HUE033457T2 - Nagy szilárdságú és hajlításálló lamella szalag - Google Patents
Nagy szilárdságú és hajlításálló lamella szalag Download PDFInfo
- Publication number
- HUE033457T2 HUE033457T2 HUE07118217A HUE07118217A HUE033457T2 HU E033457 T2 HUE033457 T2 HU E033457T2 HU E07118217 A HUE07118217 A HU E07118217A HU E07118217 A HUE07118217 A HU E07118217A HU E033457 T2 HUE033457 T2 HU E033457T2
- Authority
- HU
- Hungary
- Prior art keywords
- strip
- alábbi
- brazing
- mpa
- une
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/008—Continuous casting of metals, i.e. casting in indefinite lengths of clad ingots, i.e. the molten metal being cast against a continuous strip forming part of the cast product
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
- B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
- B23K35/0233—Sheets, foils
- B23K35/0238—Sheets, foils layered
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/016—Layered products comprising a layer of metal all layers being exclusively metallic all layers being formed of aluminium or aluminium alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F28—HEAT EXCHANGE IN GENERAL
- F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
- F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
- F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F28—HEAT EXCHANGE IN GENERAL
- F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
- F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
- F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
- F28F21/081—Heat exchange elements made from metals or metal alloys
- F28F21/084—Heat exchange elements made from metals or metal alloys from aluminium or aluminium alloys
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2101/00—Articles made by soldering, welding or cutting
- B23K2101/04—Tubular or hollow articles
- B23K2101/14—Heat exchangers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
- B23K35/24—Selection of soldering or welding materials proper
- B23K35/28—Selection of soldering or welding materials proper with the principal constituent melting at less than 950 degrees C
- B23K35/286—Al as the principal constituent
Claims (6)
- ΗΛΟΥ SZILÁRDSÁGÚ éS HAJÜTÀSÂU..Ô LAMELLA SZALAG SI»áaiM! kilnypoaioE L líajlílásáibi szalag, aminek eUjslIMm&M» %) olvadékot o>L5% Sí, < C;,S% Fíí, - , 03% C a LO-%0% && < ö,?% Mg, még ekmvösdítiea < 03¾ <4,Ö%Z», <03% Ni. ^ Ο,'}"« diszpergálö etem a ÍVb. Vb és Vlb csopurtOAI, valannnt szennyezők eg>e»^^ 0.05%-ban, összesen legfeljebb őj5%-han. és a maradék alumínium, és ebből tuskó? &>ΙίΐΜΡ*> ΟΛ b) à wskôi előmelegítjük S.^C-oál alacsonyabb Itőtnérsékletfe, előnyös«« 100 - S2(tt< S^F «lőnyósehben 450 - $20'C közé. speciálisan 470 - 520ÖC közé. ditsZjpierg^? sé^Vklvk előállításához: e) ;nelegh««gerléssel szalagot ál Hiúnk elén ij a c) lépésben »yen «alagút hulegen hangeretpfc legalább :¾¾¾¾ ;i$Őáyőá«n. ?Ő^^U**jPöbb idles redukcióval a íuiyásfeatár eg> első értékének eióráséigi é) majd Hőkezelést végiünk « szállítási óllapos eléréséig íp Μβί$^ egy második értékéig a szalag Összetevőinek, ùjs^knsiâifokbi^sp stéiklÉ -4 tő^fábátáí snasoikk írséke 10· 50%-d, előnyösen 15 40%-al aiaesoay&bb, snmtsv dsA íblyáshsiár értéke kő/vetlendl a 0? lépésben végzés bldeginmger}#' utf& Η$$φ$&9,0% Hin ·· 200 Mpa, előnyösen 120 180 ktpa, még elo»vő!íeW^A^0---rl|Í0'-:tsi^:a^í· •á. hájiltásnlló síd a g hcijiltás« ellenáll,tsa 0,10 mm vastagságú szalagot; me$ygS2%spip, és lésa« feszültség érseke 0,2% iblyáshatar tartományban ihftásai;: ásás; legalább <>0 kip.
- 2, Az I. lgén>ptmi szerint; baj Ütésálló szalag legalá 97,5%. redukcióval vegzeií': éíő&iUívií. % Az előző igévé, pontok öánnely-ke szerint* Mitásállö szalag közmiLö tekősztallizálo k-varis nélkül sóföálfttva, ahol nz. anyag vastagsága 90%-íKíí om-yobb mértékben leit csökkentve is d) lépésben végzet! biöegfíengorlés során.
- 4, Az eibzb igénypontok bármelyike s»M hapOáséliA szalag m #1Âk bssgStdéig tíKndékböí eföállitva: 0,5'UI % Si. előnyösen 0t6s-0,0.S% Si, •%U% Pe, <0,1 % Γη, Ν3-1 :1:3-13¾¾ Mîi, kiJf&Mg, Zfk#!$bÿbfl$:iy S. xx ' \<' '\5Λ - oK *>í«'í Mkc xoxu * sí s :-k u s gas. j. p ' « >v , mtmu oo mAboi ölik] I ís v fi V amSnsk Zn : tab alma m >'W íSíí 2,0'brkímosrmm Az d<vb ígénypomok hérmvlyike %m*&i ΐ»<$ΜχόΜό ,.,'ahg «gy olyan íWmétaiü ob?*Äliit ddáHIwa» aminek Snbssmima k^ebb, ín·»* 0,0!%%,
- 7. X V sxvo i -.pm so\ kp ne 7-t 'e n t ph ,.-<'! a«' ! u* \o κ v? né >x '%-<w! .s dx;/pes'%k ív:-Όííic^¢:¾.ΐ:i';iï-Èΐί >7 4 GO nm áSmcrb tâbomâsi>h;m ! és ,?0 x lö'; donxOses; %< «s 10 χ x íí tvyA, A * χ ' Us*tx^«xk s )' χ0< «Μ $. An v Kv'.é béaypoíiUik barmdjiU ,Xíxim1 hajlitassiíó siaksS.. msdskO végsd vaskorn^m kisebb. rrnm Oghmm Cdny ks-iss U, ! 5(s;;s A rtég előnyösebbe ojmpi. 9. xz ddüb î;K syposïSok bdrmelj ikv szxolml h;sîlk;xdOI6 s^dwg, ami kgalább egy jmxdékoà bevonïiïïèmggid -vsa kiásva. 10 Λ ο, kestxpom χ»mb MktéOskó xssksg, aminek ymdAm, bx'vxmatídege ftxsraatamyag Π Λ o g mg pom x."*.f.ïHi hyhiMdkx eádag, mernek jdiGékxx bmrnmmkge keteskx-xkdms m-/msapt sKmmbum fiivöixíi. 12. à 0. Igánypom szerinti hatlitife&Mô k*dag, aminek **·:$£Φ* a I !.s » s s ; s s om bt V d/χ; s, \ ' X' l'Uxïb η,χ a prmmk Oxs sxixkx i% Nxmmsx Ο-χΟρχί,-.ΟΙο x<mbs<\ ammx'k hdxoaimx&î x'tteke O 2% tevs *c-xmbskg íattmnánybas Íbixm.dáí. okéi iegd&bb ?0 Mpté H d. skvd i\\v!sxg>tiitok be ms-hike x>eum> bajibasalbx χ. dop, ammxk baOikki dkmaiks«x AO mm, cktoyfaen p'Mmm, ÖJO mm v&stafx&agxt sealagm, ötérv% IS, Ht$h íáxáiib szalag. aminek dxVáUtüisa sora» aj olvadékot áOGxmk dó áss alábbi öásaetetslbe«; í.U-hMáSg Vök'. <n:)% Cm i,k,2,o% Mm ' sk5 - kU V mag ΌΟηχχχχχΟΟ m 0, IS Ό,Ο': * Zm ; 0,Hsv díXípxrgálO elem ο VIfe. Vb M Vib csnporäbOi, vdamini x?«nnyezOíí egyenként 0'gKOjehb 0,05*1 a-ban Osssexv n kgh'beb'' Π . x'Vban, x » a m.«mtek aiumxnmuk os ebbói tuakdt xUaunk x io, bí ,s Rí kot COírnk$mmk ssO'i'-sxsi aücvonx^bb itbmO'w'kktn', vkx ó%ks> ss'O xCV-í ''•P/a n>e« Jwx-x' ,'bK'» Oxo n\»\ Kb x xjKMahvm Ssä , «.gob.' kb,% dl&^etgíHi fxHí.eíkksI; akyOkásiáhiX?: a * mek yhsiiyk'x uS,cl s*',sbxgaä sllkoíík i k'· ti a c) ièîîésben ajeit szalagot iddeges l-.engs.'fdjUlx legalább W·«,, oiór>>'0keo7tM%tiál tisgyöbb togex u-íhikenxvai így tsisö taiy-yhsíáí érték ek-imsk-g; #} *OÜd lOteáfM vgplipk asMplMl álláp«! νΜΜΜΜISSSgÿ kliâgggMk M Sgk&gcsl: «gy slfefàlk IMyishálár êOsk á|éi4sálg » s&Oag -i##!, ship a màAsillk folyásai#-|rt#ö.· H) - SöM-sk «ISiySsgis i§ ·· 40%-árs!sö;íóftyapk mißt -M : átsS folykMMM érték® koaváögptó s il) Mpgspso vêgaon tiOegMfgpsl# gsâp5 M lMöäSä«ylsSs UK) "200 Mp», »kMvMkP 120 - MO Mp, «Ság ëi»OÿOspkl>»p 140 - MO Mp» IP;:. A 1 S. Igáfgpöfí svví-v»í Milí-Maliá svakig !ág»!s!i> ;H.$%. MOMkOípvIl vvgv»« IsMegMagariiAssO MMflltv:«,
- 12, Ág elAgO igályplilpk Iginfelylká spgíípO ipylflâMllô säplsg köylMtsö Mkïfe®0002àip igklOis isiSkO! álMÓfsgg »Ois! as: äfygg vâkSàgsèg» MOkksplve a 4} ligádé» vágáSSi OMágheogerlOs »<>:»» MO .A SS. - lf, igpsiypoßSOk pMmeiyÁe MsHpil ha|lpM»lM |ga!»g g» al|febi AssMMOOP MvaáákPol glOâllflva: O.SMJHM. MU% P», Μ01%ίΜ< 1JMJ14 Μρ,ΜΟονΟΜΙ M-UMMa, • 0 J :H: Mg. 0.05-0,2% 22, eïùnyOiën4,! 0:,2¾22 kOsipli 10: A 10 - IM :!ρ4ϊ%ίΜ«Κί| bâMiglysk® MeiipO Olglfásáljd gsMôg: Pgp ôlÿafl iMMláMSO OlvgOPkii! sMáJMOa, agliek ko Of%k«« 0,S èv3J% kögfll vais. 20; A M - 1Ô, Mrmalyltó szprmp IsMiltMollô salag: ágy ollM» «»MâlâMSO íslyadglsAöl elöÓllffíO gafOsk $4 SgilsJlA klMOp:i ifff 0,800ό&,
- 21, A il· 20, itósypöpsok MftMyik« sgsHssO kajlftasálfis ygslsg,. »isä;0»p vMIlOM? AsfMfyMgsM g 4i5:í|>»fgák s»gm»sMíMiság 40 .. gpp piTvapgpm laAOOliMykag 1 ás:20 y Ui\ alpsvösg«: !,3 0» iö y ! if, «sag slOóyöáalsMo 1Μ Μ Τ§ο SO* MsmmIM osor kőapg: vág, 2;2; Á Μ - 21, IggoYgOSSiOk Mfssslylk» spmui: SggSÄtSJf «bipljg·νίρ|·"^1^ί^8' Mf#&? foil !Í::2öpi, «pwösáo 0, 1 Sospi M ?o0i á!Olyös#báf íUasns. 22, A 12: ' 22, igggypvssosik MptsOlvte sVeof! hájilásállO: M»alag, aiTloek s;lpgPiasí gsrástMáMf így valóak salPälj'ögväi losgy » loSyssialii' áfák» 0,2% tpMl Jgsgüitság: isoiolsapglsl lomisatáá 4M» MgaSáOi 20 Mis Igyvs. 24:, é Μ- 23, ägloyisplpsk MnSglylk« sMlIflkisplsMIlO säsläg^ flfflál: ,1¾¾ douyásvn :2Sosos: 4,10 ns4> váslsgMgÓ sáslsgöl AMáv®, 33; A 15 " 24, IglflPfOlM: lán«»lyík« »aallfOs lgllilisállO slslsg, amfoák faplllsi »llépéBásá Apö ils·:, lilpypsg 1 s;l ;Sfüp, Ö, 10 pfö vssiagälgäl 4:MSlgl4 ifárvs-