CN117680158A - 一种加氢精制催化剂及其制备方法、预硫化方法、开工方法 - Google Patents
一种加氢精制催化剂及其制备方法、预硫化方法、开工方法 Download PDFInfo
- Publication number
- CN117680158A CN117680158A CN202211100436.9A CN202211100436A CN117680158A CN 117680158 A CN117680158 A CN 117680158A CN 202211100436 A CN202211100436 A CN 202211100436A CN 117680158 A CN117680158 A CN 117680158A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- potassium
- carrier
- oil
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种加氢精制催化剂及其制备方法、预硫化方法、开工方法。该催化剂的制备方法包括:在浸渍活性组分之前,采用含钾的喷淋液对载体进行喷淋的步骤,以及,以含钾的活性组分浸渍液对经过喷淋的载体进行浸渍的步骤。所得催化剂在减少预硫化处理所需硫化剂用量的同时具有优异的加氢性能,预硫化过程中能够大幅降低硫化氢的排放,减小环境污染,降低生产成本和操作安全风险。
Description
技术领域
本发明属于加氢精制催化剂领域,具体涉及一种加氢精制催化剂及其制备方法、预硫化方法、开工方法。
背景技术
加氢精制技术是改善石油化工产品质量的主要手段,其核心是加氢精制催化剂。加氢精制催化剂分为负载型和非负载型,现今工业上主要应用的是负载型催化剂。负载型加氢精制催化剂一般是将活性金属(Mo、W、Ni、Co等)浸渍到载体上,浸渍法制备的催化剂活性组分分布在催化剂载体的内外表面上,包括内部深处空隙和孔的内表面上。对于加氢精制催化剂制备方法的报道很多,主要围绕制备方法和过程研究、载体改性、助剂添加等方面展开。
常规方法制备的加氢精制催化剂活性金属为氧化态,而实际使用时真正起催化作用的物质为活性组分的硫化态。氧化态催化剂在使用前,其活性金属需转化为硫化态,催化剂有较高的催化活性。因此,加氢催化剂在使用前需经过硫化活化,称之为预硫化。催化剂的预硫化对催化剂的性能具有重要影响,是催化剂应用前的重要处理步骤。催化剂的预硫化方法按载硫的方式可分为器内预硫化和器外预硫化。
器内预硫化技术是将催化剂装入反应器后再进行硫化处理。反应所需的硫化氢通常用硫化剂分解来制取,工业上通常采用二甲基二硫(以下简称DMDS)。主要的硫化步骤为:在热氢循环的状态下(反应器入口温度达180℃),逐渐向系统中注入DMDS,然后与氢气发生分解反应,释放出硫化氢气体,再与反应器中氧化态的催化剂发生反应,最终得到硫化态的催化剂。该方法主要存在三个方面的问题:(1)使用的硫化剂有毒有害、易产生环境污染;(2)装置需配备仅在开工期间使用的硫化设施及配套管线等;(3)硫化过程中装置在高温、高压、高H2S浓度存在安全环保隐患。
因而器外预硫化方法应运而生。器外预硫化技术的优势是:(1)器外预硫化技术使加氢催化剂活性金属组分的利用率提高,催化剂硫化得更充分;(2)器外预硫化技术可以节省开工时间,使开工过程更加便捷;(3)器外预硫化催化剂的开工现场避免了使用有毒的硫化物,而且也不需要安装专用的硫化设施。
CN112742487A公开了一种预硫化加氢催化剂的开工方法,方法包括:(1)将硫化剂与氧化态的加氢催化剂混合均匀;(2)将步骤(1)的混合物进行热处理;降温后加入含磷物质;(3)将步骤(2)所得物料干燥,得到预硫化催化剂;(4)将步骤(3)预硫化催化剂装入反应器,进行湿法活化开工。
CN104646034A涉及一种硫化型加氢精制催化剂的制备方法。采用浸渍溶液浸渍载体,然后经原位晶化反应和热处理得硫化型加氢精制催化剂,其中,所述的浸渍溶液含有活性金属钼酸铵和/或钨酸铵、Ni和/或Co的无机盐前驱体,同时含有硫化剂、有机络合剂和助溶剂。
CN109926101A公开了一种硫化型催化剂的开工方法,还包括了器外预硫化加氢催化剂的硫化方法,所述硫化型催化剂组合物包括:氧化态加氢催化剂、固体硫、辅助物、有机化合物和水合肼。将硫化型加氢催化剂组合物装入反应器中,进行氮气气密,氮气气密合格后逐步引入氢气,进行氢气低压气密,低压气密合格后升温升压进行高压气密;高压气密合格后,调整压力至反应压力至硫化完成,最后调整温度至反应温度,进原料油开始进行加氢反应。
ZL200810010245.7公开了一种加氢催化剂预硫化方法及加氢工艺开工方法。催化剂预硫化过程中,预硫化的部分催化剂的硫化剂引入量大大高于催化剂中活性加氢金属的理论需硫量。预硫化的加氢催化剂与未预硫化的加氢催化剂混合或分层装填在反应器中,经过开工活化,使所有催化剂均进行有效的硫化处理。该催化剂硫化活性相可能存在分布不均的问题。
CN103805235A涉及一种加氢装置湿法开工方法、低能耗加氢工艺以及加氢设备。在加氢装置反应区内装填硫化型加氢催化剂,开工过程首先用开工油通过换热达到一定温度通过催化剂床层,利用换热和活化时的反应热使得催化剂床层达到180±10℃或以上,在循环气中掺混一部分烯烃含量高的气体,利用烯烃加氢反应得到的反应热继续升温至230±5℃恒温活化,温度至270±10℃或以上时,分步换进原料油,利用原料油中加氢反应得到反应热继续升温,最后通过冷氢量和换热器来调整反应温度,转入正常生产。但在较高温度条件下,高烯烃含量的原料油,可能会导致硫化过程中积碳的形成,竞争硫化态活性金属的占位。
CN102051203A公开了一种器外预硫化催化剂的开工方法。所述方法包括:在催化剂的润湿阶段,开工油和氢气由反应器底部引入,待开工油充满反应系统后,系统闭路循环,逐步升温活化,待床层温度达到280-320℃后,活化结束。本发明方法中催化剂润湿采用开工油和氢气从反应器底部引入反应器的方式,催化剂润湿更加充分彻底,能有效防止催化剂床层中“干区”的存在,从而使得催化剂的活化更加充分。本发明开工方法工艺简单,操作便捷,活化效果较常规方法更为理想,从而有利于提高催化剂的活性。
CN111321001A公开一种加氢处理催化剂的开工方法,具体包括如下步骤:(1)向硫化后的加氢处理催化剂床层中引入开工柴油对硫化态的加氢处理催化剂进行润湿,所述开工柴油中含有含磷有机物;(2)当开工柴油穿透催化剂床层后,提高反应器温度到300-400℃进行处理10min-120min;(3)切换原料油,进行合格产品生产。
CN200710012674.3中提到一种汽油加氢精制开工方法,在特定的硫化温度和时间下对加氢脱硫催化剂进行预硫化后切换原料,并直接调整工艺参数至常规反应条件下进行汽油选择性加氢脱硫反应。该方法的不足之处在于切换原料后的稳定时间较长,该专利的具体实施例中,在小型评价装置上稳定时间长达100小时,实验时间方面的效率较低。更重要的是,众所周知,大型工业装置开工初期因为催化剂活性不稳定而造成的产品质量较差,会给企业带来较大的经济压力。
催化剂中引入助剂是提高加氢催化剂活性的最常用手段之一,加氢精制催化剂常用的助剂包括第一助剂钴、镍等金属和第二助剂磷、硼等非金属。同时,螯合剂等配制活性组分溶液过程作为络合组成的如柠檬酸、磷酸、乙二胺、乙二胺四乙酸、乙二醇等在加氢精制催化剂制备过程的应用,均取得了良好的效果。
CN110479300A公开了一种加氢催化剂及其制备方法和应用以及加氢精制的方法,该催化剂包括载体和负载在该载体上的活性金属组分A、活性金属组分B和有机螯合剂,部分活性金属组分B以三硫化物形式存在,剩余部分活性金属组分B以三氧化物形式存在,硫与活性金属组分B的原子比为2.1-2.9,催化剂的硫化度为40-85%。该催化剂的制备方法包括:(l)采用含有第VIII族金属化合物、第VIB族金属化合物和有机螯合剂的溶液C对载体进行浸渍,干燥得到固体A;(2)将含有有机硫源的溶液D与固体A接触,然后进行干燥。
CN201110321357公开了一种加氢精制催化剂硫化方法。该方法在较高温度下才向系统内引入硫化氢和注入硫化剂,可以避免Co和/或Ni的低温单独硫化,从而在较高温度和硫化氢存在的情况下,Mo和/或W与Co和/或Ni同时硫化形成高活性Mo(W)-Co(Ni)-S活性相。
ZL201510700293.9涉及一种加氢催化剂及其制备方法,该制备方法包括:(1)采用浸渍法将加氢金属活性组分的水溶性盐和有机络合剂负载到载体上,然后进行干燥、焙烧,得到半成品催化剂,所述焙烧条件使得以半成品催化剂的总量为基准,半成品催化剂中炭含量为0.03-0.5重量%;(2)以含有有机络合剂的溶液作为浸渍液,对步骤(1)所得半成品催化剂进行浸渍,然后进行干燥且不进行焙烧;(3)将作为助剂的金属元素负载到载体上;其中,步骤(3)在步骤(1)之前、之中和之后且在步骤(2)之前的任意一个或多个进行。该专利采用三步浸渍法制备催化剂,耗费大量的人力物力,会造成催化剂制备成本的大幅增加。
ZL91110935.8公开了一种钴钼加氢精制催化剂的制备方法,该方法将乙酸钴溶于水后加入乙二胺,乙酸钴和乙二胺摩尔比为1:1.5-3,使其形成钴乙二胺的混合溶液,在溶液中加入浓氨水调节pH值为12-14后加入钼酸铵充分溶解,制成含有钴钼金属的共浸液,将多孔载体用此溶液浸渍后制备催化剂。该方法的缺点是需要在无氧或微氧气氛中焙烧得到催化剂产品。
US4409131公开了一种CoMo/NiMo催化剂的制备方法,其是由含有活性组分及氨水的溶液一步浸渍载体制得的,该方法详细介绍了活性组分浸渍液的配制过程,在配制浸渍液过程中,需要加热混合物促进活性组分的溶解。
US6013598公开了一种选择性加氢脱硫催化剂的制备方法,该催化剂由活性组分钴、钼及载体氧化铝组成,是由含有活性组分并添加柠檬酸的水溶液等体积浸渍载体制得,该方法得到的催化剂氧化钼含量最高只能达到10wt%。
ZL00130284.1涉及一种裂解汽油二段加氢精制催化剂及其制备方法,该方法用氧化铝前身物,在其成型时,加入高聚物、第Ⅳ副族金属,经干燥焙烧,得到含第Ⅳ副族金属的载体,使用含有钼、钴、镍活性组分的氨共浸液浸渍,再经过干燥焙烧得到催化剂。Ⅳ副族金属的加入调节了载体的酸碱性,抑制催化剂的结焦失活速度。
ZL99113281.5涉及一种馏分油加氢精制催化剂及其制备方法,该催化剂以氧化铝或含硅氧化铝为载体,添加磷助剂,以W、Mo、Ni为活性组分,采用分段共浸渍技术,将配制的W、Mo、Ni、P共浸液通过多次浸渍,最终制备得到催化剂。
ZL00122922.2公开了一种馏分油加氢脱硫催化剂及制备方法,该催化剂以氧化铝或含硅氧化铝为载体,以Mo-Ni为活性组分,添加磷助剂。通过采用碱性的Mo-Ni-P共浸液分段共浸载体,然后将共浸渍以分步共浸的方式浸渍载体,该专利采用二步或以上制备得到催化剂。
文献“Co-Mo-Ni-W/γ-Al2O3柴油加氢精制催化剂的研制(姚媛媛,张孔远等,工业催化,2008(02):18-22.)”考察了扩孔剂及焙烧温度对载体物化性能的影响和浸渍液的配制方法对其稳定性的影响。其公开的浸渍液的配制方法主要有两种,(1)低温法配制:①将去离子水和磷酸加热后加入碱式碳酸镍(或碱式碳酸钴)和三氧化钼,继续加热搅拌至溶解,冷却至室温待用;②微热去离子水中加入偏钨酸铵和醋酸钴(或硝酸镍),搅拌溶解,冷却至室温待用;③将冷却的偏钨酸铵和醋酸钴(或硝酸镍)溶液和①中配制的镍(钴)钼磷溶液混合,搅拌均匀后定容待用。(2)高温法配制:将三氧化钼、磷酸和碱式碳酸镍(或碱式碳酸钴)溶于去离子水,加热搅拌使之完全溶解,然后加入偏钨酸铵及醋酸钴(或硝酸镍),继续加热搅拌,直至完全溶解为澄清溶液后定容待用。在配制浸渍溶液的过程中均需要加热,并加入无机酸。
CN94114194.2公开了一种烃类加氢脱硫催化剂及制备方法,该催化剂以氧化锌改性的γ-Al2O3作载体,以钴、钼为活性组分,采用钴、钼共浸液一次浸渍制备而成。制得的催化剂其组成为:CoO 1-10wt%,MoO3 5-18wt%,ZnO 1-15wt%,余量为γ-Al2O3。但催化剂的长周期稳定性运行效果有待进一步考察。
负载型催化剂活性组分(尤其是活性组分含量高的条件下)较难在载体表面形成单层分散或达到分散阈值,活性组分与载体间相互作用的适宜程度是影响催化剂有效负载量的主要因素之一。一般而言,载体上活性组分的分散度越高,有效活性位数量越多,催化剂的活性就越高,但是还要综合考虑催化剂的长周期稳定性,因此,如何改善活性组分与载体的相互作用以增加活性组分在载体上的有效负载是加氢精制催化剂研发的重点。同时催化剂在预硫化过程中,催化剂中负载的硫含量一般按催化剂中活性金属的理论需硫量确定,催化剂中引入硫化剂的量一般为所有氧化态加氢催化剂理论需硫量的90-150%。开工时,采用直接升温的操作方式。
发明内容
为了解决上述问题,本发明的目的在于提供一种加氢精制催化剂及其制备方法、预硫化方法、开工方法,该催化剂在减少预硫化处理所需硫化剂用量的同时具有优异的加氢性能,开工的过程中大幅降低硫化氢的排放,减小环境污染,降低生产成本和操作安全风险。
为了达到上述目的,本发明提供了一种加氢精制催化剂的制备方法,其中,该制备方法包括:在浸渍活性组分之前,采用含钾的喷淋液对载体进行喷淋的步骤,以及,以含钾的活性组分浸渍液对经过喷淋的载体进行浸渍的步骤。
在上述加氢精制催化剂的制备方法中,优选地,所述喷淋的时间为1min-20min,更优选为3min-10min。喷淋过程可以采用常规的喷雾设备进行,例如:农用高压电动喷雾器。
在上述加氢精制催化剂的制备方法中,优选地,所述含钾的喷淋液是将含钾的化合物(例如钾的无机盐、氢氧化钾等)溶于去离子水制成的。
在上述加氢精制催化剂的制备方法中,优选地,所述含钾的喷淋液为氢氧化钾溶液。
在上述加氢精制催化剂的制备方法中,优选地,所述含钾的喷淋液的浓度为0.1%-5%,更优选为0.5%-1%。
在上述加氢精制催化剂的制备方法中,优选地,所述含钾的喷淋液的体积占所述含钾的喷淋液与所述含钾的活性组分浸渍液的总体积的1%-20%,更优选5%-10%。
在上述加氢精制催化剂的制备方法中,优选地,所述含钾的喷淋液的pH值为12.2-13.5。
根据本发明的具体实施方案,优选地,上述加氢精制催化剂的制备方法可以包括以下步骤:喷淋载体、一次陈化、浸渍、二次陈化、干燥、焙烧,得到氧化态的催化剂。
本发明制备的催化剂中含有钾,其中,一部分钾以载体预喷淋的方式引入,一部分钾以用含有钾的活性组分浸渍液浸渍载体的方式引入,喷淋后载体需要经过陈化,再进行浸渍。即该制备方法还包括在喷淋之后进行陈化的步骤,优选地,所述陈化时间为5min-30min,更优选为10min-20min。
根据本发明的具体实施方案,优选地,采用含钾的喷淋液对载体进行喷淋的步骤与以含钾的活性组分浸渍液对经过喷淋的载体进行浸渍的步骤之间不进行干燥和焙烧;即经喷淋的载体(陈化适当时间之后),不经过干燥和焙烧,直接进行后续催化剂的制备。
本发明对催化剂的载体并不特别加以限制。根据本发明的具体实施方案,优选地,所述载体为耐高温无机氧化物,例如氧化铝、氧化硅、氧化钛和氧化锆中的一种或两种以上的组合,更优选为氧化铝。
根据本发明的具体实施方案,优选地,所述载体的吸水率为80%-120%,更优选为85%-110%。
发明人通过实验研究发现,负载型催化剂载体在活性组分浸渍液浸渍过程中会集中释放出大量的吸附热,影响后期活性组分的分散状态和催化剂的物化性能;通过预先采用含钾的喷淋液(例如氢氧化钾溶液)喷淋载体,而后采用活性组分浸渍液浸渍负载活性组分,不仅能够提高催化剂的加氢性能,而且能够有效地延长催化剂的寿命,其原因可能是:由于预先喷淋的含钾的喷淋液一方面使载体预先释放了部分吸附热,使催化剂载体在浸渍活性组分过程中的部分吸附热提前释放出来;另一方面,预先喷淋的含钾的喷淋液使催化剂载体表面的羟基数量和排布发生变化,提高了后续浸渍活性组分过程中活性组分的分散性;同时,预先喷淋的含钾的喷淋液由于毛细管效应预先占据载体相对较深的孔,使后续催化剂活性组分浸渍负载过程中形成梯度分布,活性组分分散更高效、均匀;此外,含钾的喷淋液中的碱金属钾可以与载体发生相互作用从而降低载体表面酸性。
在上述加氢精制催化剂的制备方法中,优选地,所述含钾的活性组分浸渍液的体积为1.05×(1-V)×X×T-1.25×(1-V)×X×T,优选为1.10×(1-V)×X×T-1.20×(1-V)×X×T,其中,V为所述含钾的喷淋液占所述含钾的活性组分浸渍液与所述含钾的喷淋液的总体积的体积分数,X为载体吸水率,T为载体质量克数,含钾的活性组分浸渍液的体积的单位为mL。
在上述加氢精制催化剂的制备方法中,优选地,含钾的活性组分浸渍液是通过以下步骤制备的:将氨水、多胺络合剂、水混合配制成复合溶剂,将活性组分和氢氧化钾按一定顺序加入复合溶剂中,得到含钾的活性组分浸渍液。本发明溶解活性组分用的溶剂是添加多胺络合剂的氨水,采用这种复合溶剂一方面能够提高活性组分在氨水中的溶解性、减少氨水的用量;另一方面,由于多胺络合剂的添加,能够明显提高催化剂活性组分的分散度;此外,氢氧化钾使浸渍液碱性增强,从而使金属活性组分更好地与多胺络合剂络合,提高浸渍溶液的稳定性,同时还起到调节催化剂酸性,提高催化剂加氢精制性能的作用。
本发明对配制含钾的活性组分浸渍液所用氨水浓度不做特别的限定,根据活性组分加入量确定,能使各活性组分完全溶解即可,此时活性组分与多胺络合剂形成较稳定的络合物。
根据本发明的具体实施方案,本发明采用的含钾的活性组分浸渍液为碱性浸渍液,所配制的浸渍液澄清、稳定,表面张力和粘稠度小。
根据本发明的具体实施方案,优选地,所述多胺络合剂为C2-C7的胺类化合物中的一种或两种以上的组合,例如乙二胺四乙酸、乙二胺、伯胺、仲胺和叔胺中的一种或两种以上的组合,更优选为乙二胺。
多胺络合剂的加入量根据活性组分的加入量的多少而变化,本发明并不特别加以限制,多胺络合剂加入量过高容易造成焙烧过程中大量有机物分解,过低则无法达到促进活性组分溶解、提高活性组分分散度的效果。
本发明的含钾的活性组分浸渍液在常温下(常温一般定义为10℃-30℃,优选为15℃-25℃)即可完成配制,不需要加热过程。本发明特别适用于多种活性组分、高活性组分含量催化剂的制备,尤其是采用一步浸渍将活性组分负载到载体上的催化剂制备方法,能够使活性组分在催化剂上呈高度分散状态,并有效消除催化剂上的B酸中心,减弱强L酸中心。
采用本发明的方法完成喷淋和活性组分溶液浸渍负载后,经陈化、干燥、焙烧、活化制得催化剂,其中,在浸渍活性组分之前,采用一定浓度的氢氧化钾溶液对催化剂载体进行喷淋放热的同时还能够起到对载体改性的作用。陈化、干燥、焙烧均可以按照本领域的常规方式进行,本发明并无特殊要求。最终制备得到催化剂中的氧化钾含量为0.3%-5%,优选为0.5%-2.5%。
根据本发明的具体实施方案,本发明对催化剂的活性组分并不特别加以限制,可以根据加氢用途等进行确定。优选地,所述活性组分为钼、钨、钴和镍中的一种或两种以上的组合。
根据本发明的具体实施方案,优选地,以载体总质量为100%计,所述活性组分的质量分数大于等于20%,其中,所述活性组分按活性组分金属元素的氧化物计算,例如钼以三氧化钼计、钨以三氧化钨计、钴以氧化钴计、镍以氧化镍计。
根据本发明的具体实施方案,优选地,钼以钼酸铵的形式加入,钨的加入方式可以是偏钨酸铵、钨酸和其他碱性钨酸盐中的一种或两种以上的组合,优选偏钨酸铵;钴和镍的形式加入可以是其硫酸盐、卤化物、硝酸盐和醋酸盐中的一种或两种以上的组合,优选硝酸盐或/和醋酸盐,硝酸盐、醋酸盐的溶解性好,有利于活性组分在载体上的分布。
本发明还提供了一种加氢精制催化剂,其是由上述制备方法制备的。
根据本发明的具体实施方案,活性组分在加氢精制催化剂中的分布呈现一定的梯度。
本发明还提供了上述加氢精制催化剂的预硫化方法,其中,预硫化过程中引入硫化剂的量为所述加氢精制催化剂的理论需硫量的20-70%,优选为25-50%。其中,催化剂理论需硫量为氧化态的加氢精制催化剂上的活性金属组分完全转化为硫化物(Co9S8、MoS2、Ni3S2、WS2等)时所需要的硫的量,以硫单质计。
根据本发明的具体实施方案,优选地,在上述预硫化方法中所述预硫化采用的硫化剂为单质硫和/或含硫化合物。
根据本发明的具体实施方案,优选地,所述含硫化合物为无机含硫化合物和有机含硫化合物中的一种或两种的组合;所述无机含硫化合物为二硫化碳、硫化铵中的一种或两种的组合,所述有机含硫化合物为单硫化合物和多硫化合物中的一种或两种的组合,优选为二甲基二硫、叔丁基多硫化物、叔壬基多硫、硫脲、SZ-54(生产厂家为路博润公司)、硫醇、硫酚、硫醚中的一种或两种以上的组合。
根据本发明的具体实施方案,优选地,所述预硫化还包括加入硫化助剂的步骤。通过在进行预硫化的过程中加入硫化助剂,有利于硫化剂与氧化态加氢催化剂混合均匀。
根据本发明的具体实施方案,优选地,所述硫化助剂为有机溶剂。
根据本发明的具体实施方案,优选地,所述硫化助剂为烃油和有机羧酸酯中的一种或两种的组合;所述烃油为汽油、煤油、柴油、灯油、白油、工业豆油、润滑油基础油中的一种或两种以上的组合,优选为二次加工得到的烃油,其中,所述加工为催化裂化、热裂化中的一种或两种的组合工艺;所述有机羧酸酯为含有6-60个碳原子的有机羧酸酯类,优选为脂肪酸甘油酯、动物油、菜籽油、花生油、豆油、棉籽油中的一种或两种以上的组合。
根据本发明的具体实施方案,优选地,所述硫化助剂用量为加氢精制催化剂(即未进行预硫化时的氧化态催化剂)的重量的0.5%-40%,更优选为3%-25%。
本发明还提供了一种器外预硫化加氢精制催化剂,其是由上述预硫化方法制备的。
根据本发明的具体实施方案,优选地,在上述器外预硫化加氢精制催化剂中,硫元素的含量为器外预硫化加氢精制催化剂质量的3.5-10wt%,更优选为4-7wt%。
本发明还提供了上述器外预硫化加氢精制催化剂的开工方法,其包括以下步骤:
(1)将器外预硫化加氢精制催化剂催化剂装入反应器中;
(2)将反应器经氮气气密、氢气置换和氢气气密;
(3)在氢气循环下,以反应器入口温度15-25℃/小时的速度升温,当催化剂床层温度达到150-160℃时,恒温3-5小时;当催化剂床层温度达180-220℃时,恒温2-10h;当催化剂床层温度达260-320℃,恒温2-10h(优选为2-8h),催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行操作,完成开工。
本发明所提供的预硫化加氢精制催化剂能够降低器外预硫化过程中的硫化剂用量,开工过程安全平稳,催化剂性能优异。这可能是由于:催化剂的硫化对于催化剂的性能起到了极其重要的作用,采用本发明的加氢精制催化剂的制备方法有助于形成催化剂高活性相态Ⅱ型活性中心,在硫化后其活性相晶片具有更加适当的堆垛层数和片晶长度。
本发明的加氢精制催化剂的制备方法克服了常规浸渍方法带来的浸渍效应和活性组分团簇作用,提高了活性金属组分的负载效应,活性组分在制备得到的加氢精制催化剂中形成了一定的梯度,提高了活性金属在载体表面的分散性,同时调节了活性金属与载体间的相互作用,从而提高了催化剂加氢脱硫活性和稳定性,部分硫化状态的催化剂,既保持了催化剂优异的加氢精制性能,同时意想不到地降低了器外预硫化过程中所需硫化剂的用量。在催化剂的使用过程中,油品中含有的硫化物使催化剂性能慢慢释放。
附图说明
图1为实施例3中催化剂的SEM-EDS表征结果图。
图2为实施例3中催化剂中钾的HRTEM组分分布图。
具体实施方式
为了对本发明的技术特征、目的和有益效果有更加清楚的理解,现对本发明的技术方案进行以下详细说明,但不能理解为对本发明的可实施范围的限定。
实施例1
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积289m2/g,孔容0.63cm3/g,强度154N/cm,吸水率115%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制0.25%的氢氧化钾溶液497ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为2.5min,喷淋后一次陈化的放置时间为5min,得到预喷淋载体;
(3)配制5100ml氨水和390ml三乙撑四胺混合溶液,加入钼酸铵搅拌溶解后依次加入硝酸镍、偏钨酸铵、氢氧化钾,加入去离子水将溶液体积调整到11930ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化4h,于110℃下干燥3小时,450℃焙烧4h,制得催化剂C1。
催化剂器外预硫化:
(1)将硫化剂(SZ-54,用量为催化剂C1理论需硫量的30%)、硫化助剂(汽油和豆油的重量比2:1的混合物,用量为催化剂C1重量的20%)混合均匀得预硫化原料;
(2)将催化剂C1放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C1混合均匀,放置1h后,120℃处理2h,得到器外预硫化催化剂Cs1。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs1装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度20℃/小时的速度升温,当催化剂床层温度达到150℃时,恒温5h;当催化剂床层温度达185℃时,恒温4h;当催化剂床层温度达280℃,恒温3h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
实施例2
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积281m2/g,孔容0.62cm3/g,强度177N/cm,吸水率110%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制0.5%的氢氧化钾溶液726ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为12min,喷淋后一次陈化的放置时间为7min,得到预喷淋载体;
(3)配制5200ml氨水和435g乙二胺四乙酸混合溶液,加入硝酸镍搅拌溶解后依次加入钼酸铵、硝酸钴、氢氧化钾,加入去离子水将溶液体积调整到11380ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化4.5h,于100℃下干燥4小时,480℃焙烧4h,制得催化剂C2。
催化剂器外预硫化:
(1)将硫化剂(单质硫,用量为催化剂C2理论需硫量的35%)、硫化助剂(煤油,用量为催化剂C2重量的15%)混合均匀得预硫化原料;
(2)将催化剂C2放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C2混合均匀,放置0.5h后,100℃处理2.5h,得到器外预硫化催化剂Cs2。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs2装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度25℃/小时的速度升温,当催化剂床层温度达到150℃时,恒温5h;当催化剂床层温度达180℃时,恒温3h;当催化剂床层温度达285℃,恒温4h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
实施例3
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积275m2/g,孔容0.62cm3/g,强度156N/cm,吸水率105%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制0.3%的氢氧化钾溶液588ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为3.5min,喷淋后一次陈化的放置时间为9min,得到预喷淋载体;
(3)配制5400ml的氨水和600ml乙二胺的混合溶液,加入钼酸铵搅拌溶解后依次加入乙酸钴、硝酸镍、氢氧化钾,加入去离子水将溶液体积调整到11170ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化5h,于120℃下干燥3小时,500℃焙烧4h,制得催化剂C3。
催化剂器外预硫化:
(1)将硫化剂(SZ-54,用量为催化剂C3理论需硫量的40%)、硫化助剂(白油,用量为催化剂C3重量的18%)混合均匀得预硫化原料;
(2)将催化剂C3放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C3混合均匀,放置1.5h后,90℃处理3h,得到器外预硫化催化剂Cs3。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs3装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度15℃/小时的速度升温,当催化剂床层温度达到150℃时,恒温4h;当催化剂床层温度达185℃时,恒温6h;当催化剂床层温度达290℃,恒温2h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
实施例4
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积266m2/g,孔容0.61cm3/g,强度169N/cm,吸水率100%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制2%的氢氧化钾溶液805ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为4min,喷淋后一次陈化的放置时间为12min,得到预喷淋载体;
(3)配制5500ml的氨水和420g乙二胺四乙酸的混合溶液,加入乙酸钴搅拌溶解后依次加入钼酸铵、硝酸镍、氢氧化钾,加入去离子水将溶液体积调整到10700ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化3h,于100℃下干燥5小时,420℃焙烧6h,制得催化剂C4。
催化剂器外预硫化:
(1)将硫化剂(叔丁基多硫化物和SZ-54,两者硫质量比为1:2,用量为催化剂C4理论需硫量的50%)、硫化助剂(柴油,用量为催化剂C4重量的12%)混合均匀得预硫化原料;
(2)将催化剂C4放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C4混合均匀,放置1h后,80℃处理4h,得到器外预硫化催化剂Cs4。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs4装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度15℃/小时的速度升温,当催化剂床层温度达到155℃时,恒温3h;当催化剂床层温度达190℃时,恒温4h;当催化剂床层温度达300℃,恒温4h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
实施例5
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积254m2/g,孔容0.61cm3/g,强度135N/cm,吸水率95%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制0.8%的氢氧化钾溶液890ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为3min,喷淋后一次陈化的放置时间为15min,得到预喷淋载体;
(3)配制5600ml的氨水和560g乙二胺的混合溶液,加入钼酸铵搅拌溶解后依次加入硝酸钴、硝酸镍、氢氧化钾,加入去离子水将溶液体积调整到10230ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化3.5h,于110℃下干燥4小时,520℃焙烧5h,制得催化剂C5。
催化剂器外预硫化:
(1)将硫化剂(硫醚和SZ-54,两者硫质量比为1:2,用量为催化剂C5理论需硫量的45%)、硫化助剂(柴油,用量为催化剂C5重量的10%)混合均匀得预硫化原料;
(2)将催化剂C5放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C5混合均匀,放置2h后,85℃处理4h,得到器外预硫化催化剂Cs5。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs5装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度20℃/小时的速度升温,当催化剂床层温度达到160℃时,恒温4h;当催化剂床层温度达200℃时,恒温5h;当催化剂床层温度达310℃,恒温5h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
实施例6
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积239m2/g,孔容0.6cm3/g,强度189N/cm,吸水率89%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制0.6%的氢氧化钾溶液1270ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为5.5min,喷淋后一次陈化的放置时间为18min,得到预喷淋载体;
(3)配制5800ml的氨水和450g乙二胺的混合溶液,加入钼酸铵搅拌溶解后依次加入乙酸钴、硝酸镍、氢氧化钾,加入去离子水将溶液体积调整到9320ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化2.5h,于100℃下干燥5小时,470℃焙烧5h,制得催化剂C6。
催化剂器外预硫化:
(1)将硫化剂(硫酚和SZ-54,两者硫质量比为1:2,用量为催化剂C6理论需硫量的55%)、硫化助剂(柴油,用量为催化剂C6重量的25%)混合均匀得预硫化原料;
(2)将催化剂C6放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C6混合均匀,放置2h后,90℃处理3h,得到器外预硫化催化剂Cs6。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs6装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度25℃/小时的速度升温,当催化剂床层温度达到155℃时,恒温4h;当催化剂床层温度达210℃时,恒温4h;当催化剂床层温度达320℃,恒温6h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
实施例7
本实施例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积223m2/g,孔容0.59cm3/g,强度141N/cm,吸水率84%。
(1)首先配制氢氧化钾水溶液用于预喷淋处理:配制0.4%的氢氧化钾溶液1030ml,得到喷淋液;
(2)称取氧化铝载体10kg,加入回转式浸渍锅中,采用上述配制好的氢氧化钾喷淋液对载体进行雾化喷淋处理,喷淋处理时间为7.5min,喷淋后一次陈化的放置时间为22min,得到预喷淋载体;
(3)配制6000ml氨水和590ml三乙撑四胺混合溶液,加入偏钨酸铵搅拌溶解后依次加入硝酸镍、硝酸钴、氢氧化钾,加入去离子水将溶液体积调整到9200ml,浸渍于步骤(2)所得预喷淋载体上,二次陈化2h,于110℃下干燥4小时,500℃焙烧5h,制得催化剂C7。
催化剂器外预硫化:
(1)将硫化剂(单质硫和硫化铵,两者硫质量比为2:1,用量为催化剂C7理论需硫量的20%)、硫化助剂(豆油,用量为催化剂C7重量的3%)混合均匀得预硫化原料;
(2)将催化剂C7放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂C7混合均匀,放置1h后,100℃处理2h,得到器外预硫化催化剂Cs7。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Cs7装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度15℃/小时的速度升温,当催化剂床层温度达到160℃时,恒温4h;当催化剂床层温度达220℃时,恒温8h;当催化剂床层温度达290℃,恒温3h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
对比例1
本对比例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积289m2/g,孔容0.63cm3/g,强度154N/cm,吸水率115%。
配制5100ml氨水和390ml三乙撑四胺混合溶液,加入钼酸铵搅拌溶解后依次加入硝酸镍、偏钨酸铵、氢氧化钾,加入去离子水将溶液体积调整到11930ml,浸渍于10kg载体上,陈化4h,110℃下干燥3小时,450℃焙烧4h,制得催化剂D1。
催化剂器外预硫化:
(1)将硫化剂(SZ-54,用量为催化剂D1理论需硫量的30%)、硫化助剂(汽油和豆油的重量比2:1的混合物,用量为催化剂D1重量的20%)混合均匀得预硫化原料;
(2)将催化剂D1放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂D1混合均匀,放置1h后,120℃处理2h,得到器外预硫化催化剂Ds1。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Ds1装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度20℃/小时的速度升温,当催化剂床层温度达到150℃时,恒温5h;当催化剂床层温度达185℃时,恒温4h;当催化剂床层温度达280℃,恒温3h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
对比例2
本对比例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积275m2/g,孔容0.62cm3/g,强度156N/cm,吸水率105%。
配制5400ml的氨水和600ml乙二胺的混合溶液,加入钼酸铵搅拌溶解后依次加入乙酸钴、硝酸镍、氢氧化钾,加入去离子水将溶液体积调整到11170ml,浸渍于10kg载体上,陈化5h,120℃下干燥3小时,500℃焙烧4h,制得催化剂D2。
催化剂器外预硫化:
(1)将硫化剂(SZ-54,用量为催化剂D2理论需硫量的40%)、硫化助剂(白油,用量为催化剂D2重量的18%)混合均匀得预硫化原料;
(2)将催化剂D2放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂D2混合均匀,放置1.5h后,90℃处理3h,得到器外预硫化催化剂Ds2。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Ds2装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度15℃/小时的速度升温,当催化剂床层温度达到150℃时,恒温4h;当催化剂床层温度达185℃时,恒温6h;当催化剂床层温度达290℃,恒温2h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
对比例3
本对比例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积254m2/g,孔容0.61cm3/g,强度135N/cm,吸水率95%。
配制5600ml的氨水和560g乙二胺的混合溶液,加入钼酸铵搅拌溶解后依次加入硝酸钴、硝酸镍、氢氧化钾,加入去离子水将溶液体积调整到10230ml,浸渍于10kg载体上,陈化3.5h,于110℃下干燥4小时,520℃焙烧5h,制得催化剂D3。
催化剂器外预硫化:
(1)将硫化剂(硫醚和SZ-54,两者硫质量比为1:2,用量为催化剂D3理论需硫量的45%)、硫化助剂(柴油,用量为催化剂D3重量的10%)混合均匀得预硫化原料;
(2)将催化剂D3放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂D3混合均匀,放置2h后,85℃处理4h,得到器外预硫化催化剂Ds3。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Ds3装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度20℃/小时的速度升温,当催化剂床层温度达到160℃时,恒温4h;当催化剂床层温度达200℃时,恒温5h;当催化剂床层温度达310℃,恒温5h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
对比例4
本对比例提供了一种加氢精制催化剂及其制备方法、预硫化方法和开工方法,具体包括:
催化剂制备:
实验所用载体为三叶草条型γ-Al2O3载体,载体比表面积223m2/g,孔容0.59cm3/g,强度141N/cm,吸水率84%。
配制6000ml氨水和590ml三乙撑四胺混合溶液,加入偏钨酸铵搅拌溶解后依次加入硝酸镍、硝酸钴、氢氧化钾,加入去离子水将溶液体积调整到9200ml,浸渍于10kg载体上,陈化2h,于110℃下干燥4小时,500℃焙烧5h,制得催化剂D4。
催化剂器外预硫化:
(1)将硫化剂(单质硫和硫化铵,两者硫质量比为2:1,用量为催化剂D4理论需硫量的20%)、硫化助剂(豆油,用量为催化剂D4重量的3%)混合均匀得预硫化原料;
(2)将催化剂D4放入回转式浸渍锅,预硫化原料采用喷淋方式与催化剂D4混合均匀,放置1h后,100℃处理2h,得到器外预硫化催化剂Ds4。
器外预硫化型催化剂开工方法:
(1)将器外预硫化型催化剂Ds4装入反应器中;
(2)将反应器装置经氮气气密、氢气置换和氢气气密,气密合格;
(3)在氢气循环下,以反应器入口温度15℃/小时的速度升温,当催化剂床层温度达到160℃时,恒温4h;当催化剂床层温度达220℃时,恒温8h;当催化剂床层温度达290℃,恒温3h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行正常操作。
表1列出了实施例1-7与对比例1-4所得催化剂中各组分的质量含量。
表1催化剂中各组分质量含量
通过SEM-EDS对催化剂进行元素分布分析表征及催化剂上活性组分的分布情况考察。催化剂中不同位置活性组分含量如下表2所示。实施例3中催化剂Cs3的SEM-EDS表征结果如图1所示,该催化剂含有Ni、Mo、Co、K元素,同时还含有少量的Si和P;实施例3中催化剂Cs3的钾元素的HRTEM组分分布如图2所示,可观测到K元素,且分布较均匀。
表2催化剂不同位置活性组分金属含量占活性组分总含量的百分比(%)
由表2表征结果可以看出,采用本发明的加氢催化剂制备活性组分浓度分布更合理。
催化剂评价:
原料采用裂解汽油C6-C8馏分一段加氢产品,反应工艺条件为:反应压力2.8MPa,液时体积空速2.0h-1,反应温度240℃,氢油体积比250:1。
对上述制备的催化剂Cs3、Ds2分别进行300小时评价,采用裂解汽油一段加氢产品为原料,原料性质见表3,催化剂评价在250ml绝热床加氢反应装置上进行的,催化剂采用下两段装填,装填量150ml。每12小时取样分析产品溴价、硫含量。催化剂300小时评价的平均数据见表4。
表3加氢原料油指标
表4催化剂Cs3、Ds2 300小时评价平均数据
由表2表征结果可以看出,采用本发明制备的催化剂活性组分浓度分布更合理,从表4的评价结果来看,在相同的评价工艺条件下,采用本发明制备的催化剂的加氢产品的溴价、总硫相对较低,这充分说明了本发明的催化剂具有更好的加氢活性。
当然,本发明还可有其它多种实施例,在不背离本发明精神及其实质的情况下,熟悉本领域的技术人员可根据本发明作出各种相应的改变和变形,但这些相应的改变和变形都应属于本发明权利要求的保护范围。
Claims (20)
1.一种加氢精制催化剂的制备方法,其中,该制备方法包括:在浸渍活性组分之前,采用含钾的喷淋液对载体进行喷淋的步骤,以及,以含钾的活性组分浸渍液对经过喷淋的载体进行浸渍的步骤;
其中,所述含钾的喷淋液为氢氧化钾溶液;
优选地,所述喷淋的时间为1min-20min,优选为3min-10min。
2.根据权利要求1所述的制备方法,其中,所述含钾的喷淋液的浓度为0.1%-5%,优选为0.5%-1%。
3.根据权利要求1或2所述的制备方法,其中,所述含钾的喷淋液的体积占所述含钾的喷淋液与所述含钾的活性组分浸渍液的总体积的1%-20%,优选为5%-10%。
4.根据权利要求1-3任一项所述的制备方法,其中,所述含钾的喷淋液的pH值为12.2-13.5。
5.根据权利要求1-4任一项所述的制备方法,其中,该制备方法还包括在喷淋之后进行陈化的步骤,优选地,所述陈化时间为5min-30min,更优选为10min-20min。
6.根据权利要求1-5任一项所述的制备方法,其中,采用含钾的喷淋液对载体进行喷淋的步骤与以含钾的活性组分浸渍液对经过喷淋的载体进行浸渍的步骤之间不进行干燥和焙烧。
7.根据权利要求1-6任一项所述的制备方法,其中,所述载体的吸水率为80%-120%,优选为85%-110%。
8.根据权利要求1-7任一项所述的制备方法,其中,所述载体为耐高温无机氧化物,优选为氧化铝、氧化硅、氧化钛、氧化锆中的一种或两种以上的组合,更优选为氧化铝载体。
9.根据权利要求1-8任一项所述的制备方法,其中,所述含钾的活性组分浸渍液的体积为1.05×(1-V)×X×T-1.25×(1-V)×X×T,优选为1.10×(1-V)×X×T-1.20×(1-V)×X×T;
其中,V为所述含钾的喷淋液占所述含钾的活性组分浸渍液与所述含钾的喷淋液的总体积的体积分数,X为载体吸水率,T为载体质量克数;
含钾的活性组分浸渍液的体积的单位为mL。
10.根据权利要求1-9任一项所述的制备方法,其中,所述含钾的活性组分浸渍液是通过以下步骤制备的:将氨水、多胺络合剂、水混合配制成复合溶剂,将活性组分和氢氧化钾加入复合溶剂中,得到含钾的活性组分浸渍液。
11.根据权利要求10所述的制备方法,其中,所述多胺络合剂为C2-C7的胺类化合物中的一种或两种以上的组合,优选为乙二胺四乙酸、乙二胺、伯胺、仲胺和叔胺中的一种或两种以上的组合,更优选为乙二胺。
12.根据权利要求10所述的制备方法,其中,所述活性组分为钼、钨、钴和镍中的一种或两种以上的组合;
优选地,以载体总质量为100%计,所述活性组分的质量分数大于等于20%,其中,所述钼以三氧化钼计,钨以三氧化钨计,钴以氧化钴计,镍以氧化镍计;
优选地,所述钼以钼酸铵的形式加入;
优选地,所述钨以偏钨酸铵、钨酸和碱性钨酸盐中的一种或两种以上的组合的形式加入,更优选为偏钨酸铵;
优选地,所述钴和镍以其硫酸盐、卤化物、硝酸盐和醋酸盐中的一种或两种以上的组合的形式加入,更优选为硝酸盐或/和醋酸盐。
13.一种加氢精制催化剂,其是由权利要求1-12任一项所述的制备方法制备的。
14.根据权利要求13所述的加氢精制催化剂,其中,该加氢精制催化剂的氧化钾含量为0.3%-5%,优选0.5%-2.5%。
15.权利要求13或14所述的加氢精制催化剂的预硫化方法,其中,预硫化过程中引入硫化剂的量为所述加氢精制催化剂的理论需硫量的20-70%,优选为25-50%。
16.根据权利要求15所述的预硫化方法,其中,所述预硫化采用的硫化剂为单质硫和/或含硫化合物;
优选地,所述含硫化合物为无机含硫化合物和有机含硫化合物中的一种或两种的组合;所述无机含硫化合物为二硫化碳、硫化铵中的一种或两种的组合,所述有机含硫化合物为单硫化合物和多硫化合物中的一种或两种的组合,优选为二甲基二硫、叔丁基多硫化物、叔壬基多硫、硫脲、SZ-54、硫醇、硫酚、硫醚中的一种或两种以上的组合。
17.根据权利要求15或16所述的预硫化方法,其中,所述预硫化还包括加入硫化助剂的步骤;
优选地,所述硫化助剂为有机溶剂;
优选地,所述硫化助剂为烃油和有机羧酸酯中的一种或两种的组合,所述烃油为汽油、煤油、柴油、灯油、白油、工业豆油、润滑油基础油中的一种或两种以上的组合,优选为二次加工得到的烃油,其中,所述加工为催化裂化、热裂化中的一种或两种的组合工艺;所述有机羧酸酯为含有6-60个碳原子的有机羧酸酯类,优选为脂肪酸甘油酯、动物油、菜籽油、花生油、豆油、棉籽油中的一种或两种以上的组合;
优选地,所述硫化助剂的用量为所述加氢精制催化剂的重量的0.5%-40%,更优选为3%-25%。
18.一种器外预硫化加氢精制催化剂,其是由权利要求15-17任一项所述的预硫化方法制备的。
19.根据权利要求18所述的器外预硫化加氢精制催化剂,其中,在该器外预硫化催化剂中,硫元素的含量为器外预硫化加氢精制催化剂的质量的3.5-10wt%,优选为4-7wt%。
20.权利要求18或19所述的器外预硫化加氢精制催化剂的开工方法,其包括以下步骤:
(1)将所述器外预硫化加氢精制催化剂催化剂装入反应器中;
(2)将反应器经氮气气密、氢气置换和氢气气密;
(3)在氢气循环下,以反应器入口温度15-25℃/小时的速度升温,当催化剂床层温度达到150-160℃时,恒温3-5小时;当催化剂床层温度达180-220℃时,恒温2-10h;当催化剂床层温度达260-320℃,恒温2-10h,催化剂硫化结束;
(4)调整系统工艺条件至反应条件,切换原料油进行操作,完成开工。