JP2013078563A - ゴルフボール用樹脂組成物及びゴルフボール - Google Patents
ゴルフボール用樹脂組成物及びゴルフボール Download PDFInfo
- Publication number
- JP2013078563A JP2013078563A JP2012197230A JP2012197230A JP2013078563A JP 2013078563 A JP2013078563 A JP 2013078563A JP 2012197230 A JP2012197230 A JP 2012197230A JP 2012197230 A JP2012197230 A JP 2012197230A JP 2013078563 A JP2013078563 A JP 2013078563A
- Authority
- JP
- Japan
- Prior art keywords
- golf ball
- resin composition
- carboxylic acid
- unsaturated carboxylic
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)(a−1)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸との二元共重合体、(a−2)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸との二元共重合体の金属イオン中和物、(a−3)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸とα,β−不飽和カルボン酸エステルとの三元共重合体、及び、(a−4)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸とα,β−不飽和カルボン酸エステルとの三元共重合体の金属イオン中和物からなる群より選択される少なくとも1種と、(B)分子中に、炭化水素鎖、カチオン性部位及びアニオン性部位を有する化合物とを含有するゴルフボール用樹脂組成物に関する。
【選択図】なし
Description
前記両性界面活性剤は、ベタイン型両性界面活性剤、アミドアミノ酸型両性界面活性剤、アルキルアミノ脂肪酸塩、アルキルアミンオキシド、β−アラニン型両性界面活性剤、グリシン型両性界面活性剤、スルホベタイン型両性界面活性剤及びホスホベタイン型両性界面活性剤からなる群より選択される少なくとも1種であることが好ましい。
前記ゴルフボール用樹脂組成物は、樹脂成分100質量部に対して、(C)塩基性無機金属化合物を100質量部以下含有することが好ましい。
本発明は、少なくとも一層以上のコアと前記コアを被覆するカバーとを有するゴルフボールであって、前記コアの少なくとも一層が前記ゴルフボール用樹脂組成物から形成されているゴルフボールに関する。
本発明はまた、ゴルフボール本体が前記ゴルフボール用樹脂組成物から形成されているワンピースゴルフボールに関する。
前記(a−1)成分は、オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸との二元共重合体であって、共重合体のカルボキシル基が中和されていない非イオン性のものである。前記(a−2)成分は、オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸との二元共重合体の金属イオン中和物であって、共重合体のカルボキシル基の少なくとも一部が金属イオンで中和されたアイオノマー樹脂を挙げることができる。
二元系アイオノマー樹脂の中和度=100×二元系アイオノマー樹脂中の中和されているカルボキシル基のモル数/二元系アイオノマー樹脂中のカルボキシル基の総モル数
三元系アイオノマー樹脂の中和度=100×三元系アイオノマー樹脂中の中和されているカルボキシル基のモル数/三元系アイオノマー樹脂中のカルボキシル基の総モル数
なお、陽イオン成分、陽イオン形成基、金属成分、カルボキシル基及び陰イオン形成基には、イオン化していない前駆体のモル数を含めるものとする。陽イオン成分量、陽イオン形成基量、陰イオン形成基は、例えば、中和滴定により求めてもよい。
下記式を満足することにより、ゴルフボール用樹脂組成物が、高いレベルで軟質を維持しながらも反発性が高くなる。なお、下記式においてlogは常用対数である。
log(E’/E”2)≧−6.55
(1)スラブ硬度(ショアD硬度)
ゴルフボール用樹脂組成物を用いて、熱プレス成形により、厚み約2mmのシートを作製し、23℃で2週間保存した。このシートを、測定基板などの影響が出ないように、3枚以上重ねた状態で、ASTM−D2240に規定するスプリング式硬度計ショアD型を備えた高分子計器社製自動ゴム硬度計P1型を用いて測定した。
MFRは、フローテスター(島津製作所社製、島津フローテスターCFT−100C)を用いて、JIS K7210に準じて測定した。なお、測定は、測定温度190℃、荷重2.16kgの条件で行った。
ゴルフボール用樹脂組成物を用いて、熱プレス成形にて厚み約2mmのシートを作製し、当該シートから直径28mmの円形状に打抜いたものを6枚重ねることにより、厚さ約12mm、直径28mmの円柱状試験片を作製した。この試験片についてリュプケ式反発弾性試験(試験温湿度23℃、50RH%)を行った。なお、試験片の作製及び試験方法は、JIS K6255に準じて行った。
球形体に初期荷重98Nを負荷した状態から終荷重1275Nを負荷したときまでの圧縮方向の変形量(圧縮方向に球形体が縮む量)を測定した。各球形体の圧縮変形は、表1及び2では球形体No.14の圧縮変形量との比、表3では球形体No.42の圧縮変形量との比、表4では球形体No.46の圧縮変形量との比として示した。
各球形体に198.4gの金属製円筒物を40m/秒の速度で衝突させ、衝突前後の円筒物及びゴルフボールの速度を測定し、それぞれの速度及び重量から各ゴルフボールの反発係数を算出した。測定は、各球形体について12個ずつ行って、その平均値を各球形体の反発係数とした。
アマチュアゴルファー(上級者)10人により、ドライバーを用いた実打テストを行って、各人の打撃時のフィーリングを下記基準で評価させた。10人の評価のうち、最も多い評価をそのゴルフボールの打球感とした。
評価基準
優:衝撃が少なくてフィーリングが良い。
良:普通。
不良:衝撃が大きくてフィーリングが悪い。
装置:Bruker Avance 400
測定方法:Torchia法によるT1緩和時間測定
測定周波数:100.6256207MHz
測定温度:室温
基準物質:アダマンタン
マジック角回転の回転数:5000Hz
パルス幅:4.80μsec
コンタクトタイム:2000μsec
パルスの間隔:1μsec,100msec、500msec、1sec、2sec、3sec、4sec、6sec、8sec、10sec、12sec、15sec、20sec、40sec、80sec、120sec
磁場強度:9.4T
ゴルフボール用樹脂組成物の貯蔵弾性率E’(Pa)及び損失弾性率E”(Pa)を以下の条件で測定した。
装置:ユービーエム社製動的粘弾性測定装置Rheogel−E4000
測定サンプル:ゴルフボール用樹脂組成物から、プレス成形により厚み2mmのシートを作製し、このシートから、幅4mm、クランプ間距離20mmになるように試料片を切り出した。
測定モード:引張
測定温度:12℃
加振周波数:10Hz
測定ひずみ:0.05%
表1〜4に示すように、配合材料をドライブレンドし、二軸混練型押出機によりミキシングして、ストランド状に冷水中に押し出した。押出されたストランドをペレタイザーにより切断してペレット状のゴルフボール用樹脂組成物を調製した。押出条件は、スクリュー径45mm、スクリュー回転数200rpm、スクリューL/D=35であり、配合物は、押出機のダイの位置で160〜230℃に加熱された。得られたペレット状のゴルフボール用樹脂組成物を220℃にて射出成形し、直径40mmの球形体(コア)を得た。
ニュクレルAN4319:三井・デュポンポリケミカル社製、エチレン・メタクリル酸・アクリル酸ブチル共重合体(メルトフローレイト(190℃×2.16kg):55g/10min、曲げ剛性率:21MPa、メタクリル酸含量8質量%)
ニュクレルN1560:三井・デュポンポリケミカル社製、エチレン・メタクリル酸共重合体(メルトフローレイト(190℃×2.16kg):60g/10min、曲げ剛性率:83MPa、メタクリル酸含量15質量%)
ニュクレルN2050H:三井・デュポンポリケミカル社製、エチレン・メタクリル酸共重合体(メルトフローレイト(190℃×2.16kg):500g/10min、曲げ剛性率:82MPa、メタクリル酸含量20質量%)
水酸化マグネシウム:和光純薬工業社製
オレイルベタイン:ルーブリゾール社製「Chembetaine OL」の精製品(水分と塩分を除去)
ラウリルベタイン:日油社製「ニッサンアノン BL」の精製品(水分と塩分を除去)
ステアリルベタイン:花王社製「アンヒトール86B」の精製品(水分と塩分を除去)
オレイン酸:東京化成工業社製
ステアリン酸:日油社製「粉末ステアリン酸つばき」
Claims (8)
- (A)(a−1)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸との二元共重合体、(a−2)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸との二元共重合体の金属イオン中和物、(a−3)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸とα,β−不飽和カルボン酸エステルとの三元共重合体、及び、(a−4)オレフィンと炭素数3〜8個のα,β−不飽和カルボン酸とα,β−不飽和カルボン酸エステルとの三元共重合体の金属イオン中和物からなる群より選択される少なくとも1種と、
(B)分子中に、炭化水素鎖、カチオン性部位及びアニオン性部位を有する化合物とを含有するゴルフボール用樹脂組成物。 - 前記化合物が両性界面活性剤である請求項1記載のゴルフボール用樹脂組成物。
- 前記両性界面活性剤は、ベタイン型両性界面活性剤、アミドアミノ酸型両性界面活性剤、アルキルアミノ脂肪酸塩、アルキルアミンオキシド、β−アラニン型両性界面活性剤、グリシン型両性界面活性剤、スルホベタイン型両性界面活性剤及びホスホベタイン型両性界面活性剤からなる群より選択される少なくとも1種である請求項2記載のゴルフボール用樹脂組成物。
- 樹脂成分100質量部に対して、前記化合物を1〜200質量部含有する請求項1〜3のいずれかに記載のゴルフボール用樹脂組成物。
- 樹脂成分100質量部に対して、(C)塩基性無機金属化合物を100質量部以下含有する請求項1〜4のいずれかに記載のゴルフボール用樹脂組成物。
- 請求項1〜5のいずれかに記載のゴルフボール用樹脂組成物から形成された構成部材を有するゴルフボール。
- 少なくとも一層以上のコアと前記コアを被覆するカバーとを有するゴルフボールであって、前記コアの少なくとも一層が請求項1〜5のいずれかに記載のゴルフボール用樹脂組成物から形成されているゴルフボール。
- ゴルフボール本体が請求項1〜5のいずれかに記載のゴルフボール用樹脂組成物から形成されているワンピースゴルフボール。