GB824089A - Improvements in or relating to coating with metals - Google Patents

Improvements in or relating to coating with metals

Info

Publication number
GB824089A
GB824089A GB37098/55A GB3709855A GB824089A GB 824089 A GB824089 A GB 824089A GB 37098/55 A GB37098/55 A GB 37098/55A GB 3709855 A GB3709855 A GB 3709855A GB 824089 A GB824089 A GB 824089A
Authority
GB
United Kingdom
Prior art keywords
nickel
alloy
areas
masking
phosphorus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB37098/55A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General American Transportation Corp
Original Assignee
General American Transportation Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General American Transportation Corp filed Critical General American Transportation Corp
Publication of GB824089A publication Critical patent/GB824089A/en
Expired legal-status Critical Current

Abstract

A non-metallic body is coated first with a nickel-phosphorus alloy containing 5-11% phosphorus, and then with copper. Thus a printed circuit may be made by (a) coating an insulating base with nickel-phosphorus alloy by deposition from an aqueous chemical plating bath of the nickel cation-hypophosphite anion type, (b) masking the areas of alloy on which no conductor is desired, (c) electrodepositing a layer of copper on the unmasked areas, and (d) removing the masking material and the areas of alloy masked thereby. Preferably the insulating base consists of textile-reinforced phenolformaldehyde condensation resin, and is prepared for nickel plating by being provided (i) with dispersed palladium particles to act as catalyst, and (ii) with a nickel strike from the strike bath disclosed in Specification 824,090 [Group II]. Heat treatment at 325 DEG F. preferably follows the nickel plating. Masking may be achieved by a conventional silk screen technique. Specifications 761,062, 761,556, 761,567, 785,693, 785,694, 785,695, 785,696 and 786,175 also are referred to.
GB37098/55A 1954-12-31 1955-12-28 Improvements in or relating to coating with metals Expired GB824089A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US824089XA 1954-12-31 1954-12-31

Publications (1)

Publication Number Publication Date
GB824089A true GB824089A (en) 1959-11-25

Family

ID=22171022

Family Applications (1)

Application Number Title Priority Date Filing Date
GB37098/55A Expired GB824089A (en) 1954-12-31 1955-12-28 Improvements in or relating to coating with metals

Country Status (2)

Country Link
FR (1) FR1152563A (en)
GB (1) GB824089A (en)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3769179A (en) * 1972-01-19 1973-10-30 Kewanee Oil Co Copper plating process for printed circuits
US4190474A (en) * 1977-12-22 1980-02-26 Gould Inc. Method of making a printed circuit board having mutually etchable copper and nickel layers

Also Published As

Publication number Publication date
FR1152563A (en) 1958-02-20

Similar Documents

Publication Publication Date Title
GB929799A (en) Improvements in or relating to electroless metal deposition
GB1247706A (en) Process for forming a conductive layer upon an insulating substrate
ES431240A1 (en) Electrodeposition on non-conductive surfaces
GB1094549A (en) Improvements in and relating to radioactive particles and their production
GB824089A (en) Improvements in or relating to coating with metals
US2940018A (en) Printed electric circuits
GB1095080A (en) Preparation of a non-conductive material for electroplating with copper
JPS5713165A (en) Paste of activating metallic material for electroless plating and plating method using said paste
ES254803A1 (en) Method of making printed circuits
GB892451A (en) Improvements in and relating to the manufacture of printed circuits
GB810818A (en) Improvements in or relating to processes for electrolytically coating metals with a platinum layer
GB758764A (en) Method of coating the surface of a refractory material with an electro-conductive material
JPS5534601A (en) Metalizing material and its manufacture
JPS5521536A (en) Method of forming partial nickel layer
GB809247A (en) A method of electroplating non-conductive material
GB806977A (en) Improvements in printed circuits
GB850468A (en) Improvements in or relating to electro-deposition
JPS5713164A (en) Paste of activating metallic material for electroless plating and plating method using said paste
GB640323A (en) Metal film resistor
JPS5266374A (en) Galvanization of non electrolytic nickel for semiconductor substrate
NL153945B (en) PROCESS FOR THE PREPARATION OF AN ELECTROLYTIC SOLUTION, AND THE USE OF THIS SOLUTION IN THE ELECTROLYTIC DEPOSIT OF GOLD ON A SUBSTRATE, AND THE SUBSTRATES OBTAINED THEREOF, COATED WITH A GOLD COATING.
Johnson A Study of Some Variables Affecting the Corrosion Resistance of Engineering Electroless Nickel Coatings.(Pamphlet)
GB1175832A (en) Improvements relating to the production of an Electrical Conductor Adhering to an Insulating Support
GB554370A (en) Improvements in the metallic coating of articles
GB1473223A (en) Circuit board blanks