EA201401136A1 - Стальной лист с покрытием для катодной протекторной защиты, способ изготовления детали с использованием такого листа и полученная этим способом деталь - Google Patents
Стальной лист с покрытием для катодной протекторной защиты, способ изготовления детали с использованием такого листа и полученная этим способом детальInfo
- Publication number
- EA201401136A1 EA201401136A1 EA201401136A EA201401136A EA201401136A1 EA 201401136 A1 EA201401136 A1 EA 201401136A1 EA 201401136 A EA201401136 A EA 201401136A EA 201401136 A EA201401136 A EA 201401136A EA 201401136 A1 EA201401136 A1 EA 201401136A1
- Authority
- EA
- Eurasian Patent Office
- Prior art keywords
- sheet
- steel sheet
- coated steel
- item obtained
- manufacturing details
- Prior art date
Abstract
Изобретение относится к стальному листу с покрытием для катодной протекторной защиты, содержащим от 5 до 50 мас.% цинка, от 0,1 до 15 мас.% кремния и, при необходимости, до 10 мас.% магния, суммарно до 0,3 мас.% дополнительных элементов, а также дополнительно защитный элемент, выбираемый из олова в количестве от 0,1 до 5 мас.%, индия в количестве от 0,01 до 0,5 мас.% и их комбинаций, остальное - алюминий и остаточные элементы или неизбежные примеси. Также оно относится к способу изготовления деталей горячей или холодной штамповкой и к деталям, получаемым таким способом.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/FR2012/000149 WO2013156688A1 (fr) | 2012-04-17 | 2012-04-17 | Tôle d'acier munie d'un revêtement à protection cathodique sacrificielle, procédé de fabrication d'une pièce par mise en oeuvre d'une telle tôle et pièce ainsi obtenue |
Publications (2)
Publication Number | Publication Date |
---|---|
EA201401136A1 true EA201401136A1 (ru) | 2015-03-31 |
EA030016B1 EA030016B1 (ru) | 2018-06-29 |
Family
ID=46147470
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
EA201401136A EA030016B1 (ru) | 2012-04-17 | 2012-04-17 | Стальной лист с покрытием для катодной протекторной защиты, способ изготовления детали с использованием такого листа и полученная этим способом деталь |
Country Status (22)
Country | Link |
---|---|
US (1) | US10253418B2 (ru) |
EP (1) | EP2839049B1 (ru) |
JP (1) | JP6348105B2 (ru) |
KR (3) | KR20160114735A (ru) |
CN (1) | CN104302802B (ru) |
AU (1) | AU2012377741B2 (ru) |
BR (1) | BR112014025697B1 (ru) |
CA (1) | CA2870532C (ru) |
DK (1) | DK2839049T3 (ru) |
EA (1) | EA030016B1 (ru) |
ES (1) | ES2652028T3 (ru) |
HR (1) | HRP20171855T1 (ru) |
HU (1) | HUE037303T2 (ru) |
MX (1) | MX358552B (ru) |
NO (1) | NO2839049T3 (ru) |
PL (1) | PL2839049T3 (ru) |
PT (1) | PT2839049T (ru) |
RS (1) | RS56715B1 (ru) |
SI (1) | SI2839049T1 (ru) |
UA (1) | UA112688C2 (ru) |
WO (1) | WO2013156688A1 (ru) |
ZA (1) | ZA201407327B (ru) |
Families Citing this family (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6065042B2 (ja) * | 2014-04-23 | 2017-01-25 | Jfeスチール株式会社 | 溶融Al−Zn系めっき鋼板及びその製造方法 |
JP6112131B2 (ja) * | 2014-04-23 | 2017-04-12 | Jfeスチール株式会社 | 溶融Al−Zn系めっき鋼板及びその製造方法 |
WO2015181581A1 (fr) * | 2014-05-28 | 2015-12-03 | ArcelorMittal Investigación y Desarrollo, S.L. | Tôle d'acier munie d'un revêtement à protection cathodique sacrificielle comprenant du lanthane |
JP2016060946A (ja) * | 2014-09-18 | 2016-04-25 | Jfeスチール株式会社 | 溶融Al系めっき鋼板 |
JP6337711B2 (ja) * | 2014-09-18 | 2018-06-06 | Jfeスチール株式会社 | 溶融Al系めっき鋼板 |
WO2017017484A1 (en) * | 2015-07-30 | 2017-02-02 | Arcelormittal | Method for the manufacture of a hardened part which does not have lme issues |
WO2017017485A1 (en) * | 2015-07-30 | 2017-02-02 | Arcelormittal | A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium |
WO2017017483A1 (en) * | 2015-07-30 | 2017-02-02 | Arcelormittal | Steel sheet coated with a metallic coating based on aluminum |
WO2017060745A1 (en) * | 2015-10-05 | 2017-04-13 | Arcelormittal | Steel sheet coated with a metallic coating based on aluminium and comprising titanium |
WO2017187215A1 (en) * | 2016-04-29 | 2017-11-02 | Arcelormittal | Carbon steel sheet coated with a barrier coating |
WO2018031523A1 (en) * | 2016-08-08 | 2018-02-15 | John Speer | Modified hot-dip galvanize coatings with low liquidus temperature, methods of making and using the same |
KR102031466B1 (ko) | 2017-12-26 | 2019-10-11 | 주식회사 포스코 | 표면품질 및 내식성이 우수한 아연합금도금강재 및 그 제조방법 |
WO2019231023A1 (ko) * | 2018-05-31 | 2019-12-05 | 주식회사 포스코 | Twb 용접 특성이 우수한 열간성형용 al-fe 합금화 도금강판, 열간성형 부재 및 그들의 제조방법 |
DE102019130381A1 (de) * | 2019-11-11 | 2021-05-12 | Benteler Automobiltechnik Gmbh | Kraftfahrzeugbauteil mit gesteigerter Festigkeit |
CN116265609A (zh) * | 2021-12-16 | 2023-06-20 | 中国石油天然气股份有限公司 | 一种锌合金牺牲阳极材料及其制备方法、应用、制备防腐蚀敷层的方法 |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US1225246A (en) * | 1917-05-08 | Hess Ives Corp | Color photography. | |
JPS6152337A (ja) * | 1984-08-20 | 1986-03-15 | Nippon Mining Co Ltd | 溶融亜鉛めつき用亜鉛合金 |
JP4136286B2 (ja) * | 1999-08-09 | 2008-08-20 | 新日本製鐵株式会社 | 耐食性に優れたZn−Al−Mg−Si合金めっき鋼材およびその製造方法 |
JP4537599B2 (ja) * | 2000-03-10 | 2010-09-01 | 新日本製鐵株式会社 | 外観に優れた高耐食性Al系めっき鋼板 |
KR20040006479A (ko) | 2002-07-12 | 2004-01-24 | 주식회사 하이닉스반도체 | 금속 배선 식각 방법 |
JP2006016674A (ja) * | 2004-07-02 | 2006-01-19 | Nippon Steel Corp | 自動車排気系用Al系めっき鋼板及びこれを用いたAl系めっき鋼管 |
KR100667174B1 (ko) | 2005-09-02 | 2007-01-12 | 주식회사 한국번디 | 강관의 제조장치 및 제조방법 |
CN101583486B (zh) | 2006-10-30 | 2014-08-27 | 安赛乐米塔尔法国公司 | 涂覆的钢带材、其制备方法、其使用方法、由其制备的冲压坯料、由其制备的冲压产品和含有这样的冲压产品的制品 |
KR101010971B1 (ko) * | 2008-03-24 | 2011-01-26 | 주식회사 포스코 | 저온 열처리 특성을 가지는 성형용 강판, 그 제조방법,이를 이용한 부품의 제조방법 및 제조된 부품 |
JP5600868B2 (ja) | 2008-09-17 | 2014-10-08 | Jfeスチール株式会社 | 溶融Al−Zn系めっき鋼板の製造方法 |
DE102010017354A1 (de) | 2010-06-14 | 2011-12-15 | Thyssenkrupp Steel Europe Ag | Verfahren zum Herstellen eines warmgeformten und gehärteten, mit einer metallischen Korrosionsschutzbeschichtung überzogenen Stahlbauteils aus einem Stahlflachprodukt |
-
2012
- 2012-04-17 ES ES12722750.2T patent/ES2652028T3/es active Active
- 2012-04-17 MX MX2014012626A patent/MX358552B/es active IP Right Grant
- 2012-04-17 CA CA2870532A patent/CA2870532C/fr active Active
- 2012-04-17 KR KR1020167026204A patent/KR20160114735A/ko active Application Filing
- 2012-04-17 AU AU2012377741A patent/AU2012377741B2/en active Active
- 2012-04-17 PT PT127227502T patent/PT2839049T/pt unknown
- 2012-04-17 SI SI201231186T patent/SI2839049T1/en unknown
- 2012-04-17 KR KR1020147032019A patent/KR101667131B1/ko active IP Right Grant
- 2012-04-17 KR KR1020187003561A patent/KR101886611B1/ko active IP Right Grant
- 2012-04-17 RS RS20171316A patent/RS56715B1/sr unknown
- 2012-04-17 JP JP2015506274A patent/JP6348105B2/ja active Active
- 2012-04-17 UA UAA201412154A patent/UA112688C2/uk unknown
- 2012-04-17 NO NO12722750A patent/NO2839049T3/no unknown
- 2012-04-17 PL PL12722750T patent/PL2839049T3/pl unknown
- 2012-04-17 HU HUE12722750A patent/HUE037303T2/hu unknown
- 2012-04-17 WO PCT/FR2012/000149 patent/WO2013156688A1/fr active Application Filing
- 2012-04-17 EP EP12722750.2A patent/EP2839049B1/fr active Active
- 2012-04-17 BR BR112014025697-7A patent/BR112014025697B1/pt active IP Right Grant
- 2012-04-17 US US14/394,885 patent/US10253418B2/en active Active
- 2012-04-17 DK DK12722750.2T patent/DK2839049T3/da active
- 2012-04-17 EA EA201401136A patent/EA030016B1/ru not_active IP Right Cessation
- 2012-04-17 CN CN201280073231.4A patent/CN104302802B/zh active Active
-
2014
- 2014-10-09 ZA ZA2014/07327A patent/ZA201407327B/en unknown
-
2017
- 2017-11-28 HR HRP20171855TT patent/HRP20171855T1/hr unknown
Also Published As
Publication number | Publication date |
---|---|
WO2013156688A1 (fr) | 2013-10-24 |
US20150284861A1 (en) | 2015-10-08 |
EP2839049B1 (fr) | 2017-10-18 |
PL2839049T3 (pl) | 2018-03-30 |
AU2012377741A1 (en) | 2014-12-04 |
CN104302802B (zh) | 2017-04-12 |
HRP20171855T1 (hr) | 2018-01-12 |
DK2839049T3 (da) | 2017-11-20 |
JP6348105B2 (ja) | 2018-06-27 |
BR112014025697B1 (pt) | 2020-10-20 |
JP2015520797A (ja) | 2015-07-23 |
UA112688C2 (uk) | 2016-10-10 |
EP2839049A1 (fr) | 2015-02-25 |
SI2839049T1 (en) | 2018-02-28 |
KR101667131B1 (ko) | 2016-10-17 |
CA2870532A1 (fr) | 2013-10-24 |
ZA201407327B (en) | 2017-08-30 |
MX358552B (es) | 2018-08-23 |
KR20180017229A (ko) | 2018-02-20 |
NO2839049T3 (ru) | 2018-03-17 |
RS56715B1 (sr) | 2018-03-30 |
EA030016B1 (ru) | 2018-06-29 |
ES2652028T3 (es) | 2018-01-31 |
US10253418B2 (en) | 2019-04-09 |
KR20160114735A (ko) | 2016-10-05 |
HUE037303T2 (hu) | 2018-08-28 |
MX2014012626A (es) | 2015-05-11 |
KR101886611B1 (ko) | 2018-08-09 |
KR20150008114A (ko) | 2015-01-21 |
CN104302802A (zh) | 2015-01-21 |
PT2839049T (pt) | 2018-01-08 |
CA2870532C (fr) | 2016-12-13 |
AU2012377741B2 (en) | 2016-03-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EA201401136A1 (ru) | Стальной лист с покрытием для катодной протекторной защиты, способ изготовления детали с использованием такого листа и полученная этим способом деталь | |
MX2016015550A (es) | Hoja de acero provista con un revestimiento que proporciona proteccion catodica sacrificial que contiene lantano. | |
MX2018001305A (es) | Hoja de acero revestida con un recubrimiento metalico a base de aluminio. | |
TR201902032T4 (tr) | Bir alüminyum alaşımından oluşan bir korozyon koruma kaplamasına sahip çelik ürünü ve aynı zamanda bunun üretilmesine yönelik yöntem. | |
SA516371784B1 (ar) | تركيبات طلاء بادئة من الزنك مقاومة للتآكل | |
PH12017501171A1 (en) | 5-fluoro-4-imino-3-(alkyl/substituted alkyl)-1-(arylsulfonyl)-3,4-dihydropyrimidin-2(1h)-one as a seed treatment | |
MX369651B (es) | Metodo para aplicar un recubrimiento protector a un producto plano de acero y un producto plano de acero que tiene un recubrimiento protector correspondiente. | |
MX2017002797A (es) | Producto plano de acero con un recubrimiento de ai, procedimiento para su fabricacion, elemento constructivo de acero y procedimiento para su fabricacion. | |
MA35566B1 (fr) | Souches de saccharomyces cerevisiae a aptitudes phytosanitaires | |
GB2526758A (en) | Methods for artificially aging aluminum-zinc-magnesium alloys, and products based on the same | |
IN2015DN01624A (ru) | ||
ATE474023T1 (de) | Korrosionsschutzsystem für metalle und pigment hierfür | |
MX2015013810A (es) | Composiciones antitranspirantes. | |
AU2019268204A1 (en) | Hot-dip Al-based Alloy Coated Steel Sheet Excellent in Workability | |
BR112018005593A2 (pt) | ?chapa de aço e peça revestida com um revestimento metálico e uso de uma peça? | |
MX2016004415A (es) | Hoja de acero que tiene un revestimiento de znalmg y flexibilidad mejorada y metodo de produccion correspondiente. | |
ATE548485T1 (de) | Multifunktionelle beschichtung von aluminiumteilen | |
AU2014378413A1 (en) | Emulsion composition for skin | |
MX2015014136A (es) | Aleacion para un miembro de cierre de cremallera y miembro de cierre de cremallera. | |
EA201590846A1 (ru) | Клизмы | |
RU2014124500A (ru) | Легированная скандием алюминиевая фольга с повышенными удельными электромеханическими характеристиками | |
WO2014154884A3 (en) | Electroplating bath for zinc-iron alloys, method for depositing zinc-iron alloy on a device and such a device | |
MX369158B (es) | Elemento fundido a presión de aleación hipereutéctica de aluminio-silicio y procedimiento para la producción del mismo. | |
RU2010144157A (ru) | Расплав на основе цинка для нанесения защитных покрытий на стальную полосу горячим погружением | |
MX349804B (es) | Revestimientos anticorrosion. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MM4A | Lapse of a eurasian patent due to non-payment of renewal fees within the time limit in the following designated state(s) |
Designated state(s): AM AZ BY KG MD TJ TM |