DE1104694B - Verfahren zur Herstellung von thermoplastischen Massen - Google Patents
Verfahren zur Herstellung von thermoplastischen MassenInfo
- Publication number
- DE1104694B DE1104694B DEM38260A DEM0038260A DE1104694B DE 1104694 B DE1104694 B DE 1104694B DE M38260 A DEM38260 A DE M38260A DE M0038260 A DEM0038260 A DE M0038260A DE 1104694 B DE1104694 B DE 1104694B
- Authority
- DE
- Germany
- Prior art keywords
- polypropylene
- production
- ethylene
- weight
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
DEUTSCHES
Die Erfindung bezieht sich auf ein Verfahren zur Herstellung von thermoplastischen Massen auf der
Basis von hochkristallinen hochmolekularen Propylenpolymeren, die bei niedrigen Temperaturen bessere
Festigkeitseigenschaften als reines Polypropylen aufweisen.
Es ist bekannt, daß Olefinpolymere mit kristalliner Struktur, insbesondere Polypropylen, ausgezeichnete
physikalische Eigenschaften aufweisen, wie z. B. hohe Zugfestigkeit, hohen Elastizitätsmodul und gute
Widerstandskraft gegenüber hohen Temperaturen. Polypropylen hat aber trotz dieser ausgezeichneten
Eigenschaften einen Sprödigkeitspunkt zwischen 0 und 20° C je nach dem mittleren Molekulargewicht
der Polymeren. Dies macht in besonderen Fällen die Verarbeitung schwierig, und die Verwendung der
Polymeren für Anwendungszwecke, bei denen Widerstandsfähigkeit gegenüber niedrigen Temperaturen erforderlich
ist, wird dadurch sehr beschränkt.
Es wurden bereits Versuche gemacht, diese Eigenschaft von Polypropylen dadurch zu vermeiden, daß
man andere Polymere mit sehr niedrigem Sprödigkeitspunkt zusetzt. Die Ergebnisse waren jedoch im
allgemeinen nicht besonders zufriedenstellend. Die Zusätze verändern außerdem offensichtlich alle
anderen Eigenschaften des Polymeren. Beispielsweise wurde beim Zusatz von Polyäthylen gefunden, daß es
in einer Menge von über 7O°/o dem Polypropylen zugesetzt
werden mußte, um gute Werte des Sprödigkeitspunktes zu erhalten, d. h. ungefähr —15 bis —20° C,
obwohl Polyäthylen einen Sprödigkeitspunkt von -720C hat.
Aus der USA.-Patentschrift 2 655 492 sind Mischungen aus Polyäthylen und einem Propylenanteile
enthaltenden Mischpolymerisat bekannt, die auch Produkte mit verbesserter Elastizität ergeben. Jedoch
zeigen die bekannten Massen gegenüber den erfindungsgemäß hergestellten Mischungen schlechtere
mechanische Eigenschaften.
Es wurde nun überraschenderweise gefunden, daß bei der Verwendung von Äthylenpropylenmischpolymeren,
auch solcher mit einem relativ hohen Äthylengehalt an Stelle von Polyäthylen, im Gemisch mit
hochkristallinem, hochmolekularem Polypropylen eine sehr beträchtliche Erniedrigung des Sprödigkeitspunktes
bis zu durchaus zufriedenstellenden Werten erhalten wird, während gleichzeitig die mechanischen
und thermischen Eigenschaften von Polypropylen nicht merklich beeinflußt werden.
Gegenstand der Erfindung ist ein Verfahren zur Herstellung von thermoplastischen Massen aus vorwiegend
hochkristallinen hochmolekularen Propylenpolymeren durch Erhitzen eines Gemisches aus hochkristallinem hochmolekularem Polypropylen und
Verfahren zur Herstellung
von thermoplastischen Massen
von thermoplastischen Massen
Anmelder:
Montecatini Societä Generale
per rindustria Mineraria e Chimica,
per rindustria Mineraria e Chimica,
Mailand (Italien),
und Dr. Dr. Karl Ziegler,
Mülheim/Ruhr, Kaiser-Wilhelm-Platz 1
Vertreter:
Dr.-Ing. A. ν. Kreisler, Dr.-Ing. K. Schönwald,
Dr.-Ing. A. ν. Kreisler, Dr.-Ing. K. Schönwald,
Dipl.-Chem. Dr. ph.il. H. Siebeneicher
und Dr.-Ing. Th. Meyer, Patentanwälte,
Köln 1, Deidimannhaus
Beanspruchte Priorität:
Italien vom 16. Juli 1957
Italien vom 16. Juli 1957
Franco Ranalli, Mailand (Italien),
ist als Erfinder genannt worden
ist als Erfinder genannt worden
Mischpolymerisaten aus Äthylen und Propylen, die 30 bis 70 Gewichtsprozent Äthylen enthalten, auf
Temperaturen von 180 bis 190° C unter Bildung einer homogenen Masse.
Vorzugsweise wird ein Mischpolymeres mit einem Gehalt von 50 Gewichtsprozent Äthylen verwendet.
Man erhält auf diese Weise Produkte, die nach dem Verformen eine gute Schlagfestigkeit auch bei Temperaturen
unterhalb 0° C aufweisen.
Die Menge des zuzusetzenden Äthylenpropylenmischpolymeren kann innerhalb eines relativ großen
Bereiches schwanken, je nach dem Anwendungszweck, für den die Mischung bestimmt ist, d. h. je nach den
gewünschten Eigenschaften des Materials. Im allgemeinen genügen Mengen zwischen 5 und 20%, um
den Sprödigkeitspunkt auf einen befriedigenden Wert zu erniedrigen, während die anderen Eigenschaften
nicht merklich verschlechtert werden.
Die Erfindung wird durch das nachfolgende Beispiel erläutert:
109 540/436
Zu 900 g festem Polypropylen mit einem Molekulargewicht von 120 000 bis 150 000, das bei einer Extraktion
mit n-Heptan 82% Rückstand hinterläßt, werden 2 g polyalkylierter Phenol-monosulfidkristallstabilisator
und 100 g eines Äthylenpropylenmischpol3rmeren, das 50 Gewichtsprozent Äthylen enthält,
zugesetzt. Die Mischung wird 20 Minuten bei 180 bis 190° C in einem Walzenmischer kalandriert und die
erhaltene Platte in einer Plattenpresse bei 200° C 5 Minuten geformt. Man erhält eine Platte, von der
Probestücke abgeschnitten werden, an denen der Sprödigkeitspunkt bestimmt wird.
Platten aus reinem Polypropylen werden auf analoge Weise hergestellt und geformt und dann auf
gleiche Weise Probestücke genommen. Diese Probestücke werden nach dem Verfahren gemäß ASTM geprüft
und folgende Resultate erhalten:
ASTM-Test | Reines Propylen |
Polypropylen + lO°/o Äthylen- propylen- mismpoly- merisat |
|
Sprödigkeits punkt, 0C |
D746-52T | +6 | -7 |
Vicat (5kg), 0C | — | 79 + 2 | 68±2 |
Streckgrenze, kg/cm2 |
D 412-52 | 323 ±2 | 259 ±2 |
Biegemodul E, kg/cm2 |
D747-50 | 9700 ±900 | 8100+600 |
Rockwell- R-Härte |
D785-51 | 91,3 ±1,6 | 78±1 |
Shore-D-Härte.. | — | 70 | 65 |
Claims (2)
1. Verfahren zur Herstellung von thermoplastischen Massen aus Polyolefinen und Mischpolymeren,
dadurch gekennzeichnet, daß man ein Gemisch aus hochkristallinem hochmolekularem
Polypropylen und Mischpolymeren aus Äthylen und Propylen mit einem Gehalt von 30 bis 70 Gewichtsprozent
Äthylen auf Temperaturen zwischen
180 und 190° C unter Bildung einer homogenen Masse erhitzt.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet,
daß man ein Gemisch aus 95 bis 80 Gewichtsprozent Polypropylen und 5 bis 20 Gewichtsprozent
des Mischpolymerisates verwendet.
In Betracht gezogene Druckschriften:
USA.-Patentschrift Nr. 2 655 492.
USA.-Patentschrift Nr. 2 655 492.