JP2006028517A - ゴルフボール及びスポーツ用品に使用する組成物 - Google Patents
ゴルフボール及びスポーツ用品に使用する組成物 Download PDFInfo
- Publication number
- JP2006028517A JP2006028517A JP2005206269A JP2005206269A JP2006028517A JP 2006028517 A JP2006028517 A JP 2006028517A JP 2005206269 A JP2005206269 A JP 2005206269A JP 2005206269 A JP2005206269 A JP 2005206269A JP 2006028517 A JP2006028517 A JP 2006028517A
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- group
- acid
- polymer
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】3種の成分(A)、(B)及び(C)の反応生成物を含むブレンド組成物を提供する。成分(A)は、エチレン及び/又はαオレフィン、並びに1種又は複数のα,β−エチレン性不飽和C3〜C20カルボン酸、スルホン酸又はリン酸を含むポリマーである。成分(B)は一般式(R2N)m−R’−(X(O)nORy)mを有する化合物であり、成分(C)は成分(A)及び(B)に存在する酸性基の一部又はすべてを中和する能力を有する塩基性金属イオン塩である。
【選択図】図1
Description
ブレンド成分(A)は、i)エチレン及び/又はαオレフィン、並びにii)α,β−エチレン性不飽和C3〜C20カルボン酸若しくは無水物、又はα,β−エチレン性不飽和C3〜C20スルホン酸若しくは無水物、又はα,β−エチレン性不飽和C3〜C20リン酸若しくは無水物、並びに場合によりiii)α,β−エチレン性不飽和C3〜C20カルボン酸のC1〜C10エステル、又はα,β−エチレン性不飽和C3〜C20スルホン酸のC1〜C10エステル、又はα,β−エチレン性不飽和C3〜C20リン酸のC1〜C10エステルのポリマーである。
ブレンド成分(B)は、同一分子内に酸とアミン官能基の両方を有する任意の化合物である。好ましいのは下記の一般式を有する化合物である。
(R2N)m−R’−(X(O)nORy)m
式中、Rは、水素、又はC1〜C20脂肪族系、脂環式系若しくは芳香族系であり;R’は、1個又は複数のC1〜C20直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは置換された直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは芳香族基、或いはこれだけに限定するものではないが、最大12個のアミノ酸のアミノ酸配列から導出したポリペプチドを含む最大12個の繰返し単位のオリゴマーを含む架橋基であり;XはC又はS又はPであるが、X=Cの場合、n=1且つy=1であり、X=Sの場合、n=2且つy=1であり、X=Pの場合、n=2且つy=2である。また、m=1〜3である。
例
酸塩、例えば(R2N−R’−X(O)nO−M+);又は
両性イオン塩、例えば(−YR2HN+−R’−X(O)nO−M+)
(M+は、Na+、K+、Li+、NH4 +、Zn2+、Mg2+又はCa2+であることができ、
Y−は、Cl−、Br−、I−又はClO4 −であることができ、
X、R及びR’は上記の通りである)
を含むが、これらだけに限定するものではない一般式(R2N)m−R’−(X(O)nOHy)mの化合物の任意の及びすべてのもの又は塩も含まれる。
ブレンド成分(C)は、ブレンド成分A及びBに存在する酸性基の一部又はすべてを中和する能力を有する塩基性金属イオン塩である。中和に使用する塩基性金属イオン塩の金属カチオンには、Li+、Na+、K+、Zn2+、Ca2+、Co2+、Ni2+、Cu2+、Pb2+及びMg2+があり、Li+、Na+、Zn2+、Ca2+及びMg2+が好ましい。塩基性金属イオン塩には、これらだけに限定するものではないが、例えば、ギ酸、酢酸、硝酸及び炭酸の塩、炭酸水素塩、酸化物、水酸化物及びアルコキシドがある。
a)高分子量成分(約80,000から約500,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている);並びに
b)低分子量成分(約2,000から約30,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている)
を含む双峰性ポリマーブレンド組成物を含む。
a)エチレン、5から25重量パーセントの(メタ)アクリル酸、0から40重量パーセントの(メタ)アクリレートモノマーを含み、リチウム、ナトリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで中和されたアイオノマーポリマーと、
b)(前記改質アイオノマーポリマーの総重量に対して)約5から約40重量パーセントの1種若しくは複数の脂肪酸又は前記脂肪酸の金属塩(この金属は、カルシウム、ナトリウム、亜鉛、カリウム、リチウム、バリウム及びマグネシウムからなる群から選択され、脂肪酸は好ましくはステアリン酸である)と
を混合することによって調製した1種又は複数の改質単峰性アイオノマーとを反応させることにより調製することができる。
a)高分子量成分(約80,000から約500,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、亜鉛、カルシウム、カリウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている)と、
b)低分子量成分(約2,000から約30,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、亜鉛、カルシウム、カリウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている)と
c)(前記改質アイオノマーポリマーの総重量に対して)約5から約40重量パーセントの1種若しくは複数の脂肪酸又は前記脂肪酸の金属塩(この金属は、カルシウム、ナトリウム、亜鉛、カリウム、リチウム、バリウム及びマグネシウムからなる群から選択され、脂肪酸は好ましくはステアリン酸である)と
を混合することによって調製した1種又は複数の改質双峰性アイオノマーとを反応させることにより調製することができる。
次に図を参照すると、ゴルフボール1が図示されており、これは、本明細書で記載の配合物の固体本体として形成された球状の固体センター又はコア2、球状のコア上に配置した中間層3、及びアウターカバー層4を含む。
本発明のゴルフボールのコアは不飽和ポリマーを含む。本発明のゴルフボールで使用するのに適した不飽和ポリマーは、炭化水素又は非炭化水素のいずれかの不飽和を有し、熱的に、化学的に、放射線によって、又はこれらの方法の組合せによって開始する架橋反応に関与することが可能な任意のポリマー材料を含む。不飽和ポリマーは、従来のワンピースゴルフボール及び多層ゴルフボールのコアに通常使用される任意のゴムであることができる。適切な不飽和ポリマーの非限定的な例としては、1,2−ポリブタジエン、シス−1,4−ポリブタジエン、トランス−1,4−ポリブタジエン、シス−ポリイソプレン、トランス−ポリイソプレン、ポリクロロプレン、ポリブチレン、スチレン−ブタジエンゴム、スチレン−ブタジエン−スチレンブロックコポリマー、部分的及び完全に水素化した等価物、スチレン−イソプレン−スチレンブロックコポリマー、部分的及び完全に水素化した等価物、ニトリルゴム、シリコーンゴム、ポリウレタン、並びにこれらの任意の組合せがある。
本発明のゴルフボールで使用するのに適した架橋剤には、過酸化物、イオウ化合物又はその他の既知の化学架橋剤並びにこれらの混合物がある。適切な架橋剤の非限定的な例としては、第1級、第2級又は第3級脂肪族又は芳香族有機過酸化物がある。2,5−ジメチル−2,5−ジ(tert−ブチルペルオキシ)ヘキサン及び1,4−ジ−(2−tert−ブチルペルオキシイソプロピル)ベンゼンなど、1個を超えるペルオキシ基を含有する過酸化物を使用することができる。例えばtert−ブチルペルベンゾエート及び過酸化tert−ブチルクミルなど、対称過酸化物及び非対称過酸化物の両方を使用することができる。カルボキシル基を有する過酸化物も適切である。本発明で架橋剤として使用した過酸化物の分解は、熱エネルギー、剪断、放射線、他の化学物質との反応又はこれらの任意の組合せを適用することによってもたらされる。ホモリティカルに(homolytically)及びヘテロリティカルに(heterolytically)分解した過酸化物の両方を本発明で使用することができる。適切な過酸化物の非限定的な例としては、過酸化ジアセチル;過酸化ジ−tert−ブチル;過酸化ジベンゾイル;過酸化ジクミル;2,5−ジメチル−2,5−ジ(ベンゾイルペルオキシ)ヘキサン;1,4−ビス−(t−ブチルペルオキシイソプロピル)ベンゼン;t−ブチルペルオキシベンゾエート;2,5−ジメチル−2,5−ジ−(t−ブチルペルオキシ)ヘキシン−3、例えばオハイオ州AkronのAkrochem Corp.から販売されているTrigonox145−45B;1,1−ビス(t−ブチルペルオキシ)−3,3,5−トリ−メチルシクロヘキサン、例えばコネチカット州NorwalkのR.T.Vanderbilt Co.,Inc.から販売されているVarox231−XL;及びジ−(2,4−ジクロロベンゾイル)ペルオキシドがある。架橋剤は、不飽和ポリマー100重量部に対して、約0.05重量部から約5重量部、より好ましくは約0.2重量部から約3重量部、最も好ましくは約0.2重量部から約2重量部の量でブレンドすることができる。
ゴム及び架橋剤は、不飽和カルボン酸の金属塩であることができる共架橋剤とブレンドしてもよい。これらの例としては、アクリル酸、メタクリル酸、マレイン酸、フマル酸、パルミチン酸など、炭素原子3から8個を有する不飽和脂肪酸の亜鉛塩及びマグネシウム塩があり、アクリル酸及びメタクリル酸の亜鉛塩が最も好ましい。不飽和カルボン酸金属塩は、予備形成した金属塩として、又はα,β−不飽和カルボン酸及び金属酸化物又は金属水酸化物をゴム組成物に導入し、それをゴム組成物と反応させて金属塩を形成することにより、ゴムにブレンドすることができる。不飽和カルボン酸金属塩は、任意の所望の量で、しかし好ましくは不飽和ポリマー100重量部に対して不飽和カルボン酸約10重量部から約60重量部の量でブレンドすることができる。
本発明のボールのコアを配合するのに使用する組成物はまた、1種又は複数のペプタイザーを含んでよい。用語「ペプタイザー」は不飽和ポリマーの最初の加工中に架橋を阻害するが、その後、架橋が開始したら不飽和ポリマーの架橋に関与する化学物質を意味する。
ゴルフボール組成物は1つ又は複数のクラスの1種又は複数の硬化促進剤を含むことができる。不飽和ポリマーに加えた硬化促進剤は、不飽和ポリマーの加硫速度を増大させ且つ/又は加硫温度を低下させる。硬化促進剤はゴム加工で既知の任意のクラスのものであることができ、メルカプト−、スルフェンアミド−、チウラム、ジチオカルバメート、ジチオカルバミルスルフェンアミド、キサンテート、グアニジン、アミン、チオ尿素及びジチオホスフェート硬化促進剤がある。具体的な市販の硬化促進剤としては、2−メルカプトベンゾチアゾール及びその金属又は非金属塩、例えばドイツ国、LeverkusenのBayer AGが販売しているVulkacit Mercapto C、Mercapto MGC、Mercapto ZM−5及びZM、日本国、東京のOuchisinko Chemical Industrial Company,Ltd.が販売しているNocceler M、Nocceler MZ及びNocceler M−60、並びにオハイオ州AkronのAkrochem Corporationが販売しているMBT及びZMBTがある。市販の硬化促進剤のより完全な一覧は、The Vanderbilt Rubber Handbook:第13版(1990、R.T.Vanderbilt Co.)、296〜330頁、Encyclopedia of Polymer Science and Technology、第12巻(1970、John Wiley & Sons)、258〜259頁、及びRubber Technology Handbook(1980、Hanser/Gardner Publications)、234〜236頁に記載されている。好ましい硬化促進剤としては、2−メルカプトベンゾチアゾール(MBT)及びその塩がある。
再び図1の図面を参照すると、ゴルフボール1が図示されており、これは、本明細書で記載の配合物の固体本体として形成された球状の固体センター又はコア2、球状のコア上に配置した中間層3、及びアウターカバー層4を含む。
Surlyn(登録商標)9910は、DuPontから市販されているアイオノマーの等級であり、エチレン/メタクリル酸ポリマーの亜鉛アイオノマーである。
Surlyn(登録商標)9120は、DuPontから市販されているアイオノマーの等級であり、エチレン/メタクリル酸ポリマーの亜鉛アイオノマーである。
Diak(登録商標)4は、コネチカット州NorwalkのR.T.Vanderbilt Co.から市販されている4,4’−メチレン−ビス−(シクロヘキシルアミン)カルバメートである。
11−アミノ−ウンデカン酸はSigma−Aldrich Companyから市販されている。
12−アミノ−ウンデカン酸はSigma−Aldrich Companyから市販されている。
ステアリン酸ナトリウムはSigma−Aldrich Companyから市販されている。
(Atti又はPGA圧縮)=(160−Riehle圧縮)
と表すことができる。したがって、Riehle圧縮の100は、Atti圧縮の60と同じである。
ヘッド速度:112mph
ボール速度:160mph
発射角:9deg
バックスピン:3200rpm
次に参考ボールを試験ボールに代え、対応する値を測定した。
2 固体センター又はコア
3 中間層
4 アウターカバー層
Claims (30)
- a.(A)以下を含むポリマー
i.エチレン及び/又はαオレフィン、並びに
ii.1種又は複数のα,β−エチレン性不飽和C3〜C20カルボン酸、スルホン酸又はリン酸;
b.(B)一般式(R2N)m−R’−(X(O)nORy)mを有する化合物[式中
i.Rは、
(1)水素、
(2)1種又は複数のC1〜C20脂肪族系、
(3)1種又は複数の脂環式系、
(4)1種又は複数の芳香族系、及び
(5)それらの組合せ
からなる群から選択され;
ii.R’は、
(1)1個又は複数の置換されていないC1〜C20直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは
(2)1個又は複数の置換された直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは
(3)1個又は複数の芳香族基、或いは
(4)1個又は複数のオリゴマー(最大12個の繰返し単位をそれぞれ含有する)
を含む架橋基であり;
iii.X=C又はS又はPの場合、mは1〜3であり、
iv.X=Cの場合、n=1且つy=1、
v.X=Sの場合、n=2且つy=1、
vi.X=Pの場合、n=2且つy=2];及び
c.塩基性金属イオン塩(ブレンド成分(A)及び(B)に存在する酸性基の一部又はすべてを中和する能力を有する)
の反応生成物を含むブレンド組成物。 - a.前記成分(A)は、エチレン/α,β−エチレン性不飽和C3〜C20カルボン酸コポリマー又はエチレン/α,β−エチレン性不飽和C3〜C20カルボン酸/α,β−エチレン性不飽和C3〜C20カルボン酸エステルターポリマーであり、
b.前記成分(B)は、約0.1から約40phrの量で存在し、
c.前記成分(C)は、Li+、Na+、K+、Zn2+、Ca2+、Co2+、Ni2+、Cu2+、Pb2+及びMg2+からなる群から選択されるカチオンを有する塩基性金属イオン塩である
請求項1に記載のブレンド組成物。 - a.前記成分(A)は、
i.単峰性エチレン/(メタ)アクリル酸コポリマー又はエチレン/(メタ)アクリル酸/(メタ)アクリレートターポリマー;或いは
ii.以下を含む双峰性ポリマーブレンド組成物:
(1)高分子量成分(約80,000から約500,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属イオンで部分的に中和されている);並びに
(2)低分子量成分(約2,000から約30,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属イオンで部分的に中和されている)
であり;
b.前記成分(B)は、約1から約20phrの量で存在し、アミノ酸、ポリペプチド、カルバミン酸、オキサミン酸、アントラニル酸及びそれらの組合せからなる群から選択され;
c.前記成分(C)は、Li+、Na+、K+、Ca2+、Zn2+、Mg2+及びそれらの組合せからなる群から選択されるカチオンを有する塩基性金属イオン塩である
請求項1に記載のブレンド組成物。 - a.前記成分(A)は、単峰性エチレン/(メタ)アクリル酸コポリマー又はエチレン/(メタ)アクリル酸/(メタ)アクリレートターポリマーであり;
b.前記成分(B)は、約1から約15phrの量で存在し、4,4’−メチレン−ビス(シクロヘキシルアミン)カルバメート、11−アミノウンデカン酸、12−アミノドデカン酸、ε−カプロラクタム、ω−カプロラクタム及びそれらの組合せからなる群から選択され;
c.前記成分(C)は、金属ギ酸塩、金属酢酸塩、金属硝酸塩、金属炭酸塩、金属炭酸水素塩、金属酸化物、金属水酸化物、金属アルコキシド及びそれらの組合せからなる群から選択される
請求項3に記載のブレンド組成物。 - 熱可塑性樹脂、熱硬化性樹脂、ポリウレタン樹脂、ポリエステル樹脂、ポリアミドエラストマー樹脂、ポリアミドアイオノマー、ポリウレタンアイオノマー、熱可塑性コポリエーテルエステルブロックコポリマー、熱可塑性コポリエステルエステルブロックコポリマー、熱可塑性エラストマー、熱硬化性エラストマー、合成ゴム、熱可塑性加硫物、共重合性アイオノマー、三元重合性アイオノマー、ポリウレタンアイオノマー、ポリアミドアイオノマー、ポリカーボネート、ポリオレフィン、ポリアミド、共重合性ポリアミド、ポリエステル、ポリビニルアルコール、アクリロニトリル−ブタジエン−スチレンコポリマー、ポリアリーレート、ポリアクリレート、ポリフェニレンエーテル、耐衝撃性ポリフェニレンエーテル、耐衝撃性ポリスチレン、ジアリルフタレートポリマー、メタロセン触媒ポリマー、スチレン−アクリロニトリル(SAN)(オレフィン改質SAN及びアクリロニトリル−スチレン−アクリロニトリルを含む)、スチレン−無水マレイン酸(S/MA)ポリマー、スチレンコポリマー、機能性スチレンコポリマー、機能性スチレンターポリマー、スチレンターポリマー、セルロースポリマー、液晶ポリマー(LCP)、エチレン−プロピレン−ジエンターポリマー(EPDM)、エチレン−ビニルアセテートコポリマー(EVA)、エチレン−プロピレンコポリマー、エチレンビニルアセテート、ポリ尿素、ポリシロキサン及びそれらの組合せからなる群から選択される追加のポリマーをさらに含む請求項1に記載のブレンド組成物。
- a.(A)1種又は複数のアイオノマー;及び
b.(B)一般式(R2N)m−R’−(X(O)nORy)mを有する化合物[式中
i.Rは、
(1)水素、
(2)1種又は複数のC1〜C20脂肪族系、
(3)1種又は複数の脂環式系、
(4)1種又は複数の芳香族系、及び
(5)それらの組合せ
からなる群から選択され;
ii.R’は、
(1)1個又は複数の置換されていないC1〜C20直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは
(2)1個又は複数の置換された直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは
(3)1個又は複数の芳香族基、或いは
(4)1個又は複数のオリゴマー(最大12個の繰返し単位をそれぞれ含有する)
を含む架橋基であり;
iii.X=C又はS又はPの場合、mは1〜3であり、
iv.X=Cの場合、n=1且つy=1、
v.X=Sの場合、n=2且つy=1、
vi.X=Pの場合、n=2且つy=2]
の反応生成物を含むブレンド組成物。 - a.前記1種又は複数のアイオノマーは以下からなる群から選択され
i.E/X/Yポリマーを含む単峰性アイオノマー(Eはエチレンであり、XはC3からC8のα,βエチレン性不飽和カルボン酸であり、Yはアクリル酸アルキル及びメタクリル酸アルキルからなる群から選択される軟化性コモノマーであり、ここでアルキル基は炭素原子1〜8個を有し、XはE/X/Yコポリマーの約2から約30重量%の範囲にあり、YはE/X/Yコポリマーの0から約35重量%の範囲にあり、前記アイオノマーポリマーに存在する酸性基は、亜鉛、ナトリウム、リチウム、カリウム、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属で部分的に中和されている);
ii.以下を含む双峰性アイオノマー
(1)高分子量成分(約80,000から約500,000の範囲の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属イオンで部分的に中和されている);並びに
(2)低分子量成分(約2,000から約30,000の範囲の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属イオンで部分的に中和されている);
iii.以下を含む改質単峰性アイオノマー;
(1)エチレン、
(2)5から25重量パーセントの(メタ)アクリル酸(前記改質アイオノマーポリマーの総重量に対して)、
(3)0から40重量パーセントのC1からC8−アクリル酸アルキル(前記改質アイオノマーの総重量に対して)、及び
(4)(前記改質アイオノマーの総重量に対して)約5から約40重量パーセントの脂肪酸又は脂肪酸の1種又は複数の金属塩;
iv.以下を含む改質双峰性アイオノマー:
(1)高分子量成分(約80,000から約500,000の範囲の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属イオンで部分的に中和されている);
(2)低分子量成分(約2,000から約30,000の範囲の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及びそれらの組合せからなる群から選択される金属イオンで部分的に中和されている);及び
(3)(前記改質アイオノマーポリマーの総重量に対して)約5から約40重量パーセントの脂肪酸又は脂肪酸の1種又は複数の金属塩;並びに
v.それらの組合せ;並びに
b.前記成分(B)は、約1から約20phrの量で存在し、アミノ酸、ポリペプチド、カルバミン酸、オキサミン酸、アントラニル酸及びそれらの組合せからなる群から選択される
請求項6に記載のブレンド組成物。 - a.前記アイオノマーは、単峰性エチレン/(メタクリル酸)コポリマー又はエチレン/メタクリル酸/(メタ)アクリル酸エステルターポリマーであり、
b.成分(B)は、約1から約15phrの量で存在し、4,4’−メチレン−ビス(シクロヘキシルアミン)カルバメート、11−アミノウンデカン酸、12−アミノドデカン酸、ε−カプロラクタム、ω−カプロラクタム及びそれらの組合せからなる群から選択される
請求項7に記載のブレンド組成物。 - 熱可塑性樹脂、熱硬化性樹脂、ポリウレタン樹脂、ポリエステル樹脂、ポリアミドエラストマー樹脂、ポリアミドアイオノマー、ポリウレタンアイオノマー、熱可塑性コポリエーテルエステルブロックコポリマー、熱可塑性コポリエステルエステルブロックコポリマー、熱可塑性エラストマー、熱硬化性エラストマー、合成ゴム、熱可塑性加硫物、共重合性アイオノマー、三元重合性アイオノマー、ポリウレタンアイオノマー、ポリアミドアイオノマー、ポリカーボネート、ポリオレフィン、ポリアミド、共重合性ポリアミド、ポリエステル、ポリビニルアルコール、アクリロニトリル−ブタジエン−スチレンコポリマー、ポリアリーレート、ポリアクリレート、ポリフェニレンエーテル、耐衝撃性ポリフェニレンエーテル、耐衝撃性ポリスチレン、ジアリルフタレートポリマー、メタロセン触媒ポリマー、スチレン−アクリロニトリル(SAN)(オレフィン改質SAN及びアクリロニトリル−スチレン−アクリロニトリルを含む)、スチレン−無水マレイン酸(S/MA)ポリマー、スチレンコポリマー、機能性スチレンコポリマー、機能性スチレンターポリマー、スチレンターポリマー、セルロースポリマー、液晶ポリマー(LCP)、エチレン−プロピレン−ジエンターポリマー(EPDM)、エチレン−ビニルアセテートコポリマー(EVA)、エチレン−プロピレンコポリマー、エチレンビニルアセテート、ポリ尿素、ポリシロキサン及びそれらの組合せからなる群から選択される追加のポリマーをさらに含む請求項6に記載のブレンド組成物。
- a.コア;
b.アウターカバー層;及び
c.0から5つの中間層
を含み;
d.前記コア、アウターカバー及び/又は存在する場合、中間層のうちの1つ又は複数は、
i.(A)エチレン及び/又はαオレフィン、並びに1種又は複数のα,β−エチレン性不飽和C3〜C20カルボン酸、スルホン酸又はリン酸を含むポリマー、
ii.(B)一般式(R2N)m−R’−(X(O)nORy)mを有する化合物[式中
(1)Rは、
(a)水素、
(b)1種又は複数のC1〜C20脂肪族系、
(c)1種又は複数の脂環式系、
(d)1種又は複数の芳香族系、及び
(e)それらの組合せ
からなる群から選択され;
(2)R’は、
(a)1個又は複数の置換されていないC1〜C20直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは
(b)1個又は複数の置換された直鎖状若しくは分枝状脂肪族基又は脂環式基、或いは
(c)1個又は複数の芳香族基、或いは
(d)1個又は複数のオリゴマー(最大12個の繰返し単位をそれぞれ含有する)
を含む架橋基であり;
(3)X=C又はS又はPの場合、mは1〜3であり、
(4)X=Cの場合、n=1且つy=1、
(5)X=Sの場合、n=2且つy=1、
(6)X=Pの場合、n=2且つy=2]及び
iii.(C)塩基性金属イオン塩(ブレンド成分(A)及び(B)に存在する酸性基の一部又はすべてを中和する能力を有する)
の反応生成物を含むゴルフボール。 - a.前記成分(A)は、エチレン/α,β−エチレン性不飽和C3〜C20カルボン酸コポリマー又はエチレン/α,β−エチレン性不飽和C3〜C20カルボン酸/α,β−エチレン性不飽和C3〜C20カルボン酸エステルターポリマーであり、
b.前記成分(B)は、アミノ酸、ポリペプチド、カルバミン酸、オキサミン酸、アントラニル酸及びそれらの任意の及びすべての混合物からなる群から選択され;
c.前記成分(C)は、Li+、Na+、K+、Zn2+、Ca2+、Co2+、Ni2+、Cu2+、Pb2+及びMg2+からなる群から選択されるカチオンを有する塩基性金属イオン塩である
0から3つの中間層を含む請求項10に記載のゴルフボール。 - a.前記成分(A)は、
i.単峰性エチレン/(メタ)アクリル酸コポリマー又はエチレン/(メタ)アクリル酸/(メタ)アクリレートターポリマー;或いは
ii.以下を含む双峰性ポリマー:
(1)高分子量成分(約80,000から約500,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている);並びに
(2)低分子量成分(約2,000から約30,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている)
であり;
b.前記成分(B)は、アミノ酸、ポリペプチド、カルバミン酸、オキサミン酸、アントラニル酸及びそれらの任意の及びすべての混合物からなる群から選択され;
c.前記成分(C)は、Li+、Na+、K+、Zn2+、Ca2+及びMg2+からなる群から選択されるカチオンを有する塩基性金属イオン塩である
1から約3つの中間層を含む請求項10に記載のゴルフボール。 - a.前記成分(A)は、単峰性エチレン/(メタ)アクリル酸コポリマー又はエチレン/(メタ)アクリル酸/(メタ)アクリレートターポリマーであり;
b.前記成分(B)は、4,4’−メチレン−ビス(シクロヘキシルアミン)カルバメート、11−アミノウンデカン酸、12−アミノドデカン酸、ε−カプロラクタム、ω−カプロラクタム及びそれらの組合せからなる群から選択され;
c.前記成分(C)は、金属ギ酸塩、金属酢酸塩、金属硝酸塩、金属炭酸塩、金属炭酸水素塩、金属酸化物、金属水酸化物、金属アルコキシド及びそれらの組合せからなる群から選択される
1つの中間層を有する請求項12に記載のゴルフボール。 - 前記コア、アウターカバー及び/又は存在する場合、中間層のうちの1つ又は複数は、
a.以下を含むブレンド組成物
i.エチレン、
ii.5から25重量パーセントの(メタ)アクリル酸(a、b及びcの総重量に対して)、
iii.0から40重量パーセントのC1からC8−アクリル酸アルキル(a、b及びcの総重量に対して)、及び
iv.(前記改質アイオノマーポリマーの総重量に対して)約5から約45重量パーセントの脂肪酸又は前記脂肪酸の1種又は複数の金属塩;或いは
b.以下を含む双峰性ポリマーブレンド組成物;
i.高分子量成分(約80,000から約500,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている);
ii.低分子量成分(約2,000から約30,000の分子量を有し、1種又は複数のエチレン/α,β−エチレン性不飽和C3〜C8カルボン酸コポリマー及び/又は1種又は複数のエチレン、(メタ)アクリル酸アルキル、(メタ)アクリル酸ターポリマーを含み、リチウム、ナトリウム、カリウム、亜鉛、カルシウム、マグネシウム及び任意のこれらの混合物からなる群から選択される金属イオンで部分的に中和されている);並びに
iii.(前記改質アイオノマーポリマーの総重量に対して)約5から約45重量パーセントの脂肪酸又は前記脂肪酸の1種又は複数の金属塩;或いは
c.1)と2)の組合せ
を含む改質アイオノマーポリマーをさらに含み、
d.前記改質アイオノマーポリマーに存在する酸性基の約40から100パーセントは、亜鉛、ナトリウム、リチウム、カリウム、カルシウム、マグネシウムイオン又はそれらの任意の及びすべての組合せで中和されている
請求項10に記載のゴルフボール。 - 前記コアが、
a.少なくとも1種の不飽和ポリマー;
b.少なくとも1種の架橋剤;
c.少なくとも1種の共架橋剤;
d.場合により少なくとも1種のペプタイザー;
e.場合により少なくとも1種の硬化促進剤;及び
f.場合により少なくとも1種の充填剤
をさらに含む請求項10に記載のゴルフボール。 - a.前記不飽和ポリマーは、約20から約80のムーニー粘度(ML1+4(100℃))を有し、1,2−ポリブタジエン、シス−1,4−ポリブタジエン、トランス−1,4−ポリブタジエン、シス−ポリイソプレン、トランス−ポリイソプレン、ポリクロロプレン、ポリブチレン、スチレン−ブタジエンゴム、スチレン−ブタジエン−スチレンブロックコポリマー並びに部分的及び完全に水素化した等価物、スチレン−イソプレン−スチレンブロックコポリマー並びに部分的及び完全に水素化した等価物、ニトリルゴム、シリコーンゴム、ポリウレタン、それらの任意の及びすべての組合せからなる群から選択され;
b.前記架橋剤は、前記不飽和ポリマー100重量部当たり約0.05から約5重量部の量で存在し;
c.前記ペプタイザーは、存在する場合、
i.有機イオウ化合物、
ii.有機イオウ化合物の金属塩、
iii.有機イオウ化合物の非金属塩、又は
iv.i)、ii)及びiii)の任意の及びすべての組合せ
を含み;
d.前記硬化促進剤は、存在する場合、前記不飽和ポリマー100重量部当たり約0.1から約10重量部の量で存在し;
e.前記充填剤は、存在する場合、沈降水和シリカ、石灰岩、クレー、タルク、アスベスト、バライト、グラスファイバー、アラミドファイバー、雲母、メタケイ酸カルシウム、硫酸バリウム、硫化亜鉛、リトポン、シリケート、炭化ケイ素、ケイ藻土、炭酸カルシウム又は炭酸マグネシウム又は炭酸バリウムなどの炭酸塩、硫酸カルシウム又は硫酸マグネシウム又は硫酸バリウムなどの硫酸塩、タングステン、鋼、銅、コバルト又は鉄を包含する金属、金属合金、炭化タングステン、金属酸化物、金属ステアリン酸塩、及びその他の微粒子炭素質材料並びにそれらの任意の及びすべての組合せからなる群から選択される
請求項15に記載のゴルフボール。 - a.前記不飽和ポリマーはシス−1,4−ポリブタジエンであり、約30から約60のムーニー粘度(ML1+4(100℃))を有し;
b.前記架橋剤は、前記不飽和ポリマー100重量部当たり約0.2から約3重量部の量で存在し;
c.前記ペプタイザーは、存在する場合、
i.前記不飽和ポリマー100重量部当たり約0.01から約10重量部の量で存在し;
ii.有機イオウ化合物、有機イオウ化合物の金属塩、有機イオウ化合物の非金属塩、及びそれらの組合せからなる群から選択され;
d.前記硬化促進剤は、存在する場合、前記不飽和ポリマー100重量部当たり約0.2から約5重量部の量で存在する
請求項15に記載のゴルフボール。 - a.前記不飽和ポリマーはシス−1,4−ポリブタジエンであり、約35から約50のムーニー粘度(ML1+4(100℃))を有し;
b.架橋剤は、前記不飽和ポリマー100重量部当たり約0.2から約2重量部の量で存在し;
c.前記ペプタイザーは、存在する場合、
i.前記不飽和ポリマー成分100重量部当たり約0.1から約7重量部の量で存在し;
ii.ペンタクロロチオフェノール、ジベンズアミドジフェニルジスルフィド、ペンタクロロチオフェノールの金属塩、一般式[NR1R2R3R4]+(R1、R2、R3及びR4は、水素、C1〜C20脂肪族系、脂環式系又は芳香族系及びそれらの組合せのいずれかである)を有するアンモニウムカチオンを有するペンタクロロチオフェノールのアンモニウム塩からなる群から選択され;
d.前記硬化促進剤は、存在する場合、前記不飽和ポリマー100重量部当たり約0.5から約1.5重量部の量で存在し、2−メルカプトベンゾチアゾール及び2−メルカプトベンゾチアゾールの塩からなる群から選択される
請求項15に記載のゴルフボール。 - 前記ペプタイザーは、存在する場合、ペンタクロロチオフェノール、ペンタクロロチオフェノールの亜鉛塩、ペンタクロロチオフェノールのNH4 +塩及びそれらの組合せからなる群から選択され、前記不飽和ポリマー成分100重量部当たり約0.15から約5重量部の量で存在する請求項18に記載のゴルフボール。
- 前記コアが、
a.少なくとも1種の架橋剤(0.1時間に等しいt1/2で150℃未満の第1の特徴的な分解温度を有する);
b.少なくとも1種の架橋剤(0.1時間に等しいt1/2で150℃を超える第2の特徴的な分解温度を有する)
を含む請求項15に記載のゴルフボール。 - 第1の特徴的な分解温度を有する少なくとも1種の架橋剤と第2の特徴的な分解温度を有する少なくとも1種の架橋剤との組成重量比が5:95から95:5の範囲にある請求項20に記載のゴルフボール。
- 第1の特徴的な分解温度を有する少なくとも1種の架橋剤と第2の特徴的な分解温度を有する少なくとも1種の架橋剤との組成重量比が10:90から50:50の範囲にある請求項20に記載のゴルフボール。
- 飛来速度125フィート/秒でCORが約0.790を超える請求項10に記載のゴルフボール。
- 前記コア、存在する場合、0から5つの前記中間層、又は少なくとも1つの前記カバー層のうちの1つ又は複数が、熱可塑性エラストマー、熱硬化性エラストマー、合成ゴム、熱可塑性加硫物、ポリカーボネート、ポリオレフィン、ポリアミド、共重合性ポリアミド、ポリエステル、ポリビニルアルコール、アクリロニトリル−ブタジエン−スチレンコポリマー、ポリアリーレート、ポリアクリレート、ポリフェニレンエーテル、耐衝撃性ポリフェニレンエーテル、耐衝撃性ポリスチレン、ジアリルフタレートポリマー、メタロセン触媒ポリマー、スチレン−アクリロニトリル(SAN)(オレフィン改質SAN及びアクリロニトリル−スチレン−アクリロニトリルを含む)、スチレン−無水マレイン酸(S/MA)ポリマー、スチレンコポリマー、機能性スチレンコポリマー、機能性スチレンターポリマー、スチレンターポリマー、セルロースポリマー、液晶ポリマー(LCP)、エチレン−プロピレン−ジエンターポリマー(EPDM)、エチレン−ビニルアセテートコポリマー(EVA)、エチレン−プロピレンコポリマー、エチレンビニルアセテート、ポリ尿素、ポリシロキサン及び任意のそれらの組合せからなる群から選択されるポリマーをさらに含む請求項10に記載のゴルフボール。
- 前記コアがセンター及び前記センターの周りに配置した1つ又は複数の層を含み、ある層とその隣の層との間の硬度差がショアDで2単位を超え、好ましくは5単位を超え、最も好ましくは10単位を超える請求項10に記載のゴルフボール。
- 前記硬度がコアからアウターコア層へ外側に増大する請求項25に記載のゴルフボール。
- 前記硬度がコアからアウターコア層へ外側に向かって減少する請求項25に記載のゴルフボール。
- 請求項1に記載のブレンド組成物を含むスポーツ用品の品目。
- 請求項6に記載のブレンド組成物を含むスポーツ用品の品目。
- スポーツ用衣類、長靴、スニーカー、クロッグ、サンダル、スリッポンサンダル及び靴、ゴルフシューズ、テニスシューズ、ランニングシューズ、運動靴、ハイキングシューズ、スキー板、スキーマスク、スキー靴、サイクリングシューズ、サッカーシューズ、ゴルフクラブ及びゴルフバッグからなる群から選択される請求項28に記載のスポーツ用品の品目。