JP2000181130A - トナ―および／またはトナ―混合物 - Google Patents
トナ―および／またはトナ―混合物Info
- Publication number
- JP2000181130A JP2000181130A JP35466999A JP35466999A JP2000181130A JP 2000181130 A JP2000181130 A JP 2000181130A JP 35466999 A JP35466999 A JP 35466999A JP 35466999 A JP35466999 A JP 35466999A JP 2000181130 A JP2000181130 A JP 2000181130A
- Authority
- JP
- Japan
- Prior art keywords
- toner
- al2o3
- sio2
- silicon dioxide
- pyrolysis method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 卓越した性質を有するトナーおよび／または
トナー混合物。 【解決手段】 場合により表面変性されていてよい熱分
解法により製造される酸化アルミニウム−二酸化ケイ素
混合酸化物を含有しているトナーおよび／またはトナー
混合物。
トナー混合物。 【解決手段】 場合により表面変性されていてよい熱分
解法により製造される酸化アルミニウム−二酸化ケイ素
混合酸化物を含有しているトナーおよび／またはトナー
混合物。
Description
【０００１】
【発明の属する技術分野】本発明は、トナーおよび／ま
たはトナー混合物に関する。
たはトナー混合物に関する。
【０００２】
【従来の技術】欧州特許第０５８５５４４号明細書から
は、火炎加水分解法により製造され、Ａｌ2Ｏ3 ６５〜
７２．１質量％およびＳｉＯ2 ２７．９〜３５質量％の
組成を有し、かつＢＥＴ表面積２０〜２００ｍ2／ｇを
有する非晶質構造の粉末状ケイ素−アルミニウム混合酸
化物が公知である。
は、火炎加水分解法により製造され、Ａｌ2Ｏ3 ６５〜
７２．１質量％およびＳｉＯ2 ２７．９〜３５質量％の
組成を有し、かつＢＥＴ表面積２０〜２００ｍ2／ｇを
有する非晶質構造の粉末状ケイ素−アルミニウム混合酸
化物が公知である。
【０００３】
【発明が解決しようとする課題】ところで、この方法に
より製造された混合酸化物ならびに以下に記載された方
法により表面変性された種類は、トナー添加物として卓
越した性質を有することが示された。
より製造された混合酸化物ならびに以下に記載された方
法により表面変性された種類は、トナー添加物として卓
越した性質を有することが示された。
【０００４】
【課題を解決するための手段】本発明の対象は、熱分解
法により製造される酸化アルミニウム−二酸化ケイ素混
合酸化物を含有していることにより特徴付けられるトナ
ーおよび／またはトナー混合物である。
法により製造される酸化アルミニウム−二酸化ケイ素混
合酸化物を含有していることにより特徴付けられるトナ
ーおよび／またはトナー混合物である。
【０００５】熱分解法により製造される酸化アルミニウ
ム−二酸化ケイ素混合酸化物として、好ましくは、刊行
物の欧州特許出願公告第０５８５５４４号明細書に記載
されている公知のＡｌ2Ｏ3／ＳｉＯ2混合酸化物が使用
されてよい。
ム−二酸化ケイ素混合酸化物として、好ましくは、刊行
物の欧州特許出願公告第０５８５５４４号明細書に記載
されている公知のＡｌ2Ｏ3／ＳｉＯ2混合酸化物が使用
されてよい。
【０００６】本発明の別の実施態様において、Ａｌ2Ｏ3
／ＳｉＯ2混合酸化物は、Ａｌ2Ｏ3６５±５質量％およ
びＳｉＯ2 ３５±５質量％のＡｌ2Ｏ3：ＳｉＯ2比を有
していてよい。
／ＳｉＯ2混合酸化物は、Ａｌ2Ｏ3６５±５質量％およ
びＳｉＯ2 ３５±５質量％のＡｌ2Ｏ3：ＳｉＯ2比を有
していてよい。
【０００７】本発明の別の実施態様において、熱分解法
により製造されたＡｌ2Ｏ3／ＳｉＯ 2混合酸化物は、表
面変性されていてよい。表面変性は、刊行物の欧州特許
出願公告第０７２２９９２号明細書による公知方法で行
われてよい。
により製造されたＡｌ2Ｏ3／ＳｉＯ 2混合酸化物は、表
面変性されていてよい。表面変性は、刊行物の欧州特許
出願公告第０７２２９９２号明細書による公知方法で行
われてよい。
【０００８】本発明によるトナーおよび／またはトナー
混合物は、次の利点を有する：応用技術的な利点は、ト
ナー粉末中の熱分解法による疎水性混合酸化物の使用の
際に、次の通りである： ・ トナー粉末のより良好な流動性 ・ トナーのより安定な電荷挙動（迅速な電荷保持性、
より高い電荷、時間経過後の一定の電荷）
混合物は、次の利点を有する：応用技術的な利点は、ト
ナー粉末中の熱分解法による疎水性混合酸化物の使用の
際に、次の通りである： ・ トナー粉末のより良好な流動性 ・ トナーのより安定な電荷挙動（迅速な電荷保持性、
より高い電荷、時間経過後の一定の電荷）
【実施例】例１ Ａｌ2Ｏ3／ＳｉＯ2混合酸化物の製造を以下のようにし
て行う：欧州特許第０５８５５４４号明細書の実施例１
に記載されている公知のバーナー配列に従って、核水素
(Kernwasserstoff)または反応水素(Reaktionswassersto
ff)１．４Ｎｍ3／ｈを空気５．５Ｎｍ3／ｈおよび予め
蒸発させたＳｉＣｌ4 １．３０ｋｇ／ｈと一緒に混合す
る。この約２００℃の熱混合物中に、更に、ガス状Ａｌ
Ｃｌ3 ２．３４ｋｇ／ｈ（予め約３００℃で蒸発させ
た）を付加的に供給する。得られた混合物を炎管中で燃
焼させ、その際、これらの炎管中に、付加的に空気１２
Ｎｍ3／ｈを供給する。
て行う：欧州特許第０５８５５４４号明細書の実施例１
に記載されている公知のバーナー配列に従って、核水素
(Kernwasserstoff)または反応水素(Reaktionswassersto
ff)１．４Ｎｍ3／ｈを空気５．５Ｎｍ3／ｈおよび予め
蒸発させたＳｉＣｌ4 １．３０ｋｇ／ｈと一緒に混合す
る。この約２００℃の熱混合物中に、更に、ガス状Ａｌ
Ｃｌ3 ２．３４ｋｇ／ｈ（予め約３００℃で蒸発させ
た）を付加的に供給する。得られた混合物を炎管中で燃
焼させ、その際、これらの炎管中に、付加的に空気１２
Ｎｍ3／ｈを供給する。
【０００９】炎管の通過後に、生じた粉末をフィルター
またはサイクロン中で、塩酸含有ガスから分離する。付
着した塩酸残留物を、高められた温度で処理することに
より生じた混合酸化物から分離する。
またはサイクロン中で、塩酸含有ガスから分離する。付
着した塩酸残留物を、高められた温度で処理することに
より生じた混合酸化物から分離する。
【００１０】混合酸化物は、次の分析データを有する：
ＢＥＴ比表面積７４ｍ2／ｇ、４％分散液のｐＨ値４．
４９、嵩密度４６ｇ／ｌ、突固め密度５６ｇ／ｌ。粉末
の組成：Ａｌ2Ｏ3 ６５質量％、ＳｉＯ2 ３５質量％。
ＢＥＴ比表面積７４ｍ2／ｇ、４％分散液のｐＨ値４．
４９、嵩密度４６ｇ／ｌ、突固め密度５６ｇ／ｌ。粉末
の組成：Ａｌ2Ｏ3 ６５質量％、ＳｉＯ2 ３５質量％。
【００１１】例２ 混合酸化物の表面変性を欧州特許出願公開第０７２２９
９２号明細書に記載されているようにして行う：混合酸
化物６００ｇを、鋤刃型ミキサー(Pflugscharmischer)
中に装入し、混合しながら最初に蒸留したＨ2Ｏ ３０
ｇ、引続きＨＭＤＳ（ヘキサメチルジシラザン）９０ｇ
を噴霧する。その後、１５分間さらに混合し、引続き反
応混合物を１４０℃で３時間乾燥オーブン中で乾燥させ
る。
９２号明細書に記載されているようにして行う：混合酸
化物６００ｇを、鋤刃型ミキサー(Pflugscharmischer)
中に装入し、混合しながら最初に蒸留したＨ2Ｏ ３０
ｇ、引続きＨＭＤＳ（ヘキサメチルジシラザン）９０ｇ
を噴霧する。その後、１５分間さらに混合し、引続き反
応混合物を１４０℃で３時間乾燥オーブン中で乾燥させ
る。
【００１２】生成物の物理化学的データは、次の通りで
ある：
ある：
【００１３】
【表１】
【００１４】例３ 上記のＡｌ2Ｏ3／ＳｉＯ2混合酸化物１．８ｋｇを混合
機中に装入し、混合しながらシリコーンオイル０．２７
ｋｇを噴霧し、引続き１５分間、後撹拌し、その後３０
０℃で２時間、Ｎ2雰囲気下で温度処理にかける（流動
床）。 物理化学的データ 突固め密度［ｇ／ｌ］： １０６ ＢＥＴ表面積［ｍ2／ｇ］： ５７ ｐＨ値： ４．２ Ｃ含有量［％］： １．３ 乾燥損失［％］： ０．２ 灼熱減量［％］： １．６
機中に装入し、混合しながらシリコーンオイル０．２７
ｋｇを噴霧し、引続き１５分間、後撹拌し、その後３０
０℃で２時間、Ｎ2雰囲気下で温度処理にかける（流動
床）。 物理化学的データ 突固め密度［ｇ／ｌ］： １０６ ＢＥＴ表面積［ｍ2／ｇ］： ５７ ｐＨ値： ４．２ Ｃ含有量［％］： １．３ 乾燥損失［％］： ０．２ 灼熱減量［％］： １．６
───────────────────────────────────────────────────── フロントページの続き (72)発明者 ヘルムート マンゴルト ドイツ連邦共和国 ローデンバッハ イン デア ガルテル ２ (72)発明者 ユルゲン マイヤー ドイツ連邦共和国 シュトックシュタット グロースオストハイマー シュトラーセ 51
Claims (5)
- 【請求項１】 トナーおよび／またはトナー混合物にお
いて、熱分解法により製造された酸化アルミニウム−二
酸化ケイ素混合酸化物を含有していることを特徴とす
る、トナーおよび／またはトナー混合物。 - 【請求項２】 熱分解法により製造された酸化アルミニ
ウム−二酸化ケイ素混合酸化物が表面変性されている、
請求項１記載のトナーおよび／またはトナー混合物。 - 【請求項３】 表面変性がヘキサメチルジシラザンによ
り生じている、請求項２記載のトナーおよび／またはト
ナー混合物。 - 【請求項４】 表面変性がシリコーンオイルにより生じ
ている、請求項２記載のトナーおよび／またはトナー混
合物。 - 【請求項５】 表面変性がＤ４（＝オクタメチルシクロ
テトラシロキサン）により生じている、請求項２記載の
トナーおよび／またはトナー混合物。