JP2007015918A - 結晶中の欠陥濃度低減方法 - Google Patents
結晶中の欠陥濃度低減方法 Download PDFInfo
- Publication number
- JP2007015918A JP2007015918A JP2006204610A JP2006204610A JP2007015918A JP 2007015918 A JP2007015918 A JP 2007015918A JP 2006204610 A JP2006204610 A JP 2006204610A JP 2006204610 A JP2006204610 A JP 2006204610A JP 2007015918 A JP2007015918 A JP 2007015918A
- Authority
- JP
- Japan
- Prior art keywords
- crystal
- lead
- cadmium
- indium
- sic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】非ダイヤモンド結晶から高圧高温(HP/HT)で欠陥又は歪みを除去する方法及び改良結晶を用いた電子装置を提供する。
【解決手段】1以上の欠陥を含む結晶及び反応条件下で超臨界流体となる適当な圧力媒体を用意し、結晶及び圧力媒体を高圧セル内に入れ、高圧セルを高圧装置内に置き、単結晶中の欠陥又は歪みを除去するのに十分な高い圧力及び温度の反応条件下で十分な長さの時間処理する。改良結晶上に、例えばエピタキシャル半導体層の設層、パターン形成及び金属化を行い電子装置を形成する。
【選択図】図1
【解決手段】1以上の欠陥を含む結晶及び反応条件下で超臨界流体となる適当な圧力媒体を用意し、結晶及び圧力媒体を高圧セル内に入れ、高圧セルを高圧装置内に置き、単結晶中の欠陥又は歪みを除去するのに十分な高い圧力及び温度の反応条件下で十分な長さの時間処理する。改良結晶上に、例えばエピタキシャル半導体層の設層、パターン形成及び金属化を行い電子装置を形成する。
【選択図】図1
Description
本発明は、一般に結晶に関し、特に高圧/高温(HP/HT)アニール法により結晶中のボイド、マイクロパイプ、ナノパイプ、転位、格子間欠陥、空孔及び歪み欠陥を修復する方法に関する。
単結晶は、電子装置、光電子装置、レーザー、光学系など種々広範な用途に有用である。これらの用途における結晶性能は、結晶の材料品質、特に欠陥濃度により制約されることが多い。このような欠陥としては、空隙、マイクロパイプ、ナノパイプ、転位、格子間欠陥、空孔などが重要である。欠陥はまた結晶中に歪みをもたらし、歪みは、これらの結晶からスライスしたウェーハ上に成長させたエピタキシャル層や電子装置の品質、性能及び寿命を劣化させる傾向がある。結晶成長中にこれらの欠陥をなくす又は低減するのは非常に難しいので、別の手段が有用となる。欠陥は、ガラス、プラスチック、金属などの非晶質材料にも存在し、その光学的、機械的、電気的もしくは視覚的特性を損なうおそれがある。
炭化ケイ素(SiC)の場合、電子装置用途の大面積単結晶ウェーハは幾つかのポリタイプのもの(6H、4H、15R)が市販されている。しかし、これらのウェーハは通常104〜106cm-2の濃度の転位及び10〜100cm-2の密度のマイクロパイプを含んでいる。欠陥濃度は、高周波装置用途に適当な半絶縁性SiCの方がn型SiCよりも高くなる傾向がある。マイクロパイプも転位も装置故障や劣化現象と深く関係している。炭化ケイ素系の装置が小さなすき間市場から大規模な高電力用途に浮上できなかった一つの理由は、基板欠陥に起因する装置の信頼性のなさにある。米国特許出願公開第2002−0059901号には、マイクロパイプ密度10cm-2未満のSiC結晶の成長方法が開示されている。しかし、本出願人が知る限りでは、マイクロパイプ密度1cm-2未満のSiC結晶或いはマイクロパイプを全く含まない直径25mm以上、50mm以上、75mm以上、さらには100mm以上のSiC結晶の成長方法は現在のところ得られていない。
従来から、SiC中のマイクロパイプを塞いだり、表面近傍のマイクロパイプを充填する方法を開示した文献が幾つか知られている。例えば、米国特許第5679153号には、ウェーハ中に存在するマイクロパイプを塞ぐ液相エピタキシ法が開示されている。米国特許第6214108号及び同第6217842号及び米国特許出願公開第2002−0069818号には、マイクロパイプ含有SiCウェーハ上に皮膜を設け、熱処理を行い、マイクロパイプの75μm前後を閉塞する方法が開示されている。しかし、これらの方法では、費用のかかる処理を個々のSiCウェーハ毎に1回ずつ行わなくてはならない。さらに、これらの方法では、全体にわたってマイクロパイプやマイクロボイドを含まない直径25mm以上、50mm以上、75mm以上、さらには100mm以上のSiC結晶を得ることができない。
窒化ガリウムの場合、基板は通常非GaN基板、例えばサファイア又は炭化ケイ素上にヘテロエピタキシにより製造されているので、基板の品質が低いのが現状である。格子膨張及び熱膨張の不一致のため、こうして形成されたGaNは、糸状につながった転位を約5×105〜1010cm-2の濃度で含有する。またGaNは、Ga及びN両位置の自然欠陥、例えば高い空孔濃度で成長する傾向がある。GaNを単に高温でアニールしようとしても、約750℃を超える温度でGa+N2に分解するので、不可能である。
ヒ化ガリウム及びリン化インジウムウェーハ基板の品質は、SiCやGaNよりもはるかに高品質であるが、それでも欠陥(転位、空孔)の濃度はその上に作成した電子装置の性能に悪影響を与えるのに十分な程高い。成長技術は十分に成熟しているので、少しずつでも有意な改良はありそうもない。単に高温でアニールしようとしても、ヒ素又はリンが揮発し、空孔を形成したり、さらにはGa又はInの液滴を形成したりするので、採用できない。
Banholzerらの国際公開第02/13958号には、高温高圧でのアニールによって、合成ダイヤモンドの靱性を高める方法が開示されている。空隙、マイクロもしくはナノパイプ、転位、空孔の濃度低下について具体的な教示はない。Anthonyらの国際公開第02/13958号及びVagaraliらの米国特許出願公開第2001−0031237号には、高温高圧でのアニールによって、天然ダイヤモンドの色を変えることが開示されている。これらの処理は、点欠陥(空孔、格子間欠陥、置換不純物)の性質、濃度及び分布を変更するが、空隙、マイクロもしくはナノパイプ又は転位の濃度の低下については何ら教示されていない。Webbら、J.Mater.Res.,Vol10,No.7,p1700(1996)には、合成I型ダイヤモンド結晶を1200〜1700℃、50〜60kbarでアニールし、アグリゲート−窒素解離及び金属凝集を起こすとともに、ダイヤモンド格子転位を修復することが提案されている。
ガス圧力装置内で結晶をアニールすることを開示した文献が幾つかある。米国特許第6329215号には、GaN、AlN及びInNを圧力媒体として窒素の0.1〜2GPaの高圧力下でアニールすることが記載されているが、特殊な危険なガス圧力装置を使用しなければならない。ここで高い窒素圧力を使用するのは、高温での分解を防止するためであって、欠陥の除去を目的としたものではない。Porowskiらが教示するアニール条件は、点欠陥をアニールし、原子拡散を起こすには十分であるが、糸状につながった転位、マイクロもしくはナノパイプ又は空隙の減少は示されていない。米国特許第6447600号には、Si、GaAs、InP、ZnS及びZnSeを不活性ガス中0.3GPa以下の圧力でアニールする方法が開示されている。しかし、糸状につながった転位、マイクロもしくはナノパイプ又は空隙の減少は示されおらず、Si中の空孔が集まって空隙となる可能性がある。特開平10−114533号及び特開平02−124729号公報には、ガラスをガス圧力装置内で0.2GPa以下の圧力でアニールすることが開示されている。
米国特許出願公開第2002−0059901号明細書
米国特許第5679153号明細書
米国特許第6214108号明細書
米国特許第6217842号明細書
米国特許出願公開第2002−0069818号明細書
国際公開第02/13958号パンフレット
国際公開第02/13958号パンフレット
米国特許出願公開第2001−0031237号明細書
米国特許第6329215号明細書
米国特許第6447600号明細書
特開平10−114533号公報
特開平02−124729号公報
Webb et al., J. Mater.Res., Vol10, No.7, p.1700 (1996)
このような事情で、当技術分野では、SiC、GaNなどの結晶中の欠陥を修復してその上に作成する電子及び光電子装置の性能を改良することが必要とされている。そうすれば、非線形光学用途用の結晶の場合、望ましくない光散乱が減少し、レーザーダメージ閾値が上昇する。圧電及びリラクサー強誘電結晶の場合、アニールによって降伏電界、効率及び寿命が増加する。同様に、非晶質ガラス、プラスチックス及び金属中の欠陥を修復する必要も存在する。
本発明による結晶中の欠陥濃度を低減する方法は、(i)1以上の欠陥含有結晶を用意し、(ii)反応条件下で超臨界流体となる適当な圧力媒体を用意し、(iii)前記結晶及び圧力媒体を高圧セル内に入れ、(iv)セルを高圧装置に入れ、(v)セルを高圧高温で処理し、(vi)前記結晶をセルから取り出す工程を含む。欠陥は高圧高温で圧潰及び/又はアニール消失し、歪みは除去される。
本発明はさらに、この改良結晶上に、例えばエピタキシャル半導体層の設層、パターン形成及び金属化により形成した電子装置に関する。
本発明において、結晶中の欠陥は高圧高温で圧潰及び/又はアニール消失し、歪みは除去される。本発明にしたがって処理するのに適当な結晶には、例えば単結晶、単結晶の集合体(アグリゲート)、ブール結晶、電子ウェーハ、窓、レーザーロッド、センサなどがある。
本発明の方法の要素及び変数には、結晶、圧力媒体、高圧装置、並びに圧力、温度及び時間などのアニールプロセス変数がある。本発明の方法の一実施形態では、新たな欠陥の形成を最小限に抑えるように冷却及び圧力解除の条件を制御するのが望ましい。
本発明の一実施形態では、非ダイヤモンド結晶は、(a)直接遷移型半導体材料、(b)ワイドギャップ半導体材料、(c)シンチレータ材料、(d)非線形光学材料、(e)レーザー材料、(f)リラクサー強誘電性材料、(g)圧電材料及び(h)間接遷移型半導体材料の1種以上である。本発明の非ダイヤモンド結晶の例としては、6H−SiC、4H−SiC、15R−SiC、3C−SiC、8H−SiC、2H−SiC、ケイ素(Si)、ゲルマニウム(Ge)、立方晶窒化ホウ素(cBN)、窒化ガリウム(GaN)、ガリウムアンチモン(GaSb)、窒化アルミニウム(AlN)、アルミニウムガリウムインジウム窒素(AlInGaN)、ビスマスアンチモン(BixSb1-x)、窒化インジウム(InN)、ガリウムヒ素(GaAs)、リン化ガリウム(GaP)、ガリウムインジウムリン(GaInP)、アルミニウムインジウムリン(AlInP)、インジウムアルミニウムヒ素(InAlAs)、アルミニウムガリウムアンチモン(AlGaSb)、インジウムアルミニウムガリウムヒ素(InAlGaAs)、アルミニウムインジウムガリウムリン(AlInGaP)、アルミニウムガリウムヒ素(AlGaAs)、インジウムガリウムヒ素リン(InGaAsP)、ガリウムセレン(GaSe)、リン化インジウム(InP)、インジウムセレン(InSe及びInSe2)、インジウムアンチモン(InSb)、リン化カドミウム(Cd3P2)、カドミウムインジウム硫黄(CdIn2S4)、カドミウムケイ素ヒ素(CdSiAs2)、カドミウム錫リン(CdSnP2)、酸化亜鉛(ZnO)、亜鉛セレン(ZnSe)、亜鉛テルル(ZnTe)、硫化カドミウム(CdS)、カドミウム亜鉛セレン(CdZnSe)、ベリリウム亜鉛カドミウムセレン(BeZnCdSe)、亜鉛カドミウムマグネシウムセレン(ZnCdMgSe)、亜鉛硫黄セレン(ZnSSe)、ベリリウム亜鉛セレン(BeZnSe)、ベリリウムマグネシウム亜鉛セレン(BeMgZnSe)、カドミウムテルル(CdTe)、カドミウム亜鉛テルル(CdxZn1-xTe)、水銀カドミウムテルル(HgCdTe)、硫化鉛(PbS)、鉛テルル(PbTe)、鉛セレン(PbSe)、鉛錫テルル(PbSnTe)、鉛ゲルマニウムテルル(PbGeTe)、鉛ユーロピウムテルル(PbEuTe)、鉛ユーロピウムセレン(PbEuSe)、鉛カドミウム硫黄(PbCdS)、鉛ユーロピウムセレンテルル(PbEuSeTe)、鉛硫黄セレン(PbSSe)、三ホウ酸リチウム(LiB3O5又はLBO)、オルトバナジウム酸イットリウム(YVO4)、リン酸カリウムチタニル(KTiOPO4又はKTP)、ニオブ酸カリウム(KNbO3又はKN)、ホウ酸セシウムリチウム(CsLiB6O10又はCLBO)、LiCaAlF6(LiCAF)、LiSrAlF6(LiSAF)、ジルコンチタン酸鉛(Pb(ZrxTi1-x)O3又はPZT)、マグネシウムニオブ酸鉛(Pb(Mg1/3Nb2/3)O3又はPMN)、ジルコンニオブ酸鉛(Pb(Zr1/3Nb2/3)O3又はPZN)、ビスマスケイ素酸素(BSO)、チタン酸バリウム(BTO)、鉛マグネシウムニオブチタン(Pb(Mgx/3Nb2x/3Ti1-x)O3又はPMNT)、鉛ジルコンニオブチタン(Pb(Zrx/3Nb2x/3Ti1-x)O3又はPZNT)、ハフニウム酸ストロンチウム(SrHfO3)、ハフニウム酸バリウム(BaHfO3)、シリカ、シリケート及びフルオロジルコネートをマトリックスとする希土類ランタニドイオンレーザー結晶、KCl、RbCl、NaCl、CuCl、CsI、CaF2、ZnF2、MgF2、SrF2、MnF2、ZnS、ZnSe、CaF2−ErF3、KI、RbCaF3、LiNbO3、KMgF3、Ca2PO4Cl、CaGd2(SiO4)3O、LaCl3、LiYF4、LaF3、Y3Al5O12、LiYF4、LuAlO3、YAlO3、Gd3Ga5O12、CaF2−ErF3、Er3Al5O12、Lu3Al5O12、BaYb2F8、NaF、LiF、サファイア、アレクサンドライト、フォルステライト、LiYF4、BaF2、BaY2F8、BaEr2F8、RbBr、Li2GeO3、Y2O3、Er2O3、YVO4、GdAlO3、Y3Sc2Ga3O12、NaCaErF6、CaWO4又はCaMoO4をマトリックスとするレーザー結晶、その他の同様の化合物がある。
本発明の一実施形態では、結晶は寸法約0.1〜500mmのブールである。第3の実施形態では、ブールの形態の結晶は最大寸法/最小寸法比約10未満であり、したがって結晶は過度に破損しやすいことはない。
本発明の非ダイヤモンド結晶中の欠陥を除去する方法の一実施形態では、圧力媒体は、圧力を結晶の周囲にほぼ均一に分布させることができ、したがって非静水圧応力を最小限に抑えることができるものである。本発明の一実施形態では、圧力媒体は、加工条件下で液体、超臨界流体又は低剪断強さ固体とすることができ、その内部摩擦0.2未満である。本発明の別の実施形態では、圧力媒体は、室温又はドライアイス温度(−77℃)で液体又は固体である。こうすれば、高圧セルの適切かつ安全な充填及び取り扱いが可能となり、また特殊なガス圧力装置の必要がなくなるからである。圧力伝達媒体が固体である場合、セルに過剰な空隙率を導入するのを避けるため、材料をその理論密度の約85%超まで圧縮してから、そのコンパクトをセルに入れるのが望ましい。
圧力媒体は加工温度及び圧力で安定でなければならない。即ち、圧力媒体は、セルの結晶や他の成分を分解したりそれと反応したりしないのが好ましい。固体圧力媒体組成物の例には、NaCl、NaBr、AgCl、AgBr、CaF2、SrF2などの金属ハロゲン化物がある。塩化ナトリウムは、融点付近の温度で特に効果的に作用し、その融点は、約1〜約2GPaの圧力で、約1000〜約1150℃である。別の実施形態では、圧力媒体が黒鉛又は六方晶窒化ホウ素である。さらに他の実施形態では、圧力媒体が、窒素含有流体、例えばアンモニア、ヒドラジン、メチルアミン又はメラミンである。或いはまた、圧力伝達媒体は、タルク、パイロフィライト、二硫化モリブデン、炭酸カルシウム、酸化マグネシウム、酸化ジルコニウム、メリリナイトクレー、ベントナイトクレー又はケイ酸ナトリウムの1種以上を含有することができる。別の実施形態では、圧力媒体が加工条件下で溶融ガラスである。一実施形態では、ガラスはLi2O、Na2O、K2O、MgO、CaO、SrO、BaO、B2O3、Al2O3、Ga2O3、In2O3、SiO2、GeO2、SnOx、PbOx、リン酸塩ガラス、フッ化物ガラス、窒化物ガラス、及びこれらの配合物又は混合物の1種以上を含有する。
本発明の一実施形態では、圧力媒体はアルゴン、ヘリウム、キセノン又は窒素のような不活性ガスの1種以上を含有し、これは1GPa未満の加工圧力条件と組み合わせて用いるのに適当で、したがって市販のオートクレーブや内部加熱圧力容器を使用できる。
別の実施形態では、ガスと結晶とが直接接触するのを防止するために、不活性ガス圧力媒体を、結晶を密に包囲する第2の溶融圧力媒体と組み合わせて使用する。例えば、アニール処理中に結晶中のマイクロパイプにガスが充満するのを許さないのが望ましい。第2の圧力媒体は、固体又は粉末形態のガラスとして供給し、加工中の圧力付与以前に溶融することができる。一実施形態では、かかるガラスはB2O3、SiO2、Na2O、CaO、MgO、Al2O3又はこれらの混合物又は配合物の1種以上を含有する。
実施形態によっては、アニールすべき結晶が、適切なアニールが生起するのに十分な高い温度で分解する傾向をもつ。例えば、GaNは約750℃を超える温度でGa+N2に分解し始め、またGaAs上のヒ素の蒸気圧は融点で数気圧である。この場合、圧力媒体は分解を抑制する成分を含有する必要がある。例えば、GaNの分解は、N2、アンモニアもしくは窒素活性が平衡時の値よりも高い窒素含有流体中でアニールすることによって防止できる。GaAsの分解は、圧力媒体として純ヒ素を用いるか、或いはヒ素を前述の他の圧力媒体材料と混合することによって防止できる。
結晶及び圧力媒体を、内部加熱能を有する適当な高圧装置に入れる。圧力媒体の少なくとも1成分がガスであり、加工圧力が約1GPa未満の一実施形態では、高温静水圧圧縮(HIP)又は内部加熱圧力容器を使用する。これよりも高い圧力では、ピストンシリンダプレス、ベルトプレス、多重アンビル型プレス又はトロイドプレスを使用すればよい。このようなプレスは当技術分野で周知である。さらに他の実施形態では、M.P.D’Evelynらの米国特許出願第09/683587号(2002年1月31日出願)「改良圧力容器」に記載されているようなゼロストローク装置を使用してもよい。
一実施形態では、結晶及び圧力媒体を、M.P.D’Evelynらの米国特許出願第09/683659号(2002年1月31日出願)に記載されているような封止変形可能なカプセルに入れる。この実施形態は、プロセス圧力が約0.2〜0.5GPaより高く、圧力媒体が室温でガス又は液体であるか、加工条件下でガス又は超臨界流体である場合に特に有用である。
一実施形態では、圧力容器に入れた後、圧力及び温度を所望の値に上げ、十分な長さの時間保持し、次いで温度及び圧力を制御された速度で下げ、セルを高圧装置から取りだし、アニールした結晶をセルから回収する。改良された結晶上にエピタキシャル構造を形成することができる。また改良された結晶上には、例えばエピタキシャル半導体層の設層、パターン形成及び金属化により半導体装置を形成することができる。半導体装置は、発光ダイオード(LED)、レーザーダイオード、光検出器、フィルター、トランジスタ、整流器、サイリスタ、光増幅器、エミッタ、検出器、ダイオード、スイッチ、太陽電池又は光双安定性装置とすることができる。
別の実施形態では、高圧高温でアニールすべき材料が結晶質でなく、非晶質である。結晶について上述した方法と同様の方法を使用でき、アニールをガラス転移温度より上で行っても、下で行ってもよいという特徴が加わる。アニール処理後のセルの冷却を注意深く行って、材料への新たな欠陥の導入を回避するべきである。
マイクロボイド及びナノパイプを圧潰するのに必要な圧力
結晶が炭化ケイ素である一実施形態では、ベーサル面(底面)に沿ったクリープが800℃を超える温度で顕著になり、1600℃を超える温度でc軸に平行なクリープが観察されるようになる。その活性化エネルギーはそれぞれ2.7eV及び1.9eVである。(0001)に垂直又は平衡なクリープについての応力指数はそれぞれ3.3及び4.9であり、クリープが5GPaでは100kPa(ほぼ周囲条件)の場合よりも3×1015〜1023倍速いことを示している。したがって、高い静水圧下1000〜2000℃の温度でアニールすることによりマイクロもしくはナノパイプをなくすことができる。理論に縛られるものではないが、マイクロボイドもしくはナノパイプの圧潰の最も単純な機構は、欠陥のまわりの材料の塑性降伏であると考えられる。外部圧力Pextの存在下、半径A、内部圧力Piのマイクロボイドのまわりの応力σv(R) は下記に等しい(T.R. Anthony, Diamond & Related Materials, 8, 78−88 (1999))。
結晶が炭化ケイ素である一実施形態では、ベーサル面(底面)に沿ったクリープが800℃を超える温度で顕著になり、1600℃を超える温度でc軸に平行なクリープが観察されるようになる。その活性化エネルギーはそれぞれ2.7eV及び1.9eVである。(0001)に垂直又は平衡なクリープについての応力指数はそれぞれ3.3及び4.9であり、クリープが5GPaでは100kPa(ほぼ周囲条件)の場合よりも3×1015〜1023倍速いことを示している。したがって、高い静水圧下1000〜2000℃の温度でアニールすることによりマイクロもしくはナノパイプをなくすことができる。理論に縛られるものではないが、マイクロボイドもしくはナノパイプの圧潰の最も単純な機構は、欠陥のまわりの材料の塑性降伏であると考えられる。外部圧力Pextの存在下、半径A、内部圧力Piのマイクロボイドのまわりの応力σv(R) は下記に等しい(T.R. Anthony, Diamond & Related Materials, 8, 78−88 (1999))。
σv (R)≒(Pext-Pi)(A/R)3 (1)
ここで、Rはマイクロボイドの中心からの半径方向距離である。
ここで、Rはマイクロボイドの中心からの半径方向距離である。
同様に、マイクロパイプの2Dの場合、応力σp(R)は次式で与えられる。
σp(R)≒(Pext-Pi)(A/R)2 (2)
ここで、Rはパイプの中心からの半径方向距離である。
ここで、Rはパイプの中心からの半径方向距離である。
このような欠陥を圧潰するには、塑性降伏が欠陥からおおよそ距離R=5Åまで起こらなければならない。材料の降伏強さをYで表すと(塑性流れ又はクリープいずれでも)、マイクロボイドを圧潰するのに必要な外部圧力は次式となる。
Pext=Pi+125Y マイクロボイド (3)
同様に、マイクロパイプについても、パイプを圧潰するのに必要な圧力は次式で与えられる。
同様に、マイクロパイプについても、パイプを圧潰するのに必要な圧力は次式で与えられる。
Pext=Pi+25Y マイクロパイプ (4)
マイクロパイプはマイクロボイドよりも先に圧潰し、両欠陥は、圧潰するのに材料の降伏強さよりも高い圧力を必要とする。HPは大きなPextを意味し、HTは低い降伏応力Yを意味するので、HP/HT条件はこれらの欠陥を圧潰するのに適切である。
マイクロパイプはマイクロボイドよりも先に圧潰し、両欠陥は、圧潰するのに材料の降伏強さよりも高い圧力を必要とする。HPは大きなPextを意味し、HTは低い降伏応力Yを意味するので、HP/HT条件はこれらの欠陥を圧潰するのに適切である。
欠陥の内側になんらかの内部圧力があると、欠陥が圧潰するにつれてこの内部圧力が上昇してPiA2(パイプ)又はPiA3(ボイド)を一定に保ち、これは内部圧力がそれ以上の圧潰を許さなくなるまで続く。その結果、内部圧力Piがゼロでなければ、或いは欠陥内のガスがマトリックスに溶解性でなければ、欠陥の完全な圧潰は不可能である。また、サンプルを減圧する際に外部圧力が解除されるとき、もしもこの内部圧力が欠陥のまわりに発生する応力が、周囲のマトリックスの塑性降伏を引き起こすのに十分に高いと、高圧ガスを含有する欠陥の膨張が起こりうる。その結果、このような欠陥が表面に連通していないならば、本発明の目的には、欠陥を含む元の結晶を真空下で成長させるのが好ましい。SiCについての実施例では、マイクロパイプが表面に連通しているので、マイクロパイプが圧潰する際に、マイクロパイプ内の内部圧力が上昇することはない。
本発明にしたがって処理された結晶は、半導体装置に用いるエピタキシャル構造の成長に使用できる。このような結晶からスライスされ研磨されたウェーハ及び/又は装置の具体例を以下に示す。これらの装置は欠陥濃度の低減と歪みの緩和から優れた特性を有する。例えばSiC、GaN、GaAs、InP及びZnOなどの電子材料の場合、本発明の方法にしたがって加工されたブールから切り出されたウェーハ上に作成される電子装置では、破壊電界の上昇、漏れ電流の減少、熱伝導度の上昇、発光効率の上昇、信頼性の増加が見られる。本発明の結晶上に形成することのできる装置はどのような装置構造でもとることができ、例えば発光ダイオード(LED)、検出器、フィルター、トランジスタ、整流回路、光増幅器、エミッタ、ダイオード、太陽電池、光双安定性装置、レーザーなどの装置があるが、これらに限定されない。
本発明の一実施形態では、結晶をUVLEDに使用する。UVLEDは、材料品質の上昇につれて向上することが知られている。高い材料品質、例えば転位密度が低く、マイクロボイドやナノボイドを含まないといった品質は、現在GaN分野で開発、商品化されている、レーザー、UVLED、AlGaN/GaN高電子移動度トランジスタ(HEMT)などの多くの装置にとって格別に重要である。このような高品質は、開発中の現行装置構造にとって重要なだけでなく、他の装置構造(即ち、高Al%装置構造又は他の高歪み装置構造)を実現可能にするものでもある。
本発明の別の実施形態では、結晶を逆漏れ電流密度の良好な光起電力型検出器の製造に使用する。
以下の実施例で、通常の物理気相トランスポートにより成長させた6H−SiCブールの端部から、直径約3mm厚さ1mmのSiCディスクを切り出す。SiCディスクの片面を微細研磨し、マイクロパイプの濃度を光学顕微鏡で調べる。アニール前のこのサンプルの暗視野顕微鏡写真を図1に示す。図1の幾つかの大きな暗いスポットは、ウェーハを調製するのに用いたスライスがSiCブールに存在するボイドを横切った結果である。図1中の多数の小さな暗いスポットは、通常ブールに貫通するマイクロパイプである。
SiCディスクをNaCl粉末とともにダイ内に置き、圧縮成形してピルにする。ピルをセルに設置し、ベルトプレス装置内に入れる。ピルを約5.5GPaに加圧し、約1250℃に約30分間加熱する。次にセルを冷却し、減圧し、プレスから取り出す。塩を水で溶解することにより、SiCディスクをセルから回収する。
SiCディスクがHP/HT加工中にわずかな表面損傷を受けるので、ディスクを再研磨することにより、新たな表面を出す。アニール済みディスクの明視野光学顕微鏡写真を図2に示す。画像中に暗いスポットとして認められるマイクロパイプがほんのわずか見られ、アニール処理によってマイクロパイプの濃度が2桁から3桁程度低減したことがわかる。
以上本発明を好ましい実施形態について説明したが、本発明の要旨から逸脱しない範囲で、種々の変更が可能であり、またその要素を均等物に置き換えることも可能であることが、当業者には明らかである。さらに、特定の状況又は材料を本発明の教示に適合させるために種々の改変を加えることも、本発明の要旨から逸脱しない範囲で可能である。
本明細書では、特記しない限り、単位はすべてメートル法であり、量及び%はすべて重量基準である。引用した刊行物はすべて先行技術として援用する。
Claims (16)
- 非ダイヤモンド結晶中の欠陥及び/又は歪みを除去する方法であって、
(a)欠陥及び/又は歪みを含む結晶を、反応条件下で超臨界流体の圧力媒体中に置き、
(b)前記結晶及び圧力媒体を高圧セル内に入れ、
(c)前記セルを高圧装置内で反応条件下、結晶中の欠陥又は歪みを除去するのに十分な高圧及び高温で十分な時間処理する
工程を含む方法。 - 前記圧力媒体が−77℃で固体又は液体の形態を取る、請求項1記載の方法。
- 前記結晶が、ブール、電子ウェーハ、窓、レーザーロッド又はセンサの1以上である、請求項1記載の方法。
- 前記結晶が、直接遷移型半導体材料、間接遷移型半導体材料、ワイドギャップ半導体材料、シンチレータ材料、非線形光学材料、レーザー材料、リラクサー強誘電性材料及び圧電材料から選択される、請求項1記載の方法。
- 前記結晶が、6H−SiC、4H−SiC、15R−SiC、3C−SiC、8H−SiC、2H−SiC、ケイ素(Si)、ゲルマニウム(Ge)、立方晶窒化ホウ素(cBN)、窒化ガリウム(GaN)、ガリウムアンチモン(GaSb)、窒化アルミニウム(AlN)、アルミニウムガリウムインジウム窒素(AlInGaN)、ビスマスアンチモン(BixSb1-x)、窒化インジウム(InN)、ガリウムヒ素(GaAs)、リン化ガリウム(GaP)、ガリウムインジウムリン(GaInP)、アルミニウムインジウムリン(AlInP)、インジウムアルミニウムヒ素(InAlAs)、アルミニウムガリウムアンチモン(AlGaSb)、インジウムアルミニウムガリウムヒ素(InAlGaAs)、アルミニウムインジウムガリウムリン(AlInGaP)、アルミニウムガリウムヒ素(AlGaAs)、インジウムガリウムヒ素リン(InGaAsP)、ガリウムセレン(GaSe)、リン化インジウム(InP)、インジウムセレン(InSe及びInSe2)、インジウムアンチモン(InSb)、リン化カドミウム(Cd3P2)、カドミウムインジウム硫黄(CdIn2S4)、カドミウムケイ素ヒ素(CdSiAs2)、カドミウム錫リン(CdSnP2)、酸化亜鉛(ZnO)、亜鉛セレン(ZnSe)、亜鉛テルル(ZnTe)、硫化カドミウム(CdS)、カドミウム亜鉛セレン(CdZnSe)、ベリリウム亜鉛カドミウムセレン(BeZnCdSe)、亜鉛カドミウムマグネシウムセレン(ZnCdMgSe)、亜鉛硫黄セレン(ZnSSe)、ベリリウム亜鉛セレン(BeZnSe)、ベリリウムマグネシウム亜鉛セレン(BeMgZnSe)、カドミウムテルル(CdTe)、カドミウム亜鉛テルル(CdxZn1-xTe)、水銀カドミウムテルル(HgCdTe)、硫化鉛(PbS)、鉛テルル(PbTe)、鉛セレン(PbSe)、鉛錫テルル(PbSnTe)、鉛ゲルマニウムテルル(PbGeTe)、鉛ユーロピウムテルル(PbEuTe)、鉛ユーロピウムセレン(PbEuSe)、鉛カドミウム硫黄(PbCdS)、鉛ユーロピウムセレンテルル(PbEuSeTe)、鉛硫黄セレン(PbSSe)、三ホウ酸リチウム(LiB3O5又はLBO)、オルトバナジウム酸イットリウム(YVO4)、リン酸カリウムチタニル(KTiOPO4又はKTP)、ニオブ酸カリウム(KNbO3又はKN)、ホウ酸セシウムリチウム(CsLiB6O10又はCLBO)、LiCaAlF6(LiCAF)、LiSrAlF6(LiSAF)、ジルコンチタン酸鉛(Pb(ZrxTi1-x)O3又はPZT)、マグネシウムニオブ酸鉛(Pb(Mg1/3Nb2/3)O3又はPMN)、ジルコンニオブ酸鉛(Pb(Zr1/3Nb2/3)O3又はPZN)、ビスマスケイ素酸素(BSO)、チタン酸バリウム(BTO)、鉛マグネシウムニオブチタン(Pb(Mgx/3Nb2x/3Ti1-x)O3又はPMNT)、鉛ジルコンニオブチタン(Pb(Zrx/3Nb2x/3Ti1-x)O3又はPZNT)、ハフニウム酸ストロンチウム(SrHfO3)、ハフニウム酸バリウム(BaHfO3)、シリカ、シリケート及びフルオロジルコネートをマトリックスとする希土類ランタニドイオンレーザー結晶、KCl、RbCl、NaCl、CuCl、CsI、CaF2、ZnF2、MgF2、SrF2、MnF2、ZnS、ZnSe、CaF2−ErF3、KI、RbCaF3、LiNbO3、KMgF3、Ca2PO4Cl、CaGd2(SiO4)3O、LaCl3、LiYF4、LaF3、Y3Al5O12、LiYF4、LuAlO3、YAlO3、Gd3Ga5O12、CaF2−ErF3、Er3Al5O12、Lu3Al5O12、BaYb2F8、NaF、LiF、サファイア、アレクサンドライト、フォルステライト、LiYF4、BaF2、BaY2F8、BaEr2F8、RbBr、Li2GeO3、Y2O3、Er2O3、YVO4、GdAlO3、Y3Sc2Ga3O12、NaCaErF6、CaWO4又はCaMoO4をマトリックスとするレーザー結晶のうち1種以上である、請求項4記載の方法。
- 前記結晶が寸法約0.1〜500mmのブールである、請求項4記載の方法。
- 前記結晶がGaNであり、前記反応条件がアンモニア又は窒素活性が平衡時の値よりも高い窒素含有流体の1種以上を含む、請求項4記載の方法。
- 前記結晶がSiCであり、前記反応条件が1000〜2000℃の温度を含む、請求項4記載の方法。
- 請求項1記載の方法で欠陥又は歪みを除去又は低減した結晶。
- 請求項9記載の結晶を含むエピタキシャル構造。
- 請求項9記載の結晶を含む半導体装置。
- 発光ダイオード(LED)、レーザーダイオード、光検出器、フィルター、トランジスタ、整流器、サイリスタ、光増幅器、エミッタ、検出器、ダイオード、スイッチ、太陽電池又は光双安定性装置の形態にある請求項11記載の半導体装置。
- 非ダイヤモンド結晶及び非晶質材料から選択される材料中の欠陥及び/又は歪みを除去する方法であって、
(a)欠陥及び/又は歪みを含む材料を、反応条件下で超臨界流体となる圧力媒体中に置き、
(b)欠陥及び/又は歪みを含む材料と圧力媒体を、高圧装置内で材料中の欠陥又は歪みを除去するのに十分な高圧及び高温で十分な時間処理する
工程を含む方法。 - 請求項13記載の方法で処理した材料を含む物品。
- 前記高圧が0.5GPa以上である、請求項1記載の方法。
- 前記結晶及び圧力媒体を封止・変形可能なカプセルに入れる工程をさらに含む、請求項1記載の方法。