DE60142138D1 - Legierungsbeschichtung, Verfahren zur Herstellung und Element für Hochtemperaturgeräte - Google Patents

Legierungsbeschichtung, Verfahren zur Herstellung und Element für Hochtemperaturgeräte

Info

Publication number
DE60142138D1
DE60142138D1 DE60142138T DE60142138T DE60142138D1 DE 60142138 D1 DE60142138 D1 DE 60142138D1 DE 60142138 T DE60142138 T DE 60142138T DE 60142138 T DE60142138 T DE 60142138T DE 60142138 D1 DE60142138 D1 DE 60142138D1
Authority
DE
Germany
Prior art keywords
high temperature
manufacturing process
alloy coating
temperature equipment
equipment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE60142138T
Other languages
German (de)
English (en)
Inventor
Toshio Narita
Shigenari Hayashi
Hiroshi Yakuwa
Manabu Noguchi
Matsuho Miyasaka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ebara Corp
Original Assignee
Ebara Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ebara Corp filed Critical Ebara Corp
Application granted granted Critical
Publication of DE60142138D1 publication Critical patent/DE60142138D1/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
    • F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or antivibration means on the blades or the members
    • F01D5/12—Blades
    • F01D5/28—Selecting particular materials; Particular measures relating thereto; Measures against erosion or corrosion
    • F01D5/288—Protective coatings for blades
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
    • C23C28/321—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
    • C23C28/325—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with layers graded in composition or in physical properties
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
    • C23C28/3455—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer with a refractory ceramic layer, e.g. refractory metal oxide, ZrO2, rare earth oxides or a thermal barrier system comprising at least one refractory oxide layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/54—Electroplating: Baths therefor from solutions of metals not provided for in groups C25D3/04 - C25D3/50
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/66—Electroplating: Baths therefor from melts
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
    • F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
    • F05D2230/00—Manufacture
    • F05D2230/90—Coating; Surface treatment
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F05—INDEXING SCHEMES RELATING TO ENGINES OR PUMPS IN VARIOUS SUBCLASSES OF CLASSES F01-F04
    • F05D—INDEXING SCHEME FOR ASPECTS RELATING TO NON-POSITIVE-DISPLACEMENT MACHINES OR ENGINES, GAS-TURBINES OR JET-PROPULSION PLANTS
    • F05D2300/00—Materials; Properties thereof
    • F05D2300/60—Properties or characteristics given to material by treatment or manufacturing
    • F05D2300/611—Coating
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
    • Y02T50/00—Aeronautics or air transport
    • Y02T50/60—Efficient propulsion technologies, e.g. for aircraft
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12583—Component contains compound of adjacent metal
    • Y10T428/1259—Oxide
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12806—Refractory [Group IVB, VB, or VIB] metal-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12806—Refractory [Group IVB, VB, or VIB] metal-base component
    • Y10T428/12812—Diverse refractory group metal-base components: alternative to or next to each other
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12875—Platinum group metal-base component

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Organic Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Electrochemistry (AREA)
  • Ceramic Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Turbine Rotor Nozzle Sealing (AREA)
  • Electroplating Methods And Accessories (AREA)
  • Chemical Vapour Deposition (AREA)
DE60142138T 2000-03-07 2001-03-07 Legierungsbeschichtung, Verfahren zur Herstellung und Element für Hochtemperaturgeräte Expired - Lifetime DE60142138D1 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2000062613 2000-03-07

Publications (1)

Publication Number Publication Date
DE60142138D1 true DE60142138D1 (de) 2010-07-01

Family

ID=18582598

Family Applications (1)

Application Number Title Priority Date Filing Date
DE60142138T Expired - Lifetime DE60142138D1 (de) 2000-03-07 2001-03-07 Legierungsbeschichtung, Verfahren zur Herstellung und Element für Hochtemperaturgeräte

Country Status (4)

Country Link
US (2) US6830827B2 (enExample)
EP (1) EP1132499B1 (enExample)
JP (1) JP2001323332A (enExample)
DE (1) DE60142138D1 (enExample)

Families Citing this family (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5295474B2 (ja) * 2000-09-28 2013-09-18 敏夫 成田 ニオブ基合金耐熱部材
JP4047115B2 (ja) 2002-09-13 2008-02-13 アルプス電気株式会社 軟磁性膜及びこの軟磁性膜を用いた薄膜磁気ヘッド、ならびに、前記軟磁性膜の製造方法
US7466799B2 (en) * 2003-04-09 2008-12-16 Varian Medical Systems, Inc. X-ray tube having an internal radiation shield
US6933052B2 (en) * 2003-10-08 2005-08-23 General Electric Company Diffusion barrier and protective coating for turbine engine component and method for forming
EP1715081A1 (en) * 2004-01-15 2006-10-25 Ebara Corporation Alloy coating for diffusion barrier, method for forming same, and high-temperature device member
US7778422B2 (en) * 2004-02-27 2010-08-17 Microsoft Corporation Security associations for devices
US20060165547A1 (en) * 2005-01-26 2006-07-27 Honeywell International, Inc. High strength rhenium alloys and high temperature components made from such alloys
DE102005011011A1 (de) * 2005-03-10 2006-09-14 Mtu Aero Engines Gmbh Bauteil, insbesondere Gasturbinenbauteil
US8221901B2 (en) * 2005-03-28 2012-07-17 National Institute For Materials Science Material for heat resistant component
US20070116890A1 (en) * 2005-11-21 2007-05-24 Honeywell International, Inc. Method for coating turbine engine components with rhenium alloys using high velocity-low temperature spray process
JP4716328B2 (ja) * 2006-07-05 2011-07-06 財団法人電力中央研究所 遮熱コーティングの寿命管理方法
JP5146867B2 (ja) * 2006-08-18 2013-02-20 独立行政法人物質・材料研究機構 高温耐久性に優れた耐熱部材
EP2110449A4 (en) 2006-09-13 2011-04-27 Nat Inst For Materials Science HEAT-RESISTANT ELEMENT
US8388890B2 (en) * 2006-09-21 2013-03-05 Tyco Electronics Corporation Composition and method for applying an alloy having improved stress relaxation resistance
JP5182669B2 (ja) * 2006-11-16 2013-04-17 国立大学法人北海道大学 多層合金皮膜、それを有する耐熱性金属部材および多層合金皮膜の製造方法
JP4896702B2 (ja) * 2006-12-22 2012-03-14 株式会社ディ・ビー・シー・システム研究所 合金皮膜、合金皮膜の製造方法および耐熱性金属部材
CN101168815B (zh) * 2007-12-05 2010-06-02 北京航空航天大学 片层铌钼硅基原位复合材料及其制备方法
US8361178B2 (en) * 2008-04-21 2013-01-29 Smith International, Inc. Tungsten rhenium compounds and composites and methods for forming the same
JP2012504192A (ja) * 2008-09-29 2012-02-16 ウイリアム・ディー．・ハースト 合金被覆装置及びメタライディング方法
US8367160B2 (en) * 2010-11-05 2013-02-05 United Technologies Corporation Coating method for reactive metal
EP2697408B1 (en) 2011-04-13 2018-09-12 Rolls-Royce Corporation Interfacial diffusion barrier layer including iridium on a metallic substrate
GB201109533D0 (en) * 2011-06-08 2011-07-20 Rolls Royce Plc Temperature indicating paint
CN102650064A (zh) * 2012-05-23 2012-08-29 深圳市新星轻合金材料股份有限公司 用于铝电解工业的钾冰晶石及其制备方法
JP5936487B2 (ja) * 2012-08-23 2016-06-22 キヤノン株式会社 アモルファス合金、成形用型および光学素子の製造方法
EP2918705B1 (en) 2014-03-12 2017-05-03 Rolls-Royce Corporation Coating including diffusion barrier layer including iridium and oxide layer and method of coating
CN106853436B (zh) * 2016-12-29 2020-05-19 宁夏东方钽业股份有限公司 一种钼基复合涂层及其制备方法
CN108914053B (zh) * 2018-07-20 2020-04-28 中国人民解放军国防科技大学 铱涂层原位扩散改性制备超高温涂层的方法
JP7661885B2 (ja) * 2019-10-07 2025-04-15 株式会社レゾナック 耐食性部材
CN113281243A (zh) * 2021-05-21 2021-08-20 北京航空航天大学 一种新型Co-Al-W基合金上梯度Al-Cr涂层腐蚀行为高通量表征方法
CN114574834A (zh) * 2021-12-02 2022-06-03 贵研铂业股份有限公司 一种Ta-Re层状复合材料及其制备方法和应用

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB385859A (en) * 1931-06-22 1933-01-05 Siebert G M B H G Improvements relating to catalytic reactions and catalysts for use therein
FR1385594A (fr) * 1963-02-18 1965-01-15 Union Carbide Corp Dépôt électrolytique de métaux réfractaires
DE1771763A1 (enExample) * 1967-07-03
US4517253A (en) * 1984-01-23 1985-05-14 Rose Robert M Cryoelectrodeposition
JPS6199925A (ja) * 1984-10-19 1986-05-19 Nec Corp 磁気記憶体およびその製造方法
JPS61144025A (ja) * 1984-12-18 1986-07-01 Matsushita Electric Ind Co Ltd 半導体装置の製造方法
US4731253A (en) * 1987-05-04 1988-03-15 Wall Colmonoy Corporation Wear resistant coating and process
US5273712A (en) * 1989-08-10 1993-12-28 Siemens Aktiengesellschaft Highly corrosion and/or oxidation-resistant protective coating containing rhenium
US5395221A (en) * 1993-03-18 1995-03-07 Praxair S.T. Technology, Inc. Carbide or boride coated rotor for a positive displacement motor or pump
US5427866A (en) 1994-03-28 1995-06-27 General Electric Company Platinum, rhodium, or palladium protective coatings in thermal barrier coating systems
US5556713A (en) 1995-04-06 1996-09-17 Southwest Research Institute Diffusion barrier for protective coatings
GB9612811D0 (en) 1996-06-19 1996-08-21 Rolls Royce Plc A thermal barrier coating for a superalloy article and a method of application thereof
EP0821076B1 (en) 1996-07-23 2001-11-28 ROLLS-ROYCE plc A method of aluminising a superalloy
US6007645A (en) * 1996-12-11 1999-12-28 United Technologies Corporation Advanced high strength, highly oxidation resistant single crystal superalloy compositions having low chromium content
US5817371A (en) 1996-12-23 1998-10-06 General Electric Company Thermal barrier coating system having an air plasma sprayed bond coat incorporating a metal diffusion, and method therefor
US6143141A (en) * 1997-09-12 2000-11-07 Southwest Research Institute Method of forming a diffusion barrier for overlay coatings
JP3939362B2 (ja) * 1997-10-30 2007-07-04 アルストム 高温保護コーティング
GB9724844D0 (en) * 1997-11-26 1998-01-21 Rolls Royce Plc A coated superalloy article and a method of coating a superalloy article
JPH11350196A (ja) * 1998-06-12 1999-12-21 C Uyemura & Co Ltd Ｂｎ複合ニッケル−タングステン合金皮膜及びその形成方法並びにピストンリング
US6168875B1 (en) * 1998-10-02 2001-01-02 Asea Brown Boveri Ag Coatings for turbine components
US6004372A (en) * 1999-01-28 1999-12-21 Praxair S.T. Technology, Inc. Thermal spray coating for gates and seats
US6306524B1 (en) 1999-03-24 2001-10-23 General Electric Company Diffusion barrier layer
US6207297B1 (en) * 1999-09-29 2001-03-27 Siemens Westinghouse Power Corporation Barrier layer for a MCrAlY basecoat superalloy combination

Also Published As

Publication number Publication date
US6830827B2 (en) 2004-12-14
EP1132499A2 (en) 2001-09-12
US20050079089A1 (en) 2005-04-14
EP1132499A3 (en) 2004-02-25
US6899926B2 (en) 2005-05-31
JP2001323332A (ja) 2001-11-22
EP1132499B1 (en) 2010-05-19
US20010026877A1 (en) 2001-10-04

Similar Documents

Publication Publication Date Title
DE60142138D1 (de) Legierungsbeschichtung, Verfahren zur Herstellung und Element für Hochtemperaturgeräte
DE60011163D1 (de) Glassubstrat für magnetische Medien, und Verfahren zur Herstellung desselben
DE60230777D1 (de) Bindemittelkomponenten und verfahren zur ihrer herstellung
DE50214717D1 (de) Und verfahren zu seiner herstellung
DE10135256B8 (de) Thermische Sicherung und Verfahren zur Herstellung der Thermischen Sicherung
DE60132554D1 (de) STATORBLECHKöRPER UND VERFAHREN ZUR HERSTELLUNG DESSELBEN
DE10216633B8 (de) Halbleiteranordnung und Verfahren zur Herstellung der Halbleiteranordnung
DE59802893D1 (de) Nichtkreisförmige Kühlbohrung und Verfahren zur Herstellung derselben
DE60231548D1 (de) N; formkörper und verfahren zu ihrer herstellung
DE60101771D1 (de) Keramischer Körper für Hochfrequenzanwendungen, Verwendung des Körpers und Verfahren zu dessen Herstellung
DE60235798D1 (de) Wabenförmige struktur und verfahren zur herstellung derselben
DE50213224D1 (de) Induktives bauelement und verfahren zu seiner herstellung
DE60134436D1 (de) Lebensmittel für Diabetiker und Verfahren zur Herstellung desselben
DE50201295D1 (de) Bauteil aus quarzglas sowie verfahren zur herstellung desselben
DE50113689D1 (de) Verfahren zur schnellen Herstellung von hohlen Komponenten von Strömungsmaschinen für die Fertigungsentwicklung
DE60234678D1 (de) Leiterplatte und verfahren zu ihrer herstellung
DE60205967D1 (de) Ein Steckverbinder und ein Verfahren für seine Herstellung
DE60236433D1 (de) Beschichtungszusammensetzung für polyolefinharz und verfahren zu ihrer herstellung
DE60224880D1 (de) Mikrobolometer und verfahren zu dessen herstellung
DE69920373D1 (de) Stromzuführungskörper für birne und verfahren zu seiner herstellung
DE60209281D1 (de) Wärmeaustauschelement und Verfahren zu dessen Herstellung
DE50104838D1 (de) Keramikmasse, verfahren zur herstellung der keramikmasse und verwendung der keramikmasse
DE602004011308D1 (de) Beschichtungszusammensetzung für die Filmherstellung, Verfahren zur Herstellung der Zusammensetzung und Verfahren zur Filmherstellung
DE60133890D1 (de) Hydrogeniertes, durch ringöffnung erhlatenes metathesepolymer und verfahren zur herstellung
DE60133586D1 (de) Kopfschieber und verfahren zu seiner herstellung

Legal Events

Date Code Title Description
8364 No opposition during term of opposition