CN1302082C - 用于聚酯的基于共接枝线性低密度聚乙烯和茂金属聚乙烯以及茂金属聚乙烯的共挤出粘合剂 - Google Patents
用于聚酯的基于共接枝线性低密度聚乙烯和茂金属聚乙烯以及茂金属聚乙烯的共挤出粘合剂 Download PDFInfo
- Publication number
- CN1302082C CN1302082C CNB038252481A CN03825248A CN1302082C CN 1302082 C CN1302082 C CN 1302082C CN B038252481 A CNB038252481 A CN B038252481A CN 03825248 A CN03825248 A CN 03825248A CN 1302082 C CN1302082 C CN 1302082C
- Authority
- CN
- China
- Prior art keywords
- layer
- metallocene
- blend
- 10min
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | ||||||
共接枝聚合物(A)的特性 | PE类型 | mPE | LLDPE | mPE | LLDPE | mPE | LLDPE | mPE | LLDPE |
密度(g/cm3) | 0.87 | 0.92 | 0.87 | 0.92 | 0.87 | 0.92 | 0.87 | 0.92 | |
共聚单体 | 1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 | |
组成 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | 50% | |
接枝度 | 0.9% | 0.9% | 0.9% | 0.9% | |||||
接枝单体 | MAH | MAH | MAH | MAH | |||||
MFI(g/10min)190℃,2.16kg | 0.7 | 0.7 | 0.7 | 0.7 | |||||
(A)的比例 | 15% | 25% | 15% | 25% | |||||
聚合物(B)的特性 | mPE类型 | E/1-辛烯 | E/1-辛烯 | E/1-辛烯 | E/1-辛烯 | ||||
密度(g/cm3) | 0.870 | 0.870 | 0.902 | 0.902 | |||||
MFI(g/10min)190℃,2.16kg | 5 | 5 | 10 | 10 | |||||
(B)的比例 | 85% | 75% | 85% | 75% | |||||
(A)和(B)共混物的MFI | 3 | 2.5 | 5.5 | 4.5 |
对比例1 | 对比例2 | 对比例3 | 对比例4 | ||||
mPE | LLDPE | mPE | LLDPE | mPE | LLDPE | mPE | LLDPE |
0.87 | 0.92 | 0.87 | 0.92 | 0.87 | 0.92 | 0.87 | 0.92 |
1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 |
50% | 50% | 50% | 50% | 50% | 50% | 50% | 50% |
0.9% | 0.9% | 0.9% | 0.9% | ||||
MAH | MAH | MAH | MAH | ||||
0.7 | 0.7 | 0.7 | 0.7 | ||||
25% | 25% | 15% | 25% | ||||
E/丙烯酸甲酯 | E/醋酸乙烯酯 | E/丙烯酸甲酯和mPE** | VLDPE(E/1-辛烯) | ||||
0.943 | 0.950* | 0.943和0.902** | 0.911 | ||||
8 | 20和3* | 8和10** | 6.6 | ||||
75% | 75% | 85%** | 75% |
对比例5 | 对比例6 | 对比例7 | |||
mPE | LLDPE | mPE | LLDPE | mPE | LLDPE |
0.87 | 0.92 | 0.87 | 0.92 | 0.87 | 0.92 |
1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 | 1-辛烯 | 1-丁烯 |
50% | 50% | 50% | 50% | 50% | 50% |
0.9% | 0.9% | 0.9% | |||
MAH | MAH | MAH | |||
0.7 | 0.7 | 0.7 | |||
25% | 25% | 25% | |||
LLDPE(E/1-辛烯) | LDPE | HDPE | |||
0.919 | 0.924 | 0.955 | |||
4.4 | 2 | 4 | |||
75% | 75% | 75% |
情况1 | 情况2 | 情况3 | ||||||||||
在t0时的FN/15mm | σ | 在t8时的FN/15mm | σ | 在t0时的FN/15mm | σ | 在t8时的FN/15mm | σ | 在t0时的FN/15mm | σ | 在t8时的FN/15mm | σ | |
实施例1 | 13.4 | 0.5 | 16.7 | 0.7 | 8.2 | 0.2 | 10.7 | 0.1 | - | - | - | - |
实施例2 | 14.2 | 0.5 | 17.8 | 0.4 | 10.6 | 0.3 | 12.8 | 0.4 | - | - | - | - |
实施例3 | 11.6 | 0.6 | 15.1 | 3.4 | 8.5 | 0.1 | 10.1 | 0.2 | - | - | - | - |
实施例4 | 12.5 | 0.8 | 20.1 | 1.8 | 10.4 | 0.2 | 12.1 | 0.3 | - | - | - | - |
对比例1 | 6 | 0.5 | 5.6 | 0.4 | - | - | - | - | 5.8 | 0.5 | 5.2 | 0.4 |
对比例2 | 6.1 | 0.5 | 6.6 | 0.9 | - | - | - | - | 5.7 | 0.2 | 5.8 | 0.4 |
对比例3 | 6.5 | 0.9 | 6.8 | 0.8 | - | - | - | - | 6.2 | 0.9 | 6.1 | 0.8 |
对比例4 | 4.4 | 2.1 | 1.3 | 0.2 | - | - | - | - | 4.1 | 1 | 2.1 | 0.2 |
对比例5 | 3.2 | 0.3 | 1.2 | 0.2 | - | - | - | - | 3.2 | 0.1 | 1.4 | 0.2 |
对比例6 | 2.6 | 0.2 | 1 | 0.1 | - | - | - | - | 2.7 | 0.2 | 1.2 | 0.1 |
对比例7 | 1.2 | 0.1 | 0.5 | 0.1 | - | - | - | - | 1 | 0.1 | 0.6 | 0.1 |
Claims (12)