CN115594853B - 一种非氟聚合物及其制备方法和应用 - Google Patents
一种非氟聚合物及其制备方法和应用 Download PDFInfo
- Publication number
- CN115594853B CN115594853B CN202110768306.1A CN202110768306A CN115594853B CN 115594853 B CN115594853 B CN 115594853B CN 202110768306 A CN202110768306 A CN 202110768306A CN 115594853 B CN115594853 B CN 115594853B
- Authority
- CN
- China
- Prior art keywords
- chemical formula
- polyether
- formula
- fluoropolymer
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种非氟聚合物,包括三部分:第一部分为R—*结构单元,其中R选自R1、R2和R3中的一种或者多种,R1代表C8~30烷基,R2代表C8~30烷基异氰酸酯基,R3代表C8~30酸酯基;第二部分为超支化结构聚醚,其中单个聚醚端基数为2~16个;第三部分为硅氧烷链结构单元,其中单甲基硅单元的数量为2~30个,二甲基硅单元的数量为2~30个;第二部分分别与第一部分和第三部分连接。还公开了该非氟聚合物的制备方法和应用。本发明将长链烷基结构和有机硅的结构通过超支化结构聚醚连接在一起,发挥协同效应,使得该非氟聚合物同时获得防水性能和柔软性能,在织物和纸张上具有潜在的应用优势。
Description
技术领域
本发明属于材料化学领域,特别涉及一种非氟聚合物及其制备方法和应用。该非氟聚合物为衍生自含长链烷烃和环氧、羟基官能团等非氟单体组成的聚合物。该聚合物可用于提高织物表面或者纸张表面的防水效果。
背景技术
水作为人们日常活动中经常触及的实物之一时刻在影响着人们的活动。而以棉织物为代表的传统天然纤维,拥有很好的吸湿性能,所以拒水性能很差。如今人们不复之前,受制于传统的活动范围,对于纺织品功能的要求越来越高。纺织品在许多的领域中都被要求具有防水防油等特别的性能。为了使纺织品具备一定的防水功能,开发防水型纺织品或研发出防水整理剂,对纺织品进行防水处理,势在必行。而在防水功能整理方面,以含氟聚丙烯酸酯乳液或溶液的防水效果最好,因为经其处理后的织物或基材具有极低的表面能,水很难在其表面润湿。而含氟类聚丙烯酸尤以含-C8F17基团的效果最好,即人们通常简称为C8类防水剂,但是C8类防水剂因为含有的全氟辛酸类有害物质或容易导致产生全氟辛酸类物质而遭到欧盟、美国以及其它发达国家的限制应用或禁用,到2012年底全球主要的C8氟碳防水剂供应商集体决定停止C8产品的生产,而到2015年底欧洲和北美地区已经彻底停止C8产品的销售。因此越来越多的企业开始转向C8的替代品。非氟防水剂正是主要的C8替代品之一。
目前报道的非氟防水剂的化合物主要为基于聚丙烯酸酯的或基于聚氨酯的聚合物。中国专利(申请号为201580064148.4)公开了一种基于糖醇的聚丙烯酸酯聚合物,其为织物提供抗水性。中国专利(申请号为201780041440.3)公开了一种基于聚氨酯的聚合物组合料,同样是作为非氟防水剂应用于织物。
现有的织物防水剂技术主要为以上提到的三类:第一类含氟丙烯酸酯具有最佳的防水性能,但含有对环境有巨大污染影响的全氟辛酸类有害物质而导致其被限制使用或禁用;第二类非氟丙烯酸酯和第三类非氟聚氨酯的防水性不如含氟丙烯酸酯,在实际应用中为了达到类似的防水效果,非氟丙烯酸酯/聚氨酯的使用量通常为含氟丙烯酸酯的2-5倍。在高浓度的使用量下,丙烯酸酯/聚氨酯的刚性分子链结构不可避免地带来一些负面的影响,例如增加了织物的硬度从而降低织物的手感。
除织物防水需求外,随着人们生活水平的提高,需求的多样化,在一些特殊情况下,对纸张也有防水需求。需要对纸张进行防水效果处理。
发明内容
针对这些问题,本发明通过对聚合物结构的优化组合在实现更好的防水效果的同时保持织物柔软的手感。本发明提供了一种非氟聚合物,包括:
由化学式1表示的结构单元,其中R选自R1、R2和R3中的一种或者多种,R1代表C8~30烷基,R2代表C8~30烷基异氰酸酯基,R3代表C8~30酸酯基;
超支化结构聚醚,其中单个聚醚端基数为2~16个;
由化学式2表示的结构单元,其中单甲基硅单元的数量为n个,n代表2~30的整数,二甲基硅单元的数量为m个,m代表2~30的整数;
[化学式1]
R—*
[化学式2]
其中,*为连接点;化学式1表示的结构单元连接在超支化结构聚醚的单个聚醚端基上,超支化结构聚醚连接在化学式2表示的结构单元上。
该非氟聚合物包括三部分:由化学式1表示的结构单元为第一部分;超支化结构聚醚为第二部分;由化学式2表示的结构单元为第三部分。
进一步地,超支化结构聚醚为由化学式3表示的化合物与由化学式4表示的化合物在催化剂作用下聚合生成的支化点3个以上的超支化聚醚多元醇,去掉羟基上的H形成连接点,以及打开双键形成连接点后的结构单元;
[化学式3]
[化学式4]
其中,A代表—(CH2)f—,f代表1~10的整数,w代表0~20的整数;催化剂选自醋酸钠、碳酸钠、碳酸氢钠、氢氧化钠、甲醇钠、碳酸钾、碳酸氢钾、甲醇钾、丁基锂、萘钠、钠、三乙胺、三乙烯二胺和4-二甲氨基吡啶中的一种或几种。本发明中的某个数值“以上”包括本数。
进一步地,超支化结构聚醚为由化学式5表示的结构单元;
[化学式5]
其中,单个聚醚端基上的连接点与化学式1表示的结构单元连接;非单个聚醚端基上的连接点与化学式2表示的结构单元连接。
进一步地,R1代表C10~26烷基,R2代表C10~26烷基异氰酸酯基;第二部分中的单个聚醚端基数为2~10个;n代表3~20的整数,m代表3~20的整数。
进一步地,R1代表C12~22烷基,R2代表C12~22烷基异氰酸酯基;第二部分中的单个聚醚端基数为4~8个;n代表4~10的整数,m代表4~10的整数。
在一个或多个具体实施方式中,该非氟聚合物为化学式6所示的化合物:
[化学式6]在一个或多个具体实施方式中,该非氟聚合物为化学式7所示的化合物:
[化学式7]在一个或多个具体实施方式中,该非氟聚合物为化学式8所示的化合物:
[化学式8]
在一个或多个具体实施方式中,该非氟聚合物为化学式9所示的化合物:
[化学式9]
在一个或多个具体实施方式中,该非氟聚合物为化学式10所示的化合物:
[化学式10]
本发明还提供一种如上所述的非氟聚合物的制备方法,包括超支化聚醚多元醇的合成,侧链含硅氢键的有机硅树脂的合成,以及将超支化聚醚多元醇与R单体和侧链含硅氢键的有机硅树脂连接得到非氟聚合物。
进一步地,超支化聚醚多元醇通过由化学式4表示的化合物与由化学式3表示的化合物在催化剂催化下反应合成,且所得超支化聚醚多元醇平均一个分子里有1个烯丙基和4个羟基;催化剂选自醋酸钠、碳酸钠、碳酸氢钠、氢氧化钠、甲醇钠、碳酸钾、碳酸氢钾、甲醇钾、丁基锂、萘钠、钠、三乙胺、三乙烯二胺和4-二甲氨基吡啶中的一种或几种。
进一步地,超支化聚醚多元醇的合成,具体为:聚醚改性烯丙基醇和甲醇钾加入至容器,升温至55-65℃,搅拌并抽真空保持1-2小时;然后滴加缩水甘油,滴加完毕后继续搅拌至红外环氧特征峰消失,得到超支化聚醚多元醇。
进一步地,侧链含硅氢键的有机硅树脂通过高含氢硅油TSF-484、八甲基环四硅氧烷和六甲基二硅醚在浓硫酸、碳酸钾条件下反应合成。
进一步地,侧链含硅氢键的有机硅树脂的合成,具体为:将高含氢硅油TSF-484和八甲基环四硅氧烷、六甲基二硅醚加入容器中,搅拌升温至30-35℃;加入浓硫酸搅拌5~7小时后降温至室温。加入碳酸钾搅拌直至pH值>6后停止搅拌,过滤得到侧链含硅氢键的有机硅树脂。
在一个或多个具体实施方式中,R单体选自十八烷基缩水甘油醚和异氰酸十八酯;
将超支化聚醚多元醇与R单体和侧链含硅氢键的有机硅树脂连接为:超支化聚醚多元醇先与R单体连接生成C18-III,再C18-III与侧链含硅氢键的有机硅树脂连接,具体为:
将超支化聚醚多元醇和十八烷基缩水甘油醚加入容器中,升温至80-90℃搅拌直至红外环氧特征峰消失;而后加入异氰酸十八酯,继续搅拌至红外异氰酸酯特征峰消失,而后停止搅拌降温,得到C18-III;
将侧链含硅氢键的有机硅树脂和C18-III加入容器中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌,经检测硅氢键已反应完毕后,停止搅拌并降温,得到非氟聚合物。
进一步地,还包括十八烷基缩水甘油醚的合成;十八烷基缩水甘油醚通过十八烷基醇和环氧氯丙烷在四乙基溴化铵催化下反应合成。
进一步地,十八烷基缩水甘油醚的合成具体为:将十八烷基醇放入容器中,加热至65~75℃;待十八烷基醇完全熔融后加入四乙基溴化铵和氢氧化钠,在温度保持在65-75℃之间滴加环氧氯丙烷;滴加完毕后继续搅拌4-6小时后停止加热;冷却至室温将所有反应物加入环己烷中,搅拌0.5-1小时;过滤白色固体,所得滤液在45~55℃下减压蒸馏除去环己烷即得到十八烷基缩水甘油醚。
在一个或多个具体实施方式中,R单体为异氰酸十八酯;
超支化聚醚多元醇与R单体和侧链含硅氢键的有机硅树脂连接为,超支化聚醚多元醇先与R单体连接生成C18-I,再C18-I与侧链含硅氢键的有机硅树脂连接,具体为:
将超支化聚醚多元醇和异氰酸十八酯混合并加热至80-90℃,搅拌直至红外异氰酸酯特征峰消失,而后停止搅拌降温,得到C18-I;
将侧链含硅氢键的有机硅树脂和C18-I加入容器中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌,经检测硅氢键已反应完毕后,停止搅拌并降温,得到非氟聚合物。
在一个或多个具体实施方式中,R单体选自十八烷基缩水甘油醚和乙酸酐;
超支化聚醚多元醇与R单体和侧链含硅氢键的有机硅树脂连接为,超支化聚醚多元醇先与R单体连接生成C18-II,再C18-II与侧链含硅氢键的有机硅树脂连接,具体为:
将超支化聚醚多元醇和十八烷基缩水甘油醚加入容器中,升温至80-90℃搅拌直至红外环氧特征峰消失;而后加入乙酸酐,继续搅拌2.5~3.5小时;而后停止搅拌降温,用K2CO3水溶液将产品洗涤至PH>7,再用饱和食盐水洗涤产品至中性,过滤干燥,得到C18-II;
将侧链含硅氢键的有机硅树脂和C18-II加入容器中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌,经检测硅氢键已反应完毕后,停止搅拌并降温,得到非氟聚合物。
在一个或多个具体实施方式中,R单体为硬脂酸甲酯;
超支化聚醚多元醇与R单体和侧链含硅氢键的有机硅树脂连接为,超支化聚醚多元醇先与R单体连接生成C18-IV,再C18-IV与侧链含硅氢键的有机硅树脂连接,具体为:
将超支化聚醚多元醇和硬脂酸甲酯混合并加热至80-90℃,保持搅拌加入甲醇钾并抽真空至气压小于150Pa;反应2.5~3.5小时后停止搅拌降温,用甲醇清洗后,过滤干燥,得到C18-IV;
将侧链含硅氢键的有机硅树脂和C18-IV加入容器中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌,经检测硅氢键已反应完毕后,停止搅拌并降温,得到非氟聚合物。
本发明还公开了如上所述的非氟聚合物的应用。该应用为应用于织物或者纸张。尤其是在防水织物或者防水纸张上的应用。或者在制备防水剂上的应用。尤其是在制备织物防水剂或者纸张防水剂上的应用。
本发明还公开了一种防水剂,含有如上所述的非氟聚合物。尤其是如上所述的非氟聚合物为该防水剂的主要成分或主要成分之一。该防水剂为织物防水剂或者纸张防水剂。
本发明创造性地采用了超支化聚醚多元醇的结构:一是使得多个长链烷烃分子链直接连接于同一个分子,有利于长链烷烃的结晶,从而产生防水的性能。二是聚醚的柔韧性加上超支化的结构,能为整个产品结构上提供一个软段,以增加产品的柔软性。
本发明将长链烷基结构和有机硅的结构通过超支化结构聚醚连接在一起,发挥协同效应,使得该非氟聚合物同时获得防水性能和柔软性能。而这两个特点对于织物、纸张等同时需要防水和柔软性能的应用方向有潜在的优势。
本发明不含有含氟丙烯酸酯,符合环保要求;分子结构中同时具有超支化结构和可结晶的长链烷基结构,这两个结构使得产品具有防水的性能;将有机硅,可结晶长链烷基通过化学键连接到同一个分子中,既协同了二者防水的性能,同时也成功的避免了物理共混存在的相分离的问题。
以下将结合附图对本发明的构思、具体结构及产生的技术效果作进一步说明,以充分地了解本发明的目的、特征和效果。
附图说明
图1是十八烷基缩水甘油醚的红外鉴定谱图。
图2是POH的红外鉴定谱图。
图3是C18-III和C18-Si-III的红外鉴定谱图。
图4是C18-Si-III的水接触角照片。
具体实施方式
为了使发明实现的技术手段、创造特征、达成目的和功效易于明白了解,下结合具体图示,进一步阐述本发明。但本发明不仅限于以下实施的案例。
须知,本说明书所附图式所绘示的结构、比例、大小等,均仅用以配合说明书所揭示的内容,以供熟悉此技术的人士了解与阅读,并非用以限定本发明可实施的限定条件,故不具技术上的实质意义,任何结构的修饰、比例关系的改变或大小的调整,在不影响本发明所能产生的功效及所能达成的目的下,均应仍落在本发明所揭示的技术内容得能涵盖的范围内。
实施例1化学式7所示的化合物的合成
步骤1、R单体在本实施例中主要为两种:异氰酸十八烷酯(分子式:C18H37NCO)和十八烷基缩水甘油醚(分子式:C20H40O2)。其中异氰酸十八酯为外购产品。十八烷基缩水甘油醚为自制,合成过程如下:
135g十八烷基醇(C18H37OH)放入500ml三口烧瓶中,加热至70℃。待十八烷基醇完全熔融后加入4.2g四乙基溴化铵和30g氢氧化钠(NaOH)。在温度保持在65-75℃之间滴加139g环氧氯丙烷。滴加完毕后继续搅拌4-6小时后停止加热。冷却至室温将所有反应物加入600g环己烷中,搅拌0.5-1小时。过滤掉白色固体,所得滤液在50℃下减压蒸馏除去环己烷即得到产品十八烷基缩水甘油醚,其红外鉴定谱图如图1所示。图1中的C18-OH表示十八烷基醇。
步骤2、超支化聚醚多元醇的合成过程如下:
49g烯丙基醇和0.3g甲醇钾加入至250ml烧瓶,升温至55-65℃,搅拌并抽真空保持1-2小时。然后滴加20g缩水甘油,滴加完毕后继续搅拌至红外环氧特征峰(910cm-1左右)消失。所得超支化聚醚多元醇平均官能团数为4(平均一个分子里有1个烯丙基和4个羟基)。将该4个官能团的超支化聚醚多元醇命名为POH,其红外鉴定谱图如图2所示。POH为选自化学式17、化学式18和化学式19所示的化合物中的一种或多种。事实上,化学式17、化学式18和化学式19这三种结构仅仅是支化结构不一样,但分子式是一样的,官能团的数量也是一样的。在超支化聚醚多元醇的合成反应式中以化学式17所示的化合物为例进行说明,化学式18和19所示的化合物也是通过相同的反应物、反应条件、催化剂催化合成的。后续步骤中也均采用化学式17所示的化合物为例进行说明。但需要知悉,采用化学式18或19所示的化合物,以同样方法进行是能够得到本发明所涉及的非氟聚合物的,只是其相应地超支化结构聚醚会随化学式17、18和19的支化结构不同而不同。
此外,可以用聚醚改性烯丙基醇(T-2003)代替烯丙基醇进行POH的合成,只是合成的POH中双链所在的分支会因T-2003带有11个—[O—C2H4]—组成的长链基团而不同于烯丙基醇合成的POH。同样地,通过后续步骤合成的非氟聚合物的超支化结构聚醚也会带有11个—[O—C2H4]—组成的长链基团。
事实上,烯丙基醇可以是化学式4所示的化合物。w的取值范围是0~20。
同样地,缩水甘油可以是化学式3所示的化合物。f的取值范围是1~10。
步骤3、连接超支化聚醚多元醇和R单体的连接过程如下:
将36g POH和55g十八烷基缩水甘油醚加入500ml烧瓶中,升温至80-90℃搅拌直至红外环氧特征峰(910cm-1左右)消失。而后加入52g异氰酸十八酯,继续搅拌至红外异氰酸酯特征峰(2290cm-1左右)消失。而后停止搅拌降温,得到产品,命名为C18-III,其红外鉴定谱图如图3所示。
步骤4、侧链含硅氢键的有机硅树脂的合成
将40g高含氢硅油TSF-484(迈图产品)和182g八甲基环四硅氧烷(D4),7.3g六甲基二硅醚(MM)加入500ml烧瓶中,搅拌升温至30-35℃。加入4.6g浓硫酸搅拌6小时后降温至室温。加入8.5g碳酸钾搅拌直至PH值>6后停止搅拌,过滤得到侧链含硅氢键的有机硅树脂,命名为SiH。
步骤5、连接SiH和C18-III
将21.5gSiH和96gC18-III加入500ml烧瓶中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌约3小时,经检测硅氢键已反应完毕后停止搅拌并降温(检测方法:取少量样品加入氢氧化钠水溶液中,无气泡产生则证明硅氢键反应完毕)。得到最终产品,命名为C18-Si-III,结构如化学式7所示,其红外鉴定谱图如图3所示。
实施例2化学式11所示的化合物的合成
[化学式11]
本实施例中步骤2和步骤4与实施例1同,且不存在R单体的合成,即没有实施例1中的步骤1。故这里仅列出步骤3和5。
步骤3:将36g POH和52g异氰酸十八酯混合并加热至80℃,保持搅拌至红外异氰酸酯特征峰(2290cm-1左右)消失。而后停止搅拌降温,得到产品命名为C18-I。C18-I的结构见如化学式12所示:
[化学式12]/>
步骤5:将21.5g SiH和67g C18-I加入500ml烧瓶中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌约3小时,经检测硅氢键已反应完毕后停止搅拌并降温(检测方法:取少量样品加入氢氧化钠水溶液中,无气泡产生则证明硅氢键反应完毕)。得到最终产品,命名为C18-Si-I,结构如化学式11所示。
实施例3化学式13所示的化合物的合成
[化学式13]
本实施例中步骤2和步骤4与实施例1同,且不存在R单体的合成,即没有实施例1中的步骤1。故这里仅列出步骤3和5。
步骤3、将48gPOH和73g十八烷基缩水甘油醚加入500ml烧瓶中,升温至80-90℃搅拌直至红外环氧特征峰(910cm-1左右)消失。而后加入30.4g乙酸酐,继续搅拌3小时。而后停止搅拌降温,用5%K2CO3水溶液将产品洗涤至PH>7,再用饱和食盐水洗涤产品至中性。过滤干燥,得到产品,命名为C18-II。C18-II的结构见如化学式14所示:
[化学式14]
步骤5、将21.5g SiH和76g C18-II加入500ml烧瓶中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌约3小时,经检测硅氢键已反应完毕后停止搅拌并降温(检测方法:取少量样品加入氢氧化钠水溶液中,无气泡产生则证明硅氢键反应完毕)。得到最终产品,命名为C18-Si-II,结构如化学式13所示。
实施例4化学式15所示的化合物的合成
[化学式15]
本实施例中步骤2和步骤4与实施例1同,且不存在R单体的合成,即没有实施例1中的步骤1。故这里仅列出步骤3和5。
步骤3、将38g POH和60g硬脂酸甲酯混合并加热至90℃,保持搅拌加入0.7g甲醇钾并抽真空至气压小于150Pa。反应3小时后停止搅拌降温,得到黄色固体,用甲醇清洗后得到白色固体,过滤干燥得到产品,命名为C18-IV。C18-IV的结构见如化学式16所示:
[化学式16]
步骤5、将32g SiH和178g C18-IV加入500ml烧瓶中,升温至90-100℃搅拌;加入24-36ppm的H2PtCl6搅拌约3小时,经检测硅氢键已反应完毕后停止搅拌并降温(检测方法:取少量样品加入氢氧化钠水溶液中,无气泡产生则证明硅氢键反应完毕)。得到最终产品,命名为C18-Si-IV,结构如化学式15所示。
实施例5性能检测
C18-Si-I、C18-Si-II、C18-Si-III和C18-Si-IV分别的数均分子量(Mn)、重均分子量(MW),以及不匀度指数(D)的数据见表1。
表1、4种产品的分子量数据
C18-Si-I | C18-Si-II | C18-Si-III | C18-Si-IV | |
Mn | 28,900 | 17,400 | 34,700 | 27,500 |
Mw | 55,800 | 39,100 | 79,100 | 49,500 |
D(Mw/Mn) | 1.93 | 2.25 | 2.28 | 1.80 |
防水性测试参考GB/T 4745—1997《纺织织物表面抗湿性测定沾水试验》
具体实验过程:将C18-Si系列树脂(包括C18-Si-I、C18-Si-II、C18-Si-III和C18-Si-IV)溶解于四氢呋喃中,配置成15%的溶液。经过浸染,干燥工艺后,织物表面抗湿性测试结果如表2所示。4种产品(即C18-Si-I、C18-Si-II、C18-Si-III和C18-Si-IV)在30、50、70g/L三个浓度梯度上分别对应的防水级别(ISO值)均在3以上,说明抗湿性性能良好,甚至还可以达到最高级别5。30g/L指30克C18-Si系列树脂溶于四氢呋喃形成的1L溶液中C18-Si系列树脂的浓度,换算成百分比是3%。以此类推可得到50g/L和70g/L浓度的产品。
表2、4种产品的织物表面抗湿性测试结果
用量(g/L) | C18-Si-I | C18-Si-II | C18-Si-III | C18-Si-IV |
30 | 3 | 3 | 3 | 3 |
50 | 4 | 3 | 3 | 4 |
70 | 5 | 4 | 4 | 5 |
实施例1得到的C18-Si-III的水接触角测试为110度,表明该产品具有防水的性能,见图4。图4是将C18-Si-III溶解在四氢呋喃里(浓度为10%),涂抹在玻璃片上,130℃干燥10分钟后,冷却至室温,分别滴加水滴在涂有C18-Si-III的位置(图4玻璃片中间区域)和未涂有C18-Si-III的位置(图4中玻璃片右侧区域),拍摄得到。滴加在涂有C18-Si-III的位置的水滴(即箭头1所指水滴)的水接触角由水接触角仪测试,为110度。滴加在未涂有C18-Si-III的位置的水滴(即箭头2所指水滴)整个摊在玻璃片上,未测其水接触角。
柔软性:由于不同的纺织品本身具有不同的手感,因此对于柔软性没有一个统一的测试标准。文献“C6和无氟防水剂的实践应用”《染整技术》2019年第41卷第11期中提到手感测试“采用手触摸的方法评定,主要为柔软、滑爽、蓬松方面的性能,由5人以上专业人士综合排序评定。手感最佳为5分,最差为1分。”本发明虽未给C18-Si的柔软性打分,但仅凭直接手触摸,C18-Si系列树脂(包括C18-Si-I、C18-Si-II、C18-Si-III和C18-Si-IV)几乎不影响原织物的柔软性,而通常使用的聚丙烯酸酯防水剂明显降低原织物的柔软性。
以上详细描述了本发明的较佳具体实施例。应当理解,本领域的普通技术无需创造性劳动就可以根据本发明的构思作出诸多修改和变化。因此,凡本技术领域中技术人员依本发明的构思在现有技术的基础上通过逻辑分析、推理或者有限的实验可以得到的技术方案,皆应在由权利要求书所确定的保护范围内。
Claims (16)
1.一种非氟聚合物的应用,其特征在于,应用于织物或者纸张;所述非氟聚合物包括:
由化学式1表示的结构单元,其中R选自R1、R2和R3中的一种或者多种,R1代表C8~30烷基,R2代表C8~30烷基异氰酸酯基,R3代表C8~30酸酯基;
超支化结构聚醚,其中单个聚醚端基数为2~16个;
由化学式2表示的结构单元,其中单甲基硅单元的数量为n个,n代表2~30的整数,二甲基硅单元的数量为m个,m代表2~30的整数;
[化学式1]
R—*
[化学式2]
其中,*为连接点;所述化学式1表示的结构单元连接在所述超支化结构聚醚的单个聚醚端基上,所述超支化结构聚醚连接在所述化学式2表示的结构单元上。
2.如权利要求1所述的应用,其特征在于,所述超支化结构聚醚为由化学式3表示的化合物与由化学式4表示的化合物在催化剂作用下聚合生成的支化点3个以上的超支化聚醚多元醇,去掉羟基上的H形成连接点,以及打开双键形成连接点后的结构单元;
[化学式3]
[化学式4]
其中,A代表—(CH2)f—,f代表1~10的整数,w代表0~20的整数;所述催化剂选自醋酸钠、碳酸钠、碳酸氢钠、氢氧化钠、甲醇钠、碳酸钾、碳酸氢钾、甲醇钾、丁基锂、萘钠、钠、三乙胺、三乙烯二胺和4-二甲氨基吡啶中的一种或几种。
3.如权利要求1所述的应用,其特征在于,所述超支化结构聚醚为由化学式5表示的结构单元;
[化学式5]
其中,单个聚醚端基上的连接点与所述化学式1表示的结构单元连接;非单个聚醚端基上的连接点与所述化学式2表示的结构单元连接。
4.如权利要求1所述的应用,其特征在于,所述非氟聚合物为化学式6所示的化合物:
[化学式6]
5.如权利要求4所述的应用,其特征在于,所述非氟聚合物为化学式7所示的化合物:
[化学式7]
6.如权利要求1所述的应用,其特征在于,所述非氟聚合物为化学式8所示的化合物:
[化学式8]
7.如权利要求1所述的应用,其特征在于,所述非氟聚合物为化学式9所示的化合物:
[化学式9]
8.如权利要求1所述的应用,其特征在于,所述非氟聚合物为化学式10所示的化合物:
[化学式10]
9.一种防水剂,其特征在于,含有非氟聚合物;所述非氟聚合物包括:
由化学式1表示的结构单元,其中R选自R1、R2和R3中的一种或者多种,R1代表C8~30烷基,R2代表C8~30烷基异氰酸酯基,R3代表C8~30酸酯基;
超支化结构聚醚,其中单个聚醚端基数为2~16个;
由化学式2表示的结构单元,其中单甲基硅单元的数量为n个,n代表2~30的整数,二甲基硅单元的数量为m个,m代表2~30的整数;
[化学式1]
R—*
[化学式2]
其中,*为连接点;所述化学式1表示的结构单元连接在所述超支化结构聚醚的单个聚醚端基上,所述超支化结构聚醚连接在所述化学式2表示的结构单元上。
10.如权利要求9所述的防水剂,其特征在于,所述超支化结构聚醚为由化学式3表示的化合物与由化学式4表示的化合物在催化剂作用下聚合生成的支化点3个以上的超支化聚醚多元醇,去掉羟基上的H形成连接点,以及打开双键形成连接点后的结构单元;
[化学式3]
[化学式4]
其中,A代表—(CH2)f—,f代表1~10的整数,w代表0~20的整数;所述催化剂选自醋酸钠、碳酸钠、碳酸氢钠、氢氧化钠、甲醇钠、碳酸钾、碳酸氢钾、甲醇钾、丁基锂、萘钠、钠、三乙胺、三乙烯二胺和4-二甲氨基吡啶中的一种或几种。
11.如权利要求9所述的防水剂,其特征在于,所述超支化结构聚醚为由化学式5表示的结构单元;
[化学式5]
其中,单个聚醚端基上的连接点与所述化学式1表示的结构单元连接;非单个聚醚端基上的连接点与所述化学式2表示的结构单元连接。
12.如权利要求9所述的防水剂,其特征在于,所述非氟聚合物为化学式6所示的化合物:
[化学式6]
13.如权利要求12所述的防水剂,其特征在于,所述非氟聚合物为化学式7所示的化合物:
[化学式7]
14.如权利要求9所述的防水剂,其特征在于,所述非氟聚合物为化学式8所示的化合物:
[化学式8]
15.如权利要求9所述的防水剂,其特征在于,所述非氟聚合物为化学式9所示的化合物:
[化学式9]。
16.如权利要求9所述的防水剂,其特征在于,所述非氟聚合物为化学式10所示的化合物:
[化学式10]。