CN1291048C - 镁基复合材料及其制造方法 - Google Patents
镁基复合材料及其制造方法 Download PDFInfo
- Publication number
- CN1291048C CN1291048C CN03803825.0A CN03803825A CN1291048C CN 1291048 C CN1291048 C CN 1291048C CN 03803825 A CN03803825 A CN 03803825A CN 1291048 C CN1291048 C CN 1291048C
- Authority
- CN
- China
- Prior art keywords
- magnesium
- composite material
- base composite
- magnesium base
- mentioned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
批号 | 压粉成形体 | 二氧化硅量(重量%) | 复合材料 | 反应生成量(重量%) | 机械特性 | 其他 | ||
Mg2Si | MgO | 硬度HRE | 拉伸强度(MPa) | |||||
1 | A-1 | 3.0 | B-1 | 3.7 | 3.9 | 52.2 | 102 | |
2 | A-2 | 5.0 | B-2 | 6.2 | 6.6 | 60.1 | 114 | |
3 | A-3 | 7.5 | B-3 | 9.4 | 9.9 | 69.8 | 132 | |
4 | A-4 | 10.0 | B-4 | 12.5 | 13.1 | 78.6 | 144 | |
5 | A-5 | 13.5 | B-5 | 16.8 | 17.8 | 87.4 | 146 | 工具磨耗 |
6 | A-6 | 1.5 | B-6 | 1.7 | 1.8 | 42.5 | 68 | |
7 | A-7 | 0 | B-7 | 0 | 0 | 40.2 | 63 | 凝附在工具上 |
批号 | 压粉成形体 | 混合粉末的组合 | 加热温度(℃) | 复合材料 | X射线衍射检出的有无 | ||
Mg2Si | MgO | SiO2 | |||||
8 | A-8 | Mg/二氧化硅 | 280 | B-8 | 有 | 有 | 无 |
9 | A-9 | Mg/二氧化硅 | 360 | B-9 | 有 | 有 | 无 |
10 | A-10 | Mg/二氧化硅 | 450 | B-10 | 有 | 有 | 无 |
11 | A-11 | Mg/二氧化硅 | 520 | B-11 | 有 | 有 | 无 |
12 | A-12 | Mg/二氧化硅 | 610 | B-12 | 有 | 有 | 无 |
13 | A-13 | 镁合金/二氧化硅 | 260 | B-13 | 有 | 有 | 无 |
14 | A-14 | 镁合金/二氧化硅 | 480 | B-14 | 有 | 有 | 无 |
15 | A-15 | 镁合金/二氧化硅 | 580 | B-15 | 有 | 有 | 无 |
16 | A-16 | 镁/二氧化硅 | 200 | B-16 | 无 | 无 | 有 |
17 | A-17 | 镁合金/二氧化硅 | 225 | B-17 | 无 | 无 | 有 |
批号 | 压粉成形体 | 加热温度(℃) | 复合材料 | X射线衍射的检出的有无 | |
Mg2Si | MgO | ||||
18 | A-18 | 280 | B-18 | 有 | 有 |
19 | A-19 | 340 | B-19 | 有 | 有 |
20 | A-20 | 470 | B-20 | 有 | 有 |
21 | A-21 | 575 | B-21 | 有 | 有 |
22 | A-22 | 620 | B-22 | 有 | 有 |
23 | A-23 | 190 | B-23 | 无 | 无 |
24 | A-24 | 235 | B-24 | 无 | 无 |
批号 | 压粉成形体 | 复合材料 | 生成量(重量%) | 磨耗试验后表面粗糙度Rmax(μm) | ||
Mg2Si | MgO | 钉状试验片 | 圆盘状试验片 | |||
(a) | A-(a) | B-(a) | 5.5 | 5.8 | 8.8 | 11.2 |
(b) | A-(b) | B-(b) | 5.3 | 0 | 12.3 | 26.5 |
(c) | A-(c) | B-(c) | 11.2 | 0 | 7.2 | 39.4 |
编号 | 配合组成(以重量为标准) | XRD鉴定出的相 | 平均摩擦系数(μ) | 挤出材料的拉伸强度(MPa) | ||
二氧化硅 | 石墨 | AZ31 | ||||
1 | 3 | 0 | 余部 | MgO,Mg2Si,Mg2Al3,Mg | 0.035 | 344 |
2 | 3 | 0.5 | 余部 | MgO,Mg2Si,Mg2Al3,Mg | 0.014 | 320 |
3 | 3 | 1.0 | 余部 | MgO,Mg2Si,Mg2Al3,Mg | 0.012 | 312 |
4 | 3 | 2.0 | 余部 | MgO,Mg2Si,Mg2Al3,Mg | 0.011 | 306 |
5 | 3 | 3.0 | 余部 | MgO,Mg2Si,Mg2Al3,Mg | 0.010 | 302 |
6 | 3 | 3.5 | 余部 | MgO,Mg2Si,Mg2Al3,Mg | 0.058 | 268 |
Claims (14)