CN115915988A - 人工毛发用纤维及其制造方法、以及头发装饰品 - Google Patents
人工毛发用纤维及其制造方法、以及头发装饰品 Download PDFInfo
- Publication number
- CN115915988A CN115915988A CN202180046686.6A CN202180046686A CN115915988A CN 115915988 A CN115915988 A CN 115915988A CN 202180046686 A CN202180046686 A CN 202180046686A CN 115915988 A CN115915988 A CN 115915988A
- Authority
- CN
- China
- Prior art keywords
- fiber
- mass
- antistatic agent
- artificial hair
- ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
人工毛发用纤维,其具有基材纤维、金属离子和抗静电剂,前述金属离子及前述抗静电剂存在于前述基材纤维的表面的至少一部分,前述金属离子为选自由银离子、锌离子及铜离子组成的组中的至少一种,以该人工毛发用纤维的总质量为基准,前述金属离子的含量为5.0×10‑5~1.0×10‑2质量%,前述抗静电剂为选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种,以该人工毛发用纤维的总质量为基准,前述抗静电剂的含量为0.001~1质量%。
Description
技术领域
本发明涉及人工毛发用纤维及其制造方法、头发装饰品等。
背景技术
人工毛发用纤维(用于人工毛发的纤维)能够在头发装饰品中使用。下述专利文献1中公开了使用纤维处理剂对基材纤维实施处理的技术。
现有技术文献
专利文献
专利文献1:日本特开2002-285470号公报
发明内容
发明所要解决的课题
使用头发装饰品的消费者有时无法频繁洗发,因此无法保持头皮或头发装饰品清洁,细菌繁殖,有时产生恶臭等。因此,对用于头发装饰品的人工毛发用纤维要求抗菌性。
另外,从抑制产生静电的观点出发,考虑在人工毛发用纤维中使用抗静电剂以赋予抗静电性。然而,根据本申请发明人的见解,若使用抗静电剂,则会有油腻、粗糙等使触感变差的情况,从防止使用者感到违和感的观点出发,要求人工毛发用纤维在油腻、粗糙等触感方面优异。
本发明一方面的目的在于提供抑制油腻及粗糙且具有优异的抗菌性及抗静电性的人工毛发用纤维。本发明另一方面的目的在于提供具备这样的人工毛发用纤维的头发装饰品。本发明又一方面的目的在于提供这样的人工毛发用纤维的制造方法。
用于解决课题的手段
本发明一方面涉及人工毛发用纤维,其具有基材纤维、金属离子和抗静电剂,前述金属离子及前述抗静电剂存在于前述基材纤维的表面的至少一部分,前述金属离子为选自由银离子、锌离子及铜离子组成的组中的至少一种,以该人工毛发用纤维的总质量为基准,前述金属离子的含量为5.0×10-5~1.0×10-2质量%,前述抗静电剂为选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种,以该人工毛发用纤维的总质量为基准,前述抗静电剂的含量为0.001~1质量%。
本发明另一方面涉及具备上述人工毛发用纤维的头发装饰品。
本发明又一方面涉及人工毛发用纤维的制造方法,其具备使基材纤维接触含有金属离子及抗静电剂的处理剂的工序,前述金属离子为选自由银离子、锌离子及铜离子组成的组中的至少一种,以前述处理剂的总质量为基准,前述金属离子的含量为3.0×10-4~3.0×10-2质量%,前述抗静电剂为选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种,以前述处理剂的总质量为基准,前述抗静电剂的含量为0.005~4质量%。
发明效果
根据本发明的一方面,能够提供抑制油腻及粗糙且具有优异的抗菌性及抗静电性的人工毛发用纤维。根据本发明的另一方面,能够提供具备这样的人工毛发用纤维的头发装饰品。根据本发明的又一方面,能够提供这样的人工毛发用纤维的制造方法。
具体实施方式
以下对本发明的实施方式进行详细说明。
数值范围的所谓“A以上”是指A及超过A的范围。数值范围的所谓“A以下”是指A及小于A的范围。本说明书中以区间记载的数值范围中,某一区间的数值范围的上限值或下限值能够与其他区间的数值范围的上限值或下限值任意地组合。对于本说明书中记载的数值范围,该数值范围的上限值或下限值可以替换为实验例中所示的值。所谓“A或B”,可以包含A及B中的任一者,也可以包含这两者。除非特别说明,本说明书中例示的材料可以单独使用1种或组合使用2种以上。组合物中存在多种属于各成分的物质的情况下,除非特别说明,组合物中的各成分的含量是指组合物中存在的该多种物质的合计量。“工序”这一词语不仅是独立的工序,即使在无法与其他工序明确区分的情况下,只要可实现该工序所期待的作用,则也包括在本术语中。所谓“(甲基)丙烯酸”是指丙烯酸及与之相应的甲基丙烯酸中的至少一者。
本实施方式的人工毛发用纤维具有基材纤维(纤维状的基材)、金属离子和抗静电剂,金属离子及抗静电剂存在于基材纤维的表面的至少一部分。本实施方式的人工毛发用纤维中,金属离子为选自由银离子、锌离子及铜离子组成的组中的至少一种(以下称为“金属离子A”),以该人工毛发用纤维的总质量为基准,金属离子A的含量为5.0×10-5~1.0×10-2质量%,抗静电剂为选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种(以下称为“抗静电剂A”),以该人工毛发用纤维的总质量为基准,抗静电剂A的含量为0.001~1质量%。
本实施方式的人工毛发用纤维抑制油腻及粗糙且具有优异的抗菌性及抗静电性。所谓“油腻”,是指接触纤维时感受到的纤维表面的粘性。所谓“粗糙”,是指接触纤维时感受到的纤维表面的粗糙度。作为优异的抗菌性,本实施方式的人工毛发用纤维能够具有针对金黄色葡萄球菌的优异的抗菌性。
本实施方式的人工毛发用纤维能够用作人工毛发,也能够用于得到人工毛发。本实施方式的人工毛发用纤维可以是拉伸处理后的纤维,也可以是未拉伸的纤维。
作为基材纤维的材料,可举出氯乙烯系树脂、(甲基)丙烯酸系树脂(不包括属于氯乙烯系树脂的树脂)、聚烯烃系树脂(不包括属于氯乙烯系树脂或(甲基)丙烯酸系树脂的树脂)、聚酯系树脂(不包括属于氯乙烯系树脂、(甲基)丙烯酸系树脂或聚烯烃系树脂的树脂)、聚酰胺系树脂等,也可以使用它们的混合物。例如,基材纤维可以为包含氯乙烯系树脂的方式、包含聚酯系树脂的方式、包含聚烯烃系树脂的方式等。基材纤维可以包含氯乙烯系树脂和能够与氯乙烯系树脂形成聚合物合金的成分的混合物。作为能够与氯乙烯系树脂形成聚合物合金的成分,可举出乙烯·乙酸乙烯酯共聚物(EVA)、丙烯腈·丁二烯橡胶(NBR)、热塑性聚氨酯(TPU)、聚酯系热塑性弹性体(TPEE)、甲基丙烯酸甲酯·丁二烯·苯乙烯树脂(MBS)、丙烯腈·丁二烯·苯乙烯树脂(ABS)、丙烯腈-苯乙烯共聚物(AS)、聚甲基丙烯酸甲酯(PMMA)等。
从容易得到优异的阻燃性的观点及向头发装饰品的加工性优异的观点出发,基材纤维优选包含选自由氯乙烯系树脂、聚烯烃系树脂及聚酯系树脂组成的组中的至少一种,更优选包含氯乙烯系树脂。氯乙烯系树脂为具有源自氯乙烯的结构单元的聚合物,是具有氯乙烯作为单体单元的聚合物。氯乙烯系树脂能通过本体聚合、溶液聚合、悬浮聚合、乳液聚合等而得到,从纤维的初始着色性等优异的观点出发,优选通过悬浮聚合而得到。
作为氯乙烯系树脂,可举出氯乙烯的单独聚合物(均聚物、聚氯乙烯)、氯乙烯与其他单体的共聚物等,也可以使用它们的混合物。作为氯乙烯与其他单体的共聚物,可举出氯乙烯与乙烯基酯类的共聚物(氯乙烯-乙酸乙烯酯共聚物、氯乙烯-丙酸乙烯酯共聚物等);氯乙烯与(甲基)丙烯酸化合物((甲基)丙烯酸、(甲基)丙烯酸酯等)的共聚物(氯乙烯-丙烯酸丁酯共聚物、氯乙烯-丙烯酸2-乙基己酯共聚物等);氯乙烯与烯烃类的共聚物(氯乙烯-乙烯共聚物、氯乙烯-丙烯共聚物等);氯乙烯-丙烯腈共聚物;等等。氯乙烯系树脂也可以不具有源自(甲基)丙烯酸化合物的结构单元。共聚物中,与氯乙烯不同的单体的含量能够根据成型加工性、丝特性等的要求品质而确定。从向头发装饰品的加工性优异的观点出发,氯乙烯系树脂优选包含选自由氯乙烯的单独聚合物、氯乙烯与(甲基)丙烯酸化合物的共聚物、及氯乙烯-丙烯腈共聚物组成的组中的至少一种,更优选包含选自由氯乙烯的单独聚合物及氯乙烯-丙烯腈共聚物组成的组中的至少一种。
以基材纤维的总质量为基准,基材纤维中的氯乙烯系树脂的含量可以为50质量%以上、70质量%以上、90质量%以上、95质量%以上、98质量%以上或99质量%以上。也可以为基材纤维仅由氯乙烯系树脂形成(基材纤维的实质100质量%为氯乙烯系树脂)的方式。
(甲基)丙烯酸系树脂为具有源自(甲基)丙烯酸化合物((甲基)丙烯酸、(甲基)丙烯酸酯等)的结构单元的聚合物,是具有(甲基)丙烯酸化合物作为单体单元的聚合物。
作为聚烯烃系树脂,可举出聚乙烯、聚丙烯等。
作为聚酯系树脂,可举出聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯、聚2,6-萘二甲酸乙二醇酯、聚对苯二甲酸亚甲酯等。
作为聚酰胺系树脂,可举出尼龙6、尼龙66、尼龙11、尼龙12、尼龙6/10、尼龙6/12等。
就基材纤维的平均纤度而言,从为得到细纤度的人工毛发用纤维而能减小拉伸倍率、拉伸处理后的人工毛发用纤维不易产生光泽的观点出发,在未拉伸时,优选为300分特以下,更优选为200分特以下。
金属离子A存在于基材纤维的表面的至少一部分,例如附着于基材纤维的表面的至少一部分。金属离子A能够用作抗菌成分。金属离子A可以包含于存在于基材纤维的表面的至少一部分的金属盐中。从抗菌性容易提高的观点出发,金属离子A优选包含银离子。
金属离子A可以与高分子化合物形成复合物(例如高分子化合物的金属盐),金属离子A与高分子化合物的复合物可以存在于基材纤维的表面的至少一部分。通过使金属离子A与高分子化合物形成复合物,金属离子A容易附着于基材纤维的表面。金属离子A例如可以与高分子化合物形成络合物。
高分子化合物能够具有源自各种单体的结构单元。作为赋予高分子链的单体,可举出(甲基)丙烯酸、(甲基)丙烯酸酯(聚(亚烷基二醇)烷基醚(甲基)丙烯酸酯(聚(乙二醇)甲醚(甲基)丙烯酸酯等)、(甲基)丙烯酸丁酯等)、乙烯基化合物(乙烯基咪唑(1-乙烯基咪唑等)、乙烯基吡啶(4-乙烯基吡啶等)等)、乙烯、丁二烯、2,3-二氯-1,3-丁二烯、1-氯-1,3-丁二烯、异戊二烯、苯乙烯等。高分子化合物可以具有源自(甲基)丙烯酸酯的结构单元(可以具有(甲基)丙烯酸酯作为单体单元)、可以具有源自(甲基)丙烯酸酯的结构单元、和源自乙烯基化合物的结构单元(可以具有(甲基)丙烯酸酯及乙烯基化合物作为单体单元)。
从得到优异的抗菌性的观点出发,以人工毛发用纤维的总质量为基准,金属离子A的含量为5.0×10-5质量%以上。从得到人工毛发用纤维的优异的粗糙抑制效果的观点出发,以人工毛发用纤维的总质量为基准,金属离子A的含量为1.0×10-2质量%以下。金属离子A的含量是银离子、锌离子及铜离子的合计量。
从容易得到优异的抗菌性的观点出发,以人工毛发用纤维的总质量为基准,金属离子A的含量、银离子的含量、锌离子的含量、或铜离子的含量优选为8.0×10-5质量%以上、1.0×10-4质量%以上、2.0×10-4质量%以上、3.0×10-4质量%以上、4.0×10-4质量%以上、5.0×10-4质量%以上、7.0×10-4质量%以上、8.0×10-4质量%以上、1.0×10-3质量%以上、3.0×10-3质量%以上、4.0×10-3质量%以上、4.5×10-3质量%以上、5.0×10-3质量%以上、6.0×10-3质量%以上、7.0×10-3质量%以上、或8.0×10-3质量%以上。
从容易得到人工毛发用纤维的优异的触感(油腻抑制效果、粗糙抑制效果等)的观点出发,以人工毛发用纤维的总质量为基准,金属离子A的含量、银离子的含量、锌离子的含量、或铜离子的含量优选为8.0×10-3质量%以下、7.0×10-3质量%以下、6.0×10-3质量%以下、5.0×10-3质量%以下、4.5×10-3质量%以下、4.0×10-3质量%以下、3.0×10-3质量%以下、1.0×10-3质量%以下、8.0×10-4质量%以下、7.0×10-4质量%以下、5.0×10-4质量%以下、4.0×10-4质量%以下、或3.0×10-4质量%以下。
从容易高度兼顾抗菌性及触感的观点出发,以人工毛发用纤维的总质量为基准,金属离子A的含量、银离子的含量、锌离子的含量、或铜离子的含量优选为8.0×10-5~8.0×10-3质量%、2.0×10-4~7.0×10-3质量%、4.0×10-4~6.0×10-3质量%、5.0×10-4~5.0×10-3质量%、1.0×10-3~5.0×10-3质量%、或3.0×10-3~5.0×10-3质量%。
本实施方式的人工毛发用纤维具有存在于基材纤维的表面的至少一部分的抗静电剂A。通过使用抗静电剂A,能够提高抗静电性。抗静电剂A例如附着于基材纤维的表面的至少一部分。作为抗静电剂A,能够使用不含金属离子A的化合物。
从易于使抗静电剂存在于基材纤维的表面的至少一部分(在制造人工毛发用纤维时易于提高后述的纤维处理剂的稳定性)而容易得到优异的抗静电性的观点出发,抗静电剂A为选自由阳离子性抗静电剂及非离子性(Nonionic)抗静电剂组成的组中的至少一种。
作为阳离子性抗静电剂,可举出季铵盐、胍化合物、咪唑啉化合物、吡啶鎓化合物等。胍化合物能够包含选自由胍及其盐组成的组中的至少一种。作为季铵盐,可举出四烷基氯化铵、四甲基硫酸铵、四烷基硫酸氢铵、三烷基氯化铵、芳基三烷基氯化铵等。作为胍盐,可举出胍盐酸盐、胍磷酸盐等。从容易抑制油腻及粗糙且得到优异的抗菌性及抗静电性的观点出发,抗静电剂A优选包含选自由季铵盐及胍化合物组成的组中的至少一种。
作为非离子性抗静电剂,可举出多元醇(例如,聚乙二醇等聚亚烷基二醇)、多元醇的脂肪酸酯、环氧烷聚合物(例如环氧丙烷与环氧乙烷的共聚物)等。从容易抑制油腻及粗糙且得到优异的抗菌性及抗静电性的观点出发,抗静电剂A优选包含选自由多元醇及环氧烷聚合物组成的组中的至少一种,更优选包含选自由聚亚烷基二醇及环氧丙烷与环氧乙烷的共聚物组成的组中的至少一种。
从容易抑制油腻及粗糙且得到优异的抗菌性及抗静电性的观点出发,聚亚烷基二醇(例如聚乙二醇)的重均分子量可以为下述的范围。重均分子量可以为100以上、200以上、300以上、400以上、500以上、550以上、或600以上。重均分子量可以为2000以下、1500以下、1000以下、800以下、700以下、650以下、或600以下。从上述的观点出发,重均分子量可以为100~2000、300~1000、或550~650。
从易于使抗静电剂存在于基材纤维的表面的至少一部分(制造人工毛发用纤维时容易抑制含硫化合物的沉淀,从而容易提高后述的纤维处理剂的稳定性)而容易得到优异的抗静电性的观点出发,选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种优选包含不含硫原子的抗静电剂。
本实施方式的人工毛发用纤维可以具有阴离子性抗静电剂、离子液体等作为存在于基材纤维的表面的至少一部分的抗静电剂。
作为阴离子性抗静电剂,可举出磺酸盐、硫酸酯盐、磷酸酯盐(例如聚氧亚烷基烷基醚磷酸盐)等。
作为离子液体,能够使用仅由离子(阳离子及阴离子)构成的液体化合物盐。作为离子液体的阳离子,可举出铵离子、咪唑鎓离子、吡啶鎓离子、吡咯烷鎓离子、吡咯啉鎓离子、哌啶鎓离子、吡嗪鎓离子、嘧啶鎓离子、三唑鎓离子、三嗪鎓离子、喹啉鎓离子、异喹啉鎓离子、吲哚啉鎓离子、喹喔啉鎓离子、哌嗪鎓离子、噁唑啉鎓离子、噻唑啉鎓离子、吗啉鎓离子等。作为离子液体的阴离子,可举出卤素系离子、硼系离子、磷系离子、磺酸阴离子等。作为离子液体,能够使用包含具有氨基的离子的胺盐。
从得到优异的抗静电性的观点出发,以人工毛发用纤维的总质量为基准,抗静电剂A的含量为0.001质量%以上。从得到人工毛发用纤维的优异的油腻抑制效果的观点出发,抗静电剂A的含量为1质量%以下。抗静电剂A的含量是阳离子性抗静电剂及非离子性抗静电剂的合计量。
从容易得到优异的抗静电性的观点出发,以人工毛发用纤维的总质量为基准,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为0.005质量%以上、0.01质量%以上、0.015质量%以上、0.02质量%以上、0.03质量%以上、0.05质量%以上、0.1质量%以上、0.15质量%以上、0.19质量%以上、0.2质量%以上、0.25质量%以上、0.3质量%以上、0.35质量%以上、0.4质量%以上、0.5质量%以上、0.6质量%以上、0.8质量%以上、或0.9质量%以上。
从容易得到人工毛发用纤维的优异的油腻抑制效果的观点出发,以人工毛发用纤维的总质量为基准,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为0.9质量%以下、0.8质量%以下、0.6质量%以下、0.5质量%以下、0.4质量%以下、0.35质量%以下、0.3质量%以下、0.25质量%以下、0.2质量%以下、0.19质量%以下、0.15质量%以下、0.1质量%以下、0.05质量%以下、0.03质量%以下、0.02质量%以下、0.015质量%以下、0.01质量%以下、或0.005质量%以下。
从上述的观点出发,以人工毛发用纤维的总质量为基准,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为0.005~0.9质量%、0.01~0.9质量%、0.01~0.5质量%、0.02~0.5质量%、0.02~0.4质量%、0.02~0.3质量%、0.03~0.3质量%、或0.05~0.2质量%。
抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量相对100质量份的金属离子A而言优选为下述的范围。
从容易抑制油腻及粗糙且得到优异的抗菌性及抗静电性的观点出发,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为1.0×102质量份以上、1.1×102质量份以上、2.0×102质量份以上、2.2×102质量份以上、3.0×102质量份以上、4.0×102质量份以上、4.4×102质量份以上、5.0×102质量份以上、6.0×102质量份以上、6.3×102质量份以上、7.0×102质量份以上、1.0×103质量份以上、1.1×103质量份以上、2.0×103质量份以上、2.2×103质量份以上、3.0×103质量份以上、4.0×103质量份以上、4.4×103质量份以上、5.0×103质量份以上、6.0×103质量份以上、8.0×103质量份以上、1.0×104质量份以上、1.7×104质量份以上、2.0×104质量份以上、3.0×104质量份以上、5.0×104质量份以上、或6.0×104质量份以上。
从容易抑制油腻及粗糙且得到优异的抗菌性及抗静电性的观点出发,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为1.0×105质量份以下、8.0×104质量份以下、6.0×104质量份以下、5.0×104质量份以下、3.0×104质量份以下、2.0×104质量份以下、1.7×104质量份以下、1.0×104质量份以下、8.0×103质量份以下、6.0×103质量份以下、5.0×103质量份以下、4.4×103质量份以下、4.0×103质量份以下、3.0×103质量份以下、2.2×103质量份以下、2.0×103质量份以下、1.1×103质量份以下、1.0×103质量份以下、7.0×102质量份以下、6.3×102质量份以下、6.0×102质量份以下、5.0×102质量份以下、4.4×102质量份以下、4.0×102质量份以下、3.0×102质量份以下、2.2×102质量份以下、2.0×102质量份以下、或1.1×102质量份以下。
从上述的观点出发,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为1.0×102~1.0×105质量份、3.0×102~5.0×104质量份、5.0×102~3.0×104质量份、7.0×102~2.0×104质量份、或1.0×102~1.0×104质量份。
本实施方式的人工毛发用纤维可以具有存在于基材纤维的表面的至少一部分的氨成分(不包括属于抗静电剂A的成分),也可以不具有这样的氨成分。通过使用氨成分,易于使金属离子或抗静电剂存在于基材纤维的表面的至少一部分(制造人工毛发用纤维时易于提高后述的纤维处理剂的稳定性),因而容易抑制油腻及粗糙且得到优异的抗菌性及抗静电性。作为氨成分,可举出氨、铵阳离子(NH4 +)等。氨成分可以以氢氧化铵的形式存在。
本实施方式的人工毛发用纤维可以具有存在于基材纤维的表面的至少一部分的其他添加剂(不包括属于金属离子A、抗静电剂A或氨成分的成分)。作为这样的添加剂,可举出抗菌加工剂、除臭加工剂、防霉加工剂、UV阻隔剂、柔软剂、SR加工剂、芳香加工剂、阻燃剂、消泡剂、香料等。作为添加剂,可以使用胺化合物(例如乙二胺四乙酸(EDTA)。不包括属于抗静电剂的化合物)、有机硅化合物、碱金属、聚氧乙烯烷基醚等。胺化合物可以是具有螯合作用的化合物。本实施方式的人工毛发用纤维中,有机硅化合物可以不存在于基材纤维的表面。本实施方式的人工毛发用纤维中,选自由沸石及碳化锆组成的组中的至少一种可以不存在于基材纤维的表面,基材纤维可以不含有选自由沸石及碳化锆组成的组中的至少一种。
在基材纤维的表面上,上述金属离子A、抗静电剂A、氨成分及添加剂的各自可以彼此存在于同一位置,也可以存在于彼此不同的位置。本实施方式的人工毛发用纤维可以具有存在于基材纤维的表面的至少一部分的纤维处理剂(处理剂),可以为利用纤维处理剂对表面进行处理后的人工毛发用纤维。
本实施方式的人工毛发用纤维的单纤度在拉伸处理后优选为下述的范围。单纤度优选为20分特以上。单纤度优选为100分特以下。从上述的观点出发,单纤度优选为20~100分特。
本实施方式的人工毛发用纤维可以通过使基材纤维接触含有金属离子A及抗静电剂A的纤维处理剂(处理剂)而得到,也可以通过使金属离子A、抗静电剂A等各成分分别接触基材纤维而得到。作为人工毛发用纤维的制造方法的一个例子,本实施方式的人工毛发用纤维的制造方法具备纤维处理工序,该纤维处理工序中,使基材纤维接触含有金属离子A及抗静电剂A的纤维处理剂(处理剂)。纤维处理剂可以为含有水等液状成分的处理液。在金属离子A及抗静电剂A的基础上,纤维处理剂可以含有上述氨成分、添加剂等。
从得到优异的抗菌性的观点出发,以纤维处理剂的总质量为基准,纤维处理剂中金属离子A的含量为3.0×10-4质量%以上。从得到人工毛发用纤维的优异的粗糙抑制效果的观点出发,以纤维处理剂的总质量为基准,纤维处理剂中金属离子A的含量为3.0×10-2质量%以下。即,以纤维处理剂的总质量为基准,纤维处理剂中金属离子A的含量为3.0×10-4~3.0×10-2质量%。
从容易得到优异的抗菌性的观点出发,以纤维处理剂的总质量为基准,金属离子A的含量、银离子的含量、锌离子的含量、或铜离子的含量优选为5.0×10-4质量%以上、8.0×10-4质量%以上、9.0×10-4质量%以上、9.8×10-4质量%以上、1.0×10-3质量%以上、3.0×10-3质量%以上、5.0×10-3质量%以上、8.0×10-3质量%以上、1.0×10-2质量%以上、1.5×10-2质量%以上、2.0×10-2质量%以上、或2.5×10-2质量%以上。
从容易得到人工毛发用纤维的优异的触感(油腻抑制效果、粗糙抑制效果等)的观点出发,以纤维处理剂的总质量为基准,金属离子A的含量、银离子的含量、锌离子的含量、或铜离子的含量优选为2.5×10-2质量%以下、2.0×10-2质量%以下、1.5×10-2质量%以下、1.0×10-2质量%以下、8.0×10-3质量%以下、5.0×10-3质量%以下、3.0×10-3质量%以下、1.0×10-3质量%以下、或9.8×10-4质量%以下。
从容易高度兼顾抗菌性及触感的观点出发,以纤维处理剂的总质量为基准,金属离子A的含量、银离子的含量、锌离子的含量、或铜离子的含量优选为5.0×10-4~2.5×10-2质量%、9.0×10-4~2.5×10-2质量%、1.0×10-3~2.0×10-2质量%、5.0×10-3~2.0×10-2质量%、或1.0×10-3~2.0×10-2质量%。
从得到优异的抗静电性的观点出发,以纤维处理剂的总质量为基准,纤维处理剂中抗静电剂A的含量为0.005质量%以上。从得到人工毛发用纤维的优异的油腻抑制效果的观点出发,以纤维处理剂的总质量为基准,纤维处理剂中抗静电剂A的含量为4质量%以下。即,以纤维处理剂的总质量为基准,纤维处理剂中抗静电剂A的含量为0.005~4质量%。
从容易得到优异的抗静电性的观点出发,以纤维处理剂的总质量为基准,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为0.01质量%以上、0.02质量%以上、0.05质量%以上、0.1质量%以上、0.15质量%以上、0.18质量%以上、0.19质量%以上、0.2质量%以上、0.3质量%以上、0.5质量%以上、0.8质量%以上、0.9质量%以上、1质量%以上、1.8质量%以上、2质量%以上、3质量%以上、3.5质量%以上、或3.6质量%以上。
从容易得到人工毛发用纤维的优异的油腻抑制效果的观点出发,以纤维处理剂的总质量为基准,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量为3.6质量%以下、3.5质量%以下、3质量%以下、2质量%以下、1.8质量%以下、1质量%以下、0.9质量%以下、0.8质量%以下、0.5质量%以下、0.3质量%以下、0.2质量%以下、0.19质量%以下、0.18质量%以下、0.15质量%以下、0.1质量%以下、0.05质量%以下、或0.02质量%以下。
从上述的观点出发,以纤维处理剂的总质量为基准,抗静电剂A的含量、阳离子性抗静电剂的含量、或非离子性抗静电剂的含量优选为0.01~3.6质量%、0.02~3质量%、0.05~1质量%、0.1~0.8质量%、0.1~0.5质量%、或0.1~0.3质量%。
使用纤维处理剂的情况下,能够将纤维处理剂涂布于基材纤维的表面的至少一部分。该情况下,能够使用将液体涂布于纤维的以往已知的手段。例如,可举出:利用具有附着有纤维处理剂的表面的辊将纤维处理剂涂布于人工毛发用纤维的手段(辊转印法);将基材纤维浸在储存有纤维处理剂的液体槽中的手段;介由刷子、板刷等涂布工具使纤维处理剂附着于基材纤维的手段等。
本实施方式的人工毛发用纤维的制造方法可以在纤维处理工序之前具备纺丝工序,该纺丝工序通过对含有基材纤维的材料的组合物进行纺丝从而得到基材纤维。纺丝工序中,能够对含有基材纤维的材料的组合物进行熔融纺丝(熔融变形)。
本实施方式的人工毛发用纤维的制造方法可以在纺丝工序之前具备混炼工序,该混炼工序对含有基材纤维的材料的组合物进行熔融混炼。作为用于进行熔融混炼的装置,能够使用各种通常的混炼机。作为混炼机,可举出单螺杆挤出机、双螺杆挤出机、辊、班伯里混炼机、捏合机等。
本实施方式的人工毛发用纤维的制造方法可以在纤维处理工序之前具备拉伸工序,该拉伸工序对纺丝工序中得到的丝(未拉伸丝)进行拉伸处理。
从容易呈现出纤维的强度的观点出发,拉伸工序中的拉伸倍率优选为1.5倍以上,更优选为2.0倍以上。从拉伸处理时不易发生断丝的观点出发,拉伸倍率优选为5.0倍以下,更优选为4.0倍以下。从上述的观点出发,拉伸倍率优选为1.5~5.0倍,更优选为2.0~4.0倍。
拉伸处理可以利用将未拉伸丝暂时卷绕于绕线筒之后、在与纺丝工序不连续的工序中进行拉伸的两步工序法来进行,也可以利用在不将未拉伸丝卷绕于绕线筒的情况下在与纺丝工序连续的工序中进行拉伸的直接纺丝拉伸法来进行。拉伸处理可以利用以1次拉伸至目标拉伸倍率的一步拉伸法来进行,也可以利用通过2次以上的拉伸而拉伸至目标拉伸倍率的多步拉伸法来进行。
拉伸处理的温度优选为80~120℃。若温度为80℃以上,容易充分确保纤维的强度且同时不易发生断丝。若温度为120℃以下,则容易得到纤维的适宜的触感。
本实施方式的人工毛发用纤维的制造方法可以在拉伸工序之后具备热处理工序,该热处理工序对拉伸工序中得到的丝(拉伸丝)进行热处理(退火)。通过进行热处理工序,能够降低拉伸丝的热收缩率。
热处理温度优选为100℃以上,更优选为120℃以上。热处理温度优选为200℃以下,更优选为150℃以下。热处理可以在拉伸处理之后连续地进行,也可以在暂时卷绕之后空开时间进行。
本实施方式的头发装饰品具备本实施方式的人工毛发用纤维。本实施方式的头发装饰品是能在头部摘戴的物品,也可以为仅由本实施方式的人工毛发用纤维形成的方式(例如,人工毛发用纤维的纤维束)。作为头发装饰品,可举出掩饰用假发(日文:かつら)、装饰用假发(日文:ヘアウィッグ)、假发片、辫发、接发、植发等。
实施例
以下,利用实施例更具体地对本发明进行说明,但本发明并不限于这些实施例。以下,“1.0E-03”、“1.0E+10”等表述是指“1.0×10-3”、“1.0×1010”等。
<基材纤维的准备>
准备表1~4中示出的下述基材纤维。
基材纤维A:氯乙烯系纤维、使用了聚氯乙烯(Taiyo Vinyl Corporation、商品名“TH-700”)的纤维、由具有弱轴的截面惯性矩为10×10-4mm4的出口截面的喷嘴纺丝而成的纤维(利用溶液纺丝法制作而成的纤维),平均纤度40~70分特(100根纤维的纤度的平均值)
基材纤维B:氯乙烯与丙烯酸酯的共聚物的纤维、由具有弱轴的截面惯性矩为10×10-4mm4的出口截面的喷嘴纺丝而成的纤维(利用溶液纺丝法制作而成的纤维),平均纤度40~70分特(100根纤维的纤度的平均值)
基材纤维C:聚丙烯纤维、由具有弱轴的截面惯性矩为10×10-4mm4的出口截面的喷嘴纺丝而成的纤维(利用熔融纺丝法制作而成的纤维),平均纤度40~70分特(100根纤维的纤度的平均值)
基材纤维D:PET纤维、由具有弱轴的截面惯性矩为10×10-4mm4的出口截面的喷嘴纺丝而成的纤维(利用熔融纺丝法制作而成的纤维),平均纤度40~70分特(100根纤维的纤度的平均值)
<纤维处理剂的制备>
通过将表1~4中示出的成分(金属离子源、抗静电剂、铵水等)混合来制备纤维处理剂。作为各表中示出的成分,使用下述试剂。
(金属离子源)
金属离子源A(Ag):本公司制备品,含有0.1质量%银离子的硝酸银水溶液
金属离子源B(Zn):本公司制备品,含有0.1质量%锌离子的硝酸锌水溶液
金属离子源C(Cu):本公司制备品,含有0.1质量%铜离子的硝酸铜水溶液
金属离子源D(Ag):Du Pont公司,商品名“SILVADUR 930Flex Antimicrobial”,含有银离子、氢氧化铵及聚合物的水系分散液(银离子量:0.098质量%、氢氧化铵量:0.25~1.0质量%、聚合物:具有源自1-乙烯基咪唑的结构单元及源自聚(乙二醇)甲基醚甲基丙烯酸酯的结构单元的共聚物(与银离子形成复合物的高分子化合物))
(抗静电剂)
[阳离子性抗静电剂]
阳离子性抗静电剂A:吉村油化学株式会社,商品名“GST-8”,含有20质量%胍盐酸盐的水溶液
阳离子性抗静电剂B:本公司制备品,用水将第一工业制药株式会社的商品名“CATIOGEN TML”稀释而得的水溶液(含有20质量%四烷基氯化铵的水溶液(季铵氯化物水溶液))
阳离子性抗静电剂C:本公司制备品,用水将第一工业制药株式会社的商品名“CATIOGEN ES-O”稀释而得的水溶液(含有20质量%四烷基铵硫酸盐的水溶液(季铵硫酸盐水溶液))
[非离子性抗静电剂]
非离子性抗静电剂A:本公司制备品,含有20质量%重均分子量为550~650的聚乙二醇(吉村油化学株式会社,商品名“PEG-600”)的水溶液
非离子性抗静电剂B:吉村油化学株式会社,商品名“TYO-11”,含有20质量%环氧丙烷与环氧乙烷的共聚物的水溶液
[阴离子性抗静电剂]
本公司制备品,用水将日本乳化剂株式会社的商品名“Antox EHD-PNA”稀释而得的水溶液(含有20质量%聚氧亚烷基烷基醚磷酸盐的水溶液(磷酸阴离子盐水溶液))
(铵水)
FUJIFILM Wako Pure Chemical Corporation,商品名“氨水(日文;アンモニア水)”,含有25质量%氨的氨水溶液
<纤维处理剂的稳定性>
通过目视确认来确认纤维处理剂中沉淀的有无,按下述基准进行评价。具体而言,对纤维处理剂进行搅拌后,静置,于室温下观察有无沉淀。将结果示于表1~4。
A:1周以上未形成沉淀
B:1天以上且不满1周形成沉淀
C:半天以上且不满1天形成沉淀
D:不满半天形成沉淀
<评价用纤维的制作>
于100℃对上述基材纤维进行拉伸后,利用辊转印法将上述纤维处理剂涂布于基材纤维。作为辊转印的条件,辊的半径为125mm,辊浸在纤维处理剂中至距辊的下端20mm的高度,辊旋转速度为8m/分钟。然后,于120℃进行退火,得到单纤度20~100分特的评价用纤维(人工毛发用纤维)。拉伸倍率为3.25倍,退火时的松弛率为25%。退火时的松弛率是用“(退火炉的辊的最靠近出口部分的圆周)/(退火炉的辊的最靠近入口部分的圆周)”算出的值。
将评价用纤维的表面的金属离子及抗静电剂的附着量(单位:质量%)作为评价用纤维中的有效成分的含量而示于各表中。就附着量而言,假设纤维处理剂的减少量中的固态成分附着于评价用纤维的表面,利用“((纤维处理工序中的纤维处理剂的减少量×(纤维处理剂中的各试剂的有效成分比例[%]/100))/评价用纤维的总量)×100”而算出。
<评价>
使用上述的评价用纤维对抗菌性、抗静电性、触感及阻燃性进行评价。将结果示于表1~4。如各表中所示,可知实施例中能抑制油腻及粗糙且可得到优异的抗菌性及抗静电性。
(抗菌性)
基于JIS L 1902对评价用纤维的抗菌性进行评价。作为试验菌,使用金黄色葡萄球菌,测定于37℃放置18小时前后的抗菌活性值(活菌数之差)。所谓“抗菌活性值”,是由JIS L 1902的“菌液吸收法”所定义的下述值。
A=(logCt-logC0)-(logTt-logT0)
A:抗菌活性值
Ct:培养18小时后的对象试样3检样的活菌数的算术平均值的常用对数
C0:刚接种后的对象试样3检样的活菌数的算术平均值的常用常数
Tt:培养18小时后的试验试样3检样的活菌数的算术平均值的常用对数
T0:刚接种后的试验试样3检样的活菌数的算术平均值的常用对数
(抗静电性)
将上述评价用纤维束起来得到长250mm、质量20g的纤维束。接着,将纤维束在23℃、50%RH的环境下放置24小时之后,使用数字超高阻/微电流测量仪(株式会社ADVANTEST、商品名:R8340)在施加电压10V的条件下测定表面电阻值。基于5次测定的平均值评价抗静电性。在各表中示出平均值。
(触感)
作为触感,对油腻及粗糙进行评价。将上述评价用纤维束起来得到长250mm、质量20g的纤维束。通过10名人工毛发用纤维处理技术人员(实践经验5年以上)的手触摸按下述基准对纤维束的油腻及粗糙进行评价。即使只存在一人是NG评价的情况下,也判定为“NG”,没有NG评价的情况下,算出合计分数。在各表中示出合计分数。
[油腻]
3分:不油腻
1分:具有接受范围内的油腻
NG:具有不可接受的油腻
[粗糙]
3分:不粗糙
1分:具有接受范围内的粗糙
NG:具有不可接受的粗糙
(阻燃性)
将上述的评价用纤维束起来得到10根长200mm、质量1g的纤维束。接着,将纤维束在23℃、50%RH的环境下放置24小时。然后,使用点火装置(株式会社东海,商品名:CRChukkaman)将纤维束暴露于火中3秒钟,确认火是否自然熄灭。按下述基准进行判定。
A:10根纤维束上的火均熄灭
B:1~9根纤维束上的火熄灭
C:所有纤维束上的火均没有熄灭[表1]
[表2]
[表3]
[表4]
Claims (11)
1.人工毛发用纤维,
其具有基材纤维、金属离子和抗静电剂,
所述金属离子及所述抗静电剂存在于所述基材纤维的表面的至少一部分,
所述金属离子为选自由银离子、锌离子及铜离子组成的组中的至少一种,
以该人工毛发用纤维的总质量为基准,所述金属离子的含量为5.0×10-5~1.0×10-2质量%,
所述抗静电剂为选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种,
以该人工毛发用纤维的总质量为基准,所述抗静电剂的含量为0.001~1质量%。
2.如权利要求1所述的人工毛发用纤维,其中,所述基材纤维包含氯乙烯系树脂。
3.如权利要求1或2所述的人工毛发用纤维,其中,所述基材纤维包含聚酯系树脂。
4.如权利要求1~3中任一项所述的人工毛发用纤维,其中,所述基材纤维包含聚烯烃系树脂。
5.如权利要求1~4中任一项所述的人工毛发用纤维,其中,所述金属离子包含银离子。
6.如权利要求1~5中任一项所述的人工毛发用纤维,其中,所述抗静电剂包含选自由季铵盐及胍化合物组成的组中的至少一种。
7.如权利要求1~6中任一项所述的人工毛发用纤维,其中,所述抗静电剂包含选自由聚亚烷基二醇及环氧丙烷与环氧乙烷的共聚物组成的组中的至少一种。
8.如权利要求1~7中任一项所述的人工毛发用纤维,其中,选自由所述阳离子性抗静电剂及所述非离子性抗静电剂组成的组中的至少一种包含不含硫原子的抗静电剂。
9.如权利要求1~8中任一项所述的人工毛发用纤维,其还具有存在于所述基材纤维的表面的至少一部分的氨成分。
10.头发装饰品,其具备权利要求1~9中任一项所述的人工毛发用纤维。
11.人工毛发用纤维的制造方法,其具备使基材纤维接触含有金属离子及抗静电剂的处理剂的工序,
所述金属离子为选自由银离子、锌离子及铜离子组成的组中的至少一种,
以所述处理剂的总质量为基准,所述金属离子的含量为3.0×10-4~3.0×10-2质量%,
所述抗静电剂为选自由阳离子性抗静电剂及非离子性抗静电剂组成的组中的至少一种,
以所述处理剂的总质量为基准,所述抗静电剂的含量为0.005~4质量%。