CN1466600A - 使用聚合链转移剂控制接枝共聚物的分子量 - Google Patents

使用聚合链转移剂控制接枝共聚物的分子量 Download PDF

Info

Publication number
CN1466600A
CN1466600A CNA028026977A CN02802697A CN1466600A CN 1466600 A CN1466600 A CN 1466600A CN A028026977 A CNA028026977 A CN A028026977A CN 02802697 A CN02802697 A CN 02802697A CN 1466600 A CN1466600 A CN 1466600A
Authority
CN
China
Prior art keywords
ethene
propylene
olefin
alpha
carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA028026977A
Other languages
English (en)
Other versions
CN1249112C (zh
Inventor
C��Q����
C·Q·宋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Basell Poliolefine Italia SRL
Original Assignee
Basell Poliolefine Italia SRL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basell Poliolefine Italia SRL filed Critical Basell Poliolefine Italia SRL
Publication of CN1466600A publication Critical patent/CN1466600A/zh
Application granted granted Critical
Publication of CN1249112C publication Critical patent/CN1249112C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

通过在非氧化性的气氛中进行以下步骤来降低接枝共聚物的分子量：(1)用作为自由基聚合引发剂的有机化合物处理丙烯聚合物材料，(2)在约0.5－5％的为烯丙醇衍生物的聚合链转移剂存在下，相对于100份丙烯聚合物材料，用约2－240份的至少一种乙烯基取代的接枝单体处理丙烯聚合物材料，以及(3)除去任何未反应的单体，分解任何未反应的引发剂，并且使材料中的任何残余自由基失活。

Description

使用聚合链转移剂控制接枝共聚物的分子量
                               技术领域
本发明涉及控制聚烯烃接枝共聚物的分子量的方法。
                               背景技术
聚合物的分子量及其分布是影响接枝共聚物最终性能的重要参数。在自由基聚合中，聚合物的分子量主要由反应温度、自由基引发剂浓度、以及单体浓度决定。
在气体混合反应器中，由于气相中的单体蒸气压较低，低聚合温度通常将减少气相污垢。与低反应温度有关的主要问题是以该方法制备的接枝共聚物具有不太理想的高分子量。虽然增加引发剂浓度将有助于降低分子量，但是由于接枝聚合呈现的引发效率非常低，所以对依赖引发剂浓度的分子量的影响较小。另外，接枝共聚使用纯单体进料来进行，因此对聚合物分子量的控制而言，单体浓度不是一个可以控制的参数。
在自由基聚合中使用链转移剂能通过聚合物的链断裂作用来降低其分子量。这导致了增长中的聚合物链的尺寸减小。链转移对聚合速率的影响取决于再引发速率是否与初始链增长自由基的再引发速率可以比拟。有机化合物如硫醇或烷基溴已经广泛应用于聚合过程中以控制聚合物的分子量。例如，美国专利4,000,220公开了在热塑性接枝共聚物树脂的制造中使用链转移剂，如硫醇、硫代丙酸、四氯化碳和二聚α-甲基苯乙烯。美国专利4,001,349公开了用来制备苯乙烯和饱和聚烯烃弹性体的接枝产物的链转移剂如硫醇的使用。美国专利4,308,354公开了在引发剂和链转移剂如烷基硫醇存在下，通过从聚合聚丁二烯橡胶和甲基丙烯酸甲酯、苯乙烯、以及丙烯酸甲酯或丙烯酸乙酯的混合物来生产透明的、耐冲击的聚合物。美国专利4,427,826公开了在没有自由基引发剂及存在硫醇链转移剂下，用或不用溶剂聚合1，3-二烯橡胶和一种或多种的乙烯基单体。该链转移剂通常会在最终的产物中产生令人讨厌的臭味或颜色。而除去聚合物中的链转移剂残余物也是一项艰苦的工作。
因此，需要能有效地降低聚合物的分子量而不在最终产物中留下不需要的残余物的链转移剂。
                              发明内容
本发明的降低接枝共聚物的分子量的方法包含，在基本上非氧化性的气氛中，
(1)用作为自由基聚合引发剂的有机化合物处理丙烯聚合物材料，
(2)在占单体总重量的约0.5-5％的为烯丙醇衍生物的聚合链转移剂存在下，相对于100份丙烯聚合物材料，用约2-240份的至少一种能被自由基聚合的乙烯基取代的接枝单体处理丙烯聚合物材料一段时间，此段时间与(1)同时或者在(1)之后，与(1)有或没有重叠，
(3)从所得的接枝的丙烯聚合物材料中除去任何未反应的单体，分解任何未反应的引发剂，并且使材料中的任何残余自由基失活。
在可被自由基引发剂聚合的烯丙醇的衍生物存在下，进行接枝聚合反应可有效地降低该接枝共聚物的分子量。在最终产物中链转移剂的残余物的浓度较低，因为链转移剂加入了聚合物的链中。
                             具体实施方式
“基本上非氧化性的环境”是在制备接枝共聚物过程中烯烃聚合物材料暴露在的环境或气氛，它是指反应性氧的浓度(即，呈将与聚合物材料中的自由基反应的形式的氧浓度)小于15体积％，更好是小于5体积％，最好是小于1体积％。反应性氧的最佳浓度是0.004体积％或更低。在这些限制条件内，非氧化性的气氛可以是对丙烯聚合物材料中的自由基具有氧化惰性的任何气体或者气体混合物，例如氮气、氩气、氦气和二氧化碳。
用作接枝共聚物主链的丙烯聚合物材料可以是：
(a)全同立构指数大于80，最好是约85-99的丙烯的结晶均聚物；
(b)丙烯与选自乙烯和4-10个碳α-烯烃的烯烃的结晶共聚物，条件是如果该烯烃是乙烯，则最大的聚合的乙烯量为10重量％、最好是约4重量％，而当该烯烃是4-10个碳的α-烯烃时，其最大聚合量为20重量％、最好是约16重量％，该共聚物的全同立构指数大于85；
(c)丙烯与选自乙烯和4-8个碳的α-烯烃的两种烯烃的结晶三元共聚物，条件是最大的聚合的4-8个碳的α-烯烃量为20重量％、最好是约16重量％，并且当乙烯是这些烯烃之一时，最大的聚合的乙烯量为5重量％，最好是约4％，该三元共聚物的全同立构指数大于85；
(d)一种烯烃聚合物组合物，它包含：
(i)约10-60重量％、最好是约15-55重量％的全同立构指数大于80、最好是约85-98的结晶丙烯均聚物，或者选自(a)丙烯和乙烯、(b)丙烯、乙烯和4-8个碳的α-烯烃、和(c)丙烯和4-8个碳的α-烯烃的单体的结晶共聚物，该共聚物的聚合的丙烯量大于85重量％、最好是约90-99重量％，全同立构指数大于85；
(ii)约5-25％、最好是约5-20％的乙烯与丙烯或者4-8个碳的α-烯烃的在室温下不可溶解在二甲苯中的共聚物，以及
(iii)约30-70％、最好是约20-65％的选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的弹性共聚物，该共聚物任选地含有约0.5-10％的二烯，并且含有小于70重量％、更好是约10-60％、最好是约12-55％的聚合的乙烯并在室温下可溶解于二甲苯中，其特性粘数约为1.5-4.0dl/g，其中，(ii)和(iii)的总量占总的烯烃聚合物组合物的约50-90％，(ii)/(iii)的重量比小于0.4、最好是0.1-0.3，该组合物通过至少两个阶段的聚合来制备，其挠曲模量小于150MPa；或者
(e)一种热塑性烯烃，它包含：
(i)约10-60％、最好是20-50％的全同立构指数大于80的结晶丙烯均聚物，或者选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的结晶共聚物，该共聚物聚合的丙烯量大于85％，其全同立构指数大于85；
(ii)约20-60％、最好是约30-50％的选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的非晶共聚物，该共聚物任选地含有约0.5-10％的二烯，并且含有小于70％的聚合的乙烯，在室温下可溶解于二甲苯中；以及
(iii)约3-40％、最好是约10-20％的乙烯与丙烯或者4-8个碳的α-烯烃的在室温下不可溶解在二甲苯中的共聚物，其中，该组合物的挠性模量大于150但小于1200MPa，更好是约200-1100MPa，最好是约200-1000MPa。室温或环境温度约为25℃。
用来制备(d)和(e)的4-8个碳的α-烯烃包括，例如丁烯-1、戊烯-1、己烯-1、4-甲基戊烯-1和辛烯-1。
存在时，二烯一般是丁二烯、1，1，己二烯、1，5-己二烯或亚乙基降冰片烯。
丙烯聚合物材料(d)和(e)可通过至少两个阶段的聚合来制备，在第一阶段中，丙烯；丙烯和乙烯；丙烯和α-烯烃；或者丙烯、乙烯和α-烯烃聚合形成(d)或(e)的组分(i)，而在随后的阶段中，乙烯和丙烯；乙烯和α-烯烃；或者乙烯、丙烯和α-烯烃的混合物以及任选的二烯聚合形成(d)或(e)的组分(ii)和(iii)。
聚合可在使用分开的反应器在液相、气相或液-气相中进行，在所有相态中的聚合都可分批或连续进行。例如，可以使用液体丙烯作为稀释剂来进行组分(i)的聚合。以及在气相中进行组分(ii)和(iii)的聚合而没有中间阶段，除了丙烯的部分脱气以外。所有气相都是优选的方法。
丙烯聚合物材料(d)的制备详细描述在美国专利5,212,246和5,409,992中，将它们参考结合于此。丙烯聚合物材料(e)的制备详细描述在美国专利5,302,454和5,409,992中，将它们参考结合于此。
丙烯均聚物是优选的丙烯聚合物主链材料。
该接枝共聚物通过用过氧化物或其它作为自由基聚合引发剂的化合物处理丙烯聚合物材料，在其上形成活性接枝点来制得。经化学处理该聚合物，在其中产生的自由基在该聚合物上形成活性接枝点并在这些点上引发单体的聚合。
该聚合引发剂是在此使用温度下的分解半衰期约为1-240分钟、更好是约5-100分钟、最好是约10-40分钟的聚合引发剂。有机过氧化物，尤其是那些产生烷氧自由基的有机过氧化物构成了较佳的一类引发剂。它们包括过氧化酰，如过氧化苯甲酰和过氧化二苯甲酰；二烷基和芳烷基过氧化物，如二叔丁基过氧化物、二枯基过氧化物、枯基丁基过氧化物、1，1-二叔丁基过氧-3，5，5-三甲基环己烷、2，5-二甲基-2，5-二叔丁基过氧己烷和二(α-叔丁基过氧异丙基苯)；过氧酯，如新戊酸叔丁基过氧酯、过苯甲酸叔丁酯、过辛酸叔丁酯、2，5-二过苯甲酸2，5-二甲基己酯、二过邻苯二甲酸叔丁酯、己酸叔丁基过氧-2-乙酯和己酸1，1-二甲基-3-羟基丁基过氧-2-乙酯；以及碳酸过氧酯，如二碳酸二(2-乙基己基)过氧酯、二碳酸二正丙基过氧酯和二碳酸二(4-叔丁基环己基)过氧酯。优选过氧酯。
本发明使用的接枝单体可以是能被自由基聚合的任何单体乙烯基化合物，其中乙烯基H2C＝CR-(式中R为H或甲基)连接在直链或支链脂肪族链上或者连接在单环或多环化合物的取代或未取代的芳香环、杂环或脂环上。一般的取代基可以是烷基、羟烷基、芳基和卤素基。通常，乙烯基单体将是下述种类之一：(1)乙烯基取代的芳香族、杂环或脂环族化合物，包括苯乙烯、乙烯基萘、乙烯基吡啶、乙烯基吡咯烷酮、乙烯基咔唑以及它们的同系物，例如α-和对甲基苯乙烯、甲基氯苯乙烯、对叔丁基苯乙烯、甲基乙烯基吡啶和乙基乙烯基吡啶；(2)芳香族和饱和脂肪族羧酸的乙烯基酯，包括甲酸乙烯基酯、乙酸乙烯基酯、氯乙酸乙烯基酯、氰基乙酸乙烯基酯、丙酸乙烯基酯和苯甲酸乙烯基酯；以及(3)不饱和脂肪族腈和羧酸及它们的衍生物，包括丙烯腈；甲基丙烯腈；丙烯酰胺；甲基丙烯酰胺和丙烯酸；丙烯酸酯，如丙烯酸甲酯、丙烯酸乙酯、丙烯酸羟乙酯、丙烯酸2-乙基己酯和丙烯酸丁酯；甲基丙烯酸；乙基丙烯酸；甲基丙烯酸酯，如甲基丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸丁酯、甲基丙烯酸苄基酯、甲基丙烯酸苯乙酯、甲基丙烯酸苯氧基乙酯、甲基丙烯酸环氧丙酯和甲基丙烯酸羟丙基酯；以及马来酸酐。可使用这些单体中的一种或多种。
使用的接枝单体的量约为2-240份/100份丙烯聚合物材料，更好是约5-100份/100份丙烯聚合物材料。
在接枝聚合过程中，单体还聚合形成一定量的游离的或未接枝的聚合物或共聚物。该接枝共聚物的形态是：丙烯聚合物材料为连续或基质相，接枝和未接枝的聚合的单体是分散相。
美国专利5,140,074详细描述了通过将丙烯聚合物与自由基聚合引发剂如有机过氧化物和乙烯基单体接触来制备接枝共聚物，将其参考结合于此。
用来控制接枝共聚物分子量的聚合链转移剂是可通过自由基机制聚合的并且是烯丙醇的衍生物，如醚或酯。优选烯丙基丙氧基化醚。烯丙醇的其它适宜的衍生物包括，例如乙酸烯丙酯和丁酸烯丙酯。链转移剂可与接枝单体共聚并加入接枝共聚物链中。存在的链转移剂的量占单体总重量的约0.5-5％、更好是约0.5-2％。
向接枝共聚体系中加入聚合链转移剂提供了控制接枝共聚物的分子量和分子量分布的手段。聚合链转移剂可在较低的反应温度下制备具有所需分子量的接枝共聚物，这通常使反应器污垢减少。分子量可通过调节反应温度、单体与引发剂的比例、以及链转移剂浓度来控制。加入链转移剂时，观察到较低的接枝效率。在聚合中及聚合之后，没有测得来自链转移剂的臭味。
降低接枝共聚物的分子量的方法的最后一个步骤是从所得的接枝的丙烯聚合物材料中除去任何未反应的接枝单体，分解任何未反应的引发剂，并且使材料中的任何残余的自由基失活。
全同立构指数定义为不可溶解在二甲苯中的烯烃聚合物的百分数。在室温下可溶解在二甲苯中的烯烃聚合物的重量百分数通过将2.5g该聚合物溶解在配备了搅拌器的容器中的250ml二甲苯中，并在搅拌下将其在135℃加热20分钟来确定。在持续搅拌下将该溶液冷却至25℃，然后不搅拌静置30分钟，使得固体沉淀。这些固体用滤纸过滤，剩余的溶液通过用氮气流处理来蒸发，并在80℃真空干燥该固体残余物直至重量恒定。在室温下不溶于二甲苯的聚合物的重量百分数是该聚合物的全同立构指数。用该方法得到的值基本上与通过沸腾的正庚烷来萃取测得的全同立构指数一致。
特性粘数于135℃在十氢萘中测定。
分子量通过凝胶渗透色谱法来测定。
在实施例的接枝共聚物制造中用作主链聚合物的丙烯均聚物的孔隙率根据描述于Winslow，N.M.和Shapiro，J.J.著《通过压汞测定孔径分布的仪器》(ASTM Bull.TP 49，39-44(1959年2月))，以及Rootare，H.M.著《水银孔率法回顾》(在Hirshhom，J.S.著《粉末冶金术中先进的实验技术》中，Plenum出版社，纽约，1970)。
容积密度使用ASTM D-1895来确定。
除非另有说明，说明书中所有的份和百分数都是重量的。
                              实施例1
在本实施例和以下实施例中，用作接枝共聚物所用的主链聚合物的丙烯均聚物的孔隙率为0.51cm3/g、容积密度为0.37/gcm3，购自Basell USA公司。
接枝共聚物按以下方法制备。预先混合甲基丙烯酸甲酯、丙烯酸甲酯、引发剂和表1所示量的AP-1375链转移剂(CTA)，并以1.0pph/min的进料速率加入2加仑的含有丙烯均聚物的半分批反应器中。单体与引发剂的比例(M/I)和接枝温度示于表1。每100份丙烯均聚物加入95重量份的单体(90.9份甲基丙烯酸甲酯和4.1份丙烯酸甲酯)。购自Atofina公司的Lupersol 11-新戊酸叔丁基过氧酯用作聚合引发剂。AP-1375链转移剂是烯丙基丙氧基化物，购自Lyondell ChemicalWorldwide公司。在单体加入完成后，保持反应温度30分钟。然后在氮气吹扫下用90分钟将温度升高到140℃。
                                      表1
    试样No.   反应温度(℃)   M/I比例(摩尔)  CTA(重量％)
    1   105   120  4.24
    2   105   60  0
    3   85   60  0
    4   85   120  4.24
    5   85   120  0
    6   105   60  4.24
    7   95   90  2.12
    8   85   60  4.24
    9   105   120  0
    10   95   90  2.12
    11   95   90  2.12
使用BioRad FSS-7分析仪通过傅里叶变换红外光谱(FTIR)分析该接枝共聚物在各种反应条件下的聚甲基丙烯酸甲酯(PMMA)的总加入量。表2示出了每100份丙烯均聚物(pph)的PMMA加入量、反应温度、M/I比例和加入的CTA的重量％。统计学分析显示，各可变因素和它们的相互作用在统计学上对聚合转化率的影响不显著。虽然聚合速率不同，但是聚合转化率在所有试验条件下都很高。
                                        表2
    试样No.   接枝温度(℃)    M/I比例(摩尔)  CTA(重量％)  PMMA(pph)
    1   105    120  4.24  87.7
    2   105    60  0  88.5
    3   85    60  0  83.7
    4   85    120  4.24  87.7
    5   85    120  0  86.8
    6   105    60  4.24  88.6
    7   95    90  2.12  89.2
    8   85    60  4.24  91.8
    9   105    120  0  90.9
    10   95    90  2.12  87.7
    11   95    90  2.12  84.8
表3示出了反应条件对接枝共聚物分子量的影响。统计学分析显示，所有这三个因素-反应温度、单体/引发剂的比例和链转移剂浓度，对聚合物的分子量有显著影响。
                                        表3
   试样No.   接枝温度(℃)    M/I比例(摩尔)  CTA(重量％)    Mw(103)    Mn(103)
   1   105    120  4.24    159    56
   2   105    60  0    180    64
   3   85    60  0    365    97
   4   85    120  4.24    306    87
   5   85    120  0    495    129
   6   105    60  4.24    126    43
   7   95    90  2.12    226    82
   8   85    60  4.24    267    75
   9   105    120  0    217    72
   10   95    90  2.12    227    73
   11   95    90  2.12    235    73
与引发剂浓度比较，接枝共聚物的分子量是反应温度和CTA浓度的强函数。随着反应温度或CTA浓度增加，该分子量下降。
表4示出了在各种条件下接枝共聚物的分子量分布(MWD)。统计学分析显示，只有反应温度对MWD具有显著的影响。随着接枝温度的增加，MWD变得更窄。
                                     表4
    试样No.   接枝温度(℃)   M/I比例(摩尔)  CTA(重量％)     MWD
    1   105   120  4.24     2.84
    2   105   60  0     2.81
    3   85   60  0     3.76
    4   85   120  4.24     3.52
    5   85   120  0     3.84
    6   105   60  4.24     2.93
    7   95   90  2.12     2.76
    8   85   60  4.24     3.56
    9   105   120  0     3.01
    10   95   90  2.12     3.11
    11   95   90  2.12     3.22
                               实施例2
除了购自Atofina公司的Lupersol PMS(在无味溶剂油中的50％己酸叔丁基过氧-2-乙酯)用作过氧化物引发剂，并且链转移剂是购自Lyondell ChemicalWorldwide公司的ARCAL AP 1.6-烯丙基丙氧基化物之外，在聚合链转移剂存在下，按实施例1所述制备接枝共聚物。由于接枝温度高于实施例1，所以使用热稳定性更高的过氧化物引发剂。
表1示出了各个试样的接枝温度、M/I的比例和CTA的量。
                                    表1
    试样No.   反应温度(℃)    M/I比例(摩尔)  CTA(重量％)
    1   130    140  4.24
    2   130    100  0
    3   100    100  0
    4   100    140  4.24
    5   100    140  0
    6   130    100  4.24
    7   115    120  2.12
    8   100    100  4.24
    9   130    140  0
    10   115    120  2.12
    11   115    120  2.12
表2示出了在各种反应条件下通过FTIR分析的PMMA的加入量。各可变因素和它们的相互作用在统计学上对聚合转化率的影响不显著。虽然聚合速率不同，但是聚合转化率在所有试验条件下都很高。
                                           表2
    试样No.   接枝温度(℃)   M/I比例(摩尔)  CTA(重量％)  PMMA(pph)
    1   130   140  4.24  89.3
    2   130   100  0  91.1
    3   100   100  0  95.0
    4   100   140  4.24  95.5
    5   100   140  0  92.7
    6   130   100  4.24  90.2
    7   115   120  2.12  92.8
    8   100   100  4.24  95.4
    9   130   140  0  91.0
    10   115   120  2.12  95.1
    11   115   120  2.12  96.6
表3示出了反应条件对接枝共聚物分子量的影响。统计学分析显示，反应温度对分子量的影响最显著，其次是链转移剂浓度。
                                             表3
   试样No.   接枝温度(℃)   M/I比例(摩尔)  CTA(重量％)   Mw(103)   Mn(103)
   1   130   140  4.24   69   26
   2   130   100  0   64   25
   3   100   100  0   250   63
   4   100   140  4.24   196   53
   5   100   140  0   271   74
   6   130   100  4.24   59   23
   7   115   120  2.12   107   32
   8   100   100  4.24   178   51
   9   130   140  0   73   29
   10   115   120  2.12   112   37
   11   115   120  2.12   113   37
表4示出了接枝共聚物的分子量分布(MWD)。统计学分析的结果显示，只有反应温度对MWD具有显著的影响。随着接枝温度的增加，MWD变得更窄。
                                            表4
    试样No.   接枝温度(℃)  M/I比例(摩尔)  CTA(重量％)     MWD
    1   130  140  4.24     2.65
    2   130  100  0     2.56
    3   100  100  0     3.97
    4   100  140  4.24     3.70
    5   100  140  0     3.66
    6   130  100  4.24     2.57
    7   115  120  2.12     3.34
    8   100  100  4.24     3.49
    9   130  140  0     2.52
    10   115  120  2.12     3.03
    11   115  120  2.12     3.05
本文中公开的本发明的其它特征、优点和实施方式将在本领域普通技术人员读完前述公开内容之后易于变得明显。在这方面，当本发明的具体实施方式作了相当详细的描述后，这些实施方式的变化和修改可在不偏离所述及所主张的本发明的精神和范围之内进行。

Claims (12)

1.一种降低接枝共聚物的分子量的方法，它包括，在基本上非氧化性的气氛中，
(a)用作为自由基聚合引发剂的有机化合物处理丙烯聚合物材料，
(b)在占单体总重量的约0.5-5％的为烯丙醇衍生物的聚合链转移剂存在下，相对于100份丙烯聚合物材料，用约2-240份的至少一种能用自由基聚合的乙烯基取代的接枝单体处理丙烯聚合物材料一段时间，此段时间与(a)同时或者在(a)之后，与(a)有或没有重叠，
(c)从所得的接枝的丙烯聚合物材料中除去任何未反应的单体，分解任何未反应的引发剂，并且使材料中的任何残余自由基失活。
2.根据权利要求1所述的方法，其特征在于：所述丙烯聚合物材料选自：
(a)全同立构指数大于80的丙烯的结晶均聚物；
(b)丙烯与选自乙烯和4-10个碳α-烯烃的烯烃的结晶共聚物，条件是如果该烯烃是乙烯，则最大的聚合的乙烯量为10重量％，而当该烯烃是4-10个碳的α-烯烃时，其最大聚合量为20重量％，所述共聚物的全同立构指数大于85；
(c)丙烯与选自乙烯和4-8个碳的α-烯烃的两种烯烃的结晶三元共聚物，条件是最大的聚合的4-8个碳的α-烯烃量为20重量％，并且当乙烯是这些烯烃之一时，最大的聚合的乙烯量为5重量％，所述三元共聚物的全同立构指数大于85；
(d)一种烯烃聚合物组合物，它包含：
(i)约10-60重量％的全同立构指数大于80的结晶丙烯均聚物或者选自(a)丙烯和乙烯、(b)丙烯、乙烯和4-8个碳的α-烯烃、和(c)丙烯和4-8个碳的α-烯烃的单体的结晶共聚物，所述共聚物的聚合的丙烯量大于85重量％，全同立构指数大于85；
(ii)约5-25％的乙烯与丙烯或者4-8个碳的α-烯烃的在室温下不可溶解在二甲苯中的共聚物，以及
(iii)约30-70％的选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的弹性共聚物，所述共聚物任选地含有约0.5-10％的二烯，并且含有小于70重量％的聚合的乙烯，在室温下可溶解于二甲苯中，其特性粘数约为1.5-4.0dl/g，其中，(ii)和(iii)的总量占总的烯烃聚合物组合物的约50-90％，(ii)/(iii)的重量比小于0.4，所述组合物通过至少两个阶段的聚合来制备，其挠曲模量小于150MPa；或者
(e)一种热塑性烯烃，它包含：
(i)约10-60％的全同立构指数大于80的结晶丙烯均聚物或者选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的结晶共聚物，所述共聚物的聚合的丙烯量大于85％，其全同立构指数大于85；
(ii)约20-60％的选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的非晶共聚物，所述共聚物任选地含有约0.5-10％的二烯，并且含有小于70％的聚合的乙烯并在室温下可溶解于二甲苯中；以及
(iii)约3-40％的乙烯和丙烯或者4-8个碳的α-烯烃的在室温下不可溶解在二甲苯中的共聚物，其中，该组合物的挠性模量大于150但小于1200MPa。
3.根据权利要求2所述的方法，其特征在于：所述丙烯聚合物材料是丙烯均聚物。
4.根据权利要求1所述的方法，其特征在于：所述聚合链转移剂是烯丙醇的醚。
5.根据权利要求4所述的方法，其特征在于：所述醚是烯丙基丙氧基化物。
6.根据权利要求1所述的方法，其特征在于：所述接枝单体是甲基丙烯酸甲酯和丙烯酸甲酯。
7.一种组合物，它包含
(a)含有活性接枝点的丙烯聚合物材料，
(b)相对于100份丙烯聚合物材料，约2-240份的至少一种乙烯基取代的接枝单体，
(c)占单体总重量的约0.5-5％的为烯丙醇衍生物的聚合链转移剂。
8.根据权利要求7所述的组合物，其特征在于：所述丙烯聚合物材料选自：
(a)全同立构指数大于80的丙烯的结晶均聚物；
(b)丙烯与选自乙烯和4-10个碳α-烯烃的烯烃的结晶共聚物，条件是如果该烯烃是乙烯，则最大的聚合的乙烯量为10重量％，而当该烯烃是4-10个碳的α-烯烃时，其最大聚合量为20重量％，所述共聚物的全同立构指数大于85；
(c)丙烯与选自乙烯和4-8个碳的α-烯烃的两种烯烃的结晶三元共聚物，条件是最大的聚合的4-8个碳的α-烯烃量为20重量％，并且当乙烯是这些烯烃之一时，最大的聚合的乙烯量为5重量％，所述三元共聚物的全同立构指数大于85；
(d)一种烯烃聚合物组合物，它包含：
(i)约10-60重量％的全同立构指数大于80的结晶丙烯均聚物或者选自(a)丙烯和乙烯、(b)丙烯、乙烯和4-8个碳的α-烯烃、和(c)丙烯和4-8个碳的α-烯烃的单体的结晶共聚物，所述共聚物的聚合的丙烯量大于85重量％，全同立构指数大于85；
(ii)约5-25％的乙烯和丙烯或者4-8个碳的α-烯烃的在室温下不可溶解在二甲苯中的共聚物，以及
(iii)约30-70％的选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的弹性共聚物，所述共聚物任选地含有约0.5-10％的二烯，并且含有小于70重量％的聚合的乙烯，在室温下可溶解于二甲苯中，其特性粘数约为1.5-4.0dl/g，其中，(ii)和(iii)的总量占总的烯烃聚合物组合物的约50-90％，(ii)/(iii)的重量比小于0.4，所述组合物通过至少两个阶段的聚合来制备，其挠曲模量小于150MPa；或者
(e)一种热塑性烯烃，它包含：
(i)约10-60％的全同立构指数大于80的结晶丙烯均聚物或者选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的结晶共聚物，所述共聚物的聚合的丙烯量大于85％，其全同立构指数大于85；
(ii)约20-60％的选自(a)乙烯和丙烯、(b)乙烯、丙烯和4-8个碳的α-烯烃、以及(c)乙烯和4-8个碳的α-烯烃的单体的非晶共聚物，所述共聚物任选地含有约0.5-10％的二烯，并且含有小于70％的聚合的乙烯，在室温下可溶解于二甲苯中；以及
(iii)约3-40％的乙烯和丙烯或者4-8个碳的α-烯烃的在室温下不可溶解在二甲苯中的共聚物，其中，该组合物的挠性模量大于150但小于1200MPa。
9.根据权利要求8所述的组合物，其特征在于：所述丙烯聚合物材料是丙烯均聚物。
10.根据权利要求7所述的组合物，其特征在于：所述聚合链转移剂是烯丙醇的醚。
11.根据权利要求10所述的组合物，其特征在于：所述醚是烯丙基丙氧基化物。
12.根据权利要求7所述的组合物，其特征在于：所述接枝单体是甲基丙烯酸甲酯和丙烯酸甲酯。
CN02802697.7A 2001-08-08 2002-08-05 使用聚合链转移剂控制接枝共聚物的分子量 Expired - Fee Related CN1249112C (zh)