JP2003011283A - 多層包装材料 - Google Patents
多層包装材料Info
- Publication number
- JP2003011283A JP2003011283A JP2002066728A JP2002066728A JP2003011283A JP 2003011283 A JP2003011283 A JP 2003011283A JP 2002066728 A JP2002066728 A JP 2002066728A JP 2002066728 A JP2002066728 A JP 2002066728A JP 2003011283 A JP2003011283 A JP 2003011283A
- Authority
- JP
- Japan
- Prior art keywords
- oxygen
- thermoplastic resin
- layer
- packaging material
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
収層を通しての酸素透過を長期にわたって低減させるこ
とが可能である多層包装材料を提供するにある。 【解決手段】 熱可塑性樹脂に酸化性重合体及び遷移
金属触媒を配合した樹脂組成物からなる酸素吸収層を有
し、熱可塑性樹脂が遷移金属触媒の存在下において実質
上酸化されないことを特徴とする多層包装材料。
Description
るもので、より詳細には、器壁を通しての酸素透過を長
期間にわたって安定に抑制できるボトル、カップ等の容
器や蓋体等の多層包装材料に関する。
スビン、各種プラスチック容器等が使用されているが、
容器内に残留する酸素や容器壁を透過する酸素による内
容物の変質やフレーバー低下が問題となっている。
しての酸素透過がゼロであり、容器内に残留する酸素の
みが問題であるのに対して、プラスチック容器の場合に
は器壁を通しての酸素透過が無視し得ないオーダーで生
じ、内容品の保存性の点で問題となっている。
では容器壁を多層構造とし、その内の少なくとも一層と
して、エチレン−ビニルアルコール共重合体等の耐酸素
透過性を有する樹脂を用いることが行われている。
の使用も古くから行われており、これを容器壁に適用し
た例としては、特公昭62−1824号公報の発明があ
り、これによると、酸素透過性を有する樹脂に鉄粉など
の還元性物質を主剤とする脱酸素剤を配合して成る層
と、酸素ガス遮断性を有する層とを積層して、包装用多
層構造物とする。
26号公報には、20℃及び0%RHでの酸素透過係数
が10-12cc・cm/cm2・sec・cmHg以下で且つ20℃及び
100%RHでの水分吸着量が0.5%以上であるガス
バリヤー性熱可塑性樹脂に遷移金属の有機金属錯体を配
合した樹脂組成物を中間層とし、該中間層の両側に耐湿
性熱可塑性樹脂の層を設けた積層構造物から成ることを
特徴とする多層包装材料が記載されている。
ーから成り酸素捕集特性を有する組成物または該組成物
の層を含有する包装用障壁において、組成物が酸化可能
有機成分の金属触媒酸化により酸素を捕集することを特
徴とする包装用障壁が記載されており、酸化可能有機成
分としては、ポリアミド、特にキシリレン基含有ポリア
ミドが使用されることも記載されている。
樹脂に配合して、包装材料の器壁に用いる方法は、酸素
吸収性能が大きいという点では満足できるものである
が、樹脂を固有の色相に着色するために、透明性が要求
される包装の分野には使用できないという用途上の制約
がある。
性樹脂組成物は、実質上透明である包装容器にも適用で
きるという利点を有しているが、遷移金属系触媒を配合
した基材樹脂が酸化により劣化するため、器壁を通して
の酸素透過が経時により大きくなり、また容器の強度も
低下するという欠点がある。
合体及び遷移金属触媒を配合した樹脂組成物からなる酸
素吸収層を設けた多層包装材料では、酸化性重合体の酸
化による酸素吸収が選択的に行われ、その結果として、
前述した欠点が有効に解消されることを見い出した。即
ち、本発明の目的は、優れた酸素吸収性を有すると共
に、酸素吸収層を通しての酸素透過を長期にわたって低
減させることが可能である多層包装材料を提供するにあ
る。本発明の他の目的は、酸素吸収層が酸素吸収性に優
れていると共に、酸素吸収層自体が優れた酸素バリアー
性をも保持している機能分離型の酸素吸収層を備えた多
層包装材料を提供するにある。
性樹脂に酸化性重合体及び遷移金属触媒を配合した樹脂
組成物からなる酸素吸収層を有し、熱可塑性樹脂が遷移
金属触媒の存在下において実質上酸化されないことを特
徴とする多層包装材料が提供される。本発明の多層包装
材料においては、 1.熱可塑性樹脂の酸素透過係数が、7cc・mm/m2・da
y・atm(20℃、0%RH)以下であること、 2.熱可塑性樹脂が、キシリレン基含有ポリアミドであ
ること、 3.酸化性重合体が、側鎖または末端に極性基を有する
分子量100乃至10000の樹脂であること、 4.熱可塑性樹脂の溶解度指数(SP)が9.5以上で
あり、酸化性重合体が酸乃至酸無水物変性のポリブタジ
エンであること、 5.酸化性重合体を樹脂組成物中に、0.01乃至10
重量%配合すること、 6.酸化性重合体が熱可塑性樹脂中で粒状あるいは紡錘
状に分散しており、その分散体の最小長さが400nm
以下であること、 7.酸素吸収層に、遷移金属触媒が金属量換算で少なく
とも300ppm配合されていること、 8.酸素吸収後の酸素吸収層の強度が2.0 kgf/mm2
以上を保持していること、 9.酸素吸収層の両側に耐湿性熱可塑性樹脂が設けられ
ていること、 10.酸素吸収層の熱可塑性樹脂の融点Tm1と、その
両側の耐湿性熱可塑性樹脂層の融点Tm2との関係が、
|Tm2一Tml|≦50℃を満足する関係にあること、
が好ましい。
素吸収層を備えているが、この酸素吸収層は、熱可塑性
樹脂を基材とし、これに酸化性重合体と遷移金属触媒と
を配合したこと、及び前記熱可塑性樹脂基材が遷移金属
触媒の存在下においても実質上酸化されないことが特徴
であり、これにより熱可塑性樹脂基材の酸化劣化を生じ
ることなしに、酸素吸収性を発現させることができる。
脂組成物では、樹脂が酸化を受けることにより酸素の吸
収が行われるものであり、この樹脂の酸化劣化に伴い樹
脂層自体の酸素透過度は増大する傾向を示す。これに対
して、本発明の多層包装材料に用いる酸素吸収層では、
熱可塑性樹脂基材は実質上酸化することなく、酸化性重
合体が専ら酸化を受けてこれにより酸素吸収が行われる
ため、熱可塑性樹脂基材の酸化劣化による酸素バリアー
性の低下や強度の低下を生じることなしに、酸素吸収性
を発現させることが可能となるのである。
樹脂基材は、酸素バリアー性を有するものであることが
好ましく、酸素透過係数が、7cc・mm/m2・day・atm
(20℃、0%RH)以下であることが好ましい。勿
論、用いる酸素バリアー性樹脂は遷移金属触媒の存在下
に実質上酸化されないものでなければならない。
して、ポリアミド、特にキシリレン基含有ポリアミド
や、共重合ポリエステル等の酸素バリアー性ポリエステ
ル、ポリエチレンテレフタレート、エチレン−ビニルア
ルコール共重合体等が挙げられる。その中でも特に、キ
シリレンジアミンを主体とするジアミン成分とジカルボ
ン酸成分とから誘導されたポリアミドは、酸素バリアー
性の点で好ましい。即ち、上記のキシリレン基含有ポリ
アミド樹脂は、全脂肪族ポリアミド樹脂に比して酸素透
過性が小さいという利点を有している。
の溶解度指数を有していることが好ましい。溶解度指数
(SolubilityParameter Sp 値) とは凝集エネルギー密
度(cal/c.c.)の1/2 乗値として定義されるもので、水素
結合の強さと密接に関連するものであり、値が大きいほ
ど水素結合の強さの程度が大きいことを示すものであ
る。Sp値が上記範囲内にある熱可塑性樹脂では水素結
合の程度が大きく、酸素バリアー性に優れている。
媒の存在下に酸素と反応することにより酸素を吸収する
ものである。この酸化性重合体は、側鎖または末端に極
性基を有する分子量100乃至10000の樹脂である
ことが、熱可塑性樹脂中への分散性や酸素吸収性の点で
好ましい。特に好適な酸化性重合体として、酸乃至酸無
水物変性のポリブタジエンが挙げられる。
類から誘導された重合体、特に酸乃至酸無水物変性(以
下単に酸変性という)のポリエン系重合体であることが
好ましい。ポリエン類から誘導された重合体は、重合体
中の主鎖或いは側鎖中に二重結合を有している。Smi
thの理論によると、二重結合に隣接する炭素原子は著
しく活性化されやすく、水素ガスを容易に放出するとさ
れている。ポリエンから誘導される重合体では、重合体
中の炭素−炭素二重結合に隣接する炭素原子の位置で水
素原子の引き抜きが容易に行われ、これによりラジカル
が発生すると考えられる。遷移金属触媒と上記酸化性有
機成分とを含有する組成物での酸素吸収は、当然のこと
ながら、この有機成分の酸化を経由して行われるもので
あり、この酸化は、遷移金属触媒による二重結合隣接
炭素原子からの水素原子の引き抜きによるラジカルの発
生、このラジカルへの酸素分子の付加によるパーオキ
シラジカルの発生、パーオキシラジカルによる水素原
子の引き抜きの各素反応を通して生じると信じられる。
ような少量の遷移金属触媒の共存下では、上記ラジカル
の発生や、酸素の付加には誘導期があり、これらの素反
応が必ずしも迅速且つ有効には行われていないと考えら
れる。これに対して、本発明で好適に使用される酸変性
ポリエン重合体では、上記二重結合隣接炭素原子に加え
て、カルボン酸基、カルボン酸無水物基等の官能基を有
しており、前記誘導期の短縮に有効に役立っていると信
じられる。即ち、前記官能基は何れも電子吸引性の基で
あり、前記二重結合隣接炭素原子を活性化させることが
その理由であろう。
塑性樹脂等に配合すると、熱可塑性樹脂マトリックスに
対する酸変性ポリエン系重合体の分散性が向上し、樹脂
組成物の加工性が向上するというきわめて好都合の作用
が達成される。即ち、未変性のポリエン系重合体の場
合、単に機械的な混練でポリエン系重合体を分散させる
ため、分散性が不良であり、また分散の程度も不均一の
ものとなり易いという傾向があり、また樹脂組成物の加
工性も低下するのを免れない。これに対して、酸変性ポ
リエン系重合体では、前述した官能基の存在により、S
p値の大きな熱可塑性樹脂に対する親和性が大であり、
ポリアミド樹脂等の熱可塑性樹脂に対する分散性が良好
で、樹脂組成物の加工性にも優れているという利点が達
成されるものである。
に対して0.01乃至10重量%、特に1.0乃至7重
量%の量で含有されていることが好ましい。酸化性重合
体の量が上記範囲を下回ると、酸素の吸収速度が、上記
範囲内にある場合に比してかなり低下するようになり、
好ましくない。一方、酸化性重合体の量が上記範囲を上
回ると、酸素吸収速度の点では格別の利点が得られない
と共に、酸素吸収性樹脂組成物の層を通しての酸素透過
度が大きくなり、成形性が悪くなるので好ましくない。
化性重合体が熱可塑性樹脂中で粒状あるいは紡錘状に分
散しており、その分散体の最小長さが400nm以下で
あることが、成形性、分散性、酸素吸収性や酸素吸収層
の酸素バリアー性の点で好ましい。分散体の最小長さと
は2本の平行な直線で分散体に接するように挟んだ時に
平行な直線の間隔がもっとも狭くなる部分の長さのこと
である。即ち、この酸素吸収層では、熱可塑性樹脂が連
続相及び酸化性重合体が分散相となった分散構造となる
と共に、分散相の分散粒径が上記範囲に抑制されている
ため、酸化性重合体による酸素吸収が効率よく行われる
と共に、酸化性重合体による酸素吸収が行われた後で
も、熱可塑性樹脂の連続相が維持されるため、酸素バリ
アー性が維持されるという利点がある。
換算で少なくとも300ppm含有されていることが好
ましい。遷移金属触媒の量が上記範囲を下回ると、酸素
吸収速度が上記範囲内にある場合に比してかなり低下す
るようになるので好ましくない。また、この量があまり
にも多くなると樹脂の劣化傾向が著しくなるので、80
0ppm以下であることが好ましい。
上述した組成及び分散構造をとるため、酸素吸収層中の
熱可塑性樹脂が実質上酸化劣化を受けることがなく、そ
のため、酸素吸収後の酸素吸収層の強度が2.0 kgf/m
m2以上を保持しているという利点がある。
収層を備えているという条件下で任意の多層構造をとり
うるが、一般には酸素吸収層の両側に耐湿性熱可塑性樹
脂層が設けられていることが、酸素吸収層における酸素
バリアー性低下を抑制する点で好ましい。一般に、酸素
バリアー性に優れた熱可塑性樹脂は湿度に敏感であり、
吸湿により酸素バリアー性が低下する傾向があるが、酸
素吸収層の両側に耐湿性熱可塑性樹脂層を設けることに
より、この低下傾向を抑制することができる。
樹脂の融点Tm1と、その両側の耐湿性熱可塑性樹脂層
の融点Tm2との関係が、|Tm2一Tml|≦50℃を
満足する関係にあることが、成形性、特に延伸成形性の
点で好ましい。即ち、両樹脂層の融点が上記範囲内にあ
れば、むらのない延伸成形を行うことができ、また得ら
れる容器は耐熱変形性にも優れている。
熱可塑性樹脂の好適なものとしてポリアミド樹脂が使用
される。ポリアミド樹脂としては、(a)ジカルボン酸成
分とジアミン成分とから誘導された脂肪族、脂環族或い
は半芳香族ポリアミド、(b)アミノカルボン酸或いはそ
のラクタムから誘導されたポリアミド、或いはこれらの
コポリアミド或いはこれらのブレンド物が挙げられる。
ジカルボン酸成分としては、例えばコハク酸、アジピン
酸、セバチン酸、デカンジカルボン酸、ウンデカンジカ
ルボン酸、ドデカンジカルボン酸等の炭素数4乃至15
の脂肪族ジカルボン酸やテレフタール酸やイソフタール
酸等の芳香族ジカルボン酸が挙げられる。また、ジアミ
ン成分としては、 1,6- ジアミノヘキサン、1,8-ジアミ
ノオクタン、1,10- ジアミノデカン、1,12-ジアミノド
デカン等の炭素数4〜25とくに6〜18の直鎖状又は
分岐鎖状アルキレンジアミンや、ビス(アミノメチル)
シクロヘキサン、ビス(4-アミノシクロヘキシル)メタ
ン、4,4′-ジアミノ-3,3′-ジメチルジシクロヘキシル
メタン、特にビス(4-アミノシクロヘキシル)メタン、
1,3-ビス(アミノシクロヘキシル)メタン、1,3-ビス
(アミノメチル)シクロヘキサン等の脂環族ジアミン、
m−キシリレンジアミン及び/又はp−キシリレンジア
ミン等の芳香脂肪族ジアミンが挙げられる。アミノカル
ボン酸成分としては、脂肪族アミノカルボン酸、例えば
ω−アミノカプロン酸、ω−アミノオクタン酸、ω−ア
ミノウンデカン酸、ω−アミノドデカン酸や、例えばパ
ラ−アミノメチル安息香酸、パラ−アミノフェニル酢酸
等の芳香脂肪族アミノカルボン酸等を挙げることができ
る。
内でもキシリレン基含有ポリアミドが好ましく、具体的
には、ポリメタキシリレンアジパミド、ポリメタキシリ
レンセバカミド、ポリメタキシリレンスベラミド、ポリ
パラキシリレンピメラミド、ポリメタキシリレンアゼラ
ミド等の単独重合体、及びメタキシリレン/パラキシリ
レンアジパミド共重合体、メタキシリレン/パラキシリ
レンピメラミド共重合体、メタキシリレン/パラキシリ
レンセバカミド共重合体、メタキシリレン/パラキシリ
レンアゼラミド共重合体等の共重合体、或いはこれらの
単独重合体または共重合体の成分とヘキサメチレンジア
ミンの如き脂肪族ジアミン、ピペラジンの如き脂環式ジ
アミン、パラ−ビス(2アミノエチル)ベンゼンの如き
芳香族ジアミン、テレフタル酸の如き芳香族ジカルボン
酸、ε−カプロラクタムの如きラクタム、7−アミノヘ
プタン酸の如きω−アミノカルボン酸、パラ−アミノメ
チル安息香酸の如き芳香族アミノカルボン酸等を共重合
した共重合体が挙げられるが、m−キシリレンジアミン
及び/又はp−キシリレンジアミンを主成分とするジア
ミン成分と、脂肪族ジカルボン酸及び/又は芳香族ジカ
ルボン酸とから得られるポリアミドが特に好適に用いる
ことができる。これらのキシリレン基含有ポリアミドで
は、他のポリアミド樹脂に比して酸素バリアー性に優れ
ており、本発明の目的に好ましいものである。
基濃度が40eq/106g以上、一層好適には末端ア
ミノ基濃度が50eq/106gを超えるポリアミド樹
脂であることが、ポリアミド樹脂の酸化劣化を抑制する
点で好ましい。ポリアミド樹脂の酸化劣化、つまり酸素
吸収と、ポリアミド樹脂の末端アミノ基濃度とは密接な
関係がある。即ち、ポリアミド樹脂の末端アミノ基濃度
が上述した比較的高い範囲にある場合には、酸素吸収速
度は殆どゼロかゼロに近い値に抑制されるのに対して、
ポリアミド樹脂の末端アミノ基濃度が上記範囲を下回る
ようになると、ポリアミド樹脂の酸素吸収速度が増大す
る傾向がある。上記範囲のポリアミド樹脂と酸化性重合
体との組合せを用いることにより、熱可塑性樹脂基材の
酸化劣化を抑制しつつ、酸化性重合体による酸素吸収を
選択的に行わせることが可能となるので好ましい。末端
アミノ基濃度が前記範囲内にあるポリアミド樹脂は、市
販のポリアミド樹脂の樹脂から選択して用いることがで
きる。これらのポリアミド樹脂は、容器の機械的特性及
び加工の容易さから、98%硫酸中、1.0 g/dlの濃度及
び20℃の温度で測定した相対粘度(ηrel )が1.3
乃至4.2、特に1.5乃至3.8の範囲内にあること
が望ましい。
の例として、ポリエチレンテレフタレート(PET)や
ガスバリアー性ポリエステルを用いることもできる。ガ
スバリアー性ポリエステルの1種(以下、BPRと記す
こともある。)は、重合体鎖中に、テレフタル酸成分
(T)とイソフタル酸成分(I)とを、 T:I=95: 5乃至 5:95 特に 75:25乃至25:75 のモル比で含有し且つエチレングリコール成分(E)と
ビス(2−ヒドロキシエトキシ)ベンゼン成分(BHE
B)とを、 E:BHEB=99.999:0.001 乃至2.0 :98.0 特に 99.95 :0.05 乃至40 :60 のモル比で含有する。BHEBとしては、1,3−ビス
(2−ヒドロキシエトキシ)ベンゼンが好ましい。この
ポリエステル(BPR)は、少なくともフィルムを形成
し得るに足る分子量を有するべきであり、一般にフェノ
ールとテトラクロルエタンとの50:50の重量比の混
合溶媒中、30℃の温度で測定して、0.3 乃至2.8 dl/
g、特に0.4乃至1.8dl/g の固有粘度[η]を有すること
が望ましい。
合体は、ポリエンから誘導される重合体であることが好
ましい。かかるポリエンとしては、炭素原子数4〜20
のポリエン、鎖状乃至環状の共役乃至非共役ポリエンか
ら誘導された単位を含む樹脂が好適に使用される。これ
らの単量体としては、例えばブタジエン、イソプレン等
の共役ジエン;1,4-ヘキサジエン、3-メチル-1,4-ヘキ
サジエン、4-メチル-1,4-ヘキサジエン、5-メチル-1,4-
ヘキサジエン、4,5-ジメチル-1,4-ヘキサジエン、7-メ
チル-1,6-オクタジエン等の鎖状非共役ジエン;メチル
テトラヒドロインデン、5-エチリデン-2-ノルボルネ
ン、5-メチレン-2-ノルボルネン、5-イソプロピリデン-
2-ノルボルネン、5-ビニリデン-2-ノルボルネン、6-ク
ロロメチル-5-イソプロペニル-2-ノルボルネン、ジシク
ロペンタジエン等の環状非共役ジエン;2,3-ジイソプロ
ピリデン-5-ノルボルネン、2-エチリデン-3-イソプロピ
リデン-5-ノルボルネン、2-プロペニル-2,2-ノルボルナ
ジエン等のトリエン、クロロプレンなどが挙げられる。
上の組合せで、或いは他の単量体との組み合わせで単独
重合体、ランダム共重合体、ブロック共重合体などの形
に組み込まれる。ポリエンと組み合わせで用いられる単
量体としては、炭素原子数2〜20のα- オレフィン、
例えばエチレン、プロピレン、1-ブテン、4-メチル-1-
ペンテン、1-ヘキセン、1-ヘプテン、1-オクテン、1-ノ
ネン、1-デセン、1-ウンデセン、1-ドデセン、1-トリデ
セン、1-テトラデセン、1-ペンタデセン、1-ヘキサデセ
ン、1-ヘプタデセン、1-ノナデセン、1-エイコセン、9-
メチル-1-デセン、11-メチル-1-ドデセン、12-エチル-1
-テトラデセンが挙げられ、他にスチレン、ビニルトル
エン、アクリロニトリル、メタクリロニトリル、酢酸ビ
ニル、メチルメタクリレート、エチルアクリレートなど
の単量体も使用可能である。
ポリブタジエン(BR)、ポリイソプレン(IR)、ブ
チルゴム(IIR)、天然ゴム、ニトリル−ブタジエン
ゴム(NBR),スチレン−ブタジエンゴム(SB
R)、クロロプレンゴム(CR)、エチレン−プロピレ
ン−ジエンゴム(EPDM)等を挙げることができる
が、これらの例に限定されない。
特に限定されず、ビニレン基の形で主鎖中に存在して
も、またビニル基の形で側鎖に存在していてもよい。
基、カルボン酸無水物基、水酸基が導入されていること
が好ましい。これらの官能基を導入するのに用いられる
単量体としては、上記の官能基を有するエチレン系不飽
和単量体が挙げられる。
酸またはこれらの誘導体を用いるのが望ましく、具体的
には、アクリル酸、メタクリル酸、マレイン酸、フマー
ル酸、イタコン酸、シトラコン酸、テトラヒドロフタル
酸等のα,β−不飽和カルボン酸、ビシクロ〔2,2,
1〕ヘプト−2−エン−5,6−ジカルボン酸等の不飽
和カルボン酸、無水マレイン酸、無水イタコン酸、無水
シトラコン酸、テトラヒドロ無水フタル酸等のα,β不
飽和カルボン酸無水物、ビシクロ〔2,2,1〕ヘプト
−2−エン−5,6−ジカルボン酸無水物等の不飽和カ
ルボン酸の無水物が挙げられる。
二重結合を有する樹脂をベースポリマーとし、このベー
スポリマーに不飽和カルボン酸またはその誘導体をそれ
自体公知の手段でグラフト共重合させることにより製造
されるが、前述したポリエンと不飽和カルボン酸または
その誘導体とをランダム共重合させることによっても製
造することができる。
系重合体は、不飽和カルボン酸乃至その誘導体を、0.
01乃至10重量%の量で含有していることが好まし
い。不飽和カルボン酸乃至その誘導体の含有量が上記の
範囲にあると、酸変性ポリエン系重合体の熱可塑性樹脂
への分散が良好となると共に、酸素の吸収も円滑に行わ
れる。また、末端に水酸基を有する水酸基変性ポリエン
系重合体も良好に使用することができる。
℃における粘度が1乃至200Pa・sの範囲にあるこ
とが酸素吸収性樹脂組成物の加工性の点で好ましい。
触媒としては、鉄、コバルト、ニッケル等の周期律表第
VIII族金属成分が好ましいが、他に銅、銀等の第I族金
属:錫、チタン、ジルコニウム等の第IV族金属、バナジ
ウムの第V族、クロム等VI族、マンガン等のVII族の金属
成分を挙げることができる。これらの金属成分の内でも
コバルト成分は、酸素吸収速度が大きく、本発明の目的
に特に適したものである。
無機酸塩或いは有機酸塩或いは錯塩の形で一般に使用さ
れる。無機酸塩としては、塩化物などのハライド、硫酸
塩等のイオウのオキシ酸塩、硝酸塩などの窒素のオキシ
酸塩、リン酸塩などのリンオキシ酸塩、ケイ酸塩等が挙
げられる。一方有機酸塩としては、カルボン酸塩、スル
ホン酸塩、ホスホン酸塩などが挙げられるが、カルボン
酸塩が本発明の目的に好適であり、その具体例として
は、酢酸、プロピオン酸、イソプロピオン酸、ブタン
酸、イソブタン酸、ペンタン酸、イソペンタン酸、ヘキ
サン酸、ヘプタン酸、イソヘプタン酸、オクタン酸、2
−エチルヘキサン酸、ノナン酸、3,5,5−トリメチ
ルヘキサン酸、デカン酸、ネオデカン酸、ウンデカン
酸、ラウリン酸、ミリスチン酸、パルミチン酸、マーガ
リン酸、ステアリン酸、アラキン酸、リンデル酸、ツズ
酸、ペトロセリン酸、オレイン酸、リノール酸、リノレ
ン酸、アラキドン酸、ギ酸、シュウ酸、スルファミン
酸、ナフテン酸等の遷移金属塩が挙げられる。一方、遷
移金属の錯体としては、β−ジケトンまたはβ−ケト酸
エステルとの錯体が使用され、β−ジケトンまたはβ−
ケト酸エステルとしては、例えば、アセチルアセトン、
アセト酢酸エチル、1,3−シクロヘキサジオン、メチ
レンビス−1,3ーシクロヘキサジオン、2−ベンジル
−1,3−シクロヘキサジオン、アセチルテトラロン、
パルミトイルテトラロン、ステアロイルテトラロン、ベ
ンゾイルテトラロン、2−アセチルシクロヘキサノン、
2−ベンゾイルシクロヘキサノン、2−アセチル−1,
3−シクロヘキサンジオン、ベンゾイル−p−クロルベ
ンゾイルメタン、ビス(4−メチルベンゾイル)メタ
ン、ビス(2−ヒドロキシベンゾイル)メタン、ベンゾ
イルアセトン、トリベンゾイルメタン、ジアセチルベン
ゾイルメタン、ステアロイルベンゾイルメタン、パルミ
トイルベンゾイルメタン、ラウロイルベンゾイルメタ
ン、ジベンゾイルメタン、ビス(4−クロルベンゾイ
ル)メタン、ビス(メチレン−3,4−ジオキシベンゾ
イル)メタン、ベンゾイルアセチルフェニルメタン、ス
テアロイル(4−メトキシベンゾイル)メタン、ブタノ
イルアセトン、ジステアロイルメタン、アセチルアセト
ン、ステアロイルアセトン、ビス(シクロヘキサノイ
ル)−メタン及びジピバロイルメタン等を用いることが
出来る。
る樹脂組成物においては、酸化性重合体が0.01乃至
10重量%、特に1.0乃至7重量%の量で含有されて
いることが好ましい。また、この樹脂組成物において
は、遷移金属触媒が酸素吸収層に、金属量換算で少なく
とも300ppm、具体的にはコバルトでは310乃至
800ppmの量で含有されていることが好ましい。
触媒を配合するには、種々の手段を用いることができ
る。この配合には、格別の順序はなく、任意の順序でブ
レンドを行ってよい。例えば、酸化性重合体を熱可塑性
樹脂に乾式ブレンド或いはメルトブレンドすることによ
り、両者のブレンド物を容易に調製することができる。
一方、遷移金属触媒は熱可塑性樹脂や酸化性重合体に比
して少量であるので、ブレンドを均質に行うために、一
般に遷移金属触媒を有機溶媒に溶解し、この溶液と粉末
或いは粒状の熱可塑性樹脂及び酸化性重合体とを混合
し、必要によりこの混合物を不活性雰囲気下に乾燥する
のがよい。
メタノール、エタノール、ブタノール等のアルコール系
溶媒、ジメチルエーテル、ジエチルエーテル、メチルエ
チルエーテル、テトラヒドロフラン、ジオキサン等のエ
ーテル系溶媒、メチルエチルケトン、シクロヘキサノン
等のケトン系溶媒、n−ヘキサン、シクロヘキサン等の
炭化水素系溶媒を用いることができ、一般に遷移金属触
媒の濃度が5乃至90重量%となるような濃度で用いる
のがよい。
触媒の混合、及びその後の保存は、組成物の前段階での
酸化が生じないように、非酸化性雰囲気中で行うのがよ
い。この目的に減圧下或いは窒素気流中での混合或いは
乾燥が好ましい。この混合及び乾燥は、ベント式或いは
乾燥機付の押出機や射出機を用いて、成形工程の前段階
で行うことができる。また、遷移金属触媒を比較的高い
濃度で含有する熱可塑性樹脂及び/または酸化性重合体
のマスターバッチを調製し、このマスターバッチを未配
合の熱可塑性樹脂と乾式ブレンドして、本発明の酸素吸
収性樹脂組成物を調製することもできる。尚、本発明で
熱可塑性樹脂としてポリアミド樹脂を用いる場合には、
一般的な乾燥条件である120乃至180℃の温度で、
0.5乃至2mmHgの減圧下2乃至6時間乾燥して後
述する成形に用いるのがよい。
必要ではないが、所望によりそれ自体公知の活性化剤を
配合することができる。活性化剤の適当な例は、これに
限定されないが、ポリエチレングリコール、ポリプロピ
レングリコール、エチレンビニルアルコール共重合体、
エチレン・メタクリル酸共重合体、各種アイオノマー等
の水酸基及び/またはカルボキシル基含有重合体であ
る。これらの水酸基及び/またはカルボキシル基含有重
合体は、熱可塑性樹脂100重量部当たり30重量部以
下、特に0.01乃至10重量部の量で配合することが
できる。本発明に用いる酸素吸収層には、充填剤、着色
剤、耐熱安定剤、耐候安定剤、酸化防止剤、老化防止
剤、光安定剤、紫外線吸収剤、帯電防止剤、金属セッケ
ンやワックス等の滑剤、改質用樹脂乃至ゴム、等の公知
の樹脂配合剤を、それ自体公知の処方に従って配合でき
る。例えば、滑剤を配合することにより、スクリューへ
の樹脂の食い込みが改善される。滑剤としては、ステア
リン酸マグネシウム、ステアリン酸カルシウム等の金属
石ケン、流動、天然または合成パラフィン、マイクロワ
ックス、ポリエチレンワックス、塩素化ポリエチレンワ
ックス等の炭化水素系のもの、ステアリン酸、ラウリン
酸等の脂肪酸系のもの、ステアリン酸アミド、バルミチ
ン酸アミド、オレイン酸アミド、エシル酸アミド、メチ
レンビスステアロアミド、エチレンビスステアロアミド
等の脂肪酸モノアミド系またはビスアミド系のもの、ブ
チルステアレート、硬化ヒマシ油、エチレングリコール
モノステアレート等のエステル系のもの、セチルアルコ
ール、ステアリルアルコール等のアルコール系のもの、
およびそれらの混合系が一般に用いられる。滑剤の添加
量は、熱可塑性樹脂基準で50乃至1000ppmの範
囲が適当である。
収層の少なくとも1層を他の樹脂層の少なくとも1層と
組み合わせて、カップ、トレイ、ボトル、チューブ容器
や蓋体等の形の多層包装材料とする。一般に、酸素吸収
層は、容器などの外表面に露出しないように容器などの
外表面よりも内側に設けるのが好ましく、また内容物と
の直接的な接触を避ける目的で、容器などの内表面より
外側に設けるのが好ましい。かくして、多層容器の少な
くとも1個の中間層として、酸素吸収層を設けるのが望
ましい。
合わせる他の樹脂層としては、オレフィン系樹脂や熱可
塑性ポリエステル樹脂などの耐湿性樹脂、バリアー性樹
脂等が挙げられる。オレフィン樹脂としては、低密度ポ
リエチレン(LDPE)、中密度ポリエチレン(MDP
E)、高密度ポリエチレン(HDPE)、線状低密度ポ
リエチレン(LLDPE)、線状超低密度ポリエチレン
(LVLDPE)等のポリエチレン(PE)、ポリプロ
ピレン(PP)、エチレン−プロピレン共重合体、ポリ
ブテン−1、エチレン−ブテン−1共重合体、プロピレ
ン−ブテン−1共重合体、エチレン−プロピレン−ブテ
ン−1共重合体、エチレン−酢酸ビニル共重合体、イオ
ン架橋オレフィン共重合体(アイオノマー)或いはこれ
らのブレンド物等が挙げられる。また、熱可塑性ポリエ
ステル樹脂としては、ポリエチレンテレフタレート(P
ET)、ポリブチレンテレフタレート(PBT)、ポリ
エチレンナフタレート(PEN)、或いはこれらの共重
合ポリエステル、更にはこれらのブレンド物等が挙げら
れる。更に、ガスバリヤー性樹脂の最も適当な例として
は、エチレン−ビニルアルコール共重合体(EVOH)
を挙げることができ、例えば、エチレン含有量が20乃
至60モル%、特に25乃至50モル%であるエチレン
−酢酸ビニル共重合体を、ケン化度が96モル%以上、
特に99モル%以上となるようにケン化して得られる共
重合体ケン化物が使用される。このエチレンビニルアル
コール共重合体ケン化物は、フイルムを形成し得るに足
る分子量を有するべきであり、一般に、フエノール:水
の重量比で85:15の混合溶媒中30℃で測定して0.
01 dl/g 以上、特に0.05 dl/g 以上の粘度を有する
ことが望ましい。更にまた、バリアー性樹脂の他の例と
しては、環状オレフィン系共重合体(COC)、特にエ
チレンと環状オレフィンとの共重合体、特に三井化学
(株)製のAPEL等を用いることができる。
Rとして表して、次の通りである。また、どちらの層を
内面側にするかは、目的によって自由に選択することが
できる。 二層構造:PET/OAR、PE/OAR、PP/OA
R、 三層構造:PE/OAR/PET、PET/OAR/P
ET、PE/OAR/PP、EVOH/OAR/PE
T、PE/OAR/COC、 四層構造:PE/PET/OAR/PET、PE/OA
R/EVOH/PET、PET/OAR/EVOH/P
ET、PE/OAR/EVOH/COC、 五層構造:PET/OAR/PET/OAR/PET、
PE/PET/OAR/EVOH/PET、PET/O
AR/EVOH/COC/PET、PET/OAR/P
ET/COC/PET、PE/OAR/EVOH/CO
C/PET、 六層構造:PET/OAR/PET/OAR/EVOH
/PET、PE/PET/OAR/COC/EVOH/
PET、PET/OAR/EVOH/PET/COC/
PET、 七層構造:PET/OAR/COC/PET/EVOH
/OAR/PET、 などである。
に必要により接着剤樹脂を介在させることもできる。こ
のような接着剤樹脂としては、カルボン酸、カルボン酸
無水物、カルボン酸塩、カルボン酸アミド、カルボン酸
エステル等に基づくカルボニル(−CO−)基を主鎖又
は側鎖に、1乃至700ミリイクイバレント(meq)/1
00g樹脂、特に10乃至500meq /100g樹脂の
濃度で含有する熱可塑性樹脂が挙げられる。接着剤樹脂
の適当な例は、エチレン−アクリル酸共重合体、イオン
架橋オレフィン共重合体、無水マレイン酸グラフトポリ
エチレン、無水マレイン酸グラフトポリプロピレン、ア
クリル酸グラフトポリオレフィン、エチレン−酢酸ビニ
ル共重合体、共重合ポリエステル、共重合熱可塑性等の
1種又は2種以上の組合せである。これらの樹脂は、同
時押出或いはサンドイッチラミネーション等による積層
に有用である。また、予じめ形成されたガスバリヤー性
樹脂フイルムと耐湿性樹脂フイルムとの接着積層には、
イソシアネート系或いはエポキシ系等の熱硬化型接着剤
樹脂も使用される。
層の厚みは、特に制限はないが、一般に1乃至100μ
m、特に5乃至50μmの範囲にあるのが好ましい。即
ち、酸素吸収層の厚みがある範囲よりも薄くなると酸素
吸収性能が劣り、またある範囲よりも厚くなっても酸素
吸収性の点では格別の利点がなく、樹脂量が増大するな
ど経済性の点、材料の可撓性や柔軟性が低下するなどの
容器特性の点では不利となるからである。
みは、用途によっても相違するが、一般に30乃至70
00μm、特に50乃至5000μmのあるのがよく、
一方酸素吸収性中間層の厚みは、全体の厚みの0.5乃
至95%、特に1乃至50%の厚みとするのが適当であ
る。
収層を用いる点を除けば、それ自体公知の方法で製造が
可能である。例えば、フィルム、シート或いはチューブ
の成形は、前記樹脂組成物を押出機で溶融混練した後、
T−ダイ、サーキュラーダイ(リングダイ)等を通して
所定の形状に押出すことにより行われ、T−ダイ法フィ
ルム、ブローウンフィルム等が得られる。Tダイフィル
ムはこれを二軸延伸することにより、二軸延伸フィルム
が形成される。また、前記樹脂組成物を射出機で溶融混
練した後、射出金型中に射出することにより、容器や容
器製造用のプリフォームを製造する。更に、前記樹脂組
成物を押出機を通して、一定の溶融樹脂塊に押し出し、
これを金型で圧縮成形することにより、容器や容器製造
用のプリフォームを製造する。成形物は、フイルム、シ
ート、ボトル乃至チューブ形成用パリソン乃至はパイ
プ、ボトル乃至チューブ成形用プリフォーム等の形をと
り得る。パリソン、パイプ或いはプリフォームからのボ
トルの形成は、押出物を一対の割型でピンチオフし、そ
の内部に流体を吹込むことにより容易に行われる。ま
た、パイプ乃至はプリフォームを冷却した後、延伸温度
に加熱し、延伸ブロー成形機中に供給し、金型内にセッ
トして、延伸棒の押し込みにより軸方向に延伸すると共
に、流体圧によって周方向に延伸することにより、延伸
ブローボトル等が得られる。延伸ブロー成形されたボト
ルは、それ自体公知の手段で熱固定することもでき、熱
固定はワンモールド法でブロー成形金型中で行うことも
できるし、また、ツーモールド法でブロー成形金型とは
別個の熱固定用金型で行うこともできる。他の延伸ブロ
ー成形としては、本願の出願人に係わる特許第2917
851号公報に例示されるように、パイプ乃至プリフォ
ームを一次ブロー金型を用いて最終ブロー金型成形体よ
りも大きい寸法の一次ブロー成形体とし、次いでこの一
次ブロー成形体を加熱収縮させた後、二次ブロー金型を
用いて用いて二軸延伸ブロー成形を行って最終ブロー成
形体とする二段延伸ブロー成形体が挙げられる。この延
伸ブロー成形よれば、、底部が十分に延伸薄肉化され、
熱間充填、加熱滅菌時の底部の変形、耐衝撃性に優れた
延伸ブロー成形体を得ることができる。更に、また、フ
イルム乃至シートを、真空成形、圧空成形、張出成形、
プラグアシスト成形等の手段に付することにより、カッ
プ状、トレイ状等の包装容器やフィルム乃至シートから
なる蓋材が得られる。
装袋として用いることができ、その製袋は、それ自体公
知の製袋法で行うことができ、三方或いは四方シールの
通常のパウチ類、ガセット付パウチ類、スタンディング
パウチ類、ピロー包装袋などが挙げられるが、この例に
限定されない。
の共押出成形法を用いることができ、例えば樹脂の種類
に応じた数の押出機を用いて、多層多重ダイを用いる以
外は上記と同様にして押し出し成形を行えばよい。ま
た、多層射出成形体の製造には、樹脂の種類に応じた数
の射出成形機を用いて、共射出法や逐次射出法により多
層射出成形体を製造することができる。更に、多層フィ
ルムや多層シートの製造には、押出コート法や、サンド
イッチラミネーションを用いることができ、また、予め
形成されたフィルムのドライラミネーションによって多
層フィルムあるいはシートを製造することもできる。
物の香味低下を防止しうる容器として有用である。充填
できる内容物としては、飲料ではビール、ワイン、フル
ーツジュース、炭酸ソフトドリンク等、食品では果物、
ナッツ、野菜、肉製品、幼児食品、コーヒー、ジャム、
マヨネーズ、ケチャップ、食用油、ドレッシング、ソー
ス類、佃煮類、乳製品等、その他では医薬品、化粧品、
ガソリン等、酸素存在下で劣化を起こしやすい内容品な
どが挙げられるが、これらの例に限定されない。
明はこれらの実施例に制限されるものでない。
60mlのカップ状容器ハイレトフレックス(HR78-84W
東洋製罐(株)製スチール箔/ポリプロピレン積層容
器)に水1ccを入れ、多層フィルムを蓋材として窒素
雰囲気下でヒートシールした。この容器を95℃−30
分のボイル処理を行い、30℃−80%RHにて保管
し、ガスクロマトグラフィー(GC-8AIT、GC-3B
T:共に(株)島津製作所製、検出器:TCD(100
℃)、カラム:モレキュラーシーブ5A(60℃)、キ
ャリアーガス:アルゴン)を用いて、容器内の酸素濃度
を測定した。この酸素濃度から、酸素透過量を計算し
た。
℃に調整した超純水を多層ボトルに15mlのヘッドス
ペースを残し充填した後、キャップを閉め77℃の湯浴
に5分間浸漬した。湯浴より出した充填済みの多層ボト
ルを常温常圧下にて一晩自然冷却した後にボトル内の超
純水を排出し、多層ボトル内に窒素ガスをフローしなが
ら無酸素水を充填し、気泡を混入させずにアルミキャッ
プでシールした。この多層ボトルを55℃にて保管し、
水中溶存酸素濃度計(oxygen indicate
r:orbispherelaboratories)
を用いて、多層ボトル内の水中溶存酸素濃度を測定し
た。
ルムを7cm×5cm(35cm2)に切り出し、内容
積60mlの前記ハイレトフレックス(HR78-84W東洋製
罐(株)製)に入れ、アルミ入り蓋材でヒートシールし
て密封し、23℃または50℃の条件下で保存した。一
定期間保存後ガスクロマトグラフィー(GC-8AIT、
GC-3BT:共に(株)島津製作所製、検出器:TCD
(100℃)、カラム:モレキュラーシーブ5A(60
℃)、キャリアーガス:アルゴン)を用いて、酸素濃度
を測定した。この酸素濃度から、酸素吸収組成物1g当
たりの吸収量を計算し、酸素吸収量とした。
吸収層の引張強さの測定]酸素吸収量を測り終えた単体
の酸素吸収性フィルム、またはボトルの酸素吸収層単体
を、JIS K 7127に順ずる大きさにカットし、5
kgのロードセルを装備したテンシロン(UCT-5T:
(株)オリエンテック製)を用いて引張強さを決定し
た。各サンプルは三重反復実験を実施した。
の分散観察]多層ボトルのパネル部または多層フィルム
より幅3mm、長さ12mmの酸素吸収層を含む試料片
を切り出し、シリコン製の型にてエポキシ樹脂中に埋め
込み固めた。ミクロトームにより酸素吸収層断面を面出
し後、クロロホルム(高速液体クロマトグラフ用特級:
キシダ化学(株)製)で面出し部のみ1時間攪拌洗浄・
12時間乾燥させた後、真空中で1分間、10mAでP
t蒸着し前処理した。走査型電子顕微鏡(JSM-6300F:
日本電子(株)製)で加速電圧を10kVにして前処理
したボトル壁断面を観察した。
キシリレンアジパミド(MXD6)樹脂(T-600:東洋紡
績(株)製、末端アミノ基濃度=87eq/106g)
に遷移金属触媒としてネオデカン酸コバルト(DICANATE5
000:大日本インキ化学工業(株)製)をコバルト量で3
10ppm付着させ、さらに酸化性有機成分としてマレ
イン酸変性ポリブタジエン(M-2000-20:日本石油化学
(株)製)を5重量%含有する樹脂組成物を2軸押出機
により作成した。ラボプラストミル((株)東洋精機製作
所製)にて、上記樹脂組成物より厚み20μmの酸素吸収
性フィルムを作成し、該フィルムの片面にポリエチレン
テレフタレート(PET)フィルム、他面にポリプロピ
レン(PP)フィルムを積層して、12μmPET/酸
素吸収性フィルム/50μmPPからなる多層フィルム
を得た。この多層フィルムを蓋材として前記ハイレトフ
レックスを密封し、95℃−30分のボイル処理を行
い、30℃、80%RHにおいて14日保管後の容器内
への酸素透過量を測定した。さらに、単体の酸素吸収性
フィルムを23℃及び50℃で一定期間保存した後、ガ
スクロマトグラフ装置で酸素吸収を確認し、テンシロン
にて引張強さを測定した。また、多層フィルムから調整
した試料を25000倍で電子顕微鏡により酸素吸収層
を観察した。この結果を表1及び表2に示す。
オデカン酸コバルトをコバルト量で400ppmとする
こと以外はすべて実施例1と同等の条件で多層フィルム
を作成し、容器内への酸素透過量を測定し、酸素吸収性
層を電子顕微鏡で観察した。この結果を表1に示す。
オデカン酸コバルトをコバルト量で400ppm及び酸
化性有機成分として水酸基変性ポリイソプレン(OH-ip)
(Poly ip:出光石油化学(株)製)を3重量%とする
こと以外はすべて実施例1と同様にして多層フィルムを
作成し、容器内への酸素透過量を測定し、酸素吸収性層
を電子顕微鏡で観察した。この結果を表1に示す。
脂(J-125T:三井化学(株)製)に遷移金属触媒として
前記ネオデカン酸コバルトを310ppm(コバルト
量)付着させ、酸化性有機成分として前記マレイン酸変
性ポリブタジエンを5重量%含有する樹脂組成物を2軸
押出機により作成した。上記樹脂組成物より厚み20μ
mの酸素吸収性フィルムを作成し、該フィルムの片面に
PETフィルム、他面にPPフィルムを積層して、12
μmPET/酸素吸収性フィルム/50μmPPからな
る多層フィルムを得た。この多層フィルムを蓋材として
前記ハイレトフレックスを密封し、95℃−30分のボ
イル処理を行い、30℃、80%RHにおいて14日保管
後の容器内への酸素透過量を測定した。また、多層フィ
ルムから調整した試料を実施例1と同様に酸素吸収性層
を電子顕微鏡で観察した。この結果を表1に示す。
オデカン酸コバルトをコバルト量で400ppm及び酸
化性有機成分として前記マレイン酸変性ポリブタジエン
を15wt%とすること以外はすべて実施例1と同様に
して多層フィルムを成形したが、製膜することができ
ず、酸素透過量は測定できなかった。
オデカン酸コバルトをコバルト量で200ppm及び酸
化性有機成分を配合しないとすること以外はすべて実施
例1と同様にして多層フィルムを作成し、容器内への酸
素透過量を測定した。この結果を表1に示す。
とすること以外はすべて実施例1と同等の条件で多層フ
ィルムを作成し、容器内への酸素透過量を測定した。こ
の結果を表1に示す。
オデカン酸コバルトをコバルト量で800ppm及び酸
化性有機成分を配合しないとすること以外はすべて実施
例1と同様にして多層フィルムを作成し、容器内への酸
素透過量を測定した。この結果を表1に示す。
タジエン(B-2000:日本石油化学(株)製)を5重量%配
合すること以外はすべて実施例1と同様にして単体の酸
素吸収性フィルムを成形したが、製膜することができ
ず、酸素透過量は測定できなかった。
樹脂(6007:三菱瓦斯化学(株)製、末端アミノ基濃度
=27eq/106g)に前記ネオデカン酸コバルトをコ
バルト量で400ppm付着させ、酸化性有機成分を配
合しない点を除いてすべて実施例1と同様にして単体の
酸素吸収性フィルムを作成し、50℃において7日保管
後、このフィルムの酸素吸収量を測定し、テンシロンに
て引張強さを測定した。この結果を2に示す。
で使用したMXD6樹脂に遷移金属触媒として前記ネオ
デカン酸コバルトをコバルト量で310ppm付着さ
せ、酸化性有機成分として前記マレイン酸変性ポリブタ
ジエンを5重量%含有する樹脂組成物を2軸押出機によ
り作成した。PETを内外層用射出機、上記樹脂組成物
を中間層用射出機に供給して、射出ノズルの温度を28
0℃、樹脂圧力250kgf/cm2の条件で射出金型
内に共射出成形して、目付量が32g、中間層の容積率
が6%である2種3層プリフォームを成形した。このプリ
フォームを二軸延伸ブロー成形して内容量が500ml
の2種3層の多層ボトルを得た。この多層ボトルを55
℃、28日で保存した後、容器内の溶存酸素濃度を測定
した。また、この多層ボトルから酸素吸収した酸素吸収
層を取り出し、テンシロンにて引張強さを測定した。こ
の結果を表3及び表4に示す。
で使用したMXD6樹脂に前記ネオデカン酸コバルトを
コバルト量で400ppm付着させ、酸化性有機成分を
配合しない点を除いてすべて実施例5と同様にして多層
プリフォーム及び多層ボトルを作成し、このボトルを5
5℃、28日で保存した後、容器内の溶存酸素濃度を測
定した。また、この多層ボトルより酸素吸収した酸素吸
収層を取り出しテンシロンにて引張強さを測定した。こ
の結果を表3及び表4に示す。
性重合体及び遷移金属触媒を配合した樹脂組成物からな
る酸素吸収層を設け、前記熱可塑性樹脂が遷移金属触媒
の存在下でも実質上酸化されないようにしたことによ
り、酸化性重合体の酸化による酸素吸収が選択的に行わ
れ、その結果として、優れた酸素吸収性を有すると共
に、酸素吸収層を通しての酸素透過を長期にわたって低
減させることが可能となり、包装材料の強度も優れたレ
ベルに維持することができる。
Claims (11)
- 【請求項1】 熱可塑性樹脂に酸化性重合体及び遷移金
属触媒を配合した樹脂組成物からなる酸素吸収層を有
し、熱可塑性樹脂が遷移金属触媒の存在下において実質
上酸化されないことを特徴とする多層包装材料。 - 【請求項2】 熱可塑性樹脂の酸素透過係数が、7cc・
mm/m2・day・atm(20℃、0%RH)以下である請求
項1に記載の多層包装材料。 - 【請求項3】 熱可塑性樹脂が、キシリレン基含有ポリ
アミドである請求項1または2に記載の多層包装材料。 - 【請求項4】 酸化性重合体が、側鎖または末端に極性
基を有する分子量100乃至10000の樹脂である請
求項l乃至3の何れか1項に記載の多層包装材料。 - 【請求項5】 熱可塑性樹脂の溶解度指数(SP)が
9.5以上であり、酸化性重合体が酸乃至酸無水物変性
のポリブタジエンである請求項1乃至4の何れか1項に
記載の多層包装材料。 - 【請求項6】 酸化性重合体を樹脂組成物中に0.01
乃至10重量%配合した請求項1乃至5の何れかl項に
記載の多層包装材料。 - 【請求項7】 酸化性重合体が熱可塑性樹脂中で粒状あ
るいは紡錘状に分散しており、その分散体の最小長さが
400nm以下である請求項1乃至6の何れか1項に記
載の多層包装材料。 - 【請求項8】 酸素吸収層に、遷移金属触媒が金属量換
算で少なくとも300ppm配合されている請求項1乃
至7の何れか1項に記載の多層包装材料。 - 【請求項9】 酸素吸収後の酸素吸収層の強度が2.0
kgf/mm2以上を保持している請求項1乃至8の何れか1
項に記載の多層包装材料。 - 【請求項10】 酸素吸収層の両側に耐湿性熱可塑性樹
脂層を設けている請求項1乃至9の何れか1項に記載の
多層包装材料。 - 【請求項11】 酸素吸収層の熱可塑性樹脂の融点Tm
1と、その両側の耐湿性熱可塑性樹脂層の融点Tm2との
関係が、|Tm2一Tml|≦50℃を満足している請求
項l乃至l0の何れか1項に記載の多層包装材料。