DE1444401C3 - Verfahren zur Einhüllung von Wasser, wäßrigen Lösungen oder Dispersionen in Mikrokapseln - Google Patents
Verfahren zur Einhüllung von Wasser, wäßrigen Lösungen oder Dispersionen in MikrokapselnInfo
- Publication number
- DE1444401C3 DE1444401C3 DE19631444401 DE1444401A DE1444401C3 DE 1444401 C3 DE1444401 C3 DE 1444401C3 DE 19631444401 DE19631444401 DE 19631444401 DE 1444401 A DE1444401 A DE 1444401A DE 1444401 C3 DE1444401 C3 DE 1444401C3
- Authority
- DE
- Germany
- Prior art keywords
- water
- polymeric material
- microcapsules
- solvent
- dispersions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Zum Einhüllen von Wasser, wäßrigen Lösungen oder Dispersionen in Mikrokapseln mit aus polymerem
Material bestehenden Kapselwänden wird nach Patent 1 444 402 die wäßrige Phase in der Lösung
eines wasserbeständigen, filmbildenden, polymeren Materials in einem Lösungsmittel, das mit
Wasser nicht mischbar ist und dessen Siedepunkt unterhalb von 100° C liegt, emulgiert. Die erhaltene
Emulsion wird sodann in einer wäßrigen Lösung eines hydrophilen Kolloids emulgiert, und anschließend
wird das Lösungsmittel für das polymere Material verdampft, wodurch sich das polymere Material
um die Wassertröpfchen oder Tröpfchen von in wäßriger Phase befindlichen Verbindungen herum ablagert.
Im Gegensatz hierzu ist das erfindungsgemäße Verfahren dadurch gekennzeichnet, daß das Lösungsmittel
für das polymere Material durch Zusatz einer mit diesem und mit Wasser mischbaren Flüssigkeit,
in der das polymere Material aber unlöslich ist, extrahiert wird.
Während somit gemäß Hauptpatent das Lösungsmittel des die Kapselwand bildenden polymeren Materials
durch Verdampfung entfernt wird, erfolgt die Entfernung des Lösungsmittels für das polymere Material
gemäß vorliegender Erfindung durch Extraktion mit einer Flüssigkeit, die mit Wasser und dem
Lösungsmittel für das polymere Material mischbar ist, in der das polymere Material jedoch unlöslich
ist. Dieses Verfahren bringt den Vorteil, daß man bei der Wahl des Lösungsmittels für das polymere
Material nicht mehr auf ein Lösungsmittel beschränkt ist, dessen Siedepunkt niedriger liegt als der der einzukapselnden
Flüssigkeit (Wasser). Hieraus ergibt sich eine bedeutende Erweiterung bezüglich der Auswahl
der verwendbaren Lösungsmittel und der zur Bildung der Kapselwand in Frage kommenden polymeren
Stoffe. Bei dem erfindungsgemäßen Verfahren können dadurch praktisch alle filmbildenden Polymeren
zum Bilden der Kapselwand verwendet werden, sofern sie in Wasser beständig und in einem
wasserunmischbaren Lösungsmittel löslich sind. >
Die verwendbaren polymeren Stoffe sowie die.ge- · · eigneten hydrophilen Kolloide entsprechen denen des
Hauptpatents. Ebenfalls gehen hieraus die Anwendungsmöglichkeiten der hergestellten Kapseln hervor,
so daß sich diese Anführung hier erübrigt. Zur weiteren Erörterung der Erfindung dienen die im folgenden
angeführten Ausführungsbeispiele.
B e i s ρ i e 1 1
Man löst 10 g eines Mischpolymerisates aus Vinylidenchlorid und Acrylnitril (80/20) in 100 cm3
Cyclohexanon und emulgiert in dieser Lösung 30 cm3 einer l°/oigen wäßrigen Lösung des Farbstoffes Acid
Magenta A (C. I. 42,685), worauf man die Emulsion 10 Minuten kräftig rührt. Die erhaltene Emulsion
gießt man dann in 500 cm3 einer l%igen wäßrigen Gelatinelösung bei pH 6 und 45° C.
Der so erhaltenen sekundären Emulsion setzt man allmählich eine Mischung von 450 cm3 Methanol
und 200 cm3 Wasser zu, so daß das Cyclohexanon aus dem verkapselnden Film extrahiert wird. Auf
diese Weise erhält man Mikrokapseln mit einer harten festen Kapselwand. Nötigenfalls können die Mi-
krokapseln nach bekannten Methoden getrennt
werden.
B eis ρ i el 2
Man löst 10 g eines Mischpolymerisates aus Vinylidenchlorid und Acrylnitril (80/20) in 100 cm3
Cyclohexanon und emulgiert in dieser Lösung 30 cm3 einer l%igen wäßrigen Lösung des Farbstoffes Acid
Magenta A (C. I. 42,685), worauf man die erhaltene Emulsion in 700 cm3 einer l%igen wäßrigen Gelatinelösung
bei pH 6,5 und 45° C gießt.
Dann setzt man der so erhaltenen Emulsion allmählich 250 cm3 Methanol zu, so daß das Cyclohexanon
aus dem verkapselnden Film extrahiert wird. Man erhält so Mikrokapseln mit einer harten
festen Kapselwand, die nötigenfalls nach bekannten Verfahren getrennt werden können.
Man löst 5 g Polystyrol in 50 cm3 Tetrachlorkohlenstoff,
der 0,01 g Diisobutylnaphthalinsulfonsäure als Netzmittel enthält. In dieser Lösung emulgiert
man 15 cm3 einer l°/oigen Lösung des Farbstoffes Acid Magenta A (C. I. 42,685) und gießt die Emulsion
in 300 cm3 einer l°/oigen wäßrigen Gelatinelösung bei pH 4 und 60° C.
Der so erhaltenen sekundären Emulsion setzt man dann allmählich 600 cm3 Methanol zu, so daß der
Tetrachlorkohlenstoff aus dem verkapselnden Film extrahiert wird. Man erhält eine harte feste Kapselwand.
Claims (1)
- Patentanspruch:Verfahren zum Einhüllen von Wasser, wäßrigen Lösungen oder Dispersionen in Mikrokapseln mit aus polymerem Material bestehenden Kapselwänden, wobei die wäßrige Phase in der Lösung eines wasserbeständigen, filmbildenden, polymeren Materials in einem Lösungsmittel, das mit Wasser nicht mischbar ist, emulgiert wird, diese Emulsion anschließend in einer wäßrigen Lösung eines hydrophilen Kolloids emulgiert wird und das Lösungsmittel für das polymere Material entfernt wird nach Patent 1444 402, dadurch gekennzeichnet, daß das Lösungsmittel für das polymere Material durch Zusatz einer mit diesem und mit Wasser mischbaren Flüssigkeit, in der das polymere Material aber unlöslich ist, extrahiert wird.