CN111589296A - 一种室内甲醛清除剂及其制备方法 - Google Patents
一种室内甲醛清除剂及其制备方法 Download PDFInfo
- Publication number
- CN111589296A CN111589296A CN202010520178.4A CN202010520178A CN111589296A CN 111589296 A CN111589296 A CN 111589296A CN 202010520178 A CN202010520178 A CN 202010520178A CN 111589296 A CN111589296 A CN 111589296A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde scavenger
- water
- indoor formaldehyde
- formaldehyde
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种室内甲醛清除剂及其制备方法，涉及室内空气净化领域，该甲醛清除剂为由氨基酸、多胺类化合物、二氧化钛@氮化碳量子点、水性聚合物乳液、木质渗透剂、吸湿剂、表面活性剂、柠檬提取液和水制备而成的淡白色透明乳液。本发明不仅通过氨基酸和多胺类化合物可高效、持久固定甲醛，形成稳定性好、无毒、无害的产物，同时通过二氧化钛@氮化碳量子点光催化降解甲醛，能够在普通室内条件下彻底地催化分解室内甲醛，降低甲醛存量，同时能有效地抑制病毒和细菌的活性，达到净化空气、杀菌、除臭、防霉等功效。
Description
技术领域
本发明涉及室内空气净化剂技术领域，尤其涉及一种室内甲醛清除剂及其制备方法。
背景技术
现代人平均每天超过80％时间在室内度过，同时随着我国经济的发展，人们对室内装修的要求越来越高，各类装修材料问题层见迭出。对于我国而言，原木需求量大，森林资源稀缺是一个不争的事实。人造板材很好的解决了这个问题，并且人造板材在装修用料中占据了很大的比例，但是人造板材在生产中无法避免使用到的脲醛树脂、酚醛树脂等材料，这类材料在遇热或与遇潮的情况下极易释放大量的污染气体如甲醛，严重影响人们的身心健康。
据世卫组织研究表明，甲醛作为一种毒性较高的分子，具有致癌、致突变、生殖毒性等危害，是公认的突变反应源，同时被列为一类致癌物，其致突变的机理在于，甲醛能与体内蛋白质、DNA、RNA等生物分子中游离的氨基酸自发进行化学反应，从而致使蛋白质和核酸变性使得基因突变。数据显示，甲醛浓度达0.08～0.09mg/m3时，会引发儿童轻微气喘；浓度高于0.5mg/m3时，会严重的刺激眼睛导致流泪；浓度再高时，会引起咽喉烧灼痛、呼吸困难、肺水肿等急性中毒症状；当浓度达到30mg/m3以上，会立即致死。不仅如此，日本国立大学研究表明，室内甲醛释放期一般为3-15年，甲醛的释放不仅呈现周期长的特性，还受季节、室内结构等因素的影响。
基于上述痛点，研发一款安全、高效、持久、无二次污染的甲醛清除剂，用于室内空气环境的治理迫在眉睫。
目前市场常见的甲醛清除剂主要为植物提取物、氧化性物质和氨基类物质等，植物提取物对甲醛的处理效率低，污染无法及时解决，而且生产成本较高，保质期短。而氧化性物质自身纯在稳定性不高的特性，会随时间推移不断地发生分解，而且使用过程中存在对家中器具产生一定的腐蚀作用；氨基酸对甲醛的固定作用时间短，无法完全分解，过一段时间甲醛还会发生一定的反弹，不适宜作为治本的方法。
公开号为CN102671335A的专利公开一种甲醛清除剂，其成分质量比为：植物提取液34％～40％、碳酸氢钠9％～12％、过氧化氢8％～12％、渗透剂3％～5％、纯净水35％～40％；其制备工艺为：将提取液、碳酸氢钠、过氧化氢、渗透剂、纯净水依次加入反应器中搅拌均匀即可；该发明采用植物与化学相结合的方法，在数分钟内快速分解甲醛，不反弹，无二次污染。不仅可以喷涂于物体或空气中祛除装修后的异味，还可以分解苯系物、一氧化碳、二氧化硫、和微生物等。但这种甲醛清除剂使用数月后甲醛去除率大幅度下降，依然无法长时间有效固定甲醛。
发明内容
为了解决上述技术难题，本发明的目的在于提供安全、高效、持久、无二次污染的一种室内甲醛清除剂及其制备方法。
为实现上述目的，本发明采用以下技术方案：
一种室内甲醛清除剂，包括氨基酸、多胺类化合物、二氧化钛@氮化碳量子点、水性聚合物乳液、木质渗透剂、吸湿剂、表面活性剂、柠檬提取液和水；所述氨基酸、多胺类化合物、二氧化钛@氮化碳量子点、水性聚合物乳液、木质渗透剂、吸湿剂、表面活性剂、柠檬提取液和水的质量比为：氨基酸1～5、多胺类化合物1～5、二氧化钛@氮化碳量子点0.1～1、水性聚合物乳液1～10、木质渗透剂0.2～1、吸湿剂0.5～2、表面活性剂0.3～2、柠檬提取液1～5和水70～95。
进一步的，所述氨基酸为谷氨酸和半胱氨酸混合组成，谷氨酸和半胱氨酸质量比为1～2:1～2。氨基酸可选天门冬氨酸、赖氨酸、谷氨酸、蛋氨酸、丙氨酸、色氨酸、精氨酸、半胱氨酸等中的至少一种。
进一步的，所述表面活性剂为十二碳醇脂、乙二醇和十二烷基硫酸钠混合组成，质量比为1～2:1～2:1～3。
进一步的，所述多胺类化合物为聚六亚甲基双胍、二甲双胍、二乙烯三胺中的至少一种。
进一步的，所述水性聚合物乳液可选纳米聚乙烯乳液、纳米聚丙烯酸酯乳液、纳米SiO2丙烯酸酯复合乳液、纳米TiO2/硅丙复合乳液等中的至少一种。更优选地，所述水性聚合物乳液为纳米聚乙烯乳液或纳米SiO2丙烯酸酯复合乳液。
进一步的，所述木质渗透剂为木质素磺酸铵和木质素磺酸钠混合组成，木质素磺酸铵和木质素磺酸钠质量比为1～2:1～4。
所述吸湿剂可选硫酸钠、氯化钠、氯化铵、氯化钙等中的至少一种。
所述水为去离子水。
根据上述的一种室内甲醛清除剂的制备方法，其包括如下步骤：
(1)在反应釜中先后加入多胺类化合物和水性聚合物乳液，搅拌得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入氨基酸超声溶解；
(3)搅拌条件下依次加入木质渗透剂、吸湿剂；
(4)搅拌条件下，加入适当的pH调节剂将pH调节至7～9；
(5)搅拌条件下加入表面活性剂和柠檬提取液；
(6)加入二氧化钛@氮化碳量子点；
(7)待混合均匀成为均匀胶体后，静置1～3小时，得到淡白色透明的甲醛清除液。
进一步的，以上步骤中的搅拌条件为：在30～60℃下，搅拌速度600-1000r/min，搅拌反应6-12小时。
进一步的，步骤(4)中将pH调节至7～8。
进一步的，步骤(6)为在超声条件下加入二氧化钛@氮化碳量子点。
本发明具有如下有益效果：
本发明通过水性聚合物乳液与多胺类化合物和氨基酸的复合，利用多胺类化合物和氨基酸中的氨基对甲醛分子中的碳氧双键进行生物攻击，并发生亲核反应，形成常温下稳定的大分子化合物，进而对甲醛进行固定。
本发明同时在木质渗透剂协助作用下大大提升了甲醛固定的时间广度和空间深度，不仅短期内快速高效固定甲醛，而且能够长时间持续固定甲醛，解决了现有甲醛固定时间短的问题。
本发明使用的二氧化钛@氮化碳量子点具有非常良好的可见光催化效果，能够在普通室内条件下彻底地催化分解室内甲醛，降低甲醛存量，同时能有效地抑制病毒和细菌的活性，达到净化空气、杀菌、除臭、防霉等功效。
本发明表面活性剂能够有效地协助甲醛清除剂的溶液在处理物表面形成薄膜覆盖，能够在少量的清除剂的条件下覆盖更大的面积，提高产品的使用效率。
总之，本发明制备的室内甲醛清除剂具有安全、高效、持久、无二次污染的效果，能够很好的解决室内甲醛污染的问题。
附图说明
图1为本发明制备的室内甲醛清除剂的透射电镜图。
具体实施方式
以下结合附图和具体实施例对本发明做进一步详细说明：
实施例1
按以下配比制备室内甲醛清除剂：
谷氨酸0.5份、半胱氨酸0.5份、聚六亚甲基双胍1份、二氧化钛@氮化碳量子点0.6份、纳米SiO2丙烯酸酯复合乳液2.5份、木质素磺酸铵0.3份、木质素磺酸钠0.6份、硫酸钠0.5份、十二碳醇脂0.1份、乙二醇0.1份、十二烷基硫酸钠0.1份、柠檬提取液1.2份、水92份。
以上二氧化钛@氮化碳量子点和纳米SiO2丙烯酸酯复合乳液为本领域技术人员采用常规技术手段制备，以下实施例均同。
以生产100kg的室内甲醛清除剂为例，其制备方法为：
在反应釜中先后加入1kg聚六亚甲基双胍、2.5kg纳米SiO2丙烯酸酯复合乳液，在30℃下，搅拌速度600r/min，搅拌反应6小时，得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入0.5kg谷氨酸、0.5kg半胱氨酸超声溶解；
(3)同上搅拌条件下依次加入0.3kg木质素磺酸铵、0.6kg木质素磺酸钠、0.5kg硫酸钠；
(4)同上搅拌条件下，将pH调节至7；
(5)同上搅拌条件下加入0.1kg十二碳醇脂、0.1kg乙二醇、0.1kg十二烷基硫酸钠和1.2kg柠檬提取液；
(6)超声条件下加入0.6kg二氧化钛@氮化碳量子点；超声条件的具体参数为本领域技术人员采用的常规技术手段。
(7)待搅拌均匀后，静置1小时，得到淡白色透明的甲醛清除液。
实施例2
按以下配比制备室内甲醛清除剂：
谷氨酸2.5份、半胱氨酸2.5份、聚六亚甲基双胍5份、二氧化钛@氮化碳量子点1份、纳米SiO2丙烯酸酯复合乳液5份、木质素磺酸铵0.3份、木质素磺酸钠0.6份、硫酸钠0.5份、十二碳醇脂0.4份、乙二醇0.4份、十二烷基硫酸钠0.6份、柠檬提取液1.2份、水82份。
以生产100kg的室内甲醛清除剂为例，其制备方法为：
在反应釜中先后加入5kg聚六亚甲基双胍、5kg纳米SiO2丙烯酸酯复合乳液，在45℃下，搅拌速度800r/min，搅拌反应7小时，得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入2.5kg谷氨酸、2.5kg半胱氨酸超声溶解；
(3)同上搅拌条件下依次加入0.3kg木质素磺酸铵、0.6kg木质素磺酸钠、0.5kg硫酸钠；
(4)同上搅拌条件下，将pH调节至7.5；
(5)同上搅拌条件下加入0.4kg十二碳醇脂、0.4kg乙二醇、0.16g十二烷基硫酸钠和1.2kg柠檬提取液；
(6)超声条件下加入1kg二氧化钛@氮化碳量子点；
(7)待搅拌均匀后，静置1小时，得到淡白色透明的甲醛清除液。
实施例3
按以下配比制备室内甲醛清除剂：
谷氨酸2份、半胱氨酸2份、二乙烯三胺2份、二氧化钛@氮化碳量子点0.6份、纳米聚乙烯乳液2.5份、木质素磺酸铵0.3份、木质素磺酸钠0.4份、氯化钠0.5份、十二碳醇脂0.1份、乙二醇0.2份、十二烷基硫酸钠0.2份、柠檬提取液2份、水87份。
以生产100kg的室内甲醛清除剂为例，其制备方法为：
(1)在反应釜中先后加入2kg二乙烯三胺、2.5kg纳米聚乙烯乳液，在50℃下，搅拌速度1000r/min，搅拌反应8小时，得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入2kg谷氨酸、2kg半胱氨酸超声溶解；
(3)同上搅拌条件下依次加入0.3kg木质素磺酸铵、0.4kg木质素磺酸钠、0.5kg氯化钠；
(4)同上搅拌条件下，将pH调节至8；
(5)同上搅拌条件下加入0.1kg十二碳醇脂、0.2kg乙二醇、0.2kg十二烷基硫酸钠和2kg柠檬提取液；
(6)超声条件下加入0.8kg二氧化钛@氮化碳量子点；
(7)待搅拌均匀后，静置2小时，得到淡白色透明的甲醛清除液。
实施例4
按以下配比制备室内甲醛清除剂：
谷氨酸0.5份、半胱氨酸0.5份、二乙烯三胺1份、二氧化钛@氮化碳量子点0.2份、纳米聚乙烯乳液1份、木质素磺酸铵0.1份、木质素磺酸钠0.1份、氯化铵0.3份、十二碳醇脂0.1份、乙二醇0.1份、十二烷基硫酸钠0.1份、柠檬提取液2份、水94份。
以生产100kg的室内甲醛清除剂为例，其制备方法为：
(1)在反应釜中先后加入1kg二乙烯三胺、1kg纳米聚乙烯乳液，在35℃下，搅拌速度800r/min，搅拌反应10小时，得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入0.5kg谷氨酸、0.5kg半胱氨酸超声溶解；
(3)同上搅拌条件下依次加入0.1kg木质素磺酸铵、0.1kg木质素磺酸钠、0.3kg氯化铵；
(4)同上搅拌条件下，将pH调节至8；
(5)同上搅拌条件下加入0.1kg十二碳醇脂、0.1kg乙二醇、0.1kg十二烷基硫酸钠和2kg柠檬提取液；
(6)超声条件下加入0.2kg二氧化钛@氮化碳量子点；
(7)待搅拌均匀后，静置2小时，得到淡白色透明的甲醛清除液。
实施例5
按以下配比制备室内甲醛清除剂：
谷氨酸2.5份、半胱氨酸2.5份、二乙烯三胺5份、二氧化钛@氮化碳量子点1份、纳米聚乙烯乳液5份、木质素磺酸铵0.3份、木质素磺酸钠0.4份、硫酸钠0.5份、十二碳醇脂0.4份、乙二醇0.4份、十二烷基硫酸钠0.6份、柠檬提取液2.4份、水79份。
以生产100kg的室内甲醛清除剂为例，其制备方法为：
(1)在反应釜中先后加入5kg二乙烯三胺、5kg纳米聚乙烯乳液，在60℃下，搅拌速度1000r/min，搅拌反应12小时，得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入2.5kg谷氨酸、2.5kg半胱氨酸超声溶解；
(3)同上搅拌条件下依次加入0.3kg木质素磺酸铵、0.4kg木质素磺酸钠、0.5kg硫酸钠；
(4)同上搅拌条件下，将pH调节至9；
(5)同上搅拌条件下加入0.4kg十二碳醇脂、0.4kg乙二醇、0.6kg十二烷基硫酸钠和2.4kg柠檬提取液；
(6)超声条件下加入1kg二氧化钛@氮化碳量子点；
(7)待搅拌均匀后，静置3小时，得到淡白色透明的甲醛清除液。
按照QB/T2761-2006标准，对上述实例1～5制备的室内甲醛清除剂的甲醛清除率和耐久性进行测试，具体测试方案如下：
分别取等量的上述3个配方的室内甲醛清除剂作为实验组和1个等量的水作为对照组，进行测试。
1)将3个配方的室内甲醛清除剂和水各取5ml分别涂刷在50*50cm的玻璃上，自然晾干后放入1m3气候舱，通过甲醛发生器向气候舱中通入甲醛，开启舱内风扇，采用固定式气体检测仪控制舱内甲醛浓度在0.3mg/m3，经过24h后测试其中甲醛浓度的变化。
甲醛去除率＝(C-C0)/C0*100％，
其中C为对照组反应过后的甲醛浓度；C0为实验组反应过后的甲醛浓度；
2)将实验重复5次，取平均值。
3)将喷涂过3个配方的室内甲醛清除剂和水的玻璃放置于常温常压的室内环境下300天后，再按照步骤(1)方法进行甲醛去除率测试。
具体的测试数据如下表：
| 测试项目 | 实例1 | 实例2 | 实例3 | 实例4 | 实例5 |
| 24h甲醛清除率 | 90.5％ | 97.5％ | 95.8％ | 93.1％ | 98.8％ |
| 300d甲醛清除率 | 70.5％ | 75.5％ | 81.2％ | 70..9％ | 80.5％ |
本发明实施例3制备的室内甲醛清除剂的透射电镜图参见图1所示。
经验证本发明配方具有高效、持久去除甲醛的性能，而且经多次重复和长时间实验表明甲醛净化性能优良，因此能适合作为室内甲醛清除剂使用。
本发明公开的室内甲醛清除剂，在使用时可以采用涂刷、喷洒、滚涂等方式覆盖于所需处理物表上，不仅能实现人造板材中游离甲醛清除，还能有效地除去后续溢出的甲醛，具有高效、持久、无二次污染、经济和社会效益。
以上所述仅为本发明的具体实施方式，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (10)
1.一种室内甲醛清除剂，其特征在于：包括氨基酸、多胺类化合物、二氧化钛@氮化碳量子点、水性聚合物乳液、木质渗透剂、吸湿剂、表面活性剂、柠檬提取液和水；
所述氨基酸、多胺类化合物、二氧化钛@氮化碳量子点、水性聚合物乳液、木质渗透剂、吸湿剂、表面活性剂、柠檬提取液和水的质量比为：氨基酸1～5、多胺类化合物1～5、二氧化钛@氮化碳量子点0.1～1、水性聚合物乳液1～10、木质渗透剂0.2～1、吸湿剂0.5～2、表面活性剂0.3～2、柠檬提取液1～5和水70～95。
2.根据权利要求1所述的一种室内甲醛清除剂，其特征在于：所述氨基酸为谷氨酸和半胱氨酸混合组成，谷氨酸和半胱氨酸质量比为1～2:1～2。
3.根据权利要求1所述的一种室内甲醛清除剂，其特征在于：所述表面活性剂为十二碳醇脂、乙二醇和十二烷基硫酸钠混合组成，质量比为1～2:1～2:1～3。
4.根据权利要求1所述的一种室内甲醛清除剂，其特征在于：所述多胺类化合物为聚六亚甲基双胍、二甲双胍、二乙烯三胺中的至少一种。
5.根据权利要求1所述的一种室内甲醛清除剂，其特征在于：所述水性聚合物乳液为纳米聚乙烯乳液或纳米SiO2丙烯酸酯复合乳液中的至少一种。
6.根据权利要求1所述的一种室内甲醛清除剂，其特征在于：所述木质渗透剂为木质素磺酸铵和木质素磺酸钠混合组成，木质素磺酸铵和木质素磺酸钠质量比为1～2:1～4。
7.根据权利要求1所述的一种室内甲醛清除剂的制备方法，其特征在于：包括如下步骤：
(1)在反应釜中先后加入多胺类化合物和水性聚合物乳液，搅拌得到氨基化水性聚合物乳液；
(2)向步骤(1)的氨基化水性聚合物乳液中加水稀释，搅拌均匀后加入氨基酸超声溶解；
(3)搅拌条件下依次加入木质渗透剂、吸湿剂；
(4)调节pH至7～9；
(5)搅拌条件下加入表面活性剂和柠檬提取液；
(6)加入二氧化钛@氮化碳量子点；
(7)待混合均匀成为均匀胶体后，静置1～3小时，得到淡白色透明的甲醛清除液。
8.根据权利要求7所述的一种室内甲醛清除剂的制备方法，其特征在于：步骤(1)及(3)-(5)搅拌条件为：在30～60℃下，搅拌速度600-1000r/min，搅拌反应6-12小时。
9.根据权利要求7所述的一种室内甲醛清除剂的制备方法，其特征在于：步骤(4)中将pH调节至7～8。
10.根据权利要求7所述的一种室内甲醛清除剂的制备方法，其特征在于：步骤(6)为在超声条件下加入二氧化钛@氮化碳量子点。