JP5541062B2 - ゴルフボール用材料及びその製造方法 - Google Patents
ゴルフボール用材料及びその製造方法 Download PDFInfo
- Publication number
- JP5541062B2 JP5541062B2 JP2010226156A JP2010226156A JP5541062B2 JP 5541062 B2 JP5541062 B2 JP 5541062B2 JP 2010226156 A JP2010226156 A JP 2010226156A JP 2010226156 A JP2010226156 A JP 2010226156A JP 5541062 B2 JP5541062 B2 JP 5541062B2
- Authority
- JP
- Japan
- Prior art keywords
- molecular weight
- average molecular
- golf ball
- acid
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]コアと該コアを被覆するカバーとからなるツーピースソリッドゴルフボールにおけるカバー材、または、1層以上のコアと該コアを被覆する1層以上の中間層と該中間層を被覆する1層以上のカバーとからなるマルチピースソリッドゴルフボールにおけるカバー材又は中間層材に用いられるゴルフボール用材料であって、(a)重量平均分子量(Mw)が120,000〜200,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が4.0〜7.0であるオレフィン−メタクリル酸共重合体及び/又はオレフィン−メタクリル酸−不飽和カルボン酸エステル共重合体と、
(b)重量平均分子量(Mw)が150,000〜220,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が5.5〜8.5であるオレフィン−アクリル酸共重合体及び/又はオレフィン−アクリル酸−不飽和カルボン酸エステル共重合体と、
(c)有機酸又はその金属塩と、
(d)上記(a)〜(c)成分中の酸基のうち70モル%以上を中和するための塩基性無機金属化合物と
を含有し、その樹脂混合物のショアD硬度が30〜60であり、且つ、メルトフローレート(MFR)が3.0〜10.0g/10minであることを特徴とするゴルフボール用材料。
[2]上記の(a)成分と(b)成分との混合割合が(a):(b)=90:10〜40:60(質量部)であり、(c)成分が(a)及び(b)の合計100質量部に対して5〜70質量部である[1]記載のゴルフボール用材料。
[3]上記(c)成分の有機酸が、ステアリン酸、オレイン酸及びこれらの混合物の群から選ばれる[1]又は[2]記載のゴルフボール用材料。
[4]上記(a)成分の重量平均分子量(Mw)が120,000〜180,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が4.2〜6.5である[1]、[2]又は[3]記載のゴルフボール用材料。
[5]上記(b)成分の重量平均分子量(Mw)が150,000〜200,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が5.5〜8.3である[1]〜[4]のいずれか1項記載のゴルフボール用材料。
[6]上記[1]〜[5]のいずれか1項記載のゴルフボール用材料が単軸押出機、二軸押出機及びこれらの連結型押出機により製造されるゴルフボール用材料の製造方法。
本発明のゴルフボール用材料は、(a)重量平均分子量(Mw)が120,000〜200,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が4.0〜7.0であるオレフィン−メタクリル酸共重合体及び/又はオレフィン−メタクリル酸−不飽和カルボン酸エステル共重合体、またはその金属中和物と、(b)重量平均分子量(Mw)が150,000〜220,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が5.5〜8.5であるオレフィン−アクリル酸共重合体及び/又はオレフィン−アクリル酸−不飽和カルボン酸エステル共重合体、またはその金属中和物をベース樹脂とするものである。
下記のコア配合によるシス−1,4−ポリブタジエンを主成分とするコア材料を用いて、直径37.50mm、重量(重さ)32.80gのソリッドコアを得た。
シス−1,4−ポリブタジエン 100 質量部
酸化亜鉛 5 質量部
硫酸バリウム 15 質量部
老化防止剤 0.2 質量部
アクリル酸亜鉛 25 質量部
ジクミルパーオキサイド 1.0 質量部
商品名「ニュクレルN035C」
未中和のエチレン−メタクリル酸−不飽和カルボン酸エステル3元共重合体(三井・デュポンポリケミカル社製)、重量平均分子量(Mw)155,000、分子量分布(Mw/Mn)5.76
ポリマーB
商品名「ニュクレル」
未中和のエチレン−メタクリル酸−不飽和カルボン酸エステル3元共重合体(三井・デュポンポリケミカル社製)、重量平均分子量(Mw)127,000、分子量分布(Mw/Mn)4.37
ポリマーC
商品名「ESCOR5100」
未中和のエチレン−アクリル酸2元共重合体(ExxonMobil Chemical社製)、重量平均分子量(Mw)188,000、分子量分布(Mw/Mn)6.37
ポリマーD
商品名「ニュクレルN0200H」
未中和のエチレン−メタアクリル酸2元共重合体(三井・デュポンポリケミカル社製)、重量平均分子量(Mw)132,000、分子量分布(Mw/Mn)8.43
ポリマーE
商品名「ニュクレルAN4221C」
未中和のエチレン−アクリル酸2元共重合体(三井・デュポンポリケミカル社製)、重量平均分子量(Mw)181,000、分子量分布(Mw/Mn)6.99
商品名「NAA−200」(日油(株)製)
JIS−K 7210に準拠し、温度190℃、荷重21.18N(2.16kgf)条件下で測定したMFRの値が3〜10g/10minの範囲内のものを「○」、この範囲を外れたものを「×」と評価した。
組成物を厚さ2mmのシート状に成形し、それを3枚重ね合わせてショアD硬度計にて測定した。
23±1℃の温度で、ゴルフボールを鋼板の上に置き、初期荷重98N(10kgf)から終荷重1275N(130kgf)に負荷したときのゴルフボールのたわみ量(mm)。
初速はR&Aの承認する装置であるUSGAのドラム回転式の初速計と同方式の初速測定器を用いて測定した。ボールは23±1℃の温度で3時間以上温調し、同温度で測定した。250ポンド(113.4kg)のヘッド(ストライキングマスク)を使って打撃速度143.8ft/s(43.83m/s)にてボールを打撃した。10個のボールを各々2回打撃して6.28ft(1.91m)の間を通過する時間を計測し、初速を計算した。15分間でこのサイクルを行った。
米国Automated Design Corporation製のADC Ball COR Durability Testerにより、ボールの耐久性(Durability)を評価した。ボールを空気圧で発射させた後、平行に設置した2枚の金属板に連続的に衝突させ、ボールが割れるまでに要した発射回数の平均値を用い、下記の基準に従って耐久性を評価した。(この場合、平均値とは、同種のボールを4個用意し、それぞれのボールを発射させて4個のボールがそれぞれ割れるまでに要した発射回数を平均化した値である。試験機のタイプは、縦型CORであり、金属板への入射速度を43m/sとした。)
○:150回以上
△:100〜150回
×:100回以下
Claims (6)
- コアと該コアを被覆するカバーとからなるツーピースソリッドゴルフボールにおけるカバー材、または、1層以上のコアと該コアを被覆する1層以上の中間層と該中間層を被覆する1層以上のカバーとからなるマルチピースソリッドゴルフボールにおけるカバー材又は中間層材に用いられるゴルフボール用材料であって、(a)重量平均分子量(Mw)が120,000〜200,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が4.0〜7.0であるオレフィン−メタクリル酸共重合体及び/又はオレフィン−メタクリル酸−不飽和カルボン酸エステル共重合体と、
(b)重量平均分子量(Mw)が150,000〜220,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が5.5〜8.5であるオレフィン−アクリル酸共重合体及び/又はオレフィン−アクリル酸−不飽和カルボン酸エステル共重合体と、
(c)有機酸又はその金属塩と、
(d)上記(a)〜(c)成分中の酸基のうち70モル%以上を中和するための塩基性無機金属化合物と
を含有し、その樹脂混合物のショアD硬度が30〜60であり、且つ、メルトフローレート(MFR)が3.0〜10.0g/10minであることを特徴とするゴルフボール用材料。 - 上記の(a)成分と(b)成分との混合割合が(a):(b)=90:10〜40:60(質量部)であり、(c)成分が(a)及び(b)の合計100質量部に対して5〜70質量部である請求項1記載のゴルフボール用材料。
- 上記(c)成分の有機酸が、ステアリン酸、オレイン酸及びこれらの混合物の群から選ばれる請求項1又は2記載のゴルフボール用材料。
- 上記(a)成分の重量平均分子量(Mw)が120,000〜180,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が4.2〜6.5である請求項1、2又は3記載のゴルフボール用材料。
- 上記(b)成分の重量平均分子量(Mw)が150,000〜200,000であり、かつ重量平均分子量(Mw)と数平均分子量(Mn)との比が5.5〜8.3である請求項1〜4のいずれか1項記載のゴルフボール用材料。
- 請求項1〜5のいずれか1項記載のゴルフボール用材料が単軸押出機、二軸押出機及びこれらの連結型押出機により製造されるゴルフボール用材料の製造方法。