DE3236750A1 - SURFACE REINFORCEMENT OF POROUS BODIES OR MOLDED PIECES CONTAINING FIBERS AND A CURED BINDING AGENT - Google Patents

SURFACE REINFORCEMENT OF POROUS BODIES OR MOLDED PIECES CONTAINING FIBERS AND A CURED BINDING AGENT

Info

Publication number
DE3236750A1
DE3236750A1 DE19823236750 DE3236750A DE3236750A1 DE 3236750 A1 DE3236750 A1 DE 3236750A1 DE 19823236750 DE19823236750 DE 19823236750 DE 3236750 A DE3236750 A DE 3236750A DE 3236750 A1 DE3236750 A1 DE 3236750A1
Authority
DE
Germany
Prior art keywords
fibers
binder
surface reinforcement
solvent
porous bodies
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19823236750
Other languages
German (de)
Inventor
Erling 3320 Skaevinge Olsen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rockwool AS
Original Assignee
Rockwool International AS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rockwool International AS filed Critical Rockwool International AS
Publication of DE3236750A1 publication Critical patent/DE3236750A1/en
Withdrawn legal-status Critical Current

Description

Anmelderin: Rockwool International A/S Hovedqaden 501 DK - 2640 HedehuseneApplicant: Rockwool International A / S Hovedqaden 501 DK - 2640 Hedehusene

Oberflächenverstärkung von porösen Körpern oder Formstücken, welche Fasern und ein ausgehärtetes Bindemittel enthaltenSurface reinforcement of porous bodies or molded pieces which contain fibers and a cured binder

Die Erfindung bezieht sich auf eine Oberflächenverstärkung von porösen Körpern oder Formstücken, beispielsweise Platten oder ziegeiförmigen Körpern aus Mineralwolle. 5The invention relates to a surface reinforcement of porous bodies or shaped pieces, for example plates or goat-shaped bodies made of mineral wool. 5

Unter anderem ist aus der dänischen Patentschrift 97 863 bekannt, Körper aus Mineralwolle durch Fasern aus Glas, Stein oder Schlacke zu verstärken, indem eine Lösung eines Kunststoffbindemittels aufgetragen wird. Die üblicherweise benutzte Art von Bindemitteln jedoch hat das Bestreben, die Zwischenräume zwischen den Fasern in den porösen Körpern auszuiüllen, wodurch die Körper feuchtigkeits- und luftundurchlässig werden. Die Isolations- und Schallabsorptionseigenschaften derartiger Körper sind dadurch wesentlich verringert. Das Ausfüllen der Poren ist vor allem schädlich, wenn die porösen Formstücke als Außenbeschichtung für Wände oder Decken verwendet werden, da derartige Formstücke mindestens offen für Feuchtigkeits- bzw. Dampfdiffusion sein müssen.Among other things is from the Danish patent specification 97 863 known to reinforce bodies made of mineral wool with fibers made of glass, stone or slag, by applying a solution of a plastic binder. Usually The type of binder used, however, tends to reduce the spaces between the fibers to be filled in the porous bodies, whereby the Body impermeable to moisture and air will. The insulation and sound absorption properties such bodies are significantly reduced as a result. The filling of the pores is especially harmful when the porous fittings be used as an external coating for walls or ceilings, as such fittings must be at least open to moisture and vapor diffusion.

BAD ORlGiWALBAD ORlGiWAL

Aufgabe der Erfindung ist es, die oben dargelegten Nachteile zu vermeiden. Die gestellte Aufgabe wird erfindungsgemäß durch die Oberflächen verstärkung nach Anspruch 1 gelöst. 5The object of the invention is to avoid the disadvantages set out above. The asked The object is according to the invention through the surfaces Reinforcement according to claim 1 solved. 5

Vorteilhafte Ausgestaltungen der Erfindung ergeben sich aus den Unteransprüchen.Advantageous refinements of the invention emerge from the subclaims.

Die verstärkten porösen Formkörper gemäß der Erfindung sind geeignet sowohl als Außenbeschichtung, als auch als Isolierung von Häusern. Solche Außenbeschichtungen müssen eine harte Oberfläche besitzen, ferner zur Feuchtigkeitsbzw. Dampfdiffusion durchlässig sein, und dies in Kombination mit einer guten Druck- und Zugfestigkeit. Ferner sollten die Formkörper wirtschaftlich hergestellt und montiert werden können. Die erfindungsgemäßen Formkörper besitzen diese Eigenschaften bzw. Qualitäten und können auf bestehenden Flächen mittels Zement oder mit mechanischen Mitteln angebracht werden. Eine ihrer Oberflächen ist hart und benötigt keine weitere Bearbeitung. Wenn jedoch eine andere Farbe oder Oberflächenstruktur erwünscht ist, kann die harte Oberfläche gut dazu benutzt werden, daß derartige Bearbeitungsmittel aufgetragen werden, ohne die Oberfläche der Formkörper besonders vorzubehandeln, da die Oberfläche für den Auftrag von üblichen Wandfarben oder Verputz geeignet ist.The reinforced porous moldings according to the invention are suitable both as an outer coating, as well as insulation of houses. Such external coatings must be tough Own surface, also for moisture or. Vapor diffusion be permeable, and this in combination with good compressive and tensile strength. Furthermore, the moldings should can be manufactured and assembled economically can. The moldings according to the invention have these properties or qualities and can be applied to existing surfaces using cement or mechanical means. One of its surfaces is hard and does not require any further processing. However, if a If a different color or surface structure is desired, the hard surface can be used are that such processing agents are applied without the surface of the molded body Special pretreatment, as the surface is suitable for the application of common wall paints or plastering is suitable.

Eine Außenbeschichtung und Isolierung kann mit Hilfe der Formkörper gemäß der Erfindung für etwa den halben Kostenaufwand gegenüber einerAn outer coating and insulation can with the help of the molded body according to the invention for about half the cost of a

BAD ORIGINAL . "BATH ORIGINAL. "

- X- - X-

bisher bekannten Außenisolierung hergestellt werden. Eine derartige bekannte Außenisolierung ist z.B. in der Beschreibung des europäischen Patentes 17969 erläutert. Ferner ist von Vorteil, daß das Gewicht der erfindungsgemäßen Beschichtung wesentlich geringer als das der bekannten Beschichtungssysteme ist.hitherto known external insulation can be produced. Such a known external insulation is explained e.g. in the description of European patent 17969. It is also advantageous that the weight of the coating according to the invention is significantly lower than that of the known Coating systems is.

Die Erfindung sei nachfolgend an Hand der Zeichnungen näher erläutert. Es zeigenThe invention is explained in more detail below with reference to the drawings. Show it

Figur 1 schematisch einige Fasern mit einem Bindemittel, jedoch ohne Füllmasse,Figure 1 schematically some fibers with a binder, but without filler,

Figur 2 die Fasern gemäß Figur 1 mit der Lösung eines Bindemittels undFigure 2 shows the fibers of Figure 1 with the solution of a binder and

Figur 3 die gleichen Fasern nach dem Trocknen der Füllmasse.
20FIG. 3 shows the same fibers after the filling compound has dried.
20th

Die Zeichnungen veranschaulichen die Fasern in einer Ebene, in der Praxis sind die Fasern aber in dreidimensionalen Richtungen angeordnet.The drawings illustrate the fibers in one plane, but in practice the fibers are arranged in three-dimensional directions.

Figur 1 zeigt schematisch und in vergrößertem Malistab einige Fasern 1 in einem Abschnitt eines porösen Mineralwollformkörpers. Die Fasern sind an ihren Berührungsstellen 2 mittels eines Bindemittels miteinander verbunden, z.B. durch ausgehärtetes Phenolharz, wobei Zwischenräume 3 zwischen den Fasern gebildet sind.Figure 1 shows schematically and in an enlarged Malistab some fibers 1 in a section a porous mineral wool molding. The fibers are at their contact points 2 by means of a Bonded with each other, e.g. by cured phenolic resin, with gaps 3 are formed between the fibers.

In Figur 2 ist der gleiche Abschnitt wie in Figur 1 dargestellt, jedoch ist hier eineIn Figure 2, the same section is shown as in Figure 1, but here is one

-=;-.ö QRtGIMAIL.- =; -. ö QRtGIMAIL.

flüssige Lösung einer Bindemittelfüllmasse aufgetragen, wie mit Pünktchen veranschaulicht sein soll. Die flüssige Füllmasse füllt den Zwischenraum 3 zwischen den Fasern vollständig aus. Das flüssige Bindemittel enthält ein leichtflüchtiges Lösungsmittel« Wenn das Lösungsmittel aus der Bindemittelfüllmasse verdampft, schrumpft diese um die Fasern 1 herum zusammen, wie schematisch in Figur 3 dargestellt ist, wodurch einliquid solution of a binder filler applied, as should be illustrated with dots. The liquid filler fills the Space 3 between the fibers completely. The liquid binder contains a highly volatile one Solvent «When the solvent evaporates from the binder filler, it shrinks these together around the fibers 1, as shown schematically is shown in Figure 3, whereby a

1Ö ununterbrochener Film Λ auf den Fasern gebildet wird, und zwar unter Freilassen von Zwischenräumen 3, die offen und durchgehend sind, so daß der Mineralwollformkörper für Wasserdampf und '' Luft durchlässig ist. Ein physikalischer Trocknungsprozeß findet statt mit einer großen Verringerung des Volumens. Die getrocknete Bindemittelfüllmasse 4 verstärkt die Fasern und verhindert ein Ausbiegen und Brechen der Fasern. Auf diese Weise werden auch die Berührungspunkte zwischen den Fasern verfestigt, wodurch sich die Zugfestigkeit wesentlich steigert. Die Druckfestigkeit und die Zugfestigkeit sowie die Steifigkeit des Formkörpers werden wesentlich erhöht und zusätzlich die Härte der Oberfläche, 5 ohne nennenswert die Porosität zu ändern. Einige der Fasern können in dichtem Zusammenhang in sogenannten Faserbündeln angeordnet sein. Die Bxndemittelfüllmasse kann dann die Faserbündel umgeben. Die flüssige Formmasse, die auf die porösen Formkörper aufgebracht wird, kann eine Emulsion oder eine Lösung enthalten. Das Bindemittel kann vorteilhafterweise Latex, Polyvinylacetat, Polyvinylchlorid/Vinyläther oder Copolymerisate, beispielsweise Styrol/Butadien1Ö uninterrupted film Λ is formed on the fibers, leaving free spaces 3, which are open and continuous, so that the mineral wool molding is permeable to water vapor and air. A physical drying process takes place with a large reduction in volume. The dried binder filler compound 4 strengthens the fibers and prevents the fibers from bending and breaking. In this way, the points of contact between the fibers are also strengthened, which significantly increases the tensile strength. The compressive strength and the tensile strength as well as the rigidity of the molded body are significantly increased and, in addition, the hardness of the surface, 5 without any significant change in the porosity. Some of the fibers can be arranged closely together in so-called fiber bundles. The binder filler compound can then surround the fiber bundles. The liquid molding compound that is applied to the porous molded body can contain an emulsion or a solution. The binder can advantageously latex, polyvinyl acetate, polyvinyl chloride / vinyl ether or copolymers, for example styrene / butadiene

BADBATH

oder Vinyltoluol/Acrylester sein. Das Bindemittel kann in einem Lösungsmittel aufgelöst werden, wie z.B. einem aromatischen Lösungsmittel oder Aliphaten, Ester oder Keton. Aromatische Lösungsmittel können Xylol oder Toluol sein.or vinyl toluene / acrylic ester. The binder can be dissolved in a solvent such as an aromatic solvent or aliphatic, ester or ketone. Aromatic Solvents can be xylene or toluene.

Zu der Bindemittelfüllmasse können verschiedene Stoffe zugegeben werden, um die Eigenschaften des verstärkten Produktes zu verbessern. Diese Stoffe können Pigmente oder Stoffe zur Erhöhung der Feuerwiderstandsfähigkeit oder Weichmacher sein. Wenn chloriertes Paraffin als Weichmacher benutzt wird, ergibt sich während des Trocknens eine wesentliche Verringerung des Bruchs von Fasern. Die flüssige Bindemittelfüllmasse kann mit Hilfe üblicher AufStreicheinrichtungen aufgetragen werden oder durch Eintauchen in einen Behälter mit flüssiger Bindemittelfüllmasse.Various Substances are added to improve the properties of the reinforced product. These Substances can be pigments or substances to increase fire resistance or plasticizers be. When chlorinated paraffin is used as a plasticizer, it results during drying a substantial reduction in fiber breakage. The liquid binder filler can applied with the help of conventional brushing devices or by immersion in a container with liquid binder filler.

Abhängig von der Menge des Lösungsmittels in der Füllmasse kann die Geschwindigkeit und Tiefe des Eindringens und die Porosität gesteuert bzw. geändert werden. Das flüssige Bindemittel kann, wenn gewünscht, auch durch die gesamte Dicke des betreffenden Formkörpers hindurchdringen. Das Bindemittel kann nahezu 100 % leichtflüchtiges Lösungsmittel enthalten.Depending on the amount of solvent in the filling compound, the speed and depth the penetration and the porosity can be controlled or changed. The liquid binder can, if desired, penetrate through the entire thickness of the shaped body in question. The binder can contain almost 100% volatile solvent.

Der verstärkte Mineralwollformkörper kann aus Mineralwollplatten mit unterschiedlicher Dicke oder Dichtigkeit hergestellt werden und kann auch für andere Zwecke als oben angegeben Verwendung finden.The reinforced mineral wool molding can be made from mineral wool panels with different thicknesses or tightness and can also be used for purposes other than those specified above Find.

Die Erfindung ist nicht beschränkt auf die Verstärkung von Mineralwolle, sondern kann auch im Zusammenhang mit anderen Materialien verwendet werden, die eine faserige Struktur aufweisen, wie beispielsweise Materialien aus Zellulosefasern oder Holzwolle.The invention is not limited to reinforcement of mineral wool, but can also be used in connection with other materials that have a fibrous structure, such as materials made from cellulosic fibers or wood wool.

Bei der Außenbeschichtung für Häuser reicht normalerweise ein Auftrag einer Bindemittelfüllmasse von fünf Litern pro Quadratmeter, entsprechend einer Eindringtiefe von 10 mm aus»For exterior coatings for houses, one application of a binder filler is usually sufficient of five liters per square meter, corresponding to a penetration depth of 10 mm from »

LeerseiteBlank page

Claims (3)

- y- - y- PatentansprücheClaims ( 1. Oberflächenverstärkung von porösen Körpern ^-^ oder Formstücken, welche Fasern und ein ausgehärtetes Bindemittel aufweisen, insbesondere Mineralfasern und ein ausgehärtetes Phenolharz, wobei bis zu einem gewissen Ausmaß eine elastische gitterartige Struktur mit durchgehenden Zwischenräumen zwischen den Fasern gebildet ist, dadurch gekennzeichnet, daß in die Oberflächenschicht des porösen Körpers eine Bindemittelfüllmasse eingebracht ist, die ein Lösungsmittel enthält, und daß die Füllmasse nach dem Trocknen durch Verdampfen des Lösungsmittels einen Film (4) auf den einzelnen Fasern (1) oder Faserbündeln und an deren Berührungsstellen miteinander innerhalb des porösen Körpers in solcher Weise ausformt, daß die Zwischenräume offen und durchlässig sind. (1. Surface reinforcement of porous bodies ^ - ^ or shaped pieces, which fibers and a Have hardened binder, in particular mineral fibers and a hardened one Phenolic resin, having to some extent an elastic lattice-like structure is formed with continuous spaces between the fibers, characterized in that that in the surface layer of the porous Body is introduced a binder filler which contains a solvent, and that the filling compound after drying by evaporation of the solvent a film (4) on the individual fibers (1) or fiber bundles and at their points of contact with one another formed within the porous body in such a way that the spaces are open and permeable. 2. Oberflächenverstärkung nach Anspruch 1, dadurch gekennzeichnet, daß die Bindemittelfüllmasse Latex aufweist. 2. Surface reinforcement according to claim 1, characterized in that the binder filler comprises latex. 3. Oberflächenverstärkung nach Anspruch 1, dadurch gekennzeichnet, daß das Lösungsmittel als aromatisches Lösungsmittel gewählt ist.3. surface reinforcement according to claim 1, characterized in that the solvent is used as an aromatic solvent is chosen. BAD ORfGIMALBAD ORfGIMAL
DE19823236750 1981-10-07 1982-10-05 SURFACE REINFORCEMENT OF POROUS BODIES OR MOLDED PIECES CONTAINING FIBERS AND A CURED BINDING AGENT Withdrawn DE3236750A1 (en)