CN117084931A - 一种含蚕丝蛋白的粉体组合物及其制备方法 - Google Patents
一种含蚕丝蛋白的粉体组合物及其制备方法 Download PDFInfo
- Publication number
- CN117084931A CN117084931A CN202311109667.0A CN202311109667A CN117084931A CN 117084931 A CN117084931 A CN 117084931A CN 202311109667 A CN202311109667 A CN 202311109667A CN 117084931 A CN117084931 A CN 117084931A
- Authority
- CN
- China
- Prior art keywords
- fibroin
- powder
- beta
- powder composition
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及化妆品的技术领域，更具体地说，它涉及一种含蚕丝蛋白的粉体组合物及其制备方法，其技术方案要点是，包括以下质量百分数的各组分：0.1‑10％β‑折叠蚕丝蛋白、余量为粉体原料；其中，所述粉体原料包括着色粉体、体质粉体和珠光粉体的一种或多种。本发明通过β‑折叠蚕丝蛋白的β‑折叠结构均匀分散粉体，具有提高粉体贴肤性与细腻度的优点。
Description
技术领域
本发明涉及化妆品的技术领域，更具体地说，它涉及一种含蚕丝蛋白的粉体组合物及其制备方法。
背景技术
彩妆，又名美容化妆品，主要是涂敷于脸面及指甲等部位，利用色彩的变化，赋予皮肤色彩，修整肤色或加强眼、鼻部位的阴影，以增强立体感，使之更具有魅力，同时，也可用于遮盖雀斑、伤痕和痣等皮肤的缺陷。而粉体原料是彩妆产品的最重要组成成分，对脸部起到修饰作用。
粉体材料直接加入至彩妆配方中，容易出现因各粉粒大小不相同，粉粒表面未处理而导致产品不稳定，粉体易分层的问题。现有技术通过对粉体原料进行处理，如：硅处理、氨基酸处理或硬脂酸处理等，对粉体材料进行修饰，可提高产品的稳定性。但上述处理方式存在如下问题：粉体原料应用于皮肤表面容易聚集，贴肤性欠缺。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种含蚕丝蛋白的粉体组合物及其制备方法，具有提高粉体贴肤性的优点。
本发明的上述技术目的是通过以下技术方案得以实现的，一种含蚕丝蛋白的粉体组合物，包括以下质量百分数的各组分：
0.1-10％β-折叠蚕丝蛋白、余量为粉体原料；
其中，所述粉体原料包括着色粉体、体质粉体和珠光粉体的一种或多种。
在其中一个实施例中，所述β-折叠蚕丝蛋白中β-折叠的含量大于或等于30％。
在其中一个实施例中，所述β-折叠蚕丝蛋白的长度为20-4000nm，直径为5-30nm。
上述含蚕丝蛋白的粉体组合物的制备方法，包括以下步骤：
S1、获得β-折叠蚕丝蛋白溶液与粉体原料，将所述β-折叠蚕丝蛋白溶液溶液加入至所述粉体原料中，搅拌混合均匀，获得悬浮液；
S2、移除所述悬浮液中的水分，获得目标产物。
在其中一个实施例中，在所述S1中，所述β-折叠蚕丝蛋白溶液浓度为0.3-10％。
在其中一个实施例中，所述S1还包括通过添加溶剂分散所述粉体原料，所述S2还包括移除所述溶剂，所述溶剂为水或挥发性有机溶剂。
在其中一个实施例中，在所述S1中，所述溶剂与所述粉体原料的质量比为1：3-2：1。
在其中一个实施例中，所述挥发性有机溶剂包括乙醇、异构十二烷和硅油的一种或多种。
在其中一个实施例中，在所述S2中，通过风干、烘干或冻干的方法移除水分与所述挥发性有机溶剂。
在其中一个实施例中，所述S2中的烘干温度为55-100℃。
上述一种含蚕丝蛋白的粉体组合物及其制备方法，具有以下有益效果：
其一，本发明使用β-折叠蚕丝蛋白对粉体进行处理，通过β-折叠蚕丝蛋白的β-折叠结构分散粉体，获得具有较高贴肤性的粉体组合物，增添粉体的细腻度；
其二，粉体组合物可添加在作用于皮肤的驻留类化妆品和药品的配方中，改善产品贴肤性、涂抹顺滑度，粉质更细腻服帖，改善浮粉和卡粉的情况。
附图说明
图1是本发明的步骤流程图。
具体实施方式
下面结合实施例对本发明作进一步详细描述，需指出的是，以下所述实施例旨在便于对本发明的理解，而对其不起任何限定作用。除非另有限定，本文使用的所有技术以及科学术语具有与本发明所属领域普通技术人员通常理解的相同的含义。当存在矛盾时，以本说明书中的定义为准。
如本文所用术语“由…制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形，意在覆盖非排它性的包括。例如，包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素，而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由…组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中，此短语将使权利要求为封闭式，使其不包含除那些描述的材料以外的材料，但与其相关的常规杂质除外。当短语“由…组成”出现在权利要求主体的子句中而不是紧接在主题之后时，其仅限定在该子句中描述的要素；其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时，这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围，而不论该范围是否单独公开了。例如，当公开了范围“1至5”时，所描述的范围应被解释为包括范围“1至4”、“1至3”、“1至2”、“1至2和4至5”、“1至3和5”等。当数值范围在本文中被描述时，除非另外说明，否则该范围意图包括其端值和在该范围内的所有整数和分数。
下面结合附图和实施例，对本发明进行详细描述。
一种含蚕丝蛋白的粉体组合物，包括以下质量百分数的各组分：
0.1-10％β-折叠蚕丝蛋白、余量为粉体原料；
粉体原料包括着色粉体、体质粉体和珠光粉体的一种或多种。
在实际应用中，着色粉体用于调色，包括钛白粉、铁红、铁黄、铁黑、群青、普鲁士蓝等矿物性颜料，还包括天然或合成有色有机化合物、天然提取或生物合成物，比如胭脂虫红、有机色素和色淀，如红6，红7，红33，黄6，黄7，蓝1等；
体质粉体用于调节产品涂展性、特定肤感和特定功能(比如提供防晒值)，一般指屈折率小于2.0的粉体，包括无机体质粉体(二氧化钛、氧化锌、硅粉、滑石粉、云母、高岭土等)、有机体质粉体(有机硅粉、聚甲基丙烯酸甲酯、尼龙粉等)、有机复合体质粉体(硅处理、硬脂酸盐处理等)或无机复合体质粉体(微细钛白粉处理云母、多层球状粉体等)；
珠光粉体用于增加光泽与质感，主要为云母钛或鱼鳞片。
此外，粉体原料还可以经过表面处理，比如硅处理、氨基酸处理、硬脂酸处理、多重处理。
本发明使用β-折叠蚕丝蛋白对粉体原料进行处理，通过β-折叠蚕丝蛋白的β-折叠结构帮助均匀分散粉体，而其优异的生物相容性可以帮助获得具有较高贴肤性的粉体组合物，增添粉体的细腻度。粉体组合物可添加在作用于皮肤的驻留类化妆品和药品的配方中，改善产品贴肤性、涂抹顺滑度，粉质更细腻服帖，改善浮粉和卡粉的情况。
具体的，β-折叠蚕丝蛋白中β-折叠的含量大于或等于30％。
具体的，β-折叠蚕丝蛋白的长度为20-4000nm，直径为5-30nm。
参阅图1，上述含蚕丝蛋白的粉体组合物的制备方法，包括以下步骤：
S1、获得β-折叠蚕丝蛋白溶液与粉体原料，将β-折叠蚕丝蛋白溶液加入至粉体原料中，搅拌混合均匀，获得悬浮液；
在实际操作中，可通过均质机进行处理，获得混合均匀的悬浮液即可。
S2、移除悬浮液中的水分，获得目标产物；
进一步的，在移除水分后，可对目标产物进行过筛处理，以去除产物中的部分粒径较大的杂质。
在实际操作中，将粉体原料与β-折叠蚕丝蛋白溶液均匀混合，使用高β-折叠蚕丝蛋白的结构特点吸附并均匀分散粉体，而干燥后由蚕丝蛋白包裹的粉体，获得了由外层包裹蛋白带来的贴肤性，此不改变粉体的外观、粒径。
具体的，在S1中，β-折叠蚕丝蛋白溶液浓度为0.3-10％。
具体的，S1还包括通过添加溶剂分散粉体原料，S2还包括移除溶剂，溶剂为水或挥发性有机溶剂。在实际生产中，在加入粉体原料后加入溶剂(亦可在加入粉体原料前加入)，溶剂用于帮助分散粉体原料，使粉体原料不结块，悬浮液形成粘稠的糊状物，分散完毕后，移除悬浮液水分的同时移除溶剂。
具体的，在S1中，溶剂与粉体原料的质量比为1：3-2：1。进一步的，溶剂与粉体原料的质量比为1:3-1:1。
进一步的，挥发性有机溶剂包括乙醇、异构十二烷和硅油的一种或多种。此外，挥发性有机溶剂还可选自乙酸乙酯或丙酮等，起帮助分散粉体原料作用即可。
具体的，在S2中，通过风干、烘干或冻干的方法移除水分与挥发性有机溶剂。在移除水分后，仍保留有β-折叠蚕丝蛋白的β-折叠结构，使其发挥吸附的特性。
进一步的，S2中的烘干温度为55-100℃，在此温度条件下烘干完全即可。
实施例1
本实施例提供了一种含蚕丝蛋白的粉体组合物，包括以下质量百分数的各组分：0.21％β-折叠蚕丝蛋白，余量为滑石粉。
上述一种含蚕丝蛋白的粉体组合物的具体步骤为：
S1、获得浓度为0.5％的β-折叠蚕丝蛋白溶液与滑石粉，将15gβ-折叠蚕丝蛋白溶液加入至35g滑石粉中，在1000rpm的转速下均质2分钟，获得悬浮液；
S2、使用烘箱对悬浮液进行烘干，在75℃的条件下烘干2小时，使用80目筛对干燥后的粉体进行过筛处理，获得过筛后的粉体组合物。
实施例2
本实施例提供了一种含蚕丝蛋白的粉体组合物，包括以下质量百分数的各组分：0.33％β-折叠蚕丝蛋白，余量为云母。
上述一种含蚕丝蛋白的粉体组合物的具体步骤为：
S1、获得浓度为0.5％的β-折叠蚕丝蛋白溶液与云母，将20gβ-折叠蚕丝蛋白溶液加入至30g云母中，在1000rpm的转速下均质2分钟，获得悬浮液；
S2、使用烘箱对悬浮液进行烘干，将悬浊液平铺在金属盘中，在75℃的条件下烘干2小时，使用80目筛对干燥后的粉体进行过筛处理，获得过筛后的粉体组合物。
实施例3
本实施例提供了一种含蚕丝蛋白的粉体组合物，包括以下质量百分数的各组分：0.17％β-折叠蚕丝蛋白，余量为滑石粉。
上述一种含蚕丝蛋白的粉体组合物的具体步骤为：
S1、获得浓度为0.5％的β-折叠蚕丝蛋白溶液、滑石粉与异构十二烷，取10g异构十二烷至35g滑石粉中，混合均匀，再加入10gβ-折叠蚕丝蛋白溶液，在1000rpm的转速下均质2分钟，获得悬浮液；
S2、使用烘箱对悬浮液进行烘干，将悬浊液平铺在金属盘中，在75℃的条件下烘干2小时，以去除水分与异构十二烷，使用80目筛对干燥后的粉体进行过筛处理，获得过筛后的粉体组合物。
本发明实施例1-3和所用原料用量浓度如下表所示：
| 使用原料 | 实施例1 | 实施例2 | 实施例3 |
| 0.5％β-折叠蚕丝蛋白溶液 | 15g | 20g | 10g |
| 滑石粉 | 35g | / | 35g |
| 云母 | / | 30g | / |
| 异构十二烷 | / | / | 10g |
实施例4与对比例1
依照下表配制彩妆产品，在本实施例中，彩妆产品具体为粉饼。
粉饼的具体制备步骤如下：
S1、分别称量A相、B相、C相、D相的成分；
S2、将A相和B相放入打粉机中混合均匀；
S3、将C相和D相混合均匀后，加入至打粉机中，与已混合完毕的A相和B相混合均匀，获得组合物；
S4、取8g组合物加入至铝盘中，在20MPa的条件下对组合物进行压粉两次，每次2s。
效果测试对比：
取等量实施例1与未处理的滑石粉涂于小臂内侧皮肤进行对比，肉眼可见未处理的滑石粉泛白、卡粉明显，实施例1更为贴肤，未发现卡粉情况。
取等量实施例2与未处理的云母涂于小臂内侧皮肤进行对比，肉眼可见二者均有类似的光泽感，而未处理的云母卡粉明显，实施例2更为服贴，卡粉不明显。
取等量实施例4与对比例1涂抹于相同面积的小臂内侧皮肤上，实施例4较对比例1粉质更为细腻、均匀服贴，卡粉现象不明显。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种含蚕丝蛋白的粉体组合物，其特征在于，包括以下质量百分数的各组分：
0.1-10％β-折叠蚕丝蛋白、余量为粉体原料；
其中，所述粉体原料包括着色粉体、体质粉体和珠光粉体的一种或多种。
2.根据权利要求1所述的一种含蚕丝蛋白的粉体组合物及其制备方法，其特征在于：所述β-折叠蚕丝蛋白中β-折叠的含量大于或等于30％。
3.根据权利要求2所述的一种含蚕丝蛋白的粉体组合物及其制备方法，其特征在于：所述β-折叠蚕丝蛋白的长度为20-4000nm，直径为5-30nm。
4.如权利要求1-3任一项所述的含蚕丝蛋白的粉体组合物的制备方法，其特征在于，包括以下步骤：
S1、获得β-折叠蚕丝蛋白溶液与粉体原料，将所述β-折叠蚕丝蛋白溶液加入至所述粉体原料中，搅拌混合均匀，获得悬浮液；
S2、移除所述悬浮液中的水分，获得目标产物。
5.根据权利要求4所述的一种含蚕丝蛋白的粉体组合物的制备方法，其特征在于：在所述S1中，所述β-折叠蚕丝蛋白溶液浓度为0.3-10％。
6.根据权利要求4所述的一种含蚕丝蛋白的粉体组合物的制备方法，其特征在于：所述S1还包括通过添加溶剂分散所述粉体原料，所述S2还包括移除所述溶剂，所述溶剂为水或挥发性有机溶剂。
7.根据权利要求6所述的一种含蚕丝蛋白的粉体组合物的制备方法，其特征在于：在所述S1中，所述溶剂与所述粉体原料的质量比为1：3-2：1。
8.根据权利要求6所述的一种含蚕丝蛋白的粉体组合物的制备方法，其特征在于：所述挥发性有机溶剂包括乙醇、异构十二烷和硅油的一种或多种。
9.根据权利要求6所述的一种含蚕丝蛋白的粉体组合物的制备方法，其特征在于：在所述S2中，通过风干、烘干或冻干的方法移除水分与所述挥发性有机溶剂。
10.根据权利要求9所述的一种含蚕丝蛋白的粉体组合物及其制备方法，其特征在于：所述S2中的烘干温度为55-100℃。