DE69124778T2 - Dünnes, entkohltes, kornorientiertes Siliziumstahlblech mit verbesserten magnetischen und Beschichtungseigenschaften - Google Patents

Dünnes, entkohltes, kornorientiertes Siliziumstahlblech mit verbesserten magnetischen und Beschichtungseigenschaften

Info

Publication number
DE69124778T2
DE69124778T2 DE69124778T DE69124778T DE69124778T2 DE 69124778 T2 DE69124778 T2 DE 69124778T2 DE 69124778 T DE69124778 T DE 69124778T DE 69124778 T DE69124778 T DE 69124778T DE 69124778 T2 DE69124778 T2 DE 69124778T2
Authority
DE
Germany
Prior art keywords
steel sheet
decarburization
sheet
fayalite
tempering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE69124778T
Other languages
German (de)
English (en)
Other versions
DE69124778D1 (de
Inventor
Yasuyuki Hayakawa
Katsuo Iwamoto
Michiro Komatsubara
Makoto Watanabe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
Kawasaki Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kawasaki Steel Corp filed Critical Kawasaki Steel Corp
Application granted granted Critical
Publication of DE69124778D1 publication Critical patent/DE69124778D1/de
Publication of DE69124778T2 publication Critical patent/DE69124778T2/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1244—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the heat treatment
    • C21D8/1255—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D3/00—Diffusion processes for extraction of non-metals; Furnaces therefor
    • C21D3/02—Extraction of non-metals
    • C21D3/04—Decarburising

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Metallurgy (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Electromagnetism (AREA)
  • Manufacturing Of Steel Electrode Plates (AREA)
  • Soft Magnetic Materials (AREA)
  • Chemical Treatment Of Metals (AREA)
DE69124778T 1990-11-30 1991-11-28 Dünnes, entkohltes, kornorientiertes Siliziumstahlblech mit verbesserten magnetischen und Beschichtungseigenschaften Expired - Lifetime DE69124778T2 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2336438A JPH0756048B2 (ja) 1990-11-30 1990-11-30 被膜特性と磁気特性に優れた薄型方向性けい素鋼板の製造方法

Publications (2)

Publication Number Publication Date
DE69124778D1 DE69124778D1 (de) 1997-04-03
DE69124778T2 true DE69124778T2 (de) 1997-09-11

Family

ID=18299139

Family Applications (1)

Application Number Title Priority Date Filing Date
DE69124778T Expired - Lifetime DE69124778T2 (de) 1990-11-30 1991-11-28 Dünnes, entkohltes, kornorientiertes Siliziumstahlblech mit verbesserten magnetischen und Beschichtungseigenschaften

Country Status (5)

Country Link
US (1) US5571342A (enExample)
EP (1) EP0488726B1 (enExample)
JP (1) JPH0756048B2 (enExample)
KR (1) KR940009126B1 (enExample)
DE (1) DE69124778T2 (enExample)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5507883A (en) * 1992-06-26 1996-04-16 Nippon Steel Corporation Grain oriented electrical steel sheet having high magnetic flux density and ultra low iron loss and process for production the same
EP0577124B1 (en) * 1992-07-02 2002-10-16 Nippon Steel Corporation Grain oriented electrical steel sheet having high magnetic flux density and ultra low iron loss and process for producing the same
US5472520A (en) * 1993-12-24 1995-12-05 Kawasaki Steel Corporation Method of controlling oxygen deposition during decarbutization annealing on steel sheets
TW299354B (enExample) 1995-06-28 1997-03-01 Kawasaki Steel Co
DE69513811T3 (de) † 1995-07-14 2005-09-22 Nippon Steel Corp. Verfahren zum herstellen eines kornorientierten elektrostahlblechs mit einer spiegeloberflache und mit geringem kernverlust
JP3220362B2 (ja) * 1995-09-07 2001-10-22 川崎製鉄株式会社 方向性けい素鋼板の製造方法
JP3470475B2 (ja) * 1995-11-27 2003-11-25 Ｊｆｅスチール株式会社 極めて鉄損の低い方向性電磁鋼板とその製造方法
KR100293141B1 (ko) 1997-04-16 2001-06-15 아사무라 타카싯 피막특성과 자기특성이 우수한 일방향성 전자강판과 그 제조방법및그제조방법에사용되는탈탄소둔설비
JP3552501B2 (ja) * 1997-10-28 2004-08-11 Ｊｆｅスチール株式会社 鉄損が極めて低い方向性電磁鋼板およびその製造方法
JP4531227B2 (ja) * 2000-01-20 2010-08-25 Ｊｆｅスチール株式会社 鋼帯に形成される内部酸化層の酸素目付量の測定方法及びその測定装置
US6676771B2 (en) * 2001-08-02 2004-01-13 Jfe Steel Corporation Method of manufacturing grain-oriented electrical steel sheet
US8372216B2 (en) 2008-10-20 2013-02-12 Basf Se Continuous method for treating the surface of metal strips
PL2377961T3 (pl) * 2008-12-16 2020-11-02 Nippon Steel Corporation Blacha cienka ze stali elektrotechnicznej o ziarnach zorientowanych i sposób jej wytwarzania
JP5854233B2 (ja) 2013-02-14 2016-02-09 Ｊｆｅスチール株式会社 方向性電磁鋼板の製造方法
JP6319605B2 (ja) * 2014-10-06 2018-05-09 Ｊｆｅスチール株式会社 低鉄損方向性電磁鋼板の製造方法
JP6911597B2 (ja) * 2017-07-13 2021-07-28 日本製鉄株式会社 皮膜密着性に優れる一方向性珪素鋼板及びその製造方法
EP4123038A4 (en) * 2020-07-15 2023-04-26 Nippon Steel Corporation CORNORIENTED ELECTROMAGNETIC STEEL AND METHOD OF PRODUCTION OF CORNORIENTED ELECTROMAGNETIC STEEL

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS50116998A (enExample) * 1974-02-28 1975-09-12
US4030950A (en) * 1976-06-17 1977-06-21 Allegheny Ludlum Industries, Inc. Process for cube-on-edge oriented boron-bearing silicon steel including normalizing
JPS5565367A (en) * 1978-11-08 1980-05-16 Kawasaki Steel Corp Forming method for forsterite insulation coating of directional silicon steel sheet
JPS5672178A (en) * 1979-11-13 1981-06-16 Kawasaki Steel Corp Formation of forsterite insulating film of directional silicon steel plate
JPS5941480A (ja) * 1982-09-02 1984-03-07 Kawasaki Steel Corp 方向性珪素鋼板における欠陥のないフオルステライト質被膜形成方法
JPS59226115A (ja) * 1983-06-07 1984-12-19 Kawasaki Steel Corp 均質なフオルステライト質絶縁被膜を有する一方向性珪素鋼板の製造方法
US5203928A (en) * 1986-03-25 1993-04-20 Kawasaki Steel Corporation Method of producing low iron loss grain oriented silicon steel thin sheets having excellent surface properties
JPH028330A (ja) * 1988-06-28 1990-01-11 Kawasaki Steel Corp 方向性珪素鋼板の絶縁被膜の形成方法

Also Published As

Publication number Publication date
EP0488726A3 (enExample) 1994-02-23
US5571342A (en) 1996-11-05
EP0488726B1 (en) 1997-02-26
KR920010000A (ko) 1992-06-26
EP0488726A2 (en) 1992-06-03
JPH0756048B2 (ja) 1995-06-14
JPH04202713A (ja) 1992-07-23
KR940009126B1 (ko) 1994-10-01
DE69124778D1 (de) 1997-04-03

Similar Documents

Publication Publication Date Title
DE69124778T2 (de) Dünnes, entkohltes, kornorientiertes Siliziumstahlblech mit verbesserten magnetischen und Beschichtungseigenschaften
DE4311151C1 (de) Verfahren zur Herstellung von kornorientierten Elektroblechen mit verbesserten Ummagnetisierungsverlusten
DE68925743T2 (de) Verfahren zum Herstellen kornorientierter Elektrobleche durch Schnellerwärmung
DE69527602T2 (de) Kornorientiertes Elektrostahlblech mit hoher magnetischer Flussdichte und geringen Eisenverlusten und Herstellungsverfahren
DE69218511T2 (de) Kornorientiertes Siliziumstahlblech mit ausgezeichneten primären Glasfilmeigenschaften
DE69913624T2 (de) Kornorientieres Siliziumstahlblech und Herstellungsverfahren dafür
DE102015114358B4 (de) Verfahren zum Herstellen eines kornorientierten Elektrobands und kornorientiertes Elektroband
DE19881070C2 (de) Verfahren zur Herstellung eines Stahlblechs mit magnetischer Vorzugsrichtung mit hoher magnetischer Flussdichte basierend auf einem Niedertemperaturplattenheizverfahren
DE3220255C2 (de) Verfahren zur Herstellung von kornorientiertem Elektrostahlblech oder -band
DE3229295A1 (de) Kornorientiertes elektrostahlblech und verfahren zu seiner herstellung
DE2348249C2 (de) Verfahren zum Herstellen von Siliciumstahlblech mit Goss-Textur
DE2726045A1 (de) Verfahren zur herstellung von siliciumstahl mit wuerfel-auf-kante- orientierung
DE69131977T2 (de) Verfahren zur Herstellung von kornorientiertem Elektrofeinblech mit verbesserten magnetischen Eigenschaften und Oberflächenfilmeigenschaften
DE3147584C2 (de) Verfahren zur Herstellung von kornorientiertem Siliciumstahl in Band- oder Blechform
DE69328998T2 (de) Kornorientierte Elektrobleche und Material mit sehr hoher magnetischer Flussdichte und Verfahren zur Herstellung dieser
DE69210503T2 (de) Verfahren zur Herstellung von kornorientiertem Siliziumstahlblech mit niedrigem Eisenverlust
DE10117118C1 (de) Verfahren zur Herstellung von gut umformfähigem Feinstblech und Verwendung eines Stahls
DE69028241T3 (de) Verfahren zur Herstellung von dünnen kornorientierten Elektroblechen mit geringen Eisenverlusten und hoher Flussdichte
DE69029483T2 (de) Verfahren zur Herstellung kornorientierter Elektrostahlbleche mit hoher magnetischer Flussdichte
DE2909020A1 (de) Verfahren zum herstellen eines elektromagnetischen siliziumstahls
DE69121953T2 (de) Verfahren zum Herstellen kornorientierter Elektrobleche mit geringen Eisenverlusten
DE1931420B1 (de) Verwendung eines im fluessigen Zustande vakuumbehandelten Stahls als Dynamoband
DE69310218T2 (de) Orientierte magnetische Stahlbleche und Verfahren zu ihrer Herstellung
DE69527778T2 (de) Verfahren zur Herstellung von kornorientierten Siliziumstahlblechen mit ausgezeichneten magnetischen Eigenschaften
DE69218535T2 (de) Verfahren zur Herstellung von kornorientierten Siliziumstahlblechen

Legal Events

Date Code Title Description
8364 No opposition during term of opposition