CN114058219A - 一种具有长效除醛抗菌消臭的多功能型净化涂层 - Google Patents
一种具有长效除醛抗菌消臭的多功能型净化涂层 Download PDFInfo
- Publication number
- CN114058219A CN114058219A CN202111492482.3A CN202111492482A CN114058219A CN 114058219 A CN114058219 A CN 114058219A CN 202111492482 A CN202111492482 A CN 202111492482A CN 114058219 A CN114058219 A CN 114058219A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- coating
- multifunctional
- long
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有长效除醛抗菌消臭的多功能型净化涂层，涉及墙面打底技术领域，为解决现有的涂料在表面作为涂层避免磨损脱落的前提下保证室内空气环境质量洁净健康的问题。所述多功能型净化涂层包括纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2‑苯丙异噻唑啉‑3‑酮、苯丙乳液、季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，其中：各组分的重量份数比如下：纳米氧化锌200份、硅藻土30份、纳米二氧化钛粉2份、滑石粉100份、负离子5份、轻钙粉80份、咪唑烷酮200份、无机银抗菌粉5份、高强淀粉胶粉20份、425号白色硅酸盐水泥30份，苯丙乳液10‑12份。
Description
技术领域
本发明涉及墙面打底技术领域，具体为一种具有长效除醛抗菌消臭的多功能型净化涂层。
背景技术
墙面打底一般是指对砌筑的砖墙或浇筑的砼墙进行表面找平处理，再刮与涂料层能紧密结合的腻子，再进分表面喷涂或粉刷做最后饰面，其中腻子粉是平整墙体表面的一种装饰性质的材料，是一种厚浆状涂料，是涂料粉刷前必不可少的一种产品，涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷，采用少量漆基、助剂、大量填料及适量的着色颜料配制而成，填料主要是重碳酸钙、滑石粉等。可填补局部有凹陷的工作表面，也可在全部表面刮除，通常是在底漆层干透后，施涂于底漆层表面，要求附着性好、烘烤过程中不产生裂纹。
但是，现有技术单方面添加负离子且多用于表面涂层，极易脱落掉粉反而通过空气吸入肺部易造成肺部结节，另外除甲醛等药水中大部分会含有纳米级材料的添加，常规负载于家具墙壁表面一样干燥后极易脱落被吸入后很难被分解或被肾脏排出，大多积累于肺部或通过血液带入肾脏累积，另外一些成膜型材料对一些家具表面极易造成二次污染，本发明不伤家具，不用空气净化机即可达到促使粉尘通过负离子所带负电荷的作用使得一些大分子异味以及pm2.5一类粉尘沉降，无需用电，应用于最传统的墙体顶部底部基材即可达到净化烟味霉味等各类游离态气味的功能，并对游离态甲醛等空气污染气体进行捕捉分解，因此不满足现有的需求，对此我们提出了一种具有长效除醛抗菌消臭的多功能型净化涂层。
发明内容
本发明的目的在于提供一种具有长效除醛抗菌消臭的多功能型净化涂层，以解决上述背景技术中提出的涂料在表面作为涂层避免磨损脱落的前提下保证室内空气环境质量洁净健康的问题。
为实现上述目的，本发明提供如下技术方案：一种具有长效除醛抗菌消臭的多功能型净化涂层，所述多功能型净化涂层包括纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2-苯丙异噻唑啉-3-酮、苯丙乳液、季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，其中：
各组分的重量份数比如下：纳米氧化锌200份、硅藻土30份、纳米二氧化钛粉2份、滑石粉100份、负离子5份、轻钙粉80份、咪唑烷酮200份、无机银抗菌粉5份、高强淀粉胶粉20份、425号白色硅酸盐水泥30份，苯丙乳液10-12份。
优选的，所述具有长效除醛抗菌消臭的多功能型净化涂层的加工方法：
步骤一、将纯净水加入至搅拌釜中，启动分散机，转速为200r/min，加入季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，搅拌5min，直至完全溶解且透明无颗粒；
步骤二、搅拌状态下缓慢加入纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2-苯丙异噻唑啉-3-酮和苯丙乳液，并不断提高分散机转速至1000r/min，高速分散30min；
步骤三、关闭分散机，对混合物料进行过滤，最后包装出料。
优选的，所述高强淀粉胶粉的制备工艺包括将玉米淀粉和氢氧化钠在捏合剂中充分混合,然后分别加入醚化剂、氧化剂、复合交联剂并分别反应一段时间，冷却并粉碎过筛即得产品。
优选的，所述季铵盐类稳定剂占多功能型净化涂层总量的0.3-0.6％。
优选的，所述丙烯酸铵盐类分散剂占多功能型净化涂层总量的0.3-1.2％。
优选的，所述纤维素醚占多功能型净化涂层总量的0.2-0.4％。
优选的，所述1，2-苯丙异噻唑啉-3-酮占多功能型净化涂层总量的0.1-0.3％。
优选的，所述原料与纯净水的质量比为1:0.8。
优选的，所述高强淀粉胶粉的制备工艺中氧化剂、交联剂皆为化学纯。
与现有技术相比，本发明的有益效果是：
1、本发明做于墙面抹平打底，传统净化材料用于表面容易出现脱粉等情况，用于打底找平的腻子规避了以上缺点，并且材料抗菌避免了细菌滋生引起的发霉，干燥时可将吸收存储的湿气释放，墙体或空气潮湿时吸收多余湿气，调节空气湿度，纳米二氧化钛、纳米氧化锌比表面积大，对于空气中接触到的异味分子能起很好的捕捉效果，在咪唑烷酮这类虽然属于比较传统和早期配方中使用，也被应用于一些胶水材料添加，常用来作为甲醛反应剂主要材料之一，负离子通过负离子电荷作用主被动净化空气，因其使用于墙体基层，不影响墙体外表面使用乳胶漆硅藻泥墙纸等使用，增加了纳米材料的应用，直接在物理上解决了传统涂料在表面作用涂层的磨损脱落等问题，避免传统除醛材料对表面乳胶漆或家居用品表面造成的影响，不易被人体吸入或吸收。
2、本发明采用特制的高强淀粉胶粉为主要的粘结剂，以玉米淀粉为原料，使淀粉交联聚合，并加人粘结增强剂而得到，该胶粉为浅黄色固体粉末，具有迅速溶解于冷水的特性，且性能稳定，与425号白色硅酸盐结合后在水溶液中其活性阳离子与高强淀粉胶粉中的亲水性阴离子共同作用,进一步提高了腻子的耐水性能，作为填充料,能起到增加层面厚度,减少施工难度的效果，达到粘结强度及打磨性的平衡。
3、本发明采用选用无机银抗菌粉以及1，2-苯丙异噻唑啉-3-酮作为抗菌剂，具有较高的热稳定性，对酸、碱都较为稳定，在广泛pH值范围内均能使用，有广谱的抗微生物活性，药效高、活性持久，对各种霉菌和细菌都有广泛的致死或抑制作用，且具有气相杀菌能力。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例，
一种具有长效除醛抗菌消臭的多功能型净化涂层，所述多功能型净化涂层包括纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2-苯丙异噻唑啉-3-酮、苯丙乳液、季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，其中：
各组分的重量份数比如下：纳米氧化锌200份、硅藻土30份、纳米二氧化钛粉2份、滑石粉100份、负离子5份、轻钙粉80份、咪唑烷酮200份、无机银抗菌粉5份、高强淀粉胶粉20份、425号白色硅酸盐水泥30份，苯丙乳液10-12份。
进一步，所述具有长效除醛抗菌消臭的多功能型净化涂层的加工方法：
步骤一、将纯净水加入至搅拌釜中，启动分散机，转速为200r/min，加入季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，搅拌5min，直至完全溶解且透明无颗粒；
步骤二、搅拌状态下缓慢加入纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2-苯丙异噻唑啉-3-酮和苯丙乳液，并不断提高分散机转速至1000r/min，高速分散30min；
步骤三、关闭分散机，对混合物料进行过滤，最后包装出料。
进一步，所述高强淀粉胶粉的制备工艺包括将玉米淀粉和氢氧化钠在捏合剂中充分混合,然后分别加入醚化剂、氧化剂、复合交联剂并分别反应一段时间，冷却并粉碎过筛即得产品。
进一步，所述季铵盐类稳定剂占多功能型净化涂层总量的0.3-0.6％。
进一步，所述丙烯酸铵盐类分散剂占多功能型净化涂层总量的0.3-1.2％。
进一步，所述纤维素醚占多功能型净化涂层总量的0.2-0.4％。
进一步，所述1，2-苯丙异噻唑啉-3-酮占多功能型净化涂层总量的0.1-0.3％。
进一步，所述原料与纯净水的质量比为1:0.8。
进一步，所述高强淀粉胶粉的制备工艺中氧化剂、交联剂皆为化学纯。
表1物理参数：
| 项数 | JC/T3049—1998标准 | 检测结果 |
| 容器中的状态 | 无结块、均匀 | 无结块、均匀 |
| 施工性 | 涂刮无障碍 | 涂刮无障碍 |
| 表干时间(h) | ＜5 | 3 |
| 实干时间(h) | ＜24 | 14 |
| 打磨性(％) | 20-80 | 50 |
| 耐水性(48h) | 无异常 | 无异常 |
| 耐碱性(24h) | 无异常 | 无异常 |
| 粘结强度(MPa) | ＞0.25 | 0.42 |
| 低储存稳定性 | 无起跑、裂纹、脱落 | 无起跑、裂纹、脱落 |
| 热储存稳定性 | 无起跑、裂纹、脱落 | 无起跑、裂纹、脱落 |
| 耐沾污性(％) | ≤20 | 13 |
| 耐洗刷性(次) | ≥1000 | 7000 |
| 耐温变性(10次) | 无起跑、裂纹、脱落 | 无起跑、裂纹、脱落 |
表2有害物限量参数：
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明，因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (9)
1.一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述多功能型净化涂层包括纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2-苯丙异噻唑啉-3-酮、苯丙乳液、季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，其中：
各组分的重量份数比如下：纳米氧化锌200份、硅藻土30份、纳米二氧化钛粉2份、滑石粉100份、负离子5份、轻钙粉80份、咪唑烷酮200份、无机银抗菌粉5份、高强淀粉胶粉20份、425号白色硅酸盐水泥30份，苯丙乳液10-12份。
2.根据权利要求1所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述具有长效除醛抗菌消臭的多功能型净化涂层的加工方法：
步骤一、将纯净水加入至搅拌釜中，启动分散机，转速为200r/min，加入季铵盐类稳定剂、丙烯酸铵盐类分散剂和纤维素醚，搅拌5min，直至完全溶解且透明无颗粒；
步骤二、搅拌状态下缓慢加入纳米氧化锌、硅藻土、纳米二氧化钛粉、滑石粉、负离子、轻钙粉、咪唑烷酮、无机银抗菌粉、高强淀粉胶粉、425号白色硅酸盐水泥、1，2-苯丙异噻唑啉-3-酮和苯丙乳液，并不断提高分散机转速至1000r/min，高速分散30min；
步骤三、关闭分散机，对混合物料进行过滤，最后包装出料。
3.根据权利要求2所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述高强淀粉胶粉的制备工艺包括将玉米淀粉和氢氧化钠在捏合剂中充分混合,然后分别加入醚化剂、氧化剂、复合交联剂并分别反应一段时间，冷却并粉碎过筛即得产品。
4.根据权利要求1所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述季铵盐类稳定剂占多功能型净化涂层总量的0.3-0.6％。
5.根据权利要求1所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述丙烯酸铵盐类分散剂占多功能型净化涂层总量的0.3-1.2％。
6.根据权利要求1所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述纤维素醚占多功能型净化涂层总量的0.2-0.4％。
7.根据权利要求1所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述1，2-苯丙异噻唑啉-3-酮占多功能型净化涂层总量的0.1-0.3％。
8.根据权利要求2所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述原料与纯净水的质量比为1:0.8。
9.根据权利要求3所述的一种具有长效除醛抗菌消臭的多功能型净化涂层，其特征在于：所述高强淀粉胶粉的制备工艺中氧化剂、交联剂皆为化学纯。