JP2005058341A - 粘着シート及び粘着シートの製造方法 - Google Patents
粘着シート及び粘着シートの製造方法 Download PDFInfo
- Publication number
- JP2005058341A JP2005058341A JP2003290237A JP2003290237A JP2005058341A JP 2005058341 A JP2005058341 A JP 2005058341A JP 2003290237 A JP2003290237 A JP 2003290237A JP 2003290237 A JP2003290237 A JP 2003290237A JP 2005058341 A JP2005058341 A JP 2005058341A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- film
- adhesive sheet
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】 粘着シートは、担持フィルムの一方の面にエラストマーフィルムを有し、このエラストマーフィルムの上に粘着剤層が設けられた粘着シートであって、粘着剤層が、アクリル系重合体を主成分とし、かつ、アクリル系重合体に対して相溶可能であり、常温で液状もしくはペースト状である相溶可能成分を含有する組成物から形成され、担持フィルムの加熱収縮率が、縦方向で3.0%以上、4.5%以下であり、横方向で1.2%以上、4.2%以下である。
【選択図】 なし
Description
また、前記担持フィルムは、ポリエチレン、ポリプロピレン及びポリエステルからなる群から選ばれる1つであることができる。
また、前記相溶可能成分は、カルボン酸エステルであることができる。
本発明においては、ポリオール成分として、ポリオキシアルキレン骨格を有するポリエーテルポリオールに、他のポリオール、例えば、ポリオキシテトラメチレングリコール、あるいはブタンジオール、ヘプタンジオール、ヘキサンジオール、シクロヘキサンジメタノール等のポリオールを一部混合して使用することができる。
以下に、バルク重合について具体的に説明する。反応容器にポリオールを投入し、温度が50〜80℃になるように調整し攪拌しつつ、ポリイソシアネートを添加してウレタン化を起こさせる。さらに鎖延長剤を添加して反応させた後、反応生成物をトレーに移動して、100〜150℃で4時間以上保持し、反応を完結させることによって、塊状のポリエーテルポリウレタンを得ることができる。
粘着シートを皮膚へ貼付する際に、皮膚の貼着部位を粘着シートの上から視覚的に確認することができるように、担持フィルム及びエラストマーフィルムは透明または半透明であることが好ましい。また、担持フィルムは、エラストマーフィルムに高い弾性率を付与することができるものであることが好ましく、例えば、常温常湿における引張り試験による50%伸張時のモジュラスが、2N/mm2以上、200N/mm2以下であることが好ましく、8N/mm2以上、50N/mm2以下であることがさらに好ましい。
加熱収縮率(%)=[(L1−L2)/L1]×100
本発明においては、アクリル系重合体と、カルボン酸エステルと、架橋剤とを混合して少なくとも一部に架橋体を形成することによりゲル状の粘着剤層を得ることができる。このようにして得られた粘着剤層は、微小変形領域における弾性率を低下させることができ、皮膚面の凹凸に対して粘着剤層表面の密着性(濡れ性)を向上させて皮膚に対する良好な接着性を発揮することができる。しかも粘着シートを剥離する際には、皮膚面にかかる応力を緩和したり、分散させることができるので、剥離時に皮膚面に対して物理的刺激をほとんど与えることがなく、皮膚面の角質の剥離等もほとんど生じず、皮膚の損傷も極めて少ない、という効果を有する。
なお、本発明において「フィルム」という場合には、シートを含み、「シート」という場合には、フィルムを含む概念とする。
エラストマー樹脂として、ポリエーテルポリウレタン(大日精化工業(株)製、「レザミンP−210」)を2軸スクリュー型の混練機で加熱溶融させた後、Tダイ式の押出し機を用いて厚みが30μmになるように押出し、エラストマーフィルムを形成した。
担持フィルムとして、加熱収縮率が縦方向4.5%、横方向4.2%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)を用意し、この延伸ポリプロピレンフィルムの上に形成したエラストマーフィルムをゴムロールを用いて密着させ、支持体を得た。
実施例1において、担持フィルムを加熱収縮率が縦方向3.0%、横方向1.2%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向3.4、横方向1.3の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向2.6%、横方向0.3%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向2.6%、横方向0.5%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向2.8%、横方向0.5%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向3.0%、横方向0.7%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更した以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向2.6%、横方向0.5%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更し、かつ、粘着剤層の架橋処理を23℃雰囲気下で3日間保存することにより架橋反応を完結させた以外は実施例1と同様にして、粘着シートを作製した。
実施例1において、担持フィルムを加熱収縮率が縦方向2.6%、横方向0.5%の延伸ポリプロピレンフィルム(グンゼ(株)製、「シルファンMTO」、厚み40μm)に変更し、かつ、粘着剤層の架橋処理を40℃雰囲気下で3日間保存することにより架橋反応を完結させた以外は実施例1と同様にして、粘着シートを作製した。
実施例1〜3、比較例1〜6で得られた粘着シートについて、下記に示す評価試験を行った。その結果を表1に示す。
架橋反応を施す前の粘着シートから、100mm×100mmの大きさの試料片を切り出し、ノギスを用いて縦(又は横)の長さ(L1)を測定しておく。次に、この試料片に実施例1〜3、及び比較例1〜6に示した架橋反応を施し、架橋反応後の試料片の縦(又は横)の長さ(L2)を測定する。測定したL1及びL2を下記式に代入して、変形率を求める。
変形率(%)={(L1−L2)/L1}×100
剥離シート付きの粘着シートから剥離シートを剥がし、次に、この粘着シートの粘着剤層面をアルミニウム板に貼付した状態で、エラストマーフィルムから担持フィルムを剥離して担持フィルムのみを得る。この担持フィルムから30mm×40mmの大きさの試料片を切り出し、この試料片を50ccの酢酸エチルに24時間、常温で浸漬して抽出を行った。浸漬後の抽出液をキャピラリーガスクロマトグラフィー分析装置に注入し、クロマトグラムのピーク面積から、担持フィルムに移行した液状成分量を定量した。
架橋処理を施した粘着シートについて、剥離シートからの粘着剤層の浮き上がり状態や粘着シートの変形状態を肉眼で観察し、下記基準に基づき評価を行った。
評価基準:
「○」…剥離シートからの粘着剤層の浮き上がりも、粘着シートの変形も全く認められなかった場合
「×」…剥離シートからの粘着剤層の浮き上がりが認められるか、又は粘着シートの変形が認められた場合
粘着シートを50℃の恒温機内で1ヶ月保存した後、剥離シートからの粘着剤層の浮き上がり状態、粘着シートの変形状態、粘着シートがカールしているか否かを肉眼で観察し、下記基準に基づき評価を行った。
評価基準:
「○」…剥離シートからの粘着剤層の浮き上がりも、粘着シートの変形も全く認められず、かつ、粘着シートにカールが生じていなかった場合
「×」…剥離シートからの粘着剤層の浮き上がりが認められるか、又は粘着シートの変形が認められるか、あるいは、粘着シートにカールが生じていた場合
一方、比較例1〜4の粘着シートは、変形率が大きく、製造性及び保存性に劣ったものであることが分かった。比較例5〜6の粘着シートは、粘着剤の液状成分の移行量が少なく、変形率も小さいが、保存中に粘着剤の液状成分が移行し、剥離シートからの粘着剤層の浮き上がり、粘着シートの変形、及び、粘着シートのカールが認められ、粘着シートには適用できないものであった。
Claims (5)
- 担持フィルムの一方の面にエラストマーフィルムを有し、該エラストマーフィルムの上に粘着剤層が設けられた粘着シートであって、該粘着剤層が、アクリル系重合体を主成分とし、かつ、該アクリル系重合体に対して相溶可能であり、常温で液状もしくはペースト状である相溶可能成分を含有する組成物から形成され、前記担持フィルムの加熱収縮率が、縦方向で3.0%以上、4.5%以下であり、横方向で1.2%以上、4.2%以下であることを特徴とする粘着シート。
- 前記エラストマーフィルムが、ポリエステルポリウレタン、ポリエーテルポリウレタン、ポリエーテルポリエステル及びポリエーテルポリアミドからなる群から選ばれる1つであることを特徴とする請求項1記載の粘着シート。
- 前記担持フィルムが、ポリエチレン、ポリプロピレン及びポリエステルからなる群から選ばれる1つであることを特徴とする請求項1又は2記載の粘着シート。
- 前記相溶可能成分が、カルボン酸エステルであることを特徴とする請求項1から3のいずれか1項記載の粘着シート。
- 担持フィルムとエラストマーフィルムとを積層し、別途剥離シート上に形成した粘着剤層をエラストマーフィルム面に重ねて貼り合わせた後、架橋反応を施すことを特徴とする粘着シートの製造方法。