CN115534495A - 一种速干型抗菌宠物面料加工制作方法 - Google Patents
一种速干型抗菌宠物面料加工制作方法 Download PDFInfo
- Publication number
- CN115534495A CN115534495A CN202210558999.6A CN202210558999A CN115534495A CN 115534495 A CN115534495 A CN 115534495A CN 202210558999 A CN202210558999 A CN 202210558999A CN 115534495 A CN115534495 A CN 115534495A
- Authority
- CN
- China
- Prior art keywords
- fabric
- antibacterial
- fiber
- drying
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种速干型抗菌宠物面料加工制作方法，包括以下步骤：步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维，步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度。本发明能够使宠物用面料具有清洗后快速干燥和抗菌功能的优点，缩短干燥时间，使其具有抗菌抑菌的功能，减少细菌的滋生，保证人和宠物的健康，还能够对宠物体表产生的异味进行吸附，防止异味影响居住环境，提高宠物面料的使用效果。
Description
技术领域
本发明涉及面料加工技术领域，具体为一种速干型抗菌宠物面料加工制作方法。
背景技术
随着人们生活水平的日益提高，越来越多的人开始豢养宠物，以丰富人们的精神世界，因此针对宠物使用的各种面料广泛出现，如宠物窝、宠物衣服、宠物背包等，然而目前市面上的宠物用面料通常为普通面料，由于宠物好动的特性，很容易使宠物衣服、宠物窝等制品表面沾染污垢和细菌，需要频繁进行清洗，现有的宠物面料由于不具有速干和抗菌的功能，不仅清洗后无法快速干燥，且容易在面料表面滋生大量细菌，影响人和宠物的健康安全，降低了使用者对宠物面料的体验感，不能满足当今市场的需求，由于以上存在的问题，针对性地推出了一种速干型抗菌宠物面料加工制作方法。
发明内容
本发明的目的在于提供一种速干型抗菌宠物面料加工制作方法，具备速干和抗菌功能的优点，解决了现有的宠物面料清洗后干燥速度慢和没有抗菌功能的问题。
为实现上述目的，本发明提供如下技术方案：一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
优选的，所述步骤a吸湿排汗纤维中超细丙纶纤维的重量百分比为60-80％，抑菌抗菌纤维中超细旦纤维的重量百分比为80-90％，复合消臭纤维中竹炭纤维的重量百分比为80-90％。
优选的，所述步骤b通过络筒机对纱线进行络筒工序，消除纱线表面的杂质和疵点，提高后序工序的生产效率，通过浆纱机对纱线进行浆纱工序，增加纱线的抗断裂强度。
优选的，所述步骤c染色时染料液温度控制在140-165℃，保温时间为45-60min，对面料进行湿扩幅后烘干时，烘干时间为20-35min，烘干箱中温度为150-170℃。
优选的，所述步骤d稀酸液为浓度为0.5-1g/L的醋酸溶液，烘干温度为110-130℃，烘干时长为10-20min，定型机复定型温度为125-145℃，车速为15-25m/min。
优选的，所述步骤e面料与防水透气膜和方格网眼布通过无胶复合机进行复合工序，收卷后的面料通过转运车运送至仓库储存，使面料保持在干燥环境下储存。
与现有技术相比，本发明的有益效果如下：
本发明能够使宠物用面料具有清洗后快速干燥和抗菌功能的优点，缩短干燥时间，使其具有抗菌抑菌的功能，减少细菌的滋生，保证人和宠物的健康，还能够对宠物体表产生的异味进行吸附，防止异味影响居住环境，提高宠物面料的使用效果。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
实施例1
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
实施例2
在实施例1中，再加入以下步骤：
步骤a吸湿排汗纤维中超细丙纶纤维的重量百分比为60-80％，抑菌抗菌纤维中超细旦纤维的重量百分比为80-90％，复合消臭纤维中竹炭纤维的重量百分比为80-90％。
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
实施例3
在实施例2中，再加入以下步骤：
步骤b通过络筒机对纱线进行络筒工序，消除纱线表面的杂质和疵点，提高后序工序的生产效率，通过浆纱机对纱线进行浆纱工序，增加纱线的抗断裂强度。
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
实施例4
在实施例3中，再加入以下步骤：
步骤c染色时染料液温度控制在140-165℃，保温时间为45-60min，对面料进行湿扩幅后烘干时，烘干时间为20-35min，烘干箱中温度为150-170℃。
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
实施例5
在实施例4中，再加入以下步骤：
步骤d稀酸液为浓度为0.5-1g/L的醋酸溶液，烘干温度为110-130℃，烘干时长为10-20min，定型机复定型温度为125-145℃，车速为15-25m/min。
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
实施例6
在实施例5中，再加入以下步骤：
步骤e面料与防水透气膜和方格网眼布通过无胶复合机进行复合工序，收卷后的面料通过转运车运送至仓库储存，使面料保持在干燥环境下储存。
一种速干型抗菌宠物面料加工制作方法，包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种速干型抗菌宠物面料加工制作方法，其特征在于：包括以下步骤：
步骤a：通过超细丙纶纤维与聚酯纤维混纺形成吸湿排汗纤维，通过超细旦纤维与纳米层状银系抗菌剂共混纺丝制成抑菌抗菌纤维，通过竹炭纤维添加消臭剂、抗菌剂和阻燃剂复合制成复合消臭纤维；
步骤b：通过络筒工艺将吸湿排汗纤维、抑菌抗菌纤维和复合消臭纤维卷绕于络筒表面，随后通过浆纱提高纱线的强度，浆纱完毕后使用烘箱对纱线进行烘干，烘干完毕后即可通过纺织机将纱线纺织成坯布；
步骤c：将坯布连续送入染布机进行染色处理，染色完毕后得到面料半成品，随后对面料进行湿扩幅处理并进行烘干，消除部分内应力，稳定线圈结构，稳定针织物门幅；
步骤d：扩幅定型后的面料通过稀酸液进行酸洗，酸洗通过清水冷洗将酸液洗净，喷涂吸汗剂后再次进行烘干，烘干后的面料通过定型机进行复定型，将复定型后的速干抗菌面料检验收卷；
步骤e：通过将面料与防水透气膜和方格网眼布通过无胶复合工艺进行复合，复合后形成速干型抗菌宠物面料，随后通过收卷设备对面料进行收卷。
2.根据权利要求1所述的一种速干型抗菌宠物面料加工制作方法，其特征在于：所述步骤a吸湿排汗纤维中超细丙纶纤维的重量百分比为60-80％，抑菌抗菌纤维中超细旦纤维的重量百分比为80-90％，复合消臭纤维中竹炭纤维的重量百分比为80-90％。
3.根据权利要求1所述的一种速干型抗菌宠物面料加工制作方法，其特征在于：所述步骤b通过络筒机对纱线进行络筒工序，消除纱线表面的杂质和疵点，提高后序工序的生产效率，通过浆纱机对纱线进行浆纱工序，增加纱线的抗断裂强度。
4.根据权利要求1所述的一种速干型抗菌宠物面料加工制作方法，其特征在于：所述步骤c染色时染料液温度控制在140-165℃，保温时间为45-60min，对面料进行湿扩幅后烘干时，烘干时间为20-35min，烘干箱中温度为150-170℃。
5.根据权利要求1所述的一种速干型抗菌宠物面料加工制作方法，其特征在于：所述步骤d稀酸液为浓度为0.5-1g/L的醋酸溶液，烘干温度为110-130℃，烘干时长为10-20min，定型机复定型温度为125-145℃，车速为15-25m/min。
6.根据权利要求1所述的一种速干型抗菌宠物面料加工制作方法，其特征在于：所述步骤e面料与防水透气膜和方格网眼布通过无胶复合机进行复合工序，收卷后的面料通过转运车运送至仓库储存，使面料保持在干燥环境下储存。