CN114984751A - 一种高效光触媒除甲醛材料和制备方法及应用和除甲醛地板和制备方法 - Google Patents
一种高效光触媒除甲醛材料和制备方法及应用和除甲醛地板和制备方法 Download PDFInfo
- Publication number
- CN114984751A CN114984751A CN202210654917.8A CN202210654917A CN114984751A CN 114984751 A CN114984751 A CN 114984751A CN 202210654917 A CN202210654917 A CN 202210654917A CN 114984751 A CN114984751 A CN 114984751A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- parts
- photocatalyst
- removing material
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于甲醛清除技术领域，公开了一种高效光触媒除甲醛材料和制备方法及应用和除甲醛地板和制备方法。该除甲醛材料包括：氨基酸、无机铵盐、纳米光触媒材料、成膜剂、渗透剂、亲水性表面活性剂和水。本发明的高效光触媒除甲醛材料选用无机铵盐与氨基酸作为主要成分，无毒，易溶于水，与甲醛可迅速反应，并结合纳米光触媒材料吸收甲醛的作用，实现对室内甲醛的快速消除。
Description
技术领域
本发明属于甲醛清除技术领域，更具体地，涉及一种高效光触媒除甲醛材料和制备方法及应用和除甲醛地板和制备方法。
背景技术
人造板是现有装饰材料的重要组成基材，在其生产和应用过程中，甲醛的释放量己经成为一个日益被关注的问题，众所周知，在制造人造板的过程中需要加入含有甲醛的粘胶剂，如脲醛胶等，而且根据统计显示，人造板90％以上均采用脲醛胶进行压制，因而在应用时固然会产生游离甲醛，应用在家具制造或者其他板材应用中往往会对人体产生一定的影响。为消除人造板中游离甲醛挥发对人体造成的伤害，人造板的绿色化生产己成为影响人造板市场的关键之处。
另外，鉴于游离甲醛的危害和污染现状，目前市场上出现了多种治理甲醛污染的方法，如光触媒，然而其方法存在见效慢进而影响施工进度的问题，因此，目前亟待提出一种新的高效光触媒除甲醛材料和除甲醛地板。
发明内容
本发明的目的是针对现有技术的不足，提供一种高效光触媒除甲醛材料和制备方法及应用和除甲醛地板和制备方法。本发明的高效光触媒除甲醛材料选用无机铵盐与氨基酸作为主要成分，无毒，易溶于水，与甲醛可迅速反应，并结合纳米光触媒材料吸收甲醛的作用，实现对室内甲醛的快速消除。
为了实现上述目的，本发明第一方面提供了一种高效光触媒除甲醛材料，该除甲醛材料包括：氨基酸、无机铵盐、纳米光触媒材料、成膜剂、渗透剂、亲水性表面活性剂和水。
根据本发明，优选地，所述除甲醛材料包括以重量份计的以下组分：氨基酸0.05-0.2份、无机铵盐0.1-3份、纳米光触媒材料2-10份、成膜剂0.1-2份、渗透剂0.05-1份、亲水性表面活性剂0.1-5份和水20-150份。
根据本发明，优选地，所述除甲醛材料包括以重量份计的以下组分：氨基酸0.05-0.1份、无机铵盐0.5-1份、纳米光触媒材料8-10份、成膜剂0.1-1份、渗透剂0.1-0.5份、亲水性表面活性剂1-2份和水80-100份。
根据本发明，优选地，所述氨基酸为甘氨酸和/或丙氨酸。
根据本发明，优选地，所述无机铵盐为氯化铵、硝酸铵和硫酸铵中的至少一种。
根据本发明，优选地，所述成膜剂为甲酰胺成膜剂、聚乙烯醇成膜剂、甲烯酸-甲基丙烯酸共聚物和海藻酸钠成膜剂中的至少一种。
根据本发明，优选地，所述渗透剂为JFC渗透剂、JFC-1渗透剂、JFC-2渗透剂和JFC-E渗透剂中的至少一种。
根据本发明，优选地，所述亲水性表面活性剂为吐温-20、吐温-60和吐温-80中的至少一种。
根据本发明，优选地，所述纳米光触媒材料为ZnO、ZnS、SrTiO3、SiO2和TiO2中的至少一种。
本发明第二方面提供了所述的高效光触媒除甲醛材料的制备方法，该方法包括：将所述氨基酸、无机铵盐、纳米光触媒材料、成膜剂、渗透剂、亲水性表面活性剂和水加入到反应釜中，搅拌混合均匀，得到所述高效除甲醛材料。
根据本发明，优选地，在所述反应釜中，搅拌的速率为9000-10000r/min，温度为40-70℃，时间为20-30min。
本发明第三方面提供了所述的高效光触媒除甲醛材料在制备除甲醛地板中的应用。
本发明第四方面提供了一种除甲醛地板，该地板包括从下到上依次设置的基材层、高效光触媒除甲醛材料层、水性漆底漆层和水性漆面漆层；
所述高效光触媒除甲醛材料层的材料为上述的高效光触媒除甲醛材料。
根据本发明，优选地，所述基材层为实木或单板。
根据本发明，优选地，所述水性漆面漆层包括以重量份计的以下组分：聚氨酯水性清漆60-80份和上述的高效光触媒除甲醛材料20-40份。
在本发明中，所述水性漆底漆层的材料可选用本领域技术人员已知的任何一种用于涂覆实木或单板的水性漆底漆。
本发明第五方面提供了所述的除甲醛地板的制备方法，该方法包括：在打磨抛光后的所述基材层表面依次涂覆高效光触媒除甲醛材料层、水性漆底漆层和水性漆面漆层，干燥固化，得到所述除甲醛地板。
本发明的技术方案的有益效果如下：
(1)本发明的高效光触媒除甲醛材料选用无机铵盐与氨基酸作为主要成分，无毒，易溶于水，与甲醛可迅速反应，并结合纳米光触媒材料吸收甲醛的作用，实现对室内甲醛的快速消除。
(2)根据标准JC/T 1074-20086.5和GB/T 16129-1995测试方法可知，本发明的除甲醛地板的甲醛净化性能可达到92％以上。
本发明的其它特征和优点将在随后具体实施方式部分予以详细说明。
具体实施方式
下面将更详细地描述本发明的优选实施方式。虽然以下描述了本发明的优选实施方式，然而应该理解，可以以各种形式实现本发明而不应被这里阐述的实施方式所限制。相反，提供这些实施方式是为了使本发明更加透彻和完整，并且能够将本发明的范围完整地传达给本领域的技术人员。
实施例1
本实施例提供一种高效光触媒除甲醛材料，该除甲醛材料包括：甘氨酸0.08份、氯化铵0.9份、纳米TiO2 9份、甲酰胺成膜剂0.8份、JFC-1渗透剂0.4份、吐温-80 1.5份和去离子水95份。
上述高效光触媒除甲醛材料的制备方法包括：将所述氨基酸、无机铵盐、纳米光触媒材料、成膜剂、渗透剂、亲水性表面活性剂和水加入到反应釜中，在50℃、10000r/min下搅拌20min，得到所述高效除甲醛材料。
实施例2
本实施例提供一种高效光触媒除甲醛材料，本实施例与实施例1的区别仅在于：该除甲醛材料包括：甘氨酸0.11份、氯化铵0.1份、纳米TiO2 10份、甲酰胺成膜剂0.15份、JFC-1渗透剂0.09份、吐温-80 1.8份和去离子水75份。
实施例3
本实施例提供一种高效光触媒除甲醛材料，本实施例与实施例1的区别仅在于：该除甲醛材料包括：甘氨酸0.05份、氯化铵0.25份、纳米TiO2 4份、甲酰胺成膜剂0.5份、JFC-1渗透剂0.8份、吐温-80 3份和去离子水140份。
实施例4
本实施例提供一种除甲醛地板，该地板包括从下到上依次设置的基材层、高效光触媒除甲醛材料层、水性漆底漆层和水性漆面漆层；
所述基材层为单板；
所述高效光触媒除甲醛材料层的材料为实施例1所述的高效光触媒除甲醛材料；
所述水性漆底漆层的材料为卫士宝公司的富锌漆。
所述水性漆面漆层包括以重量份计的以下组分：聚氨酯水性清漆80份和实施例1所述的高效光触媒除甲醛材料20份。
实施例5
本实施例提供一种除甲醛地板，本实施例与实施例4的区别仅在于：
所述高效光触媒除甲醛材料层的材料为实施例2所述的高效光触媒除甲醛材料；
所述水性漆面漆层包括以重量份计的以下组分：聚氨酯水性清漆80份和实施例2所述的高效光触媒除甲醛材料20份。
实施例6
本实施例提供一种除甲醛地板，本实施例与实施例4的区别仅在于：
所述高效光触媒除甲醛材料层的材料为实施例3所述的高效光触媒除甲醛材料；
所述水性漆面漆层包括以重量份计的以下组分：聚氨酯水性清漆80份和实施例3所述的高效光触媒除甲醛材料20份。
测试例
本测试例根据标准JC/T 1074-20086.5和GB/T 16129-1995对实施例4-6得到的除甲醛地板的甲醛净化性能进行测试，测试用试样尺寸1m2，样品单面测试(封侧边和底面)：密封舱容积：1m3。测试条件：温度18-22℃，相对湿度40％-60％，得到结果如表1所示。
表1
| 甲醛净化性能％ | |
| 实施例4 | 92.7％ |
| 实施例5 | 92.3％ |
| 实施例6 | 92.5％ |
以上已经描述了本发明的各实施例，上述说明是示例性的，并非穷尽性的，并且也不限于所披露的各实施例。在不偏离所说明的各实施例的范围和精神的情况下，对于本技术领域的普通技术人员来说许多修改和变更都是显而易见的。
Claims (10)
1.一种高效光触媒除甲醛材料，其特征在于，该除甲醛材料包括：氨基酸、无机铵盐、纳米光触媒材料、成膜剂、渗透剂、亲水性表面活性剂和水。
2.根据权利要求1所述的高效光触媒除甲醛材料，其中，所述除甲醛材料包括以重量份计的以下组分：氨基酸0.05-0.2份、无机铵盐0.1-3份、纳米光触媒材料2-10份、成膜剂0.1-2份、渗透剂0.05-1份、亲水性表面活性剂0.1-5份和水20-150份。
3.根据权利要求2所述的高效光触媒除甲醛材料，其中，所述除甲醛材料包括以重量份计的以下组分：氨基酸0.05-0.1份、无机铵盐0.5-1份、纳米光触媒材料8-10份、成膜剂0.1-1份、渗透剂0.1-0.5份、亲水性表面活性剂1-2份和水80-100份。
4.根据权利要求1所述的高效光触媒除甲醛材料，其中，
所述氨基酸为甘氨酸和/或丙氨酸；
所述无机铵盐为氯化铵、硝酸铵和硫酸铵中的至少一种；
所述成膜剂为甲酰胺成膜剂、聚乙烯醇成膜剂、甲烯酸-甲基丙烯酸共聚物和海藻酸钠成膜剂中的至少一种；
所述渗透剂为JFC渗透剂、JFC-1渗透剂、JFC-2渗透剂和JFC-E渗透剂中的至少一种；
所述亲水性表面活性剂为吐温-20、吐温-60和吐温-80中的至少一种；
所述纳米光触媒材料为ZnO、ZnS、SrTiO3、SiO2和TiO2中的至少一种。
5.权利要求1-4中任意一项所述的高效光触媒除甲醛材料的制备方法，其特征在于，该方法包括：将所述氨基酸、无机铵盐、纳米光触媒材料、成膜剂、渗透剂、亲水性表面活性剂和水加入到反应釜中，搅拌混合均匀，得到所述高效除甲醛材料。
6.根据权利要求5所述的高效光触媒除甲醛材料的制备方法，其中，在所述反应釜中，搅拌的速率为9000-10000r/min，温度为40-70℃，时间为20-30min。
7.权利要求1-4中任意一项所述的高效光触媒除甲醛材料在制备除甲醛地板中的应用。
8.一种除甲醛地板，其特征在于，该地板包括从下到上依次设置的基材层、高效光触媒除甲醛材料层、水性漆底漆层和水性漆面漆层；
所述高效光触媒除甲醛材料层的材料为权利要求1-4中任意一项所述的高效光触媒除甲醛材料。
9.根据权利要求8所述的除甲醛地板，其中，
所述基材层为实木或单板；
所述水性漆面漆层包括以重量份计的以下组分：聚氨酯水性清漆60-80份和权利要求1-4中任意一项所述的高效光触媒除甲醛材料20-40份。
10.权利要求8或9所述的除甲醛地板的制备方法，其特征在于，该方法包括：在打磨抛光后的所述基材层表面依次涂覆高效光触媒除甲醛材料层、水性漆底漆层和水性漆面漆层，干燥固化，得到所述除甲醛地板。