FI109032B - Austenitiskt rostfritt stål med goda egenskaper och hög strukturell stabilitet och användningar av detsamma - Google Patents
Austenitiskt rostfritt stål med goda egenskaper och hög strukturell stabilitet och användningar av detsamma Download PDFInfo
- Publication number
- FI109032B FI109032B FI944908A FI944908A FI109032B FI 109032 B FI109032 B FI 109032B FI 944908 A FI944908 A FI 944908A FI 944908 A FI944908 A FI 944908A FI 109032 B FI109032 B FI 109032B
- Authority
- FI
- Finland
- Prior art keywords
- stainless steel
- manufacture
- chemical composition
- good
- steel
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C30/00—Alloys containing less than 50% by weight of each constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Heat Treatment Of Steel (AREA)
- Laminated Bodies (AREA)
- Catalysts (AREA)
- Pens And Brushes (AREA)
- Electroplating Methods And Accessories (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Physical Vapour Deposition (AREA)
- Heat Treatment Of Articles (AREA)
Claims (11)
1. Rostfritt austenitiskt stäl med goda mekaniska egenskaper, god korrosionsbeständighet och god strukurell 5 stabilitet, kännetecknat därav, att dess ke-miska sammansättning beräknat pa vikten är 23 % < Cr < 28 % 15 % < Ni < 28 % 0,5%<Mn<6% 10 0 % < Cu < 5 % 0 % < C < 0,06 % 0 % < Si < 1 % 0%<Nb<0,5% 0 % < V < 0,5 % 15 0 % < AI < 0,1 % 3 % < Mo < 8 % 0,35 % < N < 0,8 % 1 % < W < 5 % varvid den resterande delen utgörs av järn och förorening-20 ar som hänför sig till framställningen.
2. Rostfritt stäl enligt patentkrav 1, k ä n n e-t e c k n a t därav, att dess kemiska sammansättning beräknat pä vikten är ,Τ: 23 < Cr < 26 % ·:· 25 21 % < Ni < 23 % ,:. 2 % < Μη < 3,5 % ]·’;*. 1 % < Cu < 2 % o % < C < 0,03 % 0 % < Si < 0,4 % 30 0 % < Nb < 0,5 % ·;·’ 0 % < AI < 0,1 % ·:·*’: 4,5%<Mo<6,5% ! ·:··; 0,4 % < N < 0,55 % I . 2 % < W < 3,5 % 35 varvid den resterande delen utgörs av järn och förorening-ar som hänför sig tili f ramställningen. 109032
3. Rostfritt stäl enligt patentkrav 1 eller 2, kännetecknat därav, att dess kemiska samman-sättning uppfyller följande förhällande: CP = 20 x % Cr + 0,3 x % Ni + 30 x % Si + 40 x % Mo + 5 x 5 % W + 10 x % Mn + 50 x % C - 200 x % N < 710.
4. Rostfritt stäl enligt patentkrav 3, kännetecknat därav, att dess kemiska sammansättning uppfyller följande förhällande: PRENW = % Cr + 3,3 x%Mo+ 1,6 x % N + 1,7 x % W > 47.
5. Rostfritt stäl enligt patentkrav 4, kännetecknat därav, att dess kemiska sammansättning uppfyller följande förhällande: 113 + 16 (% Mo + 0,7 % W) + 525 % N > 420.
6. Användning av rostfritt stäl enligt nägot av 15 patentkraven 1-5 för framställning av massiva delar.
7. Användning av rostfritt stäl enligt nägot av patentkraven 1-5 för framställning av utrustning avsedd för oijeplattformer.
8. Användning av rostfritt stäl enligt nägot av 20 patentkraven 1-5 för framställning av utrustning avsedd för kemiska fabriker, pappersmassafabriker, hydrometallur- • · giska anläggningar och reningsanläggningar. » * ·
9. Användning av rostfritt stäl enligt nägot av : patentkraven 1-5 för framställning av behällare avsedda ··· 25 för transport av korroderande produkter.
• 10. Användning av rostfritt stäl enligt nägot av » i · · patentkraven 1-5 för framställning av fartygsskrov.
11. Användning av rostfritt stäl enligt nägot av . patentkraven 1-5 för framställning av skiktplätar, som J I · I I 30 bestär av ett skikt av ett stäl enligt föreliggande • » ·;·* uppf inning och ett skikt av strukturstäl. i · « * * « * ·