CN118063134A - 一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法 - Google Patents
一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法 Download PDFInfo
- Publication number
- CN118063134A CN118063134A CN202410214086.1A CN202410214086A CN118063134A CN 118063134 A CN118063134 A CN 118063134A CN 202410214086 A CN202410214086 A CN 202410214086A CN 118063134 A CN118063134 A CN 118063134A
- Authority
- CN
- China
- Prior art keywords
- parts
- amber
- powder
- keel
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及饰品制作技术领域，具体涉及一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，制作步骤为：S1、准备如下份数的材料：食用乙醇10‑1000份、食品级乙酸乙酯20‑900份、化妆品级三乙醇胺1‑50份、促溶剂1‑300份、琥珀边角料500‑1500份、天然龙骨600‑2000份、猛犸牙边角料300‑1500份、碳酸钙粉10‑450份与二甲酸二异壬基酯1‑50份；S2、配制溶剂，按照比例称取食用乙醇、食品级乙酸乙酯，化妆品级三乙醇胺与促溶剂，将其倒入搅拌容器内，进行搅拌混合。本发明通过用琥珀、龙骨和猛犸象牙加工后剩余的边角料为主要成分合成饰品的制作方法，可以变废为宝，制作出造型精美、细节清晰，表面光滑细腻、质感媲美传统牙雕，且材质环保无毒的饰品，减少了资源的浪费情况。
Description
技术领域
本发明属于饰品制作技术领域，具体为一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法。
背景技术
传统琥珀饰品和猛犸象牙饰品在加工过程中会产生大量的边角料，这些边角料基本都当废品直接扔掉了。琥珀是植物油脂的化石；龙骨是一种动物化石，主要用在中药饮片上，品质差的龙骨无法入药，被直接扔掉或低价销售；龙骨和猛犸象牙都是远古动物的化石，都是不可再生的材料，传统琥珀和猛犸牙饰品加工后产生的废料直接扔了非常可惜，造成了资源的浪费，对此，我们提供了一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法。
发明内容
针对现有技术的不足，本发明提供了一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，解决了材料浪费的情况。
为实现上述目的，本发明提供如下技术方案：一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，制作步骤为：
S1、准备如下份数的材料：食用乙醇10-1000份、食品级乙酸乙酯10-1000份、化妆品级三乙醇胺1-50份、促溶剂1-300份、琥珀边角料500-1500份、天然龙骨600-2000份、猛犸牙边角料300-1500份、碳酸钙粉10-450份与二甲酸二异壬基酯1-50份；
S2、配制溶剂，按照比例称取食用乙醇、食品级乙酸乙酯，化妆品级三乙醇胺与促溶剂，按顺序放入旋转蒸馏瓶中进行搅拌混合，制得溶剂A；
S3、按比例称取琥珀边角料，将琥珀边角料人工剔除杂质后放入溶剂A中，倒入旋转蒸馏瓶中加热至70℃，蒸馏瓶以每分钟60转的速度进行旋转，等待琥珀完全溶解在溶剂A中，制得琥珀液，加热中蒸发的溶剂通过冷凝器进行回收；
S4、取天然龙骨，人工剔除杂质，将天然龙骨放置在不锈钢粉碎机中粉碎成150目的龙骨粉，将龙骨粉进行脱色处理，脱色处理后进行烘干，烘干后再次进行粉碎处理，粉碎成2000目的龙骨细粉；
S5、取猛犸象牙边角料，人工剔除杂质，将猛犸象牙边角料放置在不锈钢粉碎机中粉碎成150目的牙粉，取出牙粉进行脱色处理，脱色处理后进行烘干，烘干后再次进行粉碎处理，粉碎成2000目的细牙粉；
S6、按比例称取溶剂A、龙骨粉、牙粉、碳酸钙、二甲酸二异壬基酯。将溶剂A倒入不锈钢夹层加热釜中，加热到60度，开动搅拌器，以每分钟60转的速度边搅拌边加入龙骨粉和牙粉，龙骨粉和牙粉加入完成后，继续加入碳酸钙粉和二甲酸二异壬基酯，继续进行加热搅拌120分钟，将混合好的浆料倒入不锈钢桶中静止24h后制得浆料；
S7、将浆料加热至50℃，倒入适量S3步骤制备好的琥珀液，搅拌均匀后，倒入提前用硅胶制作好的模具内，放入真空箱内部，抽真空至-0.1MP，在-0.1MP的真空度下保持3分钟,拿出模具，放入烤箱内部，将烤箱温度调节至80℃，烘烤6-8h后取出模具，等待自然冷却；
S8、将模具内凝固好的板材取出，通过机器或者手工雕刻出饰品样式，进行打磨抛光后制得饰品；
其中各种造型的饰品模具内取出的胚子，只需经过简单的修整即可得到成品饰品，琥珀液作为浆料的稀释剂，加入的量以浆料能轻易流动为准，模具造型包括方形模具与各种造型的饰品模具。
优先地，S1步骤中具体份数的材料为：食用乙醇300份、食品级乙酸乙酯310份、化妆品级三乙醇胺15份、促溶剂100份、琥珀边角料900份、天然龙骨1500份、猛犸牙边角料1100份、碳酸钙粉210份与二甲酸二异壬基酯10份；
其中促溶剂包括天然松节油75份、化妆品级乙二醇5份、十二烷基硫酸钠10份与柠檬酸10份；
食用乙醇也被称为发酵性蒸馏酒，主要是利用薯类、谷物类、糖类作为原料，经过蒸煮、糖化、发酵等处理而得到的供食品、工业使用的含水酒精，其风味特色主要体现在蒸馏酒中醛、酸、酯、醇这四大主要杂质的含量上，不同的口味和气体会使蒸馏酒的风味不同，食用酒精浓度高的可以达到99度以上，用于工业溶剂，75度的食用酒精可以用于消毒，食用酒精还可以用来调制酒精含量不同的各种含酒精饮料；
食品级乙酸乙酯是一种用于食品行业的化学物质，可以作为香精香料使用，也可以用于酒类、食用勾兑白酒等产品的增香调香，这种乙酸乙酯的纯度很高，符合食品级标准；
促溶剂用以提高化学反应的速率和效率，促进物质的溶解和分散，以及改善产品的质量和性能，常见的促溶剂包括十二烷基硫酸钠、柠檬酸、聚乙二醇、表面活性剂等；
松节油是精油的一种，它是一种重要的工业原料，松节油是通过蒸馏松柏科植物的树脂所提取的液体，主要成分是萜烯，松节油作为化工原料应用广泛，在美术玻璃、油漆、樟脑制造、制药、松香制作等工业中均会使用松节油；
碳酸钙粉是一种白色粉体，由方解石、石灰石、白垩、贝壳原料煅烧制成，碳酸钙粉有重质碳酸钙和轻质碳酸钙两种，重质碳酸钙是将原料破碎、磨碎后制得，而轻质碳酸钙则是通过化学方法制成，即先将石灰石等原料煅烧生成石灰和二氧化碳，然后加水消化石灰生成石灰乳，通入二氧化碳后碳化石灰乳生成碳酸钙沉淀，最后经脱水、干燥和粉碎制得。
优先地，食用乙醇与食品级乙酸乙酯的浓度为99％，促溶剂为天然松节油、化妆品级乙二醇、十二烷基硫酸钠和柠檬酸，琥珀边角料为琥珀加工后产生的边角料，天然龙骨为动物骨骼化石，猛犸象牙粉为猛犸牙雕加工后产生的废料，碳酸钙粉为重质碳酸钙。
优先地，S2步骤中溶剂配置步骤通过预先将食用乙醇与食品级乙酸乙酯倒入在搅拌容器内部，进行搅拌混合，搅拌时间总时间为1h，在搅拌容器搅拌至20min后，在搅拌容器内部加入化妆品级三乙醇胺进行不断搅拌，在搅拌容器搅拌至30min后，在搅拌容器内部加入促溶剂不断搅拌，让材料充分混合。
优先地，S3步骤中将琥珀边角料放入25℃的温水中浸泡1min后，取出进行冲洗，去除外表面的杂质，旋转蒸馏瓶使用步骤为：
A1、打开电源，在旋转蒸馏瓶加料口中加入材料；
A2、调节主机高度，让材料液面平于旋转瓶液面，打开加热开关，调节温度至70℃；
A3、关闭加料口，将冷凝器与蒸发口连通；
A4、在蒸馏结束后，关闭开关，停止旋转，打开加料口，卸下旋转瓶即可。
优先地，S4步骤中天然龙骨剔除杂质通过将天然龙骨放入在清水中浸泡3h后，使用毛刷将天然龙骨外表面的杂质刷去，随后将天然龙骨再次放入清水中浸泡2h后，使用擦拭布对天然龙骨外表面进行擦拭，除去杂质；龙骨粉脱色处理通过使用氧化剂、还原剂与化学脱色剂混合在龙骨粉中，进行不断搅拌，让材料与龙骨粉混合反应，最后通过过滤，洗涤去除残留化学物质，得到脱色的龙骨粉。
优先地，S5步骤中牙粉脱色采用化学脱色处理，准备脱色剂与牙粉进行混合，并不断的搅拌，将脱色剂与牙粉产生反应，搅拌3h后，通过过滤设备将牙粉与脱色剂进行分离，并使用清水洗涤牙粉，将洗涤后的牙粉进行烘干，完成脱色。
优先地，S6步骤中搅拌速度60r/min，加热的温度为60℃。
优先地，S7步骤中真空箱使用前确保箱内的密封性，并检查设备是否完好正常使用。
优先地，S8步骤中饰品打磨砂纸目数为1000目，抛光砂纸的目数为3000目。
与现有技术相比，本发明的有益效果如下：
本发明通过用琥珀、龙骨和猛犸象牙加工后剩余的边角料为主要成分合成饰品的制作方法，可以变废为宝，制作出造型精美、细节清晰，表面光滑细腻、质感媲美传统牙雕，且材质环保无毒的饰品，可当吊坠、汽车挂饰，家居挂件、摆件等，减少了资源的浪费情况。
具体实施方式
基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，制作步骤为：
S1、准备如下份数的材料：食用乙醇300份、食品级乙酸乙酯310份、化妆品级三乙醇胺15份、促溶剂100份、琥珀边角料900份、天然龙骨1500份、猛犸牙边角料1100份、碳酸钙粉210份与二甲酸二异壬基酯10份；
S2、配制溶剂，按照比例称取食用乙醇、食品级乙酸乙酯，化妆品级三乙醇胺与促溶剂，按顺序放入旋转蒸馏瓶中进行搅拌混合，制得溶剂A；
S3、按比例称取琥珀边角料，将琥珀边角料人工剔除杂质后放入溶剂A中，倒入旋转蒸馏瓶中加热至70℃，蒸馏瓶以每分钟60转的速度进行旋转，等待琥珀完全溶解在溶剂A中，制得琥珀液，加热中蒸发的溶剂通过冷凝器进行回收；
S4、取天然龙骨，人工剔除杂质，将天然龙骨放置在不锈钢粉碎机中粉碎成150目的龙骨粉，将龙骨粉进行脱色处理，脱色处理后进行烘干，烘干后再次进行粉碎处理，粉碎成2000目的龙骨细粉；
S5、取猛犸象牙边角料，人工剔除杂质，将猛犸象牙边角料放置在不锈钢粉碎机中粉碎成150目的牙粉，取出牙粉进行脱色处理，脱色处理后进行烘干，烘干后再次进行粉碎处理，粉碎成2000目的细牙粉；
S6、按比例称取溶剂A、龙骨粉、牙粉、碳酸钙、二甲酸二异壬基酯，将溶剂A倒入不锈钢夹层加热釜中，加热到60度，开动搅拌器，以每分钟60转的速度边搅拌边加入龙骨粉和牙粉，龙骨粉和牙粉加入完成后，继续加入碳酸钙粉和二甲酸二异壬基酯，再继续进行加热搅拌120分钟，将混合好的浆料倒入不锈钢桶中静止24h后制得浆料；
S7、将浆料加热至50℃，倒入适量S3步骤制备好的琥珀液，搅拌均匀后，倒入提前用硅胶制作好的模具内，放入真空箱内部，抽真空至-0.1MP，在-0.1MP的真空度下保持3分钟,拿出模具，放入烤箱内部，将烤箱温度调节至80℃，烘烤6-8h后取出模具，等待自然冷却；
S8、将模具内凝固好的板材取出，通过机器或者手工雕刻出饰品样式，进行打磨抛光后制得饰品。
实施例2
一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，制作步骤为：
S1、准备如下份数的材料：食用乙醇300份、食品级乙酸乙酯310份、化妆品级三乙醇胺15份、促溶剂100份、琥珀边角料900份、天然龙骨1500份、猛犸牙边角料1100份、碳酸钙粉210份、二甲酸二异壬基酯10份；
S2、配制溶剂，按照比例称取食用乙醇、食品级乙酸乙酯，化妆品级三乙醇胺与促溶剂，将其倒入搅拌容器内，进行搅拌混合，制得溶剂A；
S3、按比例称取琥珀边角料，将琥珀边角料剔除杂质后放入溶剂A中，倒入旋转蒸馏瓶中加热至80℃，等待琥珀溶解在溶剂中，制得琥珀液，加热中蒸发的溶剂通过冷凝器回收；
S4、称取天然龙骨，剔除杂质，将天然龙骨放置在不锈钢粉碎机中粉碎成150目的龙骨粉，将龙骨粉进行脱色处理，烘干后再次进行粉碎处理，粉碎为2000目；
S5、称取猛犸牙边角料，剔除杂质，放置在不锈钢粉碎机中初步粉碎为150目牙粉，取出进行脱色与烘干，二次3000目的牙粉；
S6、取溶剂A，将龙骨粉与牙粉倒入内部，进行不断的搅拌，在搅拌过程中，不断的添加碳酸钙粉与二甲酸二异壬基酯，进行加热搅拌，静止24h后制得浆料；
S7、将浆料加热至70℃，倒入制备好的琥珀液搅拌后，倒入模具内，放入真空箱内部，抽真空至-0.1mp，拿出模块，放入烤箱内部，将烤箱温度调节至80℃，烘烤6-8h后取出模具，等待自然冷却；
S8、将冷却后的模具板材取出，通过手工雕刻出饰品样式，进行打磨抛光后制得饰品。
对比例1
手工雕刻的饰品为普通材质所制得。
下表为不同实施例制备出的合成饰品性质表
| 组别 | 光滑度 | 纹理 |
| 实施例1 | 光滑 | 清晰 |
| 实施例2 | 光滑 | 清晰 |
| 对比例1 | 粗糙 | 模糊 |
以上所述的实施例1，仅为本发明的较佳实施例，并非用以限定本发明的范围，本发明的上述实施例还可以做出各种变化，即凡是依据本发明申请的权利要求书及说明书内容所作的简单、等效变化与修饰，皆落入本发明专利的权利要求保护范围，本发明未详尽描述的均为常规技术内容。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其制作步骤为：
S1、准备如下份数的材料：食用乙醇10-1000份、食品级乙酸乙酯10-1000份、化妆品级三乙醇胺1-50份、促溶剂1-300份、琥珀边角料500-1500份、天然龙骨600-2000份、猛犸牙边角料300-1500份、碳酸钙粉10-450份与二甲酸二异壬基酯1-50份；
S2、配制溶剂，按照比例称取食用乙醇、食品级乙酸乙酯，化妆品级三乙醇胺与促溶剂，按顺序放入旋转蒸馏瓶中进行搅拌混合，制得溶剂A；
S3、按比例称取琥珀边角料，将琥珀边角料人工剔除杂质后放入溶剂A中，倒入旋转蒸馏瓶中加热至70℃恒温，蒸馏瓶以每分钟60转的速度进行旋转，等待琥珀完全溶解在溶剂A中，制得琥珀液，加热中蒸发的溶剂通过冷凝器进行回收；
S4、取天然龙骨，人工剔除杂质，将天然龙骨放置在不锈钢粉碎机中粉碎成150目的龙骨粉，将龙骨粉进行脱色处理，脱色处理后进行烘干，烘干后再次进行粉碎处理，粉碎成2000目的龙骨细粉；
S5、取猛犸象牙边角料，人工剔除杂质，将猛犸象牙边角料放置在不锈钢粉碎机中粉碎成150目的牙粉，取出牙粉进行脱色处理，脱色处理后进行烘干，烘干后再次进行粉碎处理，粉碎成2000目的细牙粉；
S6、按比例称取溶剂A、龙骨粉、牙粉、碳酸钙、二甲酸二异壬基酯，将溶剂A倒入不锈钢夹层加热釜中，加热到60度，开动搅拌器，以每分钟60转的速度边搅拌边加入龙骨粉和牙粉，龙骨粉和牙粉加入完成后，继续加入碳酸钙粉和二甲酸二异壬基酯，继续进行加热搅拌120分钟，将混合好的浆料倒入不锈钢桶中静止24h后制得浆料；
S7、将浆料加热至50℃，倒入适量S3步骤制备好的琥珀液，搅拌均匀后，倒入提前用硅胶制作好的模具内，放入真空箱内部，抽真空至-0.1MP，在-
0.1MP的真空度下保持3分钟，拿出模具，放入烤箱内部，将烤箱温度调节至80℃，烘烤6-8h后取出模具，等待自然冷却；
S8、将模具内凝固好的板材取出，通过机器或者手工雕刻出饰品样式，进行打磨抛光后制得饰品。
2.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于，S1步骤中具体份数的材料为：食用乙醇300份、食品级乙酸乙酯310份、化妆品级三乙醇胺15份、促溶剂100份、琥珀边角料900份、天然龙骨1500份、猛犸牙边角料1100份、碳酸钙粉210份与二甲酸二异壬基酯10份。
3.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：食用乙醇与食品级乙酸乙酯的浓度为99％，促溶剂为天然松节油、化妆品级乙二醇、十二烷基硫酸钠、柠檬酸按比例组成，琥珀边角料为琥珀加工后产生的边角料或小颗粒海漂琥珀，龙骨为动物骨骼化石，材料选用为中药材龙骨的等外品无法药用的次品龙骨，猛犸象牙粉为猛犸牙雕加工后产生的边角料，碳酸钙粉为重质碳酸钙。
4.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S2步骤中溶剂配置步骤通过预先将食用乙醇与食品级乙酸乙酯倒入在旋转蒸馏瓶内进行搅拌混合，搅拌总时间为1h，在搅拌容器搅拌至20min后，在搅拌容器内部加入化妆品级三乙醇胺进行不断搅拌，在搅拌容器搅拌至30min后，在搅拌容器内部加入促溶剂不断搅拌，让材料充分混合。
5.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S3步骤中将琥珀边角料放入25℃的温水中浸泡1min后，取出进行冲洗，去除外表面的杂质。
旋转蒸馏瓶使用步骤为：
A1、打开电源，在旋转蒸馏瓶加料口中加入材料；
A2、调节主机高度，让材料液面平于旋转瓶液面，打开加热开关，调节温度至70℃；
A3、关闭加料口，将冷凝器与蒸发口连通；
A4、打开冷凝水开关，不需要开启真空泵；
A5、在蒸馏结束后，关闭开关，停止旋转，打开加料口，卸下旋转瓶即可。
6.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S4步骤中天然龙骨剔除杂质，将天然龙骨放入清水中浸泡3h后，使用毛刷将天然龙骨外表面的杂质刷去，随后将天然龙骨再次放入清水中浸泡2h后，过滤水分，使用擦拭布对天然龙骨外表面进行擦拭，除去杂质；龙骨粉脱色处理通过使用氧化剂、还原剂与化学脱色剂混合在龙骨粉中，进行不断搅拌，让材料与龙骨粉混合反应，最后通过过滤，洗涤去除残留化学物质，得到脱色的龙骨粉。
7.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S5步骤中牙粉脱色采用化学脱色处理，准备脱色剂与牙粉进行混合，并不断的搅拌，将脱色剂与牙粉产生反应，搅拌3h后，通过过滤设备将牙粉与脱色剂进行分离，并使用清水洗涤牙粉，将洗涤后的牙粉进行烘干，完成脱色。
8.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S6步骤中搅拌速度60r/min，加热的温度为60℃。
9.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S7步骤中真空箱使用前确保箱内的密封性，并检查设备是否完好正常使用。
10.根据权利要求1所述的用琥珀、龙骨、猛犸象牙粉合成饰品的制作方法，其特征在于：S8步骤中饰品打磨砂纸目数为1000目，抛光的目数为3000目。