CN1911501A - 流化催化裂化催化剂的制造方法 - Google Patents
流化催化裂化催化剂的制造方法 Download PDFInfo
- Publication number
- CN1911501A CN1911501A CNA2006101077580A CN200610107758A CN1911501A CN 1911501 A CN1911501 A CN 1911501A CN A2006101077580 A CNA2006101077580 A CN A2006101077580A CN 200610107758 A CN200610107758 A CN 200610107758A CN 1911501 A CN1911501 A CN 1911501A
- Authority
- CN
- China
- Prior art keywords
- kaolin
- microballoon
- catalyst
- metakaolin
- calcining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 239000003054 catalyst Substances 0.000 title claims abstract description 82
- 238000004519 manufacturing process Methods 0.000 title description 5
- NLYAJNPCOHFWQQ-UHFFFAOYSA-N kaolin Chemical compound O.O.O=[Al]O[Si](=O)O[Si](=O)O[Al]=O NLYAJNPCOHFWQQ-UHFFFAOYSA-N 0.000 claims abstract description 164
- 235000012211 aluminium silicate Nutrition 0.000 claims abstract description 116
- 239000005995 Aluminium silicate Substances 0.000 claims abstract description 114
- 238000001354 calcination Methods 0.000 claims abstract description 75
- 238000000034 method Methods 0.000 claims abstract description 45
- 239000004115 Sodium Silicate Substances 0.000 claims abstract description 33
- 229910052911 sodium silicate Inorganic materials 0.000 claims abstract description 33
- NTHWMYGWWRZVTN-UHFFFAOYSA-N sodium silicate Chemical compound [Na+].[Na+].[O-][Si]([O-])=O NTHWMYGWWRZVTN-UHFFFAOYSA-N 0.000 claims abstract description 28
- 239000000203 mixture Substances 0.000 claims abstract description 25
- 238000001694 spray drying Methods 0.000 claims abstract description 23
- 239000010457 zeolite Substances 0.000 claims description 77
- 229910021536 Zeolite Inorganic materials 0.000 claims description 75
- HNPSIPDUKPIQMN-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical compound O=[Si]=O.O=[Al]O[Al]=O HNPSIPDUKPIQMN-UHFFFAOYSA-N 0.000 claims description 74
- 239000002002 slurry Substances 0.000 claims description 55
- 239000011734 sodium Substances 0.000 claims description 48
- 238000006243 chemical reaction Methods 0.000 claims description 45
- 238000002425 crystallisation Methods 0.000 claims description 44
- 230000008025 crystallization Effects 0.000 claims description 44
- 229910052708 sodium Inorganic materials 0.000 claims description 34
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 claims description 30
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 27
- 235000019795 sodium metasilicate Nutrition 0.000 claims description 20
- 239000012013 faujasite Substances 0.000 claims description 19
- 239000002245 particle Substances 0.000 claims description 19
- 239000007767 bonding agent Substances 0.000 claims description 15
- 229910052761 rare earth metal Inorganic materials 0.000 claims description 15
- 238000005342 ion exchange Methods 0.000 claims description 12
- 229910004298 SiO 2 Inorganic materials 0.000 claims description 11
- 239000011148 porous material Substances 0.000 claims description 9
- -1 rare-earth cation Chemical class 0.000 claims description 6
- 238000004523 catalytic cracking Methods 0.000 claims description 5
- 230000007812 deficiency Effects 0.000 claims 1
- 229910052782 aluminium Inorganic materials 0.000 abstract description 26
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 abstract description 25
- 239000004005 microsphere Substances 0.000 abstract description 24
- 230000008569 process Effects 0.000 abstract description 16
- 238000005336 cracking Methods 0.000 abstract description 7
- 239000012530 fluid Substances 0.000 abstract description 5
- 238000011065 in-situ storage Methods 0.000 abstract description 5
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 22
- 239000013078 crystal Substances 0.000 description 20
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 19
- 239000007787 solid Substances 0.000 description 17
- 239000000463 material Substances 0.000 description 16
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 15
- 239000002994 raw material Substances 0.000 description 14
- 239000000243 solution Substances 0.000 description 14
- 239000003795 chemical substances by application Substances 0.000 description 13
- 230000000694 effects Effects 0.000 description 12
- 238000005516 engineering process Methods 0.000 description 12
- 230000000977 initiatory effect Effects 0.000 description 12
- 239000000049 pigment Substances 0.000 description 12
- 239000000047 product Substances 0.000 description 12
- 239000000571 coke Substances 0.000 description 11
- 239000002243 precursor Substances 0.000 description 11
- 150000002910 rare earth metals Chemical class 0.000 description 11
- 239000011159 matrix material Substances 0.000 description 10
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 9
- 239000000377 silicon dioxide Substances 0.000 description 9
- 239000002253 acid Substances 0.000 description 8
- 238000001704 evaporation Methods 0.000 description 8
- 239000004927 clay Substances 0.000 description 7
- 230000008020 evaporation Effects 0.000 description 7
- 238000004537 pulping Methods 0.000 description 7
- 239000007921 spray Substances 0.000 description 7
- 238000002441 X-ray diffraction Methods 0.000 description 6
- 239000000084 colloidal system Substances 0.000 description 6
- KZHJGOXRZJKJNY-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical compound O=[Si]=O.O=[Si]=O.O=[Al]O[Al]=O.O=[Al]O[Al]=O.O=[Al]O[Al]=O KZHJGOXRZJKJNY-UHFFFAOYSA-N 0.000 description 6
- 238000001035 drying Methods 0.000 description 6
- 229910052863 mullite Inorganic materials 0.000 description 6
- 239000003921 oil Substances 0.000 description 6
- 239000000843 powder Substances 0.000 description 6
- 230000009257 reactivity Effects 0.000 description 6
- 230000000052 comparative effect Effects 0.000 description 5
- 239000002270 dispersing agent Substances 0.000 description 5
- 239000012452 mother liquor Substances 0.000 description 5
- 238000012360 testing method Methods 0.000 description 5
- QGZKDVFQNNGYKY-UHFFFAOYSA-O Ammonium Chemical compound [NH4+] QGZKDVFQNNGYKY-UHFFFAOYSA-O 0.000 description 4
- 230000015572 biosynthetic process Effects 0.000 description 4
- 238000000227 grinding Methods 0.000 description 4
- 230000006872 improvement Effects 0.000 description 4
- 229910052742 iron Inorganic materials 0.000 description 4
- 238000006386 neutralization reaction Methods 0.000 description 4
- TVMXDCGIABBOFY-UHFFFAOYSA-N octane Chemical compound CCCCCCCC TVMXDCGIABBOFY-UHFFFAOYSA-N 0.000 description 4
- 238000002360 preparation method Methods 0.000 description 4
- PAWQVTBBRAZDMG-UHFFFAOYSA-N 2-(3-bromo-2-fluorophenyl)acetic acid Chemical compound OC(=O)CC1=CC=CC(Br)=C1F PAWQVTBBRAZDMG-UHFFFAOYSA-N 0.000 description 3
- VQTUBCCKSQIDNK-UHFFFAOYSA-N Isobutene Chemical compound CC(C)=C VQTUBCCKSQIDNK-UHFFFAOYSA-N 0.000 description 3
- 241000446313 Lamella Species 0.000 description 3
- 230000008901 benefit Effects 0.000 description 3
- 230000003197 catalytic effect Effects 0.000 description 3
- 238000007796 conventional method Methods 0.000 description 3
- 238000002474 experimental method Methods 0.000 description 3
- 238000001914 filtration Methods 0.000 description 3
- 230000004048 modification Effects 0.000 description 3
- 238000012986 modification Methods 0.000 description 3
- 239000000741 silica gel Substances 0.000 description 3
- 229910002027 silica gel Inorganic materials 0.000 description 3
- 229910052596 spinel Inorganic materials 0.000 description 3
- 239000011029 spinel Substances 0.000 description 3
- 230000008719 thickening Effects 0.000 description 3
- PAYRUJLWNCNPSJ-UHFFFAOYSA-N Aniline Chemical compound NC1=CC=CC=C1 PAYRUJLWNCNPSJ-UHFFFAOYSA-N 0.000 description 2
- CDBYLPFSWZWCQE-UHFFFAOYSA-L Sodium Carbonate Chemical compound [Na+].[Na+].[O-]C([O-])=O CDBYLPFSWZWCQE-UHFFFAOYSA-L 0.000 description 2
- PMZURENOXWZQFD-UHFFFAOYSA-L Sodium Sulfate Chemical compound [Na+].[Na+].[O-]S([O-])(=O)=O PMZURENOXWZQFD-UHFFFAOYSA-L 0.000 description 2
- FKNQFGJONOIPTF-UHFFFAOYSA-N Sodium cation Chemical compound [Na+] FKNQFGJONOIPTF-UHFFFAOYSA-N 0.000 description 2
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 2
- 238000009825 accumulation Methods 0.000 description 2
- 230000009471 action Effects 0.000 description 2
- 239000011230 binding agent Substances 0.000 description 2
- 230000008859 change Effects 0.000 description 2
- 239000007795 chemical reaction product Substances 0.000 description 2
- 239000003153 chemical reaction reagent Substances 0.000 description 2
- 230000002950 deficient Effects 0.000 description 2
- 238000011010 flushing procedure Methods 0.000 description 2
- 238000002347 injection Methods 0.000 description 2
- 239000007924 injection Substances 0.000 description 2
- QSHDDOUJBYECFT-UHFFFAOYSA-N mercury Chemical compound [Hg] QSHDDOUJBYECFT-UHFFFAOYSA-N 0.000 description 2
- 229910052753 mercury Inorganic materials 0.000 description 2
- 229910001723 mesolite Inorganic materials 0.000 description 2
- 238000002156 mixing Methods 0.000 description 2
- 239000002808 molecular sieve Substances 0.000 description 2
- 239000010413 mother solution Substances 0.000 description 2
- 238000012856 packing Methods 0.000 description 2
- 238000002161 passivation Methods 0.000 description 2
- 239000003208 petroleum Substances 0.000 description 2
- 238000012805 post-processing Methods 0.000 description 2
- 239000000376 reactant Substances 0.000 description 2
- 239000013049 sediment Substances 0.000 description 2
- URGAHOPLAPQHLN-UHFFFAOYSA-N sodium aluminosilicate Chemical compound [Na+].[Al+3].[O-][Si]([O-])=O.[O-][Si]([O-])=O URGAHOPLAPQHLN-UHFFFAOYSA-N 0.000 description 2
- 238000010561 standard procedure Methods 0.000 description 2
- 230000008961 swelling Effects 0.000 description 2
- 238000012546 transfer Methods 0.000 description 2
- 238000011144 upstream manufacturing Methods 0.000 description 2
- 238000005406 washing Methods 0.000 description 2
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- BPQQTUXANYXVAA-UHFFFAOYSA-N Orthosilicate Chemical compound [O-][Si]([O-])([O-])[O-] BPQQTUXANYXVAA-UHFFFAOYSA-N 0.000 description 1
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 description 1
- 239000005864 Sulphur Substances 0.000 description 1
- KMWBBMXGHHLDKL-UHFFFAOYSA-N [AlH3].[Si] Chemical compound [AlH3].[Si] KMWBBMXGHHLDKL-UHFFFAOYSA-N 0.000 description 1
- YKTSYUJCYHOUJP-UHFFFAOYSA-N [O--].[Al+3].[Al+3].[O-][Si]([O-])([O-])[O-] Chemical compound [O--].[Al+3].[Al+3].[O-][Si]([O-])([O-])[O-] YKTSYUJCYHOUJP-UHFFFAOYSA-N 0.000 description 1
- 239000000654 additive Substances 0.000 description 1
- 230000000996 additive effect Effects 0.000 description 1
- 230000002776 aggregation Effects 0.000 description 1
- 238000004220 aggregation Methods 0.000 description 1
- 239000004411 aluminium Substances 0.000 description 1
- HPTYUNKZVDYXLP-UHFFFAOYSA-N aluminum;trihydroxy(trihydroxysilyloxy)silane;hydrate Chemical compound O.[Al].[Al].O[Si](O)(O)O[Si](O)(O)O HPTYUNKZVDYXLP-UHFFFAOYSA-N 0.000 description 1
- 150000003863 ammonium salts Chemical class 0.000 description 1
- 238000013459 approach Methods 0.000 description 1
- 238000009933 burial Methods 0.000 description 1
- 229910052799 carbon Inorganic materials 0.000 description 1
- 238000006555 catalytic reaction Methods 0.000 description 1
- 150000001768 cations Chemical class 0.000 description 1
- 238000009614 chemical analysis method Methods 0.000 description 1
- 239000011362 coarse particle Substances 0.000 description 1
- 239000012612 commercial material Substances 0.000 description 1
- 238000006114 decarboxylation reaction Methods 0.000 description 1
- 230000018044 dehydration Effects 0.000 description 1
- 238000006297 dehydration reaction Methods 0.000 description 1
- 239000008367 deionised water Substances 0.000 description 1
- 238000013461 design Methods 0.000 description 1
- 229910001649 dickite Inorganic materials 0.000 description 1
- 238000005906 dihydroxylation reaction Methods 0.000 description 1
- 238000009826 distribution Methods 0.000 description 1
- 239000000428 dust Substances 0.000 description 1
- 230000009969 flowable effect Effects 0.000 description 1
- 239000012634 fragment Substances 0.000 description 1
- 239000007789 gas Substances 0.000 description 1
- 239000000499 gel Substances 0.000 description 1
- 239000011521 glass Substances 0.000 description 1
- 239000003673 groundwater Substances 0.000 description 1
- 229910052621 halloysite Inorganic materials 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- PMYUVOOOQDGQNW-UHFFFAOYSA-N hexasodium;trioxido(trioxidosilyloxy)silane Chemical compound [Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[O-][Si]([O-])([O-])O[Si]([O-])([O-])[O-] PMYUVOOOQDGQNW-UHFFFAOYSA-N 0.000 description 1
- 230000036571 hydration Effects 0.000 description 1
- 238000006703 hydration reaction Methods 0.000 description 1
- 238000001027 hydrothermal synthesis Methods 0.000 description 1
- 238000007654 immersion Methods 0.000 description 1
- 239000000411 inducer Substances 0.000 description 1
- 229910052500 inorganic mineral Inorganic materials 0.000 description 1
- 230000003993 interaction Effects 0.000 description 1
- 230000001788 irregular Effects 0.000 description 1
- 229910052622 kaolinite Inorganic materials 0.000 description 1
- 238000003475 lamination Methods 0.000 description 1
- 238000012423 maintenance Methods 0.000 description 1
- 230000014759 maintenance of location Effects 0.000 description 1
- 239000011707 mineral Substances 0.000 description 1
- 150000007522 mineralic acids Chemical class 0.000 description 1
- 239000011268 mixed slurry Substances 0.000 description 1
- 238000011020 pilot scale process Methods 0.000 description 1
- 150000004291 polyenes Chemical class 0.000 description 1
- 238000003672 processing method Methods 0.000 description 1
- 230000001105 regulatory effect Effects 0.000 description 1
- 239000004576 sand Substances 0.000 description 1
- 238000004088 simulation Methods 0.000 description 1
- 229910000029 sodium carbonate Inorganic materials 0.000 description 1
- 159000000000 sodium salts Chemical class 0.000 description 1
- 229910052938 sodium sulfate Inorganic materials 0.000 description 1
- 235000011152 sodium sulphate Nutrition 0.000 description 1
- UPDATVKGFTVGQJ-UHFFFAOYSA-N sodium;azane Chemical compound N.[Na+] UPDATVKGFTVGQJ-UHFFFAOYSA-N 0.000 description 1
- 241000894007 species Species 0.000 description 1
- 238000003756 stirring Methods 0.000 description 1
- 239000000126 substance Substances 0.000 description 1
- 239000000758 substrate Substances 0.000 description 1
- 238000010998 test method Methods 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- 239000002699 waste material Substances 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0027—Powdering
- B01J37/0045—Drying a slurry, e.g. spray drying
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
- B01J29/084—Y-type faujasite
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G11/00—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
- C10G11/02—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils characterised by the catalyst used
- C10G11/04—Oxides
- C10G11/05—Crystalline alumino-silicates, e.g. molecular sieves
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/16—Clays or other mineral silicates
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Crystallography & Structural Chemistry (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- General Chemical & Material Sciences (AREA)
- Catalysts (AREA)
- Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US09/942,971 | 2001-08-31 | ||
| US09/942,971 US6696378B2 (en) | 2001-08-31 | 2001-08-31 | Fluid catalytic cracking catalyst manufacturing process |
Related Parent Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CNB028169603A Division CN1330415C (zh) | 2001-08-31 | 2002-08-07 | 流化催化裂化催化剂的制造方法 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| CN1911501A true CN1911501A (zh) | 2007-02-14 |
Family
ID=25478899
Family Applications (2)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CNA2006101077580A Pending CN1911501A (zh) | 2001-08-31 | 2002-08-07 | 流化催化裂化催化剂的制造方法 |
| CNB028169603A Expired - Fee Related CN1330415C (zh) | 2001-08-31 | 2002-08-07 | 流化催化裂化催化剂的制造方法 |
Family Applications After (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CNB028169603A Expired - Fee Related CN1330415C (zh) | 2001-08-31 | 2002-08-07 | 流化催化裂化催化剂的制造方法 |
Country Status (11)
| Country | Link |
|---|---|
| US (1) | US6696378B2 (enExample) |
| EP (1) | EP1420883A1 (enExample) |
| JP (1) | JP2005526587A (enExample) |
| KR (1) | KR20040031018A (enExample) |
| CN (2) | CN1911501A (enExample) |
| AU (1) | AU2002329711B2 (enExample) |
| BR (1) | BR0212221A (enExample) |
| CA (1) | CA2458367A1 (enExample) |
| MX (1) | MXPA04001888A (enExample) |
| TW (1) | TWI226263B (enExample) |
| WO (1) | WO2003020423A1 (enExample) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN108948774A (zh) * | 2018-08-31 | 2018-12-07 | 邳州市金丰木质纤维粉有限公司 | 一种木质纤维粉的制备方法 |
Families Citing this family (29)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JP4991083B2 (ja) * | 2000-09-22 | 2012-08-01 | バスフ・カタリスツ・エルエルシー | 構造的に強化された分解用触媒 |
| US6942784B2 (en) * | 2000-09-22 | 2005-09-13 | Engelhard Corporation | Structurally enhanced cracking catalysts |
| US6673235B2 (en) * | 2000-09-22 | 2004-01-06 | Engelhard Corporation | FCC catalysts for feeds containing nickel and vanadium |
| US6656347B2 (en) * | 2000-09-22 | 2003-12-02 | Engelhard Corporation | Structurally enhanced cracking catalysts |
| US20030089640A1 (en) * | 2001-10-17 | 2003-05-15 | Rostam Madon | FCC catalysts for feeds containing nickel and vanadium |
| US7101473B2 (en) * | 2002-05-31 | 2006-09-05 | Engelhard Corporation | Method of enhancing the activity of FCC catalysts |
| CN1275855C (zh) * | 2003-03-28 | 2006-09-20 | 中国石油化工股份有限公司 | 用高岭土合成的纳米级y型沸石及其制备方法 |
| US6942783B2 (en) * | 2003-05-19 | 2005-09-13 | Engelhard Corporation | Enhanced FCC catalysts for gas oil and resid applications |
| US20060060504A1 (en) * | 2004-09-08 | 2006-03-23 | Vierheilig Albert A | Additives for metal contaminant removal |
| CN1332754C (zh) * | 2004-09-15 | 2007-08-22 | 中国石油化工股份有限公司 | 一种使用硅粘结剂的裂化催化剂的制备方法 |
| CN100377782C (zh) * | 2004-09-15 | 2008-04-02 | 中国石油化工股份有限公司 | 一种烃类裂化催化剂的制备方法 |
| RU2008103182A (ru) * | 2005-06-29 | 2009-08-10 | В.Р.Грейс Энд Ко.-Конн. (Us) | Пентасильный катализатор для легких олефинов в псевдоожиженных каталитических установках |
| US9108181B2 (en) | 2007-06-20 | 2015-08-18 | Basf Corporation | Structurally enhanced cracking catalysts |
| US8278235B2 (en) * | 2007-06-20 | 2012-10-02 | Basf Corporation | Structurally enhanced cracking catalysts |
| US7754638B2 (en) * | 2007-11-30 | 2010-07-13 | Corning Incorporated | Zeolite-based honeycomb body |
| RU2412903C1 (ru) * | 2009-08-03 | 2011-02-27 | Открытое акционерное общество "Салаватнефтеоргсинтез" | СПОСОБ ПОЛУЧЕНИЯ ГРАНУЛИРОВАННОГО БЕЗ СВЯЗУЮЩЕГО ЦЕОЛИТА ТИПА NaY ВЫСОКОЙ ФАЗОВОЙ ЧИСТОТЫ |
| US8372269B2 (en) * | 2009-10-02 | 2013-02-12 | Basf Corporation | Heavy metals trapping co-catalyst for FCC processes |
| US9029291B2 (en) | 2011-01-12 | 2015-05-12 | Basf Corporation | Rare earth-containing attrition resistant vanadium trap for catalytic cracking catalyst |
| CN103253684B (zh) * | 2012-02-16 | 2015-04-29 | 中国石油天然气股份有限公司 | 一种直接法原位晶化合成小晶粒zsm-5分子筛的方法 |
| WO2013123297A2 (en) | 2012-02-17 | 2013-08-22 | Kior, Inc. | Catalyst composition with increased bulk active site accessibility for the catalytic thermoconversion of biomass to liquid fuels and chemicals and for upgrading bio-oils |
| US9428695B2 (en) | 2013-02-12 | 2016-08-30 | Saudi Basic Industries Corporation | Conversion of plastics to olefin and aromatic products with product recycle |
| US9447332B2 (en) | 2013-02-12 | 2016-09-20 | Saudi Basic Industries Corporation | Conversion of plastics to olefin and aromatic products using temperature control |
| EP3122456B1 (en) | 2014-03-28 | 2019-05-08 | Agency For Science, Technology And Research | Method for preparing a sodium faujasite catalyst and its use in producing acrylic acid |
| CN108463285B (zh) * | 2015-11-24 | 2021-11-16 | 巴斯夫公司 | 用于提高丁烯产率的流化催化裂化催化剂 |
| KR102157788B1 (ko) * | 2017-07-03 | 2020-09-18 | 주식회사 엘지화학 | 알루미노실리케이트 입자 제조방법 및 이를 포함하는 타이어용 고무 조성물 제조방법 |
| US20230294083A1 (en) * | 2020-08-19 | 2023-09-21 | Basf Corporation | Fluid catalytic cracking catalyst composition for enhanced butylenes yields with metal passivation functionality |
| CN112516984A (zh) * | 2020-12-23 | 2021-03-19 | 山西晋坤矿产品股份有限公司 | 一种利用煤矸石制备高活性石油催化裂化催化剂的方法 |
| CN120359186A (zh) * | 2022-12-14 | 2025-07-22 | 巴斯夫公司 | 使用含水高岭土的沸石合成 |
| CN118562480B (zh) * | 2024-06-26 | 2025-01-28 | 中国石油大学(华东) | 压裂液破胶剂载体及其制备方法和应用 |
Family Cites Families (28)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US4493902A (en) | 1983-02-25 | 1985-01-15 | Engelhard Corporation | Fluid catalytic cracking catalyst comprising microspheres containing more than about 40 percent by weight Y-faujasite and methods for making |
| US4606813A (en) | 1983-02-25 | 1986-08-19 | Engelhard Corporation | Fluid catalytic cracking catalyst for cracking sulfur containing petroleum feedstocks and a process for using it |
| US4628042A (en) | 1983-06-20 | 1986-12-09 | Engelhard Corporation | Porous mullite |
| US4581340A (en) | 1983-09-15 | 1986-04-08 | Engelhard Corporation | Fluid cracking catalyst and method of making same from waste catalyst manufacture fines |
| US5976355A (en) | 1984-03-09 | 1999-11-02 | Stone & Webster Engineering Corp. | Low residence time catalytic cracking process |
| US4631262A (en) | 1985-06-05 | 1986-12-23 | Engelhard Corporation | Method of making seed solution useful in zeolite catalyst manufacture |
| US5071539A (en) | 1985-08-30 | 1991-12-10 | Engelhard Corporation | FCC catalysts of increased effective heat capacity |
| US5234578A (en) | 1988-08-26 | 1993-08-10 | Uop | Fluidized catalytic cracking process utilizing a high temperature reactor |
| US4965233A (en) | 1988-10-20 | 1990-10-23 | Engelhard Corporation | Novel zeolite fluid cracking catalysts and preparation thereof from mixtures of calcined clay |
| US5023220A (en) | 1988-11-16 | 1991-06-11 | Engelhard Corporation | Ultra high zeolite content FCC catalysts and method for making same from microspheres composed of a mixture of calcined kaolin clays |
| US5316656A (en) | 1990-05-07 | 1994-05-31 | Uop | Hydrocarbon conversion processes with molecular sieve agglomerates having improved transport properties |
| US5243121A (en) | 1992-03-19 | 1993-09-07 | Engelhard Corporation | Fluid catalytic cracking process for increased formation of isobutylene and isoamylenes |
| US5300469A (en) | 1992-12-08 | 1994-04-05 | Engelhard Corporation | Composition for passivating vanadium in catalytic cracking and preparation thereof |
| US5358632A (en) | 1993-07-16 | 1994-10-25 | Uop | FCC feed injection with non-quiescent mixing |
| US5462652A (en) | 1993-09-24 | 1995-10-31 | Uop | Short contact FCC process with catalyst blending |
| US5395809A (en) | 1993-11-01 | 1995-03-07 | Engelhard Corporation | Modified microsphere FCC catalysts |
| US5413978A (en) | 1993-11-30 | 1995-05-09 | Engelhard Corporation | Catalytically inert particles for blending with petroleum cracking catalyst |
| US5723040A (en) | 1994-09-22 | 1998-03-03 | Stone & Webster Engineering Corporation | Fluid catalytic cracking process and apparatus |
| US5662868A (en) | 1994-09-22 | 1997-09-02 | Stone & Webster Engineering Corporation | Short residence time cracking apparatus and process |
| US5521133A (en) | 1994-11-29 | 1996-05-28 | Engelhard Corporation | Phosphorus bound porous microspheres |
| US5559067A (en) * | 1995-03-31 | 1996-09-24 | Engelhard Corporation | Modified microsphere FCC catalysts and manufacture thereof |
| US5993645A (en) | 1995-12-08 | 1999-11-30 | Engelhard Corporation | Catalyst for cracking oil feedstocks contaminated with metal |
| FI101156B (fi) | 1996-08-30 | 1998-04-30 | Fortum Oil Oy | Kiertomassareaktoriin perustuva menetelmä ja laite hiilivetyjen konver toimiseksi |
| US6004527A (en) | 1997-09-29 | 1999-12-21 | Abb Lummus Global Inc. | Method for making molecular sieves and novel molecular sieve compositions |
| US6010618A (en) | 1997-12-05 | 2000-01-04 | Uop Llc | FCC process with two zone short contact time reaction conduit |
| US6063263A (en) | 1998-04-24 | 2000-05-16 | Uop Llc | Process for feed contacting with immediate catalyst separation |
| JP4991083B2 (ja) | 2000-09-22 | 2012-08-01 | バスフ・カタリスツ・エルエルシー | 構造的に強化された分解用触媒 |
| US6656347B2 (en) * | 2000-09-22 | 2003-12-02 | Engelhard Corporation | Structurally enhanced cracking catalysts |
-
2001
- 2001-08-31 US US09/942,971 patent/US6696378B2/en not_active Expired - Fee Related
-
2002
- 2002-08-07 WO PCT/US2002/025023 patent/WO2003020423A1/en not_active Ceased
- 2002-08-07 KR KR10-2004-7002918A patent/KR20040031018A/ko not_active Ceased
- 2002-08-07 CN CNA2006101077580A patent/CN1911501A/zh active Pending
- 2002-08-07 AU AU2002329711A patent/AU2002329711B2/en not_active Ceased
- 2002-08-07 CN CNB028169603A patent/CN1330415C/zh not_active Expired - Fee Related
- 2002-08-07 JP JP2003524725A patent/JP2005526587A/ja active Pending
- 2002-08-07 MX MXPA04001888A patent/MXPA04001888A/es not_active Application Discontinuation
- 2002-08-07 EP EP02765955A patent/EP1420883A1/en not_active Withdrawn
- 2002-08-07 CA CA002458367A patent/CA2458367A1/en not_active Abandoned
- 2002-08-07 BR BRPI0212221-9A patent/BR0212221A/pt not_active IP Right Cessation
- 2002-08-14 TW TW091118299A patent/TWI226263B/zh not_active IP Right Cessation
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN108948774A (zh) * | 2018-08-31 | 2018-12-07 | 邳州市金丰木质纤维粉有限公司 | 一种木质纤维粉的制备方法 |
Also Published As
| Publication number | Publication date |
|---|---|
| CN1330415C (zh) | 2007-08-08 |
| US6696378B2 (en) | 2004-02-24 |
| JP2005526587A (ja) | 2005-09-08 |
| CA2458367A1 (en) | 2003-03-13 |
| AU2002329711B8 (en) | 2003-03-18 |
| WO2003020423A1 (en) | 2003-03-13 |
| BR0212221A (pt) | 2006-05-23 |
| EP1420883A1 (en) | 2004-05-26 |
| US20030050181A1 (en) | 2003-03-13 |
| MXPA04001888A (es) | 2004-06-15 |
| CN1549746A (zh) | 2004-11-24 |
| KR20040031018A (ko) | 2004-04-09 |
| TWI226263B (en) | 2005-01-11 |
| AU2002329711B2 (en) | 2007-10-04 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CN1330415C (zh) | 流化催化裂化催化剂的制造方法 | |
| CN1225311C (zh) | 结构增强的裂化催化剂 | |
| US6942784B2 (en) | Structurally enhanced cracking catalysts | |
| EP1502648A1 (en) | Structurally enhanced cracking catalysts | |
| AU2002329711A1 (en) | FCC catalyst manufacturing process | |
| US10807076B2 (en) | Mesoporous FCC catalysts with excellent attrition resistance | |
| US20040235642A1 (en) | Enhanced FCC catalysts for gas oil and resid applications | |
| CN109312238B (zh) | 具有衍生自结晶勃姆石的氧化铝的fcc催化剂 | |
| US9682366B2 (en) | Method of producing FCC catalysts with reduced attrition rates | |
| AU2003243265B2 (en) | Method of enhancing the activity of FCC catalysts | |
| US4299733A (en) | High octane FCC catalyst |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| C06 | Publication | ||
| PB01 | Publication | ||
| C10 | Entry into substantive examination | ||
| SE01 | Entry into force of request for substantive examination | ||
| C02 | Deemed withdrawal of patent application after publication (patent law 2001) | ||
| WD01 | Invention patent application deemed withdrawn after publication |