CN1320040C - 层体系及其制备方法 - Google Patents
层体系及其制备方法 Download PDFInfo
- Publication number
- CN1320040C CN1320040C CNB038236141A CN03823614A CN1320040C CN 1320040 C CN1320040 C CN 1320040C CN B038236141 A CNB038236141 A CN B038236141A CN 03823614 A CN03823614 A CN 03823614A CN 1320040 C CN1320040 C CN 1320040C
- Authority
- CN
- China
- Prior art keywords
- coating composition
- layer
- coating
- coating systems
- top layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
抗划层(K) | 顶层(D) | 泰伯磨损试验机雾度测试(%) | 储存在水中后的划格法测试(天) | |
实施例7 | 实施例1/2 | 实施例4 | 2.4 | >14 |
实施例8 | 实施例3 | 实施例 | 2.9 | >14 |
对比例9 | 实施例1/2 | 无 | 12 | >14 |
对比例10 | 实施例3 | 无 | 20 | >10 |
抗划层(K) | 顶层(D) | 施涂底涂层后的烘烤温度(℃) | 施涂底涂层后的烘烤时间(分钟) | 泰伯磨损试验机测试浊度(%) | |
实施例11 | 实施例1/2 | 实施例4 | 130 | 60 | 2.4 |
实施例12 | 实施例1/2 | 实施例4 | 130 | 30 | 5.7 |
实施例13 | 实施例3 | 实施例4 | 130 | 60 | 2.9 |
实施例14 | 实施例3 | 实施例4 | 130 | 45 | 10.8 |
实施例15 | 实施例3 | 实施例4 | 130 | 30 | 8.8 |
实施例16 | 实施例3 | 实施例4 | 130 | 15 | 14.3 |
实施例17 | 实施例1/2 | 实施例4 | 127 | 15 | 15.5 |
实施例18 | 实施例1/2 | 实施例4 | 127 | 30 | 11.1 |
实施例19 | 实施例1/2 | 实施例4 | 127 | 45 | 5.0 |
抗划层(K) | 顶层(D) | 顶涂层中的固体含量 | 泰伯磨损试验机测试浊度(%) | |
实施例20 | 实施例3 | 实施例4 | 1.0 | 2.9 |
实施例21 | 实施例3 | 实施例4 | 0.8 | 2.1 |
实施例22 | 实施例3 | 实施例4 | 1.5 | 无粘附力 |
实施例23 | 实施例3 | 实施例4 | 2.0 | 无粘附力 |
实施例24 | 实施例3 | 实施例4 | 0.5 | 15.7 |
实施例25 | 实施例1/2 | 实施例4 | 1.0 | 2.4 |
抗划层(K) | 顶层(D) | 顶涂层中的增塑剂类型 含量(%) | 泰伯磨损试验机测试浊度(%) | |
实施例26 | 实施例1/2 | 实施例5 | MPTS 5 | 2.1 |
实施例27 | 实施例1/2 | 实施例5 | MPTS 10 | 4.5 |
实施例28 | 实施例3 | 实施例5 | MPTS 10 | 7.3 |
实施例29 | 实施例3 | 实施例5 | MPTS 5 | 2.3 |
实施例30 | 实施例3 | 实施例4 | MTS 10 | 2.9 |
实施例31 | 实施例3 | 实施例6 | GPTS 10 | 3.0 |
抗划层(K) | 顶层(D) | 流动控制剂的量(%) | 泰伯磨损试验机测试浊度(%) | |
实施例32 | 实施例1/2 | 实施例4 | 0.5 | 3.6 |
实施例33 | 实施例1/2 | 实施例4 | 0.3 | 2.1 |
实施例34 | 实施例3 | 实施例4 | 0.5 | 5.5 |
实施例35 | 实施例3 | 实施例4 | 0.3 | 2.9 |
Claims (28)