JP2007128660A - リチウム二次電池用正極板の製造方法およびこの製造方法による正極を用いたリチウム二次電池 - Google Patents
リチウム二次電池用正極板の製造方法およびこの製造方法による正極を用いたリチウム二次電池 Download PDFInfo
- Publication number
- JP2007128660A JP2007128660A JP2005317934A JP2005317934A JP2007128660A JP 2007128660 A JP2007128660 A JP 2007128660A JP 2005317934 A JP2005317934 A JP 2005317934A JP 2005317934 A JP2005317934 A JP 2005317934A JP 2007128660 A JP2007128660 A JP 2007128660A
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- electrode plate
- binder
- secondary battery
- lithium secondary
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】リチウム二次電池用正極板正極板の製造方法として、結着剤は結着剤Aと結着剤Bからなり、結着剤Aは200〜400℃で接着力が低下する結着剤であり、結着剤Bは200〜400℃で接着力が低下しない結着剤であり、熱処理温度は200℃〜400℃の温度で行う。
【選択図】図1
Description
ニッケル複合酸化物、前記結着剤、および前記カルボキシメチルセルロースとを前記分散媒に混練分散して正極板用ペーストを作製する工程と、前記正極板用ペーストを前記集電体に塗着し正極板前駆体にする工程と、前記正極板前駆体を熱処理する工程と、前記正極板前駆体を熱処理した後、圧延する工程とからなるリチウム二次電池用正極板の製造方法であって、前記結着剤は結着剤Aと結着剤Bからなり、前記結着剤Aは200〜400℃で接着力が低下する結着剤であり、前記結着剤Bは200〜400℃で接着力が低下しない結着剤であり、前記熱処理の温度は200〜400℃であるリチウム二次電池用正極板の製造方法である。
正極活物質としてリチウム含有ニッケル複合酸化物、結着剤、および増粘剤としてカルボキシメチルセルロースとを分散媒に混練分散させた正極板用ペーストを、集電体に塗着、熱処理、圧延してなるリチウム二次電池用正極板の製造方法において、
前記リチウム含有ニッケル複合酸化物、前記結着剤、および前記カルボキシメチルセルロース(以下、CMCと略す)とを前記分散媒に混練分散して正極板用ペーストを作製する工程と、前記正極板用ペーストを前記集電体に塗着し正極板前駆体にする工程と、前記正極板前駆体を熱処理する工程と、前記正極板前駆体を熱処理した後、圧延する工程とからなるリチウム二次電池用正極板の製造方法であって、前記結着剤は結着剤Aと結着剤Bからなり、前記結着剤Aは200〜400℃で接着力が低下する結着剤であり、前記結着剤Bは200〜400℃で接着力が低下しない結着剤であり、前記熱処理の温度は200〜400℃である。
、およびフロロアコキシ(以下、PFAと略す)が好ましい。
されている。このような極板群は有底電池ケース8に挿入されている。有底電地ケース8に挿入した極板群には非水電解液が注入されている。正極板5に正極リード3を溶接により接続され、負極板6に負極リード9を溶接により接続されている。極板群の上端部には上部絶縁板4が配置され、極板群の下端部には下部絶縁板10が配置されている。有底電池ケース8の開口部と封口板1は、絶縁ガスケット2を介してかしめにより封口されている。このようにして直径17mm、高さ50mmの円筒形リチウム二次電池を作製する。正極板5は集電体としてAl箔の両面に形成したものである。セパレータ7はポリプロピレン(以下、PPと略す)製微多孔質フィルムである。有底電池ケース8は、耐有機電解液性のステンレス鋼板を深絞り成形することにより得られたものである。
以下に、正極板の詳細な製造方法について述べる。
正極活物質としてリチウム含有ニッケル複合酸化物のLiNixMnyCo(1-x-y)O2粉末(X=Y=0.33)を50重量部、導電剤としてアセチレンブラックを1.5重量部、CMC1重量部を水99重量部に溶解した水溶液43.5重量部、結着剤Aとしてアクリル系ゴム質共重合体50重量部が溶解した水溶液1.5重量部、および結着剤BとしてPTFE50重量部が水に分散したもの1.5重量部とを配合した。これらを混合分散することにより正極用ペーストを得た。次に、この正極用ペーストを集電体として厚み20μmのAl箔にダイコーターを用いて0.22mmの厚みになるように塗工し、乾燥した。その後、結着剤Aのアクリル系ゴム質共重合体分解させガス化させるために300℃で10分間熱処理を行った。この後、ロールプレス機により厚みが0.17mmになるまで圧延した。所定の寸法に切断して正極板5を得た。この正極板を用いて作製した円筒形リチウム二次電池を作製した。
実施例1の熱処理温度を200℃とした以外は実施例1と同じ電池を作製した。
実施例1の熱処理温度を400℃とした以外は実施例1と同じ電池を作製した。
実施例1の結着剤Aとしてアクリル系ゴム質共重合体50重量部を溶解した水溶液2.5重量部に、結着剤BとしてPTFE50重量部を水に分散させたもの0.5重量部にした以外は実施例1と同じ電池を作製した。
実施例1の結着剤Aとしてアクリル系ゴム質共重合体50重量部を溶解した水溶液0.5重量部に、結着剤BとしてPTFE50重量部を水に分散させたもの2.5重量部にした以外は実施例1と同じ電池を作製した。
実施例1の正極の作製において、結着剤Aとしてアクリル系ゴム質共重合体50重量部を溶解した水溶液を1.5重量部に、およびFEP50重量部を水に分散させたもの溶液を1.5重量部にした以外は実施例1と同じ電池を作製した。
実施例1の正極の作製において、結着剤Aとしてアクリル系ゴム質共重合体50重量部を溶解した水溶液を1.5重量部におよび、PFA50重量部を水に分散させたもの水溶液を1.5重量部にした以外は実施例1と同じ電池を作製した。
実施例1の結着剤Aとしてゴム系樹脂50重量部を溶解した水溶液1.5重量部にした以外は実施例1と同じ電池を作製した。
実施例1の結着剤Bとしてシリコン系樹脂50重量部を水に分散させたもの1.5重量部にした以外は実施例1と同じ電池を作製した。
実施例1の結着剤Aとしてアクリル系ゴム質共重合体50重量部を溶解した水溶液2.7重量部に、結着剤BとしてPTFE50重量部を水に分散させたもの0.3重量部にした以外は実施例1と同じ電池を作製した。
実施例1の結着剤Aとしてアクリル系ゴム質共重合体50重量部を溶解した水溶液0.3重量部に、結着剤BとしてPTFE50重量部を水に分散させたもの2.7重量部にした以外は実施例1と同じ電池を作製した。
実施例1の熱処理温度を180℃とした以外は実施例1と同じ電池を作製した。
実施例1の熱処理温度を450℃とした以外は実施例1と同じ電池を作製した。
結着剤としてアクリル系ゴム質共重合体50重量部を溶解した水溶液3.0重量部のみにした以外は実施例1と同じ電池を作製した。
結着剤としてフッ素系樹脂50重量部を水に分散させたもの3.0重量部のみにした以外は実施例1と同じ電池を作製した。
クラック率は0%が望ましいが、正極板と負極板とをセパレータ7を介して渦巻き状に捲回して極板群を作製する場合において、クラック率が20%までなら極板群を作製することができる。しかし、クラック率が20%より大きくなると、正極板が切れ易くなり極板群が作製できなくなり、極板群の生産性が低下する。このことから、クラック率の閾値として20%までが良好な範囲とする。
また、実施例1のように熱処理温度300℃だけでなく、実施例2および3のように熱処理温度200および400℃にしても、アクリル系ゴム質共重合体がガス化は進行し、接着力が低下するため、柔軟性の低下が防がれることにより、クラックは発生していない(実施例1〜3)。
らなかった。これは、400℃より高くすると、アクリル系ゴム質共重合体のほとんどがガス化することにより、密着強度が極端に弱くなったものと考えられる。
2 絶縁ガスケット
3 正極リード
4 上部絶縁板
5 正極板
6 負極板
7 セパレータ
8 有底電池ケース
9 負極リード
10 下部絶縁
Claims (3)
- 正極活物質としてリチウム含有ニッケル複合酸化物、結着剤、および増粘剤としてカルボキシメチルセルロースとを分散媒に混練分散させた正極板用ペーストを、集電体に塗着、熱処理、圧延してなるリチウム二次電池用正極板の製造方法において、前記リチウム含有ニッケル複合酸化物、前記結着剤、および前記カルボキシメチルセルロースとを前記分散媒に混練分散して正極板用ペーストを作製する工程と、前記正極板用ペーストを前記集電体に塗着し正極板前駆体にする工程と、前記正極板前駆体を熱処理する工程と、前記正極板前駆体を熱処理した後、圧延する工程とからなるリチウム二次電池用正極板の製造方法であって、前記結着剤は結着剤Aと結着剤Bからなり、前記結着剤Aは200〜400℃で接着力が低下する結着剤であり、前記結着剤Bは200〜400℃で接着力が低下しない結着剤であり、前記熱処理の温度は200〜400℃であるリチウム二次電池用正極板の製造方法。
- 前記結着剤Aはアクリル系ゴム質共重合体であり、前記結着剤Bはフッ素系樹脂である請求項1に記載のリチウム二次電池用正極板の製造方法。
- 請求項1および2に記載の製法方法による正極、炭素材料を活物質とする負極、セパレータおよびリチウム塩を有機溶媒に溶解した非水電解液とを備えたリチウム二次電池。