタクリレート[ダイセル化学工業株式会社製、「HEMAC」]等の水酸基を含有するアクリルモノマー類を用いることもできる。
さらに、分子内に紫外線吸収性ユニットを有するアクリル系モノマー、分子内に酸化防止性ユニットを有するアクリル系モノマー、分子内に帯電防止性ユニットを有するアクリル系モノマーなどを用いることができる。これらのアクリル系モノマーを用いることにより、コーティング層に、良好な紫外線吸収能、酸化防止能、帯電防止能を付与することができる。
本発明においては、当該ポリエステル変性アクリルポリオール樹脂は、特に延伸時の耐クラック性、耐候性の点から、ポリエステル含有アクリルモノマー、メチル(メタ)アクリレート及び水酸基を含有する(メタ)アクリレートから構成される共重合体が好ましく、カプロラクトン変性メタクリレート、メチルメタクリレート及び2−ヒドロキシエチルメタクリレートから構成される共重合体であることが特に好ましい。
溶液重合法により、当該ポリエステル変性アクリルポリオール樹脂を製造する場合には、適当な溶媒中において、油溶性の有機過酸化物やアゾ系化合物などのラジカル重合開始剤の存在下に、前記の各モノマーを共重合させればよい。
この際、重合溶媒としては、例えば酢酸メチル、酢酸エチル等のエステル類、ベンゼン、トルエン、キシレン等の芳香族炭化水素、アセトン、シクロヘキサノン、メチルエチルケトン等のケトン類、テトラヒドロフラン等のエーテル類など、公知の溶媒を使用することができる。また、これらの溶媒は単独で、又は2種以上混合して用いることができる。重合開始剤の使用量は、特に制限はないが、モノマー全量に対し、0.05〜2質量%程度である。
一方、乳化重合法により、当該ポリエステル変性アクリルポリオール樹脂を製造する場合には、必要に応じ乳化剤を用いて単量体成分を乳化させ、水溶性の有機過酸化物、アゾ系化合物、過硫酸塩などの重合開始剤の存在下に、共重合させればよい。
このようにして得られたエステル変性アクリルポリオール樹脂は、重量平均分子量が15,000〜80,000の範囲にあることが必要である。また、ガラス転移温度が42〜60℃の範囲にあることが好ましい。
また、上記したイソシアネート類のアダクト変性体、ビュレット変性体、イソシアヌレート変性体、ウレトンイミン変性体、ウレトジオン変性体、カルボジイミド変性体、弾性変性ポリイソシアネート等のいわゆる変性ポリイソシアネートも使用できる。
また、前記弾性変性ポリイソシアネートとは、前記のトリレンジイソシアネート、キシリレンジイソシアネート、ジフェニルメタンジイソシアネート、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート等のジイソシアネート類をモノマーとして用い、これに弾性を有する活性水素含有化合物をウレタン反応させ、NCO末端のプレポリマーとしたものである。
イソシアネート類を弾性変性するために用いられる弾性を有する活性水素含有化合物としては、ポリエステルポリオール、ポリカーボネートポリオール、ポリエーテルポリオール、ポリオレフィンポリオール、動植物系ポリオール又はこれらのコポリオールなどが挙げられる。
本発明においては、(B)成分として、前記ポリイソシアネート系化合物を1種単独で用いてもよく、2種以上を組み合わせて用いてもよいが、これらの中で、延伸時の耐クラック性の観点から、ジイソシアネート類のアダクト変性体、イソシアヌレート変性体及び弾性変性ポリイソシアネートが好適である。
また、前記(A)成分と(B)成分の配合割合については、(B)成分のイソシアネート基と(A)成分の水酸基とのモル比[NCO]/[OH]が0.5〜1.5の範囲にあることが好ましい。該モル比が0.5以上であれば未反応の水酸基が少なくなり、耐水性などの塗膜性能が良好となり、一方1.5以下であれば過剰のイソシアネート基が少なくなり、塗膜にべた付きが残りにくい上、塗膜が脆くなるのを抑制することができる。より好ましい[NCO]/[OH]は0.8〜1.2である。
この粒子の平均粒径が上記範囲にあれば、きめ細かい塗膜表面を有し、かつ艶消し効果を有効に発揮することができる。
無機粒子としては、例えばシリカ、アルミナ、マイカ、炭酸カルシウム、硫酸バリウム、ケイ砂、シラスバルーンなどを用いることができ、有機粒子としては、例えばポリエチレン粒子、ポリスチレン粒子、アクリル系樹脂粒子、ポリカーボネート粒子、ベンゾグアナミン/ホルムアルデヒド縮合物粒子、ベンゾグアナミン/メラミン/ホルムアルデヒド縮合物粒子、尿素系樹脂粒子、さらにはワックス粒子などを用いることができる。
本発明においては、これらの粒子は1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。また、架橋化されたアクリルウレタン系コーティング層中の前記艶消し用粒子の含有量は、所望する表面光沢度にもよるが、固形分濃度で通常0.05〜10質量%程度、好ましくは0.1〜5質量%である。
当該塗工液は、溶剤型の場合、適当な溶媒中に、前記(A)成分のポリエステル変性アクリルポリオール樹脂、前記(B)成分の硬化剤としてのポリイソシアネート系化合物、及び必要に応じて、前記艶消し用の無機粒子や有機粒子、各種添加剤を加え、均一に溶解又は分散させることにより調製することができる。
前記溶媒としては、例えば酢酸メチル、酢酸エチル等のエステル類、ベンゼン、トルエン、キシレン等の芳香族炭化水素、アセトン、シクロヘキサノン、メチルエチルケトン等のケトン類、テトラヒドロフラン等のエーテル類など、公知の溶媒を使用することができる。また、これらの溶媒は単独で、又は2種以上混合して用いることができる。
また、各種添加剤としては例えば添加型(低分子量型)の紫外線吸収剤や酸化防止剤や帯電防止剤、レベリング剤、充填剤、着色剤、加水分解防止剤、消泡剤などを含有させることができる。
塗工に適した濃度としては、固形分濃度で、通常5〜50質量%程度、好ましくは10〜40質量%である。
このようにして得られたアクリルウレタン系コーティング層形成用塗工液を、従来公知の方法、例えばバーコート法、ナイフコート法、ロールコート法、ブレードコート法、ダイコート法、グラビアコート法などを用い、非塩化ビニル系樹脂基材の粘着剤層とは反対側の面に塗布し、30〜80℃程度の温度で30秒〜5分間程度加熱乾燥処理することにより、架橋化されたアクリルウレタン系コーティング層を形成することができる。
この架橋化されたアクリルウレタン系コーティング層の厚さに特に制限はないが、通常1〜8μm程度、好ましくは3〜6μmである。
このように粘着剤層に剥離シートを貼付する場合には、該剥離シートの剥離剤層面に粘着剤を塗布して、所定の厚さの粘着剤層を設けたのち、これを非塩化ビニル系樹脂基材の一方の面に貼付し、該粘着剤層を転写し、剥離シートはそのまま貼り付けた状態にしておいてもよい。
なお、マーキング用粘着シートの性能は、以下に示す方法に従って評価した。
(1)耐クラック性
延伸時の外観(クラック発生の有無など)を、下記の評価基準に従って評価した。
なお、延伸は、剥離シートを剥がした25mm×100mmの粘着シートの長手方向を、オリエンテック社製、「TENSILON RTA−100」を用いて行った。
評価基準
○:10%延伸時においてクラックの発生なし
△:5%延伸時においてクラックの発生なし
×:5%延伸時においてクラックの発生
(2)耐薬品擦過性
綿布に、イソプロピルアルコール(IPA)、コンパウンド入りWAX(WAX)及びケロシンをそれぞれ浸み込ませたものを用い、荷重4.9Nにてマーキング用粘着シートの架橋化されたアクリルウレタン系コーティング層表面を10往復して耐擦過試験を行い、試験前後のグロス値の変化率を求め、下記の評価基準で評価した。
○:試験前後でグロス変化率が10%未満、試験後に傷が入らない
△:試験前後でグロス変化率が10〜20%未満、試験後にわずかに傷が入る
×:試験前後でグロス変化率が20%以上、試験後に傷が入る
(3)グロス値
日本電色工業(株)製のグロスメーターを使用し、JIS K 7105に準拠して60°光沢度(グロス値)を測定した。
(4)耐薬品浸漬性
23℃、50%RH下において、剥離シートを剥がした25mm×50mmの粘着シートをメラミン樹脂塗装板に貼付し、同環境下にて24時間放置後、ガソリン中へ30分間浸漬した後の外観を目視観察し、下記の判定基準に従って評価した。
○:外観変化なし
△:僅かにくもり発生又は僅かにコーティング層の剥がれあり
×:明らかな外観異常あり
(5)耐候性
23℃、50%RH下において、剥離シートを剥がした65mm×25mmの粘着シートをメラミン塗装板に2kgローラーで1往復して貼付し、24時間放置した。
その後、サンシャインウエザオメータ[スガ試験機社製、機種名「WEL−SUN−HCH」]を用いて、1000時間の促進耐候試験を行った。
試験後の粘着シートを目視観察し、下記の判定基準に従って耐候性を評価した。
○:外観変化なし
×:白色化又はクラックの発生
(6)耐ブロッキング性
架橋化されたアクリルウレタン系コーティング層と剥離シートの裏面が接するように、210mm×297mmの粘着シートを5枚重ね合わせた。その上に1961N/m2の荷重をかけ、30℃の恒温槽中に3日間放置した。その後、粘着シートを上から順に手で剥がし、コーティング層と剥離シート裏面の界面で抵抗なく剥がれるかブロッキングを、下記の判定基準に従って評価した。
○:ブロッキングなし
×:ブロッキングあり
<重量平均分子量(Mw)>
GPC法
測定機器:「HLC−8120」東ソー社製
カラム:TSK−GelSuper HM−MX1
カラム温度:40℃
展開溶媒:THF(テトラヒドロフラン)
流速:0.6mL/min
<ガラス転移温度(Tg)>
DSC装置
測定機器:「DSC6200」Seiko Instruments社製
温度条件:−30℃〜100℃(昇温速度8℃/min)
非塩化ビニル系樹脂基材として、厚さ100μmのポリエステル系熱可塑性エラストマーフィルム[倉敷紡績社製、商品名「ES−9470BK」]を用いた。ポリエチレンラミネート紙をシリコーン系剥離剤で剥離処理した厚さ170μmの剥離シート[王子製紙社製、商品名「SP−12HLカイ」]の剥離処理面に、アクリル系粘着剤[リンテック社製、商品名「SK」、エポキシ化合物架橋剤含有]を塗布乾燥して、厚さ30μmの粘着剤層を形成した。
前記ポリエステル系熱可塑性エラストマーフィルムの一方の面に、前記粘着剤層付き剥離シートを、該粘着剤層が対面するように貼付し、該粘着剤層を転写した。
一方、酢酸エチル100質量部に対し、ポリエステル変性アクリルポリオール樹脂[亜細亜工業(株)製、商品名「EEX−19」、樹脂のTg=47℃、Mw=68,000、溶媒トルエン、25℃粘度8500mPa・s、固形分濃度54.5質量%]100質量部、及び硬化剤[亜細亜工業(株)製、商品名「#8000」、脂肪族ジイソシアネートのシアヌレート変性体、固形分濃度48.1質量%、NCO含量10.1質量%、溶媒トルエン]17質量部を加え、固形分濃度29質量%の塗工液を調製した。
次に、前記ポリエステル系熱可塑性エラストマーフィルムの粘着剤層とは、反対側の面に、前記の塗工液を、乾燥後の厚さが4μmになるようにマイヤーバーNo.12で塗布し、70℃で1分間加熱処理して、架橋化されたアクリルウレタン系コーティング層を形成することにより、マーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
実施例1において、ポリエステル変性アクリルポリオール樹脂として、[亜細亜工業(株)製、商品名「NX62−1」、樹脂のTg=47℃、Mw=38,000、溶媒トルエン、25℃粘度3000mPa・s、固形分濃度54.9質量%]100質量部を用い、かつ硬化剤「#8000」(前出)の量を15質量部に変更した以外は、実施例1と同様な操作を行い、固形分濃度29質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
実施例3
実施例2において、艶消し剤[亜細亜工業(株)製、商品名「艶消し剤M」、平均粒径3.5μmのポリカーボネート樹脂、分散媒体キシレン/シクロヘキサノン、固形分濃度7質量%]10質量部をさらに添加した以外は、実施例2と同様な操作を行い、固形分濃度28質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
実施例4
実施例3において、「艶消し剤M」(前出)の量を30質量部に変更した以外は、実施例3と同様にして固形分濃度26質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
実施例5
実施例1において、ポリエステル変性アクリルポリオール樹脂として、[亜細亜工業(株)製、商品名「NX62−2」、樹脂のTg=47℃、Mw=18,000、溶媒トルエン、25℃粘度1050mPa・s、固形分濃度55.5質量%]100質量部を用い、硬化剤「#8000」(前出)の量を15質量部に変更し、さらに艶消し剤[亜細亜工業(株)製、商品名「艶消し剤Y」、平均粒径8.3μmのポリエチレンワックス、分散媒トルエン、固形分濃度10質量%]20質量部を添加した以外は、実施例1と同様な操作を行い、固形分濃度28質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
厚さ100μmの非塩化ビニル系樹脂基材「ES−9470BK」(前出)上に、コーティング層を設けなかったこと以外は、実施例1と同様な操作を行い、マーキング用粘着シートを作製した。このマーキング用粘着シートの性能評価結果を第1表に示す。
比較例2
実施例2において、硬化剤を用いなかったこと以外は、実施例2と同様な操作を行い、固形分濃度27質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
比較例3
実施例1において、ポリエステル変性アクリルポリオール樹脂として、[亜細亜工業(株)製、商品名「HX86−66」、樹脂のTg=46℃、Mw=10,000、溶媒酢酸ブチル、25℃粘度450mPa・s、固形分濃度47.9質量%]100質量部を用い、硬化剤「#8000」(前出)の量を44質量部に変更した以外は、実施例1と同様な操作を行い、固形分濃度28質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
比較例4
比較例3において、ポリエステル変性アクリルポリオール樹脂として、[亜細亜工業(株)製、商品名「KX43−30」、樹脂のTg=40℃、Mw=10,000、溶媒イプゾール150/PMA、25℃粘度780mPa・s、固形分濃度50.5質量%]100質量部を用いた以外は、比較例3と同様な操作を行い、固形分濃度29質量%の塗工液を調製し、さらにマーキング用粘着シートを作製した。
このマーキング用粘着シートの性能評価結果を第1表に示す。
Claims (6)
- 非塩化ビニル系樹脂基材の一方の面に粘着剤層を有すると共に、他方の面に、(A)重量平均分子量が15,000〜80,000のポリエステル変性アクリルポリオール樹脂と、(B)硬化剤としてポリイソシアネート系化合物を含む、架橋化されたアクリルウレタン系コーティング層を有することを特徴とするマーキング用粘着シート。
- (A)成分のポリエステル変性アクリルポリオール樹脂のガラス転移温度が42〜60℃である請求項1に記載のマーキング用粘着シート。
- 架橋化されたアクリルウレタン系コーティング層が、平均粒径1〜5μmの無機粒子及び/又は有機粒子を含む請求項1又は2に記載のマーキング用粘着シート。
- (B)成分のポリイソシアネート系化合物が、脂肪族、脂環式、芳香族及び芳香脂肪族イソシアネート、並びにこれらのアダクト変性体、ビュレット変性体、イソシアヌレート変性体、ウレトンイミン変性体、ウレトジオン変性体、カルボジイミド変性体及び弾性変性ポリイソシアネートの中から選ばれる少なくとも1種である請求項1〜3のいずれかに記載のマーキング用粘着シート。
- (B)成分のイソシアネート基と(A)成分の水酸基とのモル比[NCO]/[OH]が0.5〜1.5である請求項1〜4のいずれかに記載のマーキング用粘着シート。
- 架橋化されたアクリルウレタン系コーティング層の厚さが、1〜8μmである請求項1〜5のいずれかに記載のマーキング用粘着シート。