CN1995140A - 一种单组分硅烷改性聚醚密封胶及其制备方法 - Google Patents
一种单组分硅烷改性聚醚密封胶及其制备方法 Download PDFInfo
- Publication number
- CN1995140A CN1995140A CN 200510132669 CN200510132669A CN1995140A CN 1995140 A CN1995140 A CN 1995140A CN 200510132669 CN200510132669 CN 200510132669 CN 200510132669 A CN200510132669 A CN 200510132669A CN 1995140 A CN1995140 A CN 1995140A
- Authority
- CN
- China
- Prior art keywords
- seal gum
- agent
- seal
- gum
- single component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例1 | 对比实施例1 | |
份 | ||
MS-polymer | 38.5 | 38.5 |
邻苯二甲酸二辛酯 | 13.3 | 13.3 |
碳酸钙 | 40.2 | 40.2 |
二氧化钛 | 4.1 | 4.1 |
聚酰胺触变剂 | 0.5 | 0.5 |
紫外线吸收剂 | 0.15 | -- |
紫外线稳定剂 | 0.15 | -- |
气相二氧化硅 | 2.2 | 2.2 |
乙烯基三甲氧基硅烷 | 0.3 | 0.3 |
N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷 | 0.5 | 0.5 |
改性有机锡 | 0.1 | 0.1 |
总计 | 100 | 97.7 |
拉伸强度(MPa) | 3.16 | 3.20 |
伸长率(%) | 263.55 | 248.70 |
撕裂强度(N/mm) | 16.51 | 17.34 |
耐候性试验结果(小时) | 3000无裂缝 | 2000微裂 |
Claims (13)